• Tribology and Lubricants
• /
• 제26권2호
• /
• pp.142-148
• /
• 2010

The purpose of this study is to find how to be formed the wet film thickness during the low friction coating process for a piston skirt with application to the theory of screen printing. In other words, in this research, it is to derive the general expressions predicting the pressure under a blade and the volume of coating fluid passing through the blade edge. Using these expressions, it is to be approved that the current operation characteristics of a screen printing system to a sample blade coating process for low friction coating on a piston skirt can be quantitatively assessed.

• Corrosion Science and Technology
• /
• 제22권3호
• /
• pp.193-200
• /
• 2023

Titanium alloy (grade-4) is commonly used in industrial and medical applications. To improve its corrosion resistance and biocompatibility for medical use, it is necessary to form a titanium oxide film. In this study, the morphology of the oxide film formed by anodizing Ti-grade 4 using different electrolytes was analyzed. Wetting properties before and after surface modification with SAM coating were also observed. Electrolytes used were categorized as A, B, and C. Electrolyte A consisted of 0.3 M oxalic acid and ethylene glycol. Electrolyte B consisted of 0.1 M NH₄F and 0.1 M H₂O in ethylene glycol. Electrolyte C consisted of 0.07 M NH₄F and 1 M H₂O in ethylene glycol. Samples B and C exhibited a porous structure, while sample A formed a thickest oxide film with a droplet-like structure. AFM analysis and contact angle measurements showed that sample A with the highest roughness exhibited the best hydrophilicity. After surface modification with SAM coating, it displayed superior hydrophobicity. Despite having the thickest oxide film, sample A showed the lowest insulation resistance due to its irregular structure. On the other hand, sample C with a thick and regular porous oxide film demonstrated the highest insulation resistance.

• 설비공학논문집
• /
• 제17권5호
• /
• pp.459-467
• /
• 2005

The effect of anti freezing solution liquid film on the frost prevention is experimentally investigated. It is desirable that the antifreezing solution spreads widely on the heat exchanger surface forming thin liquid film to prevent frost nucleation and reduce the thermal resistance across the film. A porous layer coating technique is adopted to improve the wettedness of the anti freezing solution on a parallel plate heat exchanger. The antifreezing solution spreads widely on the heat exchanger surface with 100 $\mu$m thickness by the capillary force resulting from the porous structure. It is observed that the antifreezing solution liquid film prevents a parallel plate heat exchanger from frosting. The reductions of heat and mass transfer rate caused by thin liquid film are only $1\~2\%$ compared with those for non-liquid film surface.

• 한국세라믹학회지
• /
• 제44권12호
• /
• pp.733-739
• /
• 2007

NiO-YSZ anode-supported single cell was prepared by spin-coating YSZ and LSM slurries as electrolyte and cathode, respectively. Dense YSZ electrolyte film was successfully prepared on the porous NiO-YSZ anode substrate by tuning pre-sintering temperature of NiO-YSZ and co-firing temperature. The thickness of YSZ film was controlled by the solid content of slurry and coating cycles. The experimental conditions affecting on the thickness of YSZ film was discussed. Single cells with the active electrode area ${\sim}0.8\;cm^2$ were prepared by spin-coating the cathode layers of LSM-YSZ mixture and LSM consequently as well. The effects of the pre-sintering temperature and thus the microstructure of NiO-YSZ substrate on the current-voltage characteristics of co-fired cell were investigated.

• 한국세라믹학회지
• /
• 제36권8호
• /
• pp.791-798
• /
• 1999

다공성 NiO-YSZ 기판위에 전착법(EPD; Electrophoretic Deposition)법과 담금(Dip-coating)법에 의해 음극지지형 고체연료전지용 이트리아 안정화 지르코니아 박막 제조법을 연구하였다. 이를 위해 슬러리 농도 및 시간에 따른 박막의 무게, 박막의 결함 및 미세구조변화에 영향을 주는 제조조건들을 살펴 봄으로써 전착법과 담금법의 차이를 보았다. 담금법에서는 막생성 초기인 30초까지 막의 무게가 증가하지만 그 후에는 탈락이 일어나 시간을 증가하여도 막의 무게가 오히려 감소하였다. 전착법에서는 임계 인가전류 이상에서 시간에 따라 막의 무게가 증가하고 균일하고 치밀한 막이 형성하였다 전장이 매우 낮은 0.035 mA/$cm^2$ 의 정전류를 120초 이상 장시간 인가하면 막의 흘러내림(sagging)으로 인한 결함이 발생하였다. 전착법에 의해 균일하고도 치밀하게 가스 누출성이 없는 음극지지형 고체산화물 연료전지에 적합한 전해질 박막을 제조할 수 있었다.

• 한국수소및신에너지학회논문집
• /
• 제17권2호
• /
• pp.204-211
• /
• 2006

The electrolyte in the solid oxide fuel cell must be dense enough to avoid gas leakage and thin enough to reduce the ohmic resistance. In order to manufacture the thin and dense electrolyte layer, 8 mol% $Y_2O_3$ stabilized-$ZrO_2$ (8YSZ) electrolyte layers were coated on the porous tubular substrate by the novel vacuum slurry dip-coating process. The effects of the slurry concentration, presintering temperature, and vacuum pressure on the thickness and the gas permeability of the coated electrolyte layers have been examined in the vacuum slurry coating process. The vacuum-coated electrolyte layers showed very low gas permeabilities and had thin thicknesses. The single cell with the vacuum-coated electrolyte layer indicated a good performance of $495\;mW/cm^2$, 0.7 V at $700^{\circ}C$. The experimental results show that the vacuum dip-coating process is an effective method to fabricate dense thin film on the porous tubular substrate.

• Corrosion Science and Technology
• /
• 제21권4호
• /
• pp.290-299
• /
• 2022

Anodizing is an electrochemical surface treatment method conferring corrosion resistance and durability by forming a thick anodization film on the metal surface. Aluminum has a long service life and high thermal conductivity and formability, as well as excellent corrosion resistance. Aluminum 3003 alloy has improved formability, strength, and corrosion resistance due to the addition of a small amount of manganese. However, corrosion occurs in seawater and environments polluted with corrosion-inducing substances, which reduce corrosion resistance. Therefore, it is necessary to artificially form a thick anodized film to improve corrosion resistance. In this study, the anodization treatment time was 4 minutes, and voltages of 10 V, 20 V, 30 V, 40 V, 50 V, 60 V, 70 V, 80 V, 90 V, and 100 V were applied. The thickness and pore size of the oxide film increased according to the applied voltage. A barrier film was formed under voltage conditions from 10 V to 50 V, and a porous film was formed under voltage conditions from 60 V to 100 V. After anodizing, coating was applied. Wettability and corrosion resistance were observed before and after coating according to the surface shape and thickness of the oxide film.

• 한국전기전자재료학회논문지
• /
• 제28권12호
• /
• pp.821-825
• /
• 2015

Anti-reflective (AR) thin film was fabricated on a glass substrate by sol-gel method. The coating solution was synthesized with TEOS (tetraethlyorthosilicate) and poly ethylene glycol (PEG, 4.0 wt%). As the withdrawal speed of coating was changed from 0.1 mm/sec to 0.3 mm/sec, the thickness and refractive index of prepared thin films were changed. The reflectance and transmittance of coating glass fabricated by the withdrawal speed of 0.1 mm/sec were 0.62% and 95.0% in visible light range. The refractive index and thickness of single layer thin film were n= 1.29 and ca. 99.0 nm.

• 한국표면공학회지
• /
• 제30권3호
• /
• pp.183-190
• /
• 1997

Fabrication and crystallization characteristics of yttria($T_2O_3$) stabilized zirconia(YSZ) thin film by sol-gel process were studied. YSZ sol was synthesized with zirconium n-propoxide($Zr(OC_3H_7)_4)$) and yttrium nitrate pentahydrate ($Y(NO_3)_3.5H_2O$). YSZ film was prepared by depositing the polymeric sol on porous $Al_2O_3$ substrate by spin-coating, and the film characteristics were investigated by FRIR, TG-DTA, XRD, DSC, optical microscopy and SEM. The film topology was uniform and cracks were not found. It was found that the annealing temperature and the concentration of stabilizer affect the crystallization of YSZ film. The YSZ film began to crystallize from amorphous to tetragonal phase at 40$0^{\circ}C$, and it was not converted to cubic structure until $1100^{\circ}C$. It seemed that the grains were formed over $700^{\circ}C$and the average grain size was obtained about 0.2$\mu\textrm{m}$.

• 한국태양에너지학회:학술대회논문집
• /
• 한국태양에너지학회 2009년도 추계학술발표대회 논문집
• /
• pp.367-370
• /
• 2009

It is important to reduce a reflection of light as a solar cell is device that directly converts the energy of solar radiation to electrical energy in oder to improve efficiency of solar cells. The antireflection coating has proven effective in providing substantial increase in solar cell efficiency. This paper investigates the formation of thin film PSi(porous silicon) layer on the surface of crystalline silicon substrates without other ARC(antirefiection coating) layers. On the other hand the formation of $SO_{2}/SiN_x$ ARC layers on the surface of crystalline silicon substrates. After that, the structure of PSi and $SO_2/SiN_x$ ARC was investigated by SEM and reflectance. The formation of PSi layer and $SO_{2}/SiN_x$ ARC layers on the textured silicon wafer result about 5% in the wavelength region from 0.4 to $1.0{\mu}m$. It is achieved on the textured crystalline silicon solar cell that each efficiency is 14.43%, 16.01%.