• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.7
• /
• pp.432-436
• /
• 2017

IZO transistors with $Al_2O_3$ as gate dielectrics have been investigated. To improve permittivity in an ambient dielectric layer, we grew $Al_2O_3$ by atomic layer deposition directly onto the substrates. Then, we prepared IZO semiconductor solutions with 0.1 M indium nitrate hydrate [$In(NO_3)_3{\cdot}xH_2O$] and 0.1 M zinc acetate dehydrate [$Zn(CH_3COO)_2{\cdot}2H_2O$] as precursor solutions; the IZO solution made with a molar ratio of 7:3 was then prepared. It has been found that these oxide transistors exhibit low operating voltage, good turn-on voltage, and an average field-effect mobility of $0.90cm^2/Vs$ in ambient conditions. Studies of low-voltage driving of IZO transistors with atomic layer-deposited high-k $Al_2O_3$ as gate dielectric provide data of relevance for the potential use of these materials and this technology in transparent display devices and displays.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.12
• /
• pp.812-816
• /
• 2017

$Fe_3O_4$ was prepared on the $TiO_2-coated$ natural mica substrate. The natural mica has an average particle size of $22{\mu}m$. The substrate was coated on $TiO_2$ thin films using hydrothermal synthesis at pH 1.5-2.5 at $75^{\circ}C$. The Fe precursor solution was prepared by mixing $FeSO_4$ (for $Fe^{2+}$ ion) and $FeCl_3$ (for $Fe^{3+}$ ions) with different molar ratios such as 1/2, 1/1, 2/1, 3/0, and $Fe_3O_4$ only. X-ray diffraction analysis shows that the crystal structure depends on the $FeCl_3-to-FeSO_4$ molar ratio. $Fe_3O_4$ crystal phase could be obtained at higher $FeSO_4$ contents.

• Food Science and Biotechnology
• /
• v.15 no.6
• /
• pp.838-843
• /
• 2006

The chemical processes involved in the formation of green pigment in crushed garlic cloves were investigated based on the principle of pink pigmentation in macerated onions. Intact greening and non-greening garlic cloves were either left untreated or heated at $90^{\circ}C$ for 3 min to inactivate enzyme activities. First, a colorless ether soluble compound referred to as color developer reacted with glycine (among all free amino acids) in garlic to form a second compound insoluble in ether. The latter compound then reacted with formaldehyde to yield the green colored pigment. Alliinase activity was necessary for the production of color developer and for the development of green pigment. In greening garlic that had been heat treated, green pigmentation did not proceed due to the heat-inactivation of alliinase, but the addition of alliinase solution into the garlic homogenates restored the pigmentation. However, this phenomenon was not observed in non-greening garlic with or without heat treatment. Finally, the mechanism of green pigment formation in crushed garlicis similar to that of pink pigment formation in macerated onions.

• Clean Technology
• /
• v.23 no.3
• /
• pp.314-324
• /
• 2017

To verify the viability of Co, Ru and Zr-based catalyst for $CO_2$ (dry) reforming reaction, catalysts were fabricated using cordierite, silicon carbide and rota monolithic substrates, and they were compared with the conventional $Co-Ru-Zr/SiO_2$ catalyst in terms of performance and durability. Cordierite monolith was showed high activity with the least amount of active component. In addition, when Cordierite monolith was coated with Co-Ru-Zr in various ways, most excellent performance was showed at a precursor solution coating method. In particular, when 0.9 wt% Co-Ru-Zr/Cordierite was used for reaction, it was observed that 95% $CO_2$ conversion was maintained for 300 h at $900^{\circ}C$.

• Journal of Ginseng Research
• /
• v.20 no.1
• /
• pp.54-59
• /
• 1996

Red Ginseng extracts sol'n was sterilized at 85f for 20 mins and/or stored at 4$0^{\circ}C$ for 6 months and centrifuged for 20 mins at 8,500xg in order to investigate the changes in chemical components of supernatants and the properties of precipitates. Contents of crude saponin and ginsenoside-$Rb_1$, -$Rg_1$, -Re were partially decreased during heating and storage. Starch contents were decreased from 26.81% in red ginseng extracts to 17.50-8.81% in supernatants, whereas free sugar contents were increased from 15.50% to 20.29~21.35% by heating and storage. The contents of protein and minerals in supernatants were decreased, but acidic polysaccharides and polyphenol compounds were not changed. pH values of supernatants and precipitates were decreased. The absorbances of brown color precursor and brown pigment in precipitates, detected at 285 nm and 440 nm were remarkably increased. The Overa11 data suggest that precipitates in red ginseng extracts sol'n formed during steilization and storage are provably the brown pigments resulting from Maillard reaction of amino compounds with reducing sugar which could be released from starch and protein matrix and $Cu^+$, $Ca^{2+}$ and $Fe^{3+}$ ions are implicated with the reaction incorporated.

• Journal of Sensor Science and Technology
• /
• v.26 no.6
• /
• pp.414-419
• /
• 2017

The optical characteristics of cresol red, phenol red, and neutral red immobilized in the thin film were investigated with absorbance measurement in order to find a sensing part of a fiber-optic pH sensor. Sol-Gel method with tetramethyl orthosilicate as a precursor was used to immobilize the pH indicators in the thin film. The absorbance spectra were measured when pH indicators were immobilized in the film and were dissolved in the buffer solution. Experimental results showed that the absorbance spectra could be changed when the pH indicator is immobilized in the thin film. As compared with other pH indicators, the neutral red exhibited similar absorbance spectra regardless of physical conditions and was sensitive over whole pH range between 4 and 11. In addition, the absorbance ratio of base peak to acid peak tended to increase in proportion to the increase in pH. Experimental results indicate that the neutral red is a good pH indicator for fabrication of a sensing part of the fiber-optic pH sensor.

• Advances in nano research
• /
• v.2 no.2
• /
• pp.77-88
• /
• 2014

Solvothermal treatment of late transition metal acetylacetonates in a novel medium composed either of pure acetophenone or acetophenone mixtures with amino alcohols offers a general approach to uniform hydrophilic metal nanoparticles with high crystallinity and low degree of aggregation. Both pure metal and mixed-metal particles can be accesses by this approach. The produced materials have been characterized by SEM-EDS, TEM, FTIR in the solid state and by Nanoparticle Tracking Analysis in solutions. The chemical mechanisms of the reactions producing nanoparticles has been followed by NMR. Carrying out the process in pure acetophenone produces palladium metal, copper metal with minor impurity of $Cu_2O$, and NiO. The synthesis starting from the mixtures of Pd and Ni acetylacetonates with up to 20 mol% of Pd, renders in minor yield the palladium-based metal alloy along with nickel oxide as the major phase. Even the synthesis starting from a mixed solution of $Cu(acac)_2$ and $Ni(acac)_2$ produces oxides as major products. The situation is improved when aminoalcohols such as 2-aminoethanol or 2-dimethylamino propanol are added to the synthesis medium. The particles in this case contain metallic elements and pairs of individual metals (not metal alloys) when produced from mixed precursor solutions in this case.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2003.10a
• /
• pp.957-962
• /
• 2003

The preparation of $Al_2$O$_3$-SiO$_2$ thin films from less than one micron to several tens of microns in thickness had been prepared from metal alkoxide sols. Two methods, dip-withdrawal and electrophoretic deposition, were employed for thin films and sheets formation. The requirements to be satisfied by the solution for preparing uniform and strong films and by the factors affecting thickness and other properties of the films were examined. for the preparation of thin, continuous $Al_2$O$_3$-SiO$_2$ films, therefore, metal-organic-derived precursor solutions contained Si and Al in a chemically polymerized form has been developed and produced in a clear liquid state. In the process of applying to substrates, this liquid left a transparent, continuous film that could be converted to crystalline $Al_2$O$_3$-SiO$_2$ upon heating to 100$0^{\circ}C$. And, a significant change of the film density took place in the crystallization process, thus leading to the strict requirements as to the film thickness, which could survive crystallization.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.167.2-167.2
• /
• 2014

In this work, ZnO shell on mesoporous $SiO_2$ ($ZnO/SiO_2$) was prepared by atomic layer deposition (ALD). Diethylzinc (DEZ) and $H_2O$ were used as precursor of ZnO shell. $ZnO/SiO_2$ sample was characterized by X-ray diffraction (XRD), N2 sorption isotherms, X-ray photoelectron spectroscopy (XPS), Scanning electron microscopy (SEM) and Fourier-transform infrared spectroscopy (FT-IR). $ZnO/SiO_2$ showed higher adsorption capacity of MB than that of bare mesoporous $SiO_2$ and the adsorption capacities of $ZnO/SiO_2$ could be regenerated by UV exposure through the photocatalytic degradation of the adsorbed MB. This system could be used for removing organic dye from water by adsorption and reused after saturation of adsorption due to its photocatalytic regeneration.

• Journal of the Korean Vacuum Society
• /
• v.17 no.2
• /
• pp.122-129
• /
• 2008

Ferroelectric properties of the PMT-PT were also studied from the temperature dependence of hysteresis loops using a method slightly modified from Sawyer-Tower's. Dielectric, pyroelectric and piezoelectric properties of the ceramics in the system PMT-PT were investigated. The resulted densities of the PMT-PT ceramics system were greater than 97 % of the theoretical value. As observed SEM micrograph of the fracture surfaces of the PMT-PT ceramics system, the average grain sizes were increased about 3-5 ${\mu}m$ to 6-8 ${\mu}m$ with increasing sintering temperature. The specimens with PT<0.30 for PMT-PT solid solution system exhibited the dielectric and pyroelectric properties of a typical relaxor ferroelectrics. The composition with the maximum dielectric constant exhibits relatively superior pyroelectric and piezoelectric properties.