• Journal of Welding and Joining
• /
• v.34 no.6
• /
• pp.62-68
• /
• 2016

Laser welding has superior characteristic such as low distortion, high welding speed, easy automation and real time control. But it is easy to occur weld defects such as porosity, crater, humping bead in the area of welding start and end. These weld defects can be suppressed by applying the wave shape control. In this study CW fiber laser was used for welding of $0.5mm^t$ pure titanium. Penetration properties were evaluated with the time of slope up and down. After then the bead shape was observed, and the maximum depth and the area of crater were measured. The bead shape of welding start area changed to be sharp with increase of slope up time and non-weld area of welding start increased. The crater and humping bead were suppressed with slope down time. The cooling rate of crater area was understood through measure of the hardness. Also, The distribution tendency of alloying elements was observed by EPMA and EDS. When wave shape control didn't applied to weld, the hardness of end weld increased due to rapid cooling rate and the hardness of rear part in the crater was higher than that of fore part. On the other hand, when the wave shape control was used for end weld, the increase of hardness in the end weld couldn't be found due to gradual cooling rate.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.2
• /
• pp.344-350
• /
• 2010

The improved photocatalytic performance of a carbon/$TiO_2$ composite was studied for the Bisphenol A (BPA) decomposition. Titanium tetraisopropoxide (TTIP) and a rice husk from Korea were heterogeneously mixed as the titanium and carbon sources, respectively, for 3 h at room temperature, and then thermally treated at $600^{\circ}C$ for 1 h in $H_2$ gas. The transmission electron microscopy (TEM) images revealed that the bulk carbon partially covered the $TiO_2$ particles, and the amount that was covered increased with the addition of the rice husk. The acquired carbon/$TiO_2$ composite exhibited an anatase structure and a novel peak at $2{\theta}=32^{\circ}$, which was assigned to bulk carbon. The specific surface area was significantly enhanced to 123~164 $m^2/g$ in the carbon/$TiO_2$ composite, compared to $32.43m^2/g$ for the pure $TiO_2$. The X-ray photoelectron spectroscopy (XPS) results showed that the Ti-O bond was weaker in the carbon/$TiO_2$ composite than in the pure $TiO_2$, resulting in an easier electron transition from the Ti valence band to the conduction band. The carbon/$TiO_2$ composite absorbed over the whole UV-visible range, whereas the absorption band in the pure$TiO_2$ was only observed in the UV range. These results agreed well with an electrostatic force microscopy (EFM) study that showed that the electrons were rapidly transferred to the surface of the carbon/$TiO_2$ composite compared to the pure $TiO_2$. The photocatalytic performance of the BPA removal was optimized at a Ti:C ratio of 9.5:0.5, and this photocatalytic composite completely decomposed 10.0 ppm BPA after 210 min, whereas the pure $TiO_2$ achieved no more than 50% decomposition under any conditions.

• The Journal of Korean Academy of Prosthodontics
• /
• v.44 no.1
• /
• pp.112-123
• /
• 2006

Purpose: The biocompatibility and bio-adhesive property of a dental implant abutment are important for proper soft tissue healing and maintenance of osseointegration of implant. However, studies of soft tissue healing and mucosal attachment of various materials of implant abutment other than titanium are still needed. In this study, cell attachment, proliferation, cytotoxicity of human gingival fibroblast for ceramic, gold alloy, Ni-Cr alloy and, commercially available pure titanium as a control were evaluated, using MTS and scanning electron microscopy. Materials and Methods: Specimen was designed to disc, 4mm diameter and 1mm thickness, made of ceramic, gold alloy, Ni-Cr alloy and commercially available pure titanium. Primary culture of human gingival fibroblasts were grown in Dulbecco's modified Eagle's medium with 10% fetal bovine serum and 1% antibiotics. Cells were inoculated in the multiwell plates placed the specimen disc. Cell Titer 96 AQucous One Solution Cell Proliferation Assay were done after 1hour 3hours, 24hours, 3days, 5days of incubation. The discs were processed for scanning electron micrography to evaluate cell attachment and morphologic change. Results: The results were obtained as fellows. 1. The ceramic showed high cell attachment and proliferation and low cytotoxicity, which is as much bioadhesive and biocompatible as titanium. 2. The gold alloy represented limited proliferation of human gingival fibroblast and the highest cytotoxicity among tested materials (p<0.05). 3. The Ni-Cr alloy limited the proliferaion of the human gingival fibroblast compared to titanium(p<0.05) but cytotoxicity on the bottom of well was not so considerable, compared to titanium. 4. On the scanning electron micrographs , the ceramic showed good attachment and proliferation of human gingival fibroblast, which was similar to titanium. But gold alloy and Ni-Cr alloy showed the shrinkage of gingival fibroblast both after 24 hours and 3 days. On 5th day, small amount of the human gingival fibroblast proliferation was observed on the Ni-Cr alloy, while the shrinkage of gingival fibroblast was still observed on the gold alloy. Conclusions: These results suggest that the ceramic abutment is as biocompatible as titanium to make proper mucosal seal. The gold alloy has a high cytotoxicity to limit proliferation of gingival fibroblast, which suggest limited use on the anterior tooth where soft tissue healing is recommeded.

• Korean Journal of Materials Research
• /
• v.23 no.4
• /
• pp.240-245
• /
• 2013

Electrochemical surface treatment is commonly used to form a thin, rough, and porous oxidation layer on the surface of titanium. The purpose of this study was to investigate the formation of nanotubular titanium oxide arrays during short anodization processing. The specimen used in this study was 99.9% pure cp-Ti (ASTM Grade II) in the form of a disc with diameter of 15 mm and a thickness of 1 mm. A DC power supplier was used with the anodizing apparatus, and the titanium specimen and the platinum plate ($3mm{\times}4mm{\times}0.1mm$) were connected to an anode and cathode, respectively. The progressive formation of $TiO_2$ nanotubes was observed with FE-SEM (Field Emission Scanning Electron Microscopy). Highly ordered $TiO_2$ nanotubes were formed at a potential of 20 V in a solution of 1M $H_3PO_4$ + 1.5 wt.% HF for 10 minutes, corresponding with steady state processing. The diameters and the closed ends of $TiO_2$ nanotubes measured at a value of 50 cumulative percent were 100 nm and 120 nm, respectively. The $TiO_2$ nanotubes had lengths of 500 nm. As the anodization processing reached 10 minutes, the frequency distribution for the diameters and the closed ends of the $TiO_2$ nanotubes was gradually reduced. Short anodization processing for $TiO_2$ nanotubes of within 10 minutes was established.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.12 no.3
• /
• pp.1105-1110
• /
• 2011

After pure titanium Ingot(G2) with 400mm in diameter was manufactured, the analysis of its ingredients showed that the oxygen content was 0.073wt% and the iron content was 0.03wt%, which made ASTM Gr.2 standardization satisfactory. The processed titanium ingot produced 42mm wire rod, and hot rolling of 18th phase produced 9mm wire rod. The hardness analysis of 15.8mm wire rod, which was processed in hot rolling of 10th phase from the surface to the center, resulted in almost constant value with Hv150~200. The last 9mm wire rod had a different yield strength and elongation percentage depending on the temperature as it was led in to a hot roller. However, tensile strength revealed an approximate value and made ASTM B863 standardization satisfactory.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.33 no.2
• /
• pp.205-211
• /
• 2013

This paper studies on mechanical properties, fractures, and ultrasonic characteristics of Pure Titanium welds using ultrasonic attenuation. Ti specimen was made by using AR purge gas. When the titanium weld specimen is fractured, Tensile tests were conducted in order to observe the ultrasonic signal changes. A scanning electron microscope(SEM) was used to observe changes in failure surface and an ultrasonic normal probe with the central frequency of 4 MHz was used to obtain ultrasonic signals. As a result, the value of the mechanical properties in the weld zone was lower than that in the base zone and heat affected zone(HAZ) from Ti. Also the grain size in the weld zone was bigger than that in the weld zone and HAZ from Ti. Ultrasonic signals using a RMS method presents correlation between envelope area and the tensile strength. Consequently, the ultrasonic method could be potential tool for integrity evaluation of the Ti weld zone.

• Journal of Powder Materials
• /
• v.17 no.5
• /
• pp.365-372
• /
• 2010

The evolution of sinterability, microstructure and mechanical properties for the spark plasma sintered(SPS) Ti from commercial pure titanium(CP-Ti) was studied. The densification of titanium with 200 mesh and 400 mesh pass powder was achieved by SPS at $750{\sim}1100^{\circ}C$ under 10 MPa pressure and the flowing $H_2$+Ar mixed gas atmosphere. The microstructure of Ti sintered up to $800^{\circ}C$ consisted of equiaxed grains. In contrast, the growth of large elongated grains was shown in sintered bodies at $900^{\circ}C$ with the 400 mesh pass powder and the lamella grains microstructure had been developed by increasing sintering temperature. The Vickers hardness of 240~270 HV and biaxial strength of 320~340 MPa were found for the specimen prepared at $950^{\circ}C$.

• Resources Recycling
• /
• v.28 no.5
• /
• pp.68-73
• /
• 2019

Ilmenite is one of the principal ores for the production of titanium dioxide. To produce titanium dioxide with purity higher than 99.9% from ilmenite, Ti(IV) should be separated from the dissolved impurities such as Fe(III), Si(IV), and Mn(II) present in ilmenite. In this work, a hydrometallurgical process was investigated to recover pure titanium dioxide from ilmenite by HCl leaching followed by separation and hydrolysis of Ti(IV). An optimum leaching condition was obtained by investigating the effect of HCl concentration, pulp density, and leaching time on the leaching percentage of Ti(IV), Fe(III), Si(IV), and Mn(II). Ammonium hydroxide and sodium hydroxide solutions were employed as neutralizing agents to hydrolyze Ti(IV) from the stripping solution of Ti(IV). Titanium dioxide of the anatase phase was obtained by calcination of the hydrolyzed precipitates with $NH_4OH$ solution. A hydrometallurgical process can be developed to produce pure $TiO_2$ powders from ilmenite.

• Journal of Periodontal and Implant Science
• /
• v.35 no.4
• /
• pp.851-861
• /
• 2005

The nature of the implant surface can directly influence cellular response, ultimately affecting the rate and quality of new bone tissue formation. The aim of this in vitro study was to investigate if human osteoblast-like cells, Saos-2, would respond differently when plated on disks of magnesium titanate and machined titanium. Magnesium titanate disks were prepared using Micro Arc Oxidation(MAO) methods. Control samples were machined commercially pure titanium disks. The cell adhesion, proliferation and differentiation were evaluated by measuring cell number, and alkaline phosphatase(ALPase) activity at 1 day and 6 day after plating on the titanium disks. Measurement of cell number and ALPase activity in Saos-2 cells at 1 day did not demonstrate any difference between machined titanium and magnesium titanate. When compared to machined titanium disks, the number of cells was reduced on the magnesium titanate disks at 6 day, while ALPase activity was more pronounced on the magnesium titanate. Enhanced differentiation of cells grown on magnesium titanate samples was indicated by decreased cell proliferation and increased ALPase activity.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.306-306
• /
• 2007

The surface was transformed to porous titanium oxide by the anodization of pure titanium. Titanium was anodized in non-aqueous and aqueous electrolytes at different potentials between 5 V and 150 V. Various electrolytes were compose of ethylene glycerol, $H_2SO_4,\;NH_4F\;and\;H_2O$. We obtained titania nanotube arrays on the micro pore of titanium. Micro pores and nano tubes were obtained by anodization at high potentials and low potentials, respectively. Morphologies of nanotubes and micro pore were characterized by FE-SEM. The unique surface structure is very attractive to electrical and medical applications such as gas sensor, biosensor, dental implant and stent.