• 대한치과기공학회지
• /
• 제38권3호
• /
• pp.175-183
• /
• 2016

Purpose: Observation of Oxide Film Formation and Bonding Strength according to surface treatment of Co-Cr Alloy for porcelain fused to Metal. Methods: metal specimens $0.5mm{\times}25mm{\times}4mm$ in size were made using Co-Cr alloys for porcelain fused to metal crown (Heraenium P, Tae jung Medis). Dental porcelain $0.5mm{\times}25mm{\times}4mm$ in size was sintered on the metal specimens after changing the etching time, sandblasting condition, and heat treatment temperature. Subsequently, the bonding strength was compared by the three-point flexural strength test using a universal testing machine (UTM) to observe the fracture surface and oxidized layers. Results: With regard to the experimental group treated with acid-etching, Specimen 1 treated for 25 minutes (B-3) showed the highest bonding strength, and Specimen 2 treated only with sandblasting showed the most excellent bonding force at 3.5 bar (C-3). With regard to the experimental group treated with sandblasting at 3.5 bar after acid-etching for 25 minutes, Specimen 3 with heat treatment at $980^{\circ}C$ (D-3) showed the highest bonding strength. Conclusion: The specimen which went through both sandblasting and etching, showed an excellent ceramicmetal bond strength.

• 대한의생명과학회지
• /
• 제14권2호
• /
• pp.105-113
• /
• 2008

The objective of this study was to evaluate the influence of surface modifications on the bonding characteristics and cytotoxicity of specific titanium porcelain bonded to milling titanium and cast titanium. Milling titanium and cast titanium samples were divided into 8 test groups. These groups are as follow: i) sandblasted with particles of different size of $220{\mu}m\;and\;50{\mu}m$, ii) different sequences of sandblasting treatment and etching treatment, iii) etched with different etching solutions, and iv) preheated or not. The surface characteristics of specimens were characterized by the test of mean roughness of surface and SEM. The bond strength of titanium-ceramic systems was measured by using three-point bending test and SEM. The results show that the mean roughness of surface of sample sandblasted with $220{\mu}m$ aluminum oxide increased and bond strength were higher than sample sandblasted with $50{\mu}m$ aluminum oxide. The mean roughness of surface decreased, but the bond strength increased when the samples sandblasted with $220{\mu}m$ aluminum oxide were preheated. The sample sandblasted with $220{\mu}m$ aluminum oxide after oxidized with occupational corrosive agent I (50% NaOH, 10% $CuSO_4{\cdot}5H_2O$) and II (35% $HNO_3$, 5% HF) showed higher bond strength than sample oxidized with 30% $HNO_3$ after sandblasted with $220{\mu}m$ aluminum oxide. Group NaCuNF220SP (milling Ti: 35.3985 MPa, casting Ti: 37.2306 MPa) which was treated with occupational corrosive agent I (50% NaOH, 10% $CuSO_4{\cdot}5H_2O$) and II (35% $HNO_3$, 5% HF), followed by sandblasting with $220{\mu}m$ aluminum oxide and preheating at $750^{\circ}C$ for 1 hour showed the highest bond strength and significant differences (P<0.05). The method for modifying surface of titanium showed excellent stability of cells.

• The Journal of Advanced Prosthodontics
• /
• 제3권4호
• /
• pp.221-228
• /
• 2011

PURPOSE. Veneering porcelain might be delaminated from underlying zirconia-based ceramics. The aim of this study was the evaluation of the effect of different surface treatments and type of zirconia (white or colored) on shear bond strength (SBS) of zirconia core and its veneering porcelain. MATERIALS AND METHODS. Eighty zirconia disks (40 white and 40 colored; 10 mm in diameter and 4 mm thick) were treated with three different mechanical surface conditioning methods (Sandblasting with $110{\mu}m$ $Al_2O_3$ particle, grinding, sandblasting and liner application). One group had received no treatment. These disks were veneered with 3 mm thick and 5 mm diameter Cercon Ceram Kiss porcelain and SBS test was conducted (cross-head speed = 1 mm/min). Two and one way ANOVA, Tukey's HSD Past hoc, and T- test were selected to analyzed the data (${\alpha}=0.05$). RESULTS. In this study, the factor of different types of zirconia ceramics (P=.462) had no significant effect on SBS, but the factors of different surface modification techniques (P=.005) and interaction effect (P=.018) had a significant effect on SBS. Within colored zirconia group, there were no significant differences in mean SBS among the four surface treatment subgroups (P=0.183). Within white zirconia group, "Ground group" exhibited a significantly lower SBS value than "as milled" or control (P=0.001) and liner (P=.05) groups. CONCLUSION. Type of zirconia did not have any effect on bond strength between zirconia core and veneer ceramic. Surface treatment had different effects on the SBS of the different zirconia types and grinding dramatically decreased the SBS of white zirconia- porcelain.

• 대한치과보철학회지
• /
• 제56권4호
• /
• pp.269-277
• /
• 2018

목적: 본 연구는 글라스 용융침투 처리가 지르코니아와 초저온 소성 전장도재와의 전단결합강도에 미치는 영향을 평가하였다. 재료 및 방법: 표면처리 방법에 따라 대조군 (처리 안함), ZirLiner처리군 (ZL군), 글라스 용융침투처리군 (ZG군), 글라스 용융침투 후 Sandblasting 처리군 (ZGS군)으로 분류하였다 (n = 12). 모든 실험군은 초저온 소성 전장도재를 사용하여 지름 6 mm ${\times}$ 두께 3 mm가 되도록 축성하고 소성하였다. 지르코니아와 전장도재 사이의 결합강도는 만능시험기를 이용하여 측정하였고 지르코니아 시편의 결합계면, 도재파절 양상은 SEM과 EDX로 관찰하였다. 결과: 지르코니아 표면처리 방법에 따라 전장도재와의 결합강도가 ZirLiner군, 대조군, 글라스 용융침투군 순으로 나타났으나 통계학적으로 유의한 차이는 없었다 (P > .05). 글라스 용융침투 후 Sandblasting 처리군은 다른 모든 군에 비해 유의하게 낮은 전단결합강도를 보였다 (P < .05). 결론: 글라스 용융침투 지르코니아의 Sandblasting처리는 초저온 소성 전장도재와의 현저한 결합력 감소를 야기시키므로 사용이 제한되어야 할 것으로 사료된다.

• 대한치과보철학회지
• /
• 제47권1호
• /
• pp.46-52
• /
• 2009

연구목적: 최근 임플란트 상부보철물의 주재료로서 티타늄의 수요가 증가하고 있고, 급속도로 발전하고 있는 CAD/CAM (computer - aided design/computer-aided manufacturing) 기술이 접목되어 티타늄을 절삭하여 제작하는 방법이 주목을 받고 있으며 치과 임상에서 점점 그 영역이 넓어지고 있다. 다만, 하나의 티타늄괴를 절삭하여 만드는 방법의 특성상 기계적 유지력을 얻을 수 있는 비드 등을 형성할 수 없고, 통상적인 재료인 금 합금이나 도재용 합금 주조체에 비해 도재와의 결합력도 떨어지는 것이 보완해야 할 점으로 지적되고 있다. 이에 본 연구는 절삭형 티타늄을 이용한 보철물 제작에 많이 사용되고 있는 열중합 의치상 레진, 간접 복합 레진, 도재와 Grade II 순수 티타늄 사이의 결합 강도를 비교 평가해 보고자 하였다. 연구 재료 및 방법: 지름 9 mm, 높이 10 mm의 Grade II 순수 티타늄 원통형 시편 37개를 3군으로 나누어 각각 직경 7 mm, 높이 1 mm의 열중합 의치상 레진 (Lucitone 199, DENTSPLY Trubyte, York, USA), 간접 복합 레진 (Sinfony, 3M ESPE, Seefeld, Germany), 도재 (Triceram, Dentaurum, Ispringen, Germany)와 결합시켰다. 시편은 $5-55^{\circ}C$에서 1000회 열순환 처리 후, 범용 시험기 (Instron, Universal Testing Machine, Model 4465, USA)를 이용하여 1 mm/min의 속도로 하중을 가하여 전단결합강도를 측정하였다. 파절된 단면의 양상을 관찰하고 각 군별 파절양상을 조사하였다. 측정값은 one-way ANOVA와 Scheffe's multiple range test (${\alpha}=0.05$)로 분석하였다. 결과: 열중합 의치상 레진인 Lucitone 199 ($17.82{\pm}5.13\;MPa$)의 결합 강도가 가장 높았으며, 도재인 Triceram ($12.97{\pm}2.11\;MPa$), 복합레진인 Sinfony ($6.00{\pm}1.31\;MPa$) 순으로 감소하였다. Lucitone 199와 Sinfony 군의 파절 양상은 대부분이 부착성 파절인 데에 반해 Triceram 군에서는 복합성 파절이 많았다. 결론: CAD/CAM을 이용한 절삭형 티타늄 구조물 상방에 전장용 심미 재료로는 열중합형 의치상 레진이 가장 강한 결합 강도를 보인다. 기존의 주조체의 유지구 등에서 얻는 강도에 비해 약하고, 부착성 파절이 많은 점 등은 향후 이들 재료와 티타늄간의 결합력을 높이기 위한 보다 많은 연구가 이루어져야 할 것을 시사한다.

• 대한치과기공학회지
• /
• 제38권4호
• /
• pp.291-298
• /
• 2016

Purpose: This study was to evaluate the effect of coloring liquids on the shear bond strength between zirconia and veneering ceramic. Methods: Zirconia(15 mm in diameter, 2.5 mm in thickness; n=40) used in the experiment were divided into 5 groups depending on the coloring liquid. Each specimen were polished using a polishing machine(LaboPol-2, Struers, UK). A cylinder of veneering porcelain(6 mm in diameter, 3 mm in thickness) was fabricated and fired on zirconia surfaces. The shear bond strength was measured using a universal testing machine(Model 4302, Instron, USA). All data were analyzed statistically using a one-way ANOVA and Tukey's multiple comparisons test. After the shear bond test, fracture surfaces were examined by SEM. Results: Colored zirconia showed a higher shear bonding strength than that of uncolored zirconia except for colored zirconia immersed in Zirkonzahn coloring liquid. In particular, colored zirconia immersed in Kuwotech coloring liquid showed the highest shear bond strength. After the shear bond test, mixed failure patterns were mainly observed in the failure between zirconia and veneering ceramic. Conclusion: Coloring liquid enhanced the shear bond strength zirconia and veneering ceramic than uncolored zirconia.

• 대한치과기공학회지
• /
• 제35권4호
• /
• pp.271-280
• /
• 2013

Purpose: This study was to assess the effect of surface and heat treatment on the bond strength of veneering ceramics to zirconia. Methods: The specimens were divided into 7 groups according to surface treatment and heat treatment conditions prior to porcelain application. ten specimens from each group were subjected to a 3-point flexural test. In addition the influence of surface and heat treatment on surface roughness values and phase transformation of zirconia was evaluated. Statistical analysis was performed with one-way ANOVA and post hoc Tukey's test. Results: Bond strength ranged from $20.67{\pm}3.13MPa$ to $32.69{\pm}4.52$. Bond strength of surface treatment group was lower than that of control group but only $Al_2O_3$ sandblasting group was significant difference. Bond strength of heat treatment group was higher than that of surface treatment group but there was no statistical significance. Conclusion: Bond strength of veneering ceramics to zirconia was affected by surface and heat treatment.

• 대한치과보철학회지
• /
• 제49권3호
• /
• pp.191-196
• /
• 2011

연구 목적: 본 연구는 여러 가지 금속-도재 합금의 도재결합강도를 측정하여 임상에 적용하는 것이 적절한지 평가하고자 하였다. 연구 재료 및 방법: 금속도재소부 전장관으로 가장 많이 사용되는 Ni-Cr 합금(Group 1)과 75% 금합금(Group 2) 및 최근 도재금 합금으로 판매되고 있는 52.5% (Group 3), 51.5% (Group 4), 32% (Group 5), 10% 금합금(Group 6)이 시편으로 제작되었다. 시편은 각각 5개씩 제작되었으며, 제작된 시편에 전용 도재를 소성하고 3점 굴곡 시험을 통하여 도재와 각 금속간의 결합강도를 측정하였다. 결과: Group 1의 도재 결합강도가 $40.62{\pm}3.32$ MPa로 다른 실험군의 도재결합 강도에 비해 통계학적으로 유의성 있게 가장 높은 결합강도를 보였고(P<.05), 다음으로 Group 2가 $37.47{\pm}1.57$ MPa, Group 3이 $35.85{\pm}1.48$ MPa, Group 4가 $35.04{\pm}1.34$ MPa, Group 5가 $33.17{\pm}1.62$ MPa, Group 6가 $30.75{\pm}1.21$ MPa 순으로 결합강도가 감소하였다. Group 2, 3, 4 의 도재결합 강도는 Group 6와 통계학적으로 유의성을 보여주고 있으나(Duncan's test, P<.05), Group 3과 4는 Group 5와 서로 유의한 차이를 보이지 않았다(Duncan's test, P>.05). 도재 결합 강도 차이는 금 함량이 높을수록 강도가 높았고, 모든 실험군에서 ISO 9693에서 제시하는 기준치(25 MPa)보다 높은 수치를 나타내었다. 결론: 실험에 포함된 모든 합금들이 임상적으로 사용 가능할 것으로 추정된다.

• 대한치과보철학회지
• /
• 제27권1호
• /
• pp.143-179
• /
• 1989

To observe the bonding behavior of palladium-based alloys to porcelain; 1. Pd-Co binary alloy with the higher cobalt content, 2. Pd-Co binary alloy with the lower cobalt content, 3. Pd-Ag-Sn ternary alloy, 4. Pd-Ag binary alloy, 5. Pd-Cu-Au ternary alloy and 6. Pd-Cu binary alloy were made as 6 groups of experimental alloys. Each group of alloy was divided into 4 sub-groups such as one sub-group that was not degassed and three sub-groups that degassed for 5 minutes, 10 minutes and 15 minutes. On each specimen, weight changes after degassing, morphological changes of oxide layer by changing the degassing time, compositional changes at metal-ceramic interface and bond strength of metal-ceramic measured with planar shear test were observed and compared. The results of the present study allow the following conclusions to be drawn: 1. The alloy showing the greatest bond strength was Pd-Cu alloy without gold and bond strength was decreased by alloying gold to them. 2. Although Pd-Co alloy showed the most prominent oxidation behavior, bond strength of them to porcelain was not greatly high by the formation of porosities at metal-ceramic interfaces. 3. Likewise tin, cobalt formed the peaks on line profiles at metal-ceramic interface, however copper did not exhibit such peaks on line profiles. 4. Mainly, oxide layer on Pd-Co alloy was composed with cobalt, and for Pd-Co alloy with higher cobalt content the rise of bond strength was not significant by increased degassing time. 5. On Pd-Ag alloy not containing tin, during degassing for 15 minutes silver content was increased at metal-ceramic interface. 6. As an oxidized element, tin formed the oxide layers that widen their area by increasing the degassing time, while cobalt and copper showed the morphological changes of particle or crystal on oxide layer.

• 대한치과보철학회지
• /
• 제28권1호
• /
• pp.165-191
• /
• 1990

Although a number of studies have been performed to assure that residual stress caused by a mismatch of alloy porcelain thermal expansion can contribute to clinical failure of a ceramometal restoration, the interactive influence of cooling rate on the magnitude of thermal expansion difference and on bond strength between them have not been extensively analyzed. The objective of this study was to determine the influence of cooling rate and the number of firing cycles on the expansion mismatch and the flexural failure resistance of metal porcelain strip. Tested alloys included one Pd-Ag alloy, one Ni-Cr-Be alloy with two kinds of porcelain, Vita and Ceramco. Metal specimens were cast into rods with a height of 13mm and a diameter of 5mm. Subsequently, the castings were subjected to scheduled firing cycles without porcelain. And the porcelain specimens after being fired were trimmed into a bar with a final dimension of $5{\times}5{\times}25mm$. Thermal expansions of the alloys and porcelains were measured by using a push rod or a differential dialometer respecitvely. Porcelain glass transition temperatures and expansion values were derived alloy-porcelain pairs were assessed by comparing expansion values of the components at a porcelain glass transition temperature. Calculations were made using combinations of a Ni-Cr alloy or Pd-Ag alloy with each of two porcelain products. Metal-porcelain strip specimens were subjected to four point loading in an Instron testing machine until crack occured at the metal-cramic interface at the time of sharp decrease of load on recorder. On the basis of this study, the following conclusions may be stated: 1. Regardless of the kinds of ceramometal combinations, both of calculated and experimental data revealed that the double fired specimens exhibited a significantly lower flexural strength. 2. By the rise of the amount of mismatch, bond strength were decreased. 3. Thermal expansion value of Pd-Ag alloys were higher than that of Ni-Cr alloys. 4. Expansion curves of metal were proportional to the increase of temperature and were not affected by the experimental conditions, however porcelains did not show the same magnitude of metal, and a shift of the glass transition temperature to higher temperatures was observed when cooled rapidly 5. Alloy-porcelain thermal compatibility appeared more dependent on the porcelain than the alloy.