GaN thin fan were grown by spin coated colloidal GaOOH precursor. Polycrystalline GaNs with crystalline size of $10{\sim}100nm$ were grown on $SiO_2$ substrate. The shape of crystallite above $900^{\circ}C$ had the hexagonal plate and column type. X-ray diffraction patterns for them correspond to those of the hexagonal wurtzite GaN. With increasing droplets. i.e, thickness of deposited layers, XRD intensity increased. PL (photoluminescence) spectrum consisted with an weak near band-edge emission at 3.45 eV and a broad donor-acceptor emission band at 3.32 eV. From the low temperature PL measurement on GaN grown at $800^{\circ}C$ that the shallow donor-acceptor recombination induced emission was more intense than the near band-edge excitonic emission.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.3
• /
• pp.222-227
• /
• 2010

ZnO nanorods array have been grown on the seed crystal coated Si(100) substrate by hydrothermal method. The growth, structural and optical properties of ZnO nanorods array were investigated with a variation of precursor concentration from 0.01 M to 0.04 M. The array density of grown ZnO nanorods per same area was increased with increasing the concentration of precursor solution. Vertically aligned ZnO nanorods with hexagonal wurtzite structure have highly preferred c-axis orientation along (002) lattice plane. Especially, ZnO nanorods array developed from 0.04 M precursor solution showed a diameter of about 85 nm and length of 1.2 {\mu}m$ without any crystallographic defects. The photoluminescence spectra of ZnO nanorods from heavier precursor concentration exhibited stronger UV emission around 380 nm corresponding with near-band-edge emission.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.582-584
• /
• 2004

The light-emitting properties of poly(2-triethylgermyl-1,4-phenylenevinylene) (TEG-PPV) are compared with those of the silyl-substituted PPV homologue, poly(2-trimethylsilyl-1,4phenylenevinylene) (TMS-PPV). The precursor polymer is solution-processable. After carrying out thermal elimination on the precursor polymer film, the resulting fully conjugated polymer film was found to exhibit high thermal stability in air, and absorption that is shifted to the longer wavelength region owing to the extension of the n-conjugated system. TEG-PPV exhibits efficient green light emission; the maximum PL emission of a TEG-PPV thin film was found to be at 515 nm. The HOMO and LUMO energy levels were also determined using photo-emission spectroscopy. The performance of the TEG-PPV EL device was found to be comparable to that of the TMS-PPV device.

• Journal of the Korean Vacuum Society
• /
• v.19 no.6
• /
• pp.483-488
• /
• 2010

ZnO nano-fibrous thin films with various precursor concentrations ranging from 0.2 to 1.0 mol (M) were grown by spin-coating method and effects of the precursor concentration on surface and optical properties of the ZnO nano-ribrous thin films were investigated by using scanning electron microscopy (SEM) and photoluminescence (PL). ZnO nuclei were formed at the precursor concentration below 0.4 M and the ZnO nano-fibrous thin films were grown at the precursor concentration above 0.6 M. Further increase in the precursor concentration, the thickness of the ZnO nano-fibrous thin films is gradually increased. The intensity and the full-width at half-maximum (FWHM) of the near-band-edge emission (NBE) is increased as the precursor concentration is increased. The deep-level emission (DLE) is red-shifted as the precursor concentration is increased.

• Bulletin of the Korean Chemical Society
• /
• v.16 no.11
• /
• pp.1089-1093
• /
• 1995

The p-xylyl radical has been produced in a jet from the precursor p-xylene with a corona excited supersonic expansion. Rotationally cooled vibronic emission spectra in the transition of 12A2→12B2 of the p-xylyl radical have been recorded using a Fourier transform spectrometer. The spectra were analyzed on the basis of the known vibrational frequencies and the bandshapes given by the rotational selection rules.

• Bulletin of the Korean Chemical Society
• /
• v.30 no.1
• /
• pp.114-118
• /
• 2009

A new Zn/O single source precursor, TMEDA-Zn$(eacac)_2$, has been synthesized by using N, N, N’, N’-tetramethylethylendiamine (TMEDA), sodium ethyl-acetoacetate, and $ZnCl_2$. From this organometallic precursor, ZnO thin films have been successfully grown on Si (100) substrates through the metal organic chemical vapor deposition (MOCVD) method at relatively mild conditions in the temperature range of 390~430 ${^{\circ}C}$. The synthesized ZnO films have been found to possess average grain sizes of about 70 nm with an orientation along the c-axis. The precursor and ZnO films are characterized through infrared spectroscopy, nuclear magnetic resonance spectroscopy, EI-FAB-spectroscopy, elemental analyses, thermal analysis, X-ray diffraction, and field emission scanning electron microscopic analyses.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.6
• /
• pp.1993-1996
• /
• 2011

The vibronically well-resolved emission spectrum was recorded from the corona discharge of precursor 2,3,4-trifluorotoluene in a corona excited supersonic expansion with a pinhole-type glass nozzle using a long-path monochromator in the visible region. From the analysis of the observed spectrum, we found the evidence of the presence of the difluorobenzyl radicals in the corona discharge of the precursor. A possible mechanism is proposed for the formation of difluorobenzyl radicals in the gas phase on the basis of the observed emission intensity of the difluorobenzyl radicals produced.

• Current Photovoltaic Research
• /
• v.1 no.2
• /
• pp.115-121
• /
• 2013

ZnO film has been used for CIGS solar cells as a buffer layer as itself or by doping Mg and Sn; ZnO film also has been used as a transparent conducting layer by doping Al or B for solar cells. Since ZnO itself is a host material for many applications it is necessary to understand the electrical and optical properties of ZnO film itself with various preparation conditions. We prepared ZnO films by converting ZnS precursor into ZnO film by thermal annealing. ZnO film was formed at low temperature as low as $500^{\circ}C$ by annealing a ZnS precursor layer in air. In the air annealing, the electrical resistivity decreased monotonically with increasing annealing temperature; the intensity of the green photoluminescence at 505 nm increased up to $750^{\circ}C$ annealing. The electrical resistivity further decreased and the intensity of green emission also increased in reducing atmospheres. The results suggest that deep-level defects originated by oxygen vacancy enhanced green emission, which reduce light transmittance and enhance the recombination of electrons in conduction band and holes in valence. More oxidizing environment is necessary to obtain defect-free ZnO film for higher transparency.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.1
• /
• pp.33-37
• /
• 2013

In this research, we investigated the effect of mole concentration of precursor on morphological, structural and optical properties of ZnO nanorods. ZnO nanorods were hydrothermally grown on c-plane sapphire substrates in aqueous solution which contains zinc nitrate hexahydrate and hexamethylenetetramine at 90oC in the precursor range of 0.01 M to 0.025 M. With the increase of mole concentration, length and diameter of ZnO nanorods increased. In all the conditions, the growth direction of rods was longitudinally c-axis direction. From the strong emission peak at 380 nm of PL spectra at room temperature, we could confirm that the crystal quality of ZnO nanorods is good to emit radiative recombination spectra.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.65 no.11
• /
• pp.1835-1839
• /
• 2016

In this study, ZnO nanorods were grown by a hydrothermal method. $SiO_2/Si$ wafers and glass were used as substrates. ~20 nm-thick ZnO thin films were rf magnetron sputtered for seed layers. The precursor was prepared by mixing zinc nitrate hexahydrate and hexamethylenetetramine (hexamine) in DI water. The concentration of zinc nitrate hexahydrate was fixed at 0.05 mol, and that of hexamine was varied between 0 mol to 0.1 mol. The reactor containing substrates and precursor was put in an oven maintained at $90^{\circ}C$ for 1 h. X-ray diffraction was carried out to analyze the crystallinity of ZnO nanorods, and a field emission scanning electron microscope was employed to observe the morphology of nanorods. Transmittance and absorbance were measured by a UV-Vis spectrophotometer. Photoluminescence measurements were conducted using 266 nm light.