• Journal of the Korean Ceramic Society
• /
• v.49 no.6
• /
• pp.523-527
• /
• 2012

Silicon carbide (SiC) has recently drawn an enormous amount of industrial interest due to its useful mechanical properties, such as its thermal resistance, abrasion resistance and thermal conductivity at high temperatures. In this study, RF thermal plasma (PL-35 Induction Plasma, Tekna CO., Canada) was utilized for the synthesis of high-purity SiC powder from an organic precursor (hexamethyldisilazane, vinyltrimethoxysilane). It was found that the SiC powders obtained by the RF thermal plasma treatment included free carbon and amorphous silica ($SiO_2$). The SiC powders were further purified by a thermal treatment and a HF treatment, resulting in high-purity SiC nano-powder. The particle diameter of the synthesized SiC powder was less than 30 nm. Detailed properties of the microstructure, phase composition, and free carbon content were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), a thermogravimetric (TG) analysis, according to the and Brunauer-Emmett-Teller (BET) specific surface area from N2 isotherms at 77 K.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.05b
• /
• pp.11-14
• /
• 2004

In this paper, the effect of adhesion properties of semiconductive-insulating interface layer of silicone rubber on electrical properties was investigated. The modifications produced on the silicone surface by oxygen plasma were accessed using ATR-FTIR, contact angle and AFM. Adhesion was obtained from T-peel tests of semiconductive layer having different treatment durations. In addition, ac breakdown test was carried out for elucidating the change of electrical property with duration of plasma treatment. From the results, the treatment in the oxygen plasma produced a noticeable increase in surface energy, which can be mainly ascribed to the the creation of O-H and C=O. It is observed that adhesion performance was determined by not surface energy but roughness level of silicone surface. It is found that ac dielectric strength was increased with improving the adhesion between the semiconductive and insulating interface.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.12a
• /
• pp.81-86
• /
• 2006

In this paper, we designed the cylindrical type light source that had a electromagnetic principle of inductively coupled plasma, and measured its electrical-optical properties. Using the principle of transformer, electrically equivalent circuit of cylindrical type light source was analyzed. According to the parameters of electromagnetic induction which were diameter of coil with 0.3~1.2 mm, number of turns with 4~12 turns, distance with 40~120 mm and RF power with 10~150 W, the electrical and optical properties were measured. When diameter of coil was 0.3 mm, number of turns was 8 turns and distance was 40 mm, the highest brightness of 29,730 $cd/m^2$ was shown with RF power 150 W. The relationship between electromagnetic induction and plasma discharges was shown by mode transition from E-mode to H-mode.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.220-223
• /
• 2004

Inductively coupled plasma is commonly used for electrodeless lamp due to its ease of plasma generation. Optical characteristics significantly depend on the RF power and gas pressure of the plasma. This paper describes the measurement of luminance as a function of RF power and gas pressure with a goal of finding optimal operating conditions of the electrodeless lamp. The gas pressure was varied from 10[mTorr] to 300[mTorr] or 500[mTorr] and the RF power was varied from 10[W] to 200[W]. It was found that the luminance tends to be decreased when argon and neon pressure is increased, and the luminance is increased as RF power is increased. It was also found that the luminance per unit RF power is high when the argon and neon pressure is low and when the RF power is in the range of $30[W]{\sim}40[W]$ or 10[W].

• Textile Coloration and Finishing
• /
• v.6 no.4
• /
• pp.27-33
• /
• 1994

Wool fabrics were treated with low temperature oxygen plasma and/or protease, and examined for their mechanical and dyeing properties. By plasma-treatment the strength of wool fabric increased and higher rate of weight loss for protease treatment was obtained. When dyed by levelling type acid dye equilibrium dye uptake appeared same, but rate of dyeing increased by the plasma treatment, while, with milling type acid dye, both of them increased greatly in the order of untreatedplasma/protease-treated. It was assumed from the above results that plasma affects the surface of fiber, and enzyme attacks mainly the inner part of fiber. This was confirmed again by scanning electron microscope.

• Textile Coloration and Finishing
• /
• v.23 no.3
• /
• pp.195-200
• /
• 2011

Silicone-coated fabric were treated by oxygen low temperature plasma to improve the adhesion. The surface of silicone-coated fabric was modified with gaseous plasma of several discharge power in the presence of oxygen gas at 1Torr pressure. Oxygen plasma treatment introduces oxygen-containing functional groups and micro-pittings on the silicone-coated fabric surface. The treated fabrics with oxygen low temperature plasma were measured by contact angle analyzer and XPS(X-ray photoelectron spectroscopy), and interfacial adhesion was measured by T-peel test. The surface of fabric was investigated by SEM photographs. The chemical and physical modification of the surface wettabillity by plasma treatment can increase the adhesion.

• Textile Coloration and Finishing
• /
• v.16 no.6
• /
• pp.30-34
• /
• 2004

Polyacrylontrile fiber was modified with argon low temperature plasma by RF glow discharge at 240 mTorr, 40 W to investigate the surface morphological changes and mechanical characteristics such as elongation, tenacity, and modulus. Analysis of the SEM images revealed that the plasma treatment resulted in significant ablation on the surfaces rendering a severe crack formation. The morphological changes were evident with short treatment time of argon plasma although longer treatment time damaged the surface more severely. The mechanical characteristics such as tenacity and elongation were deteriorated due to the plasma treatment. The tenacity of the fiber treated with argon-plasma for 5 min showed a decreased value up to 21.9 % when compared to the untreated fiber. While the corresponding initial modulus(0 - 1 %) increased markedly up to 44.3 %.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07a
• /
• pp.513-514
• /
• 2005

In plasma processing reactors, it is common practice to control plasma density and ion bombardment energy by manipulating excitation voltage and frequency. In this paper, a dually excited capacitively coupled rf plasma reactor is self-consistently simulated with a three moment model. Effects of phase differences between primary and secondary voltage waves, simultaneously modulated at various combination of commensurate frequencies, on plasma properties are investigated. The simulation results show that plasma potential and density as well as primary self-dc bias are nearly unaffected by the phase lag between the primary and the secondary voltage waves. The results also show that, with the secondary frequency substantially lower than the primary frequency, secondary self-dc bias remains constant regardless of the phase lag. As the secondary frequency approaches to the primary frequency, however, the secondary self-dc bias becomes greatly altered by the phase lag, and so does the ion bombardment energy at the secondary electrode. These results demonstrate that ion bombardment energy can be more carefully controlled through plasma simulation.

• Journal of the Korean Society of Safety
• /
• v.16 no.3
• /
• pp.61-67
• /
• 2001

In this study the electrical and mechanical characteristics of PET films ore analyzed after plasma surface treatment. After plasma treatment, the surface potential decay, surface potential and dielectric property were evaluated to analyze the electrical insulating property, and the tensile strength was measured as the mechanical characteristic. When plasma treatment was conducted for less than 10 minutes, it was found that the electrical insulating property was improved through evaporation of low molecular weight materials md cleaning of surface. However, for more than 10 minutes, the insulating property of plasma treated PET films was decreased due to excessive discharge energy. The tensile strength was hardly changed by Plasma treatment.

• The Bulletin of The Korean Astronomical Society
• /
• v.36 no.1
• /
• pp.33.1-33.1
• /
• 2011

The plasma sheet of the Earth's magnetosphere is a sheet of hot plasmas in the magnetotail region, dividing the two (northern and southern) lobes of the Earth's magnetic field. It is the key region that is often closely linked to various electromagnetic dynamics in the Earth's magnetosphere-ionosphere system. In particular, it is the region that is most crucial for substorms, which is one of the most dynamic phenomena in the Earth's magnetosphere. The question of substorm triggering remains highly controversial until today, and at the center of the controversy there are several critical physics issues of the plasma sheet. In this talk I will introduce some of the physics issues of the plasma sheet. The specific topics that this talk will cover are (i) the general properties of the plasma sheet, (ii) fast plasma jets and plasma transport problem, (iii) stability/instability problem, and (iv) effects of thin current sheet. I will also present some of our group's recent findings regarding these topics, as obtained by comprehensive analyses of various observational data. The level and content of this talk are designed to be comprehensible to not only space physicists but also the scientists in a related field such as solar and heliospheric physics.