• Membrane Journal
• /
• v.25 no.2
• /
• pp.107-114
• /
• 2015

PTMSP-NaA zeolite composite membranes were prepared by adding 0~50 wt% NaA zeolite to PTMSP. The membranes were characterized by FT-IR, $^1H$-NMR, GPC, DSC, TGA, SEM. The permeabilities of $H_2$ and $N_2$ gases through PTMSP-NaA zeolite composite membranes was studied as a function of NaA zeolite contents. According to TGA measurements, when zeolite was inserted into the polymer, weight loss temperature and weight loss wt% of PTMSP-NaA zeolite composite membranes were decreased. Based on SEM observation, NaA zeolite was dispersed in the PTMSP-NaA zeolite composite membrane with the size $2{\sim}5{\mu}m$. The permeability of PTMSP-NaA zeolite composite membranes increased added as NaA zeolite content increased. On the contrary, the selectivity ($H_2/N_2$) of the composite membranes decreased as NaA zeolite content increased. PTMSP-NaA zeolite composite membrane showed better permeability and selectivity ($H_2/N_2$) of $H_2$ and $N_2$ than PTMSP-NaY zeolite composite membrane.

• Membrane Journal
• /
• v.22 no.5
• /
• pp.342-351
• /
• 2012

In this study, PTMSP[poly(1-trimethylsilyl-1-propyne)]/PDMS[poly(dimethylsioxane)]-NaY zeolite and PTMSP/PDMS-NaA zeolite composite membranes were made to incorporate zeolite into PTMSP/PDMS graft copolymer in order to improve the selectivity and thermal stability, the drop of permeability by physical aging effect during long period of time for the PTMSP membrane. To investigate the physico-chemical characteristics of composite membranes, the analytical methods such as FT-IR, $^1H$-NMR, TGA, SEM, and GPC have been utilized. The gas permeability and selectivity properties of $H_2$ and $N_2$ were evaluated. The permeability of the PTMSP/PDMS-NaY zeolite and PTMSP/PDMS-NaA zeolite composite membranes than PTMSP/PDMS graft copolymer membrane increased, increased as zeolite content increased. On the contrary, the selectivity ($H_2/N_2$) of the composite membranes decreased as zeolite content increased. PTMSP/PDMS-NaA zeolite composite membrane showed better permeability and separation factor than PTMSP/PDMS-NaY zeolite composite membrane.

• Membrane Journal
• /
• v.24 no.4
• /
• pp.285-291
• /
• 2014

The PTMSP[Poly(1-trimethylsilyl-1-propyne)]-NaY zeolite composite membranes were prepared by adding 0~50 wt% NaY zeolite to PTMSP. In order to investigate the characteristics of these membranes, we used the analytical methods such as FT-IR, $^1H$-NMR, GPC, DSC, TGA, and SEM. Gas permeation experiments were carried out at $23{\sim}26^{\circ}C$, $2kgf/cm^2$, and the permselectivity of $H_2$ and $N_2$ gases through the composite membranes was studied as a function of the NaY zeolite contents. According to TGA measurements, when NaY zeolite was inserted within the PTMSP, thermal stability of PTMSP was enhanced. Based on SEM observation, NaY zeolite was dispersed in the PTMSP-NaY zeolite composite membrane with a size of $1.5{\mu}m$. The permeability of $H_2$ and $N_2$ through the PTMSP-NaY zeolite composite membranes increased as NaY zeolite content increased. On the contrary, the selectivity($H_2/N_2$) of the PTMSP-NaY zeolite composite membranes decreased as zeolite content increased.

• Membrane Journal
• /
• v.22 no.5
• /
• pp.318-325
• /
• 2012

PTMSP-PMMH-NaY zeolite composite membranes were prepared by the addition of 10, 20, 30, and 40 wt% NaY zeolite contents to PTMSP containing 20 wt% PMMH dendrimer. To investigate the physico-chemical characteristics of composite membranes, the analytical methods such as FT-IR, TGA, and SEM have been utilized, and the gas permeability and selectivity properties of hydrogen and nitrogen were evaluated. The permeability of the PTMSP-PMMH-NaY zeolite composite membranes increased as NaY zeolite content increased, the permeabilities of hydrogen and nitrogen gases were observed being 3,950~592,000 barrer and 1,550~143,000 barrer, respectively. Simultaneously, selectivity of hydrogen against nitrogen did not show a discernible difference at 0~30 wt% range of NaY zeolite contents and increased from 2.2 to 4.2 at 30~40 wt% range.