• 대한금속재료학회지
• /
• 제46권10호
• /
• pp.646-651
• /
• 2008

The electrolytic reduction of spent oxide fuel involves the liberation of oxygen in a molten LiCl electrolyte, which results in a chemically aggressive environment that is too corrosive for typical structural materials. It is essential to choose the optimum material for the process equipment handling molten salt. IN713LC is one of the candidate materials proposed for application in electrolytic reduction process. In this study, yttria-stabilized zirconia (YSZ) top coat was applied to a surface of IN713LC with an aluminized metallic bond coat by an optimized plasma spray process, and were investigated the corrosion behavior at $675^{\circ}C$ for 216 hours in the molten salt $LiCl-Li_2O$ under an oxidizing atmosphere. The as-coated and tested specimens were examined by OM, SEM/EDS and XRD, respectively. The bare superalloy reveals obvious weight loss, and the corrosion layer formed on the surface of the bare superalloy was spalled due to the rapid scale growth and thermal stress. The top coatings showed a much better hot-corrosion resistance in the presence of $LiCl-Li_2O$ molten salt when compared to those of the uncoated superalloy and the aluminized bond coatings. These coatings have been found to be beneficial for increasing to the hot-corrosion resistance of the structural materials for handling high temperature lithium molten salts.

• 대한금속재료학회지
• /
• 제50권9호
• /
• pp.685-690
• /
• 2012

Decalcomania is a new method for SOFCs (solid oxide fuel cells) unit cell fabrication. A tight and dense $5{\mu}m$ Yttria-stabilized zirconia (8YSZ) electrolyte layer on anode substrate was fabricated by the decalcomania method. After 8YSZ as the electrolyte starting material was calcined at $1200^{\circ}C$, the particle size was controlled by the attrition mill. The median particle size (D50) of each 8YSZ was $39.6{\mu}m$, $9.30{\mu}m$, $6.35{\mu}m$, and $3.16{\mu}m$, respectively. The anode substrate was coated with decalcomania papers which were made by using 8YSZ with different median particle sizes. In order to investigate the effect of median particle sizes and sintering conditions on the electrolyte density, each sample was sintered for 2, 5 and 10 h, respectively. 8YSZ with a median particle size of $3.16{\mu}m$ which was sintered at $1400^{\circ}C$ for 10 had the highest density. With this 8YSZ, a SOFCs unit cell was manufactured with a $5{\mu}m$ layer by the decalcomania method. Then the unit cell was run at $800^{\circ}C$. The Open Circuit Voltage (OCV) and Maximum power density (MPD) was 1.12 V and $650mW/cm^2$, respectively.

• KEPCO Journal on Electric Power and Energy
• /
• 제7권1호
• /
• pp.161-165
• /
• 2021

In general, SOFCs mainly use Ni-YSZ cermet, a mixture of Ni and YSZ, as an anode material, which is stable in a high-temperature reducing atmosphere. However, when SOFCs have operated at a high temperature for a long time, the structural change of Ni occurs and it results in the problem of reducing durability and efficiency. Accordingly, a development of a new anode material that can replace existing nickel and exhibits similar performance is in progress. In this study, SrTiO₃, which is a perovskite-based mixed conductor and one of the candidate materials, was used. In order to increase the electrical conduction properties, Y_0.08Sr_0.92Fe_0.3Ti_0.7O₃, doped with 0.08 mol of Y³⁺ in Sr-site and 0.03 mol of transition metal Fe³⁺ in Ti-site, was synthesized and its chemical diffusion coefficient and reaction constant were measured. Its electrical conductivity changes were also observed while changing the oxygen partial pressure at a constant temperature. The performance as a candidate electrode material was verified by predicting the defect area through the electrical conductivity pattern according to the oxygen partial pressure.

• Corrosion Science and Technology
• /
• 제20권6호
• /
• pp.451-465
• /
• 2021

In this investigation, electrochemical characteristics and damage behavior of 316L stainless steel polymer electrolyte membrane fuel cell(PEMFC) were analyzed by potentiodynamic and potentiostatic tests in cathode operating condition of PEMFC. As the result of potentiodynamic polarization test, range of passive region was larger than range of active region. In the result of potentiostatic test, damage depth and width, pit volume, and surface roughness were increased 1.57, 1.27, 2.48, and 1.34 times, respectively, at 1.2 V compared to 0.6 V at 24 hours. Also, as a result of linear regression analysis of damage depth and width graph, trend lines of damage depth and width according to applied potentials were 16.6 and 14.3 times larger, respectively. This demonstrated that applied potential had a greater effect on pitting damage depth of 316L stainless steel. The damage tendency values were 0.329 at 6 hours and 0.633 at 24 hours with applied potentials, representing rapid growth in depth direction according to the test times and applied potentials. Scanning electron microscopy images revealed that surface of specimen exhibited clear pitting damage with test times and applied potentials, which was thought to be because a stable oxide film was formed by Cr and Mo.

• 한국표면공학회지
• /
• 제55권1호
• /
• pp.32-37
• /
• 2022

In a carbon-zero social atmospher, research is underway to reduce the use of fossil fuels. Interest in cleaner energy sources and their storage system is growing, and among them, research on effective energy storage is being actively conducted. Energy storage system(ESS) can be divided into secondary batteries, fuel cells, and capacitors, and the superiority of energy density of secondary batteries has a dominent influence on the ESS market. However, as problems with secondary batteries, charge/discharge speed, safety, and deterioration of electrodes are being highlighted. In this study, an electrode for supercapacitor with superior charge/discharge speed and specific capacitance is manufactured. The manufactured spinel nickel cobalt electrodes had specific capacitances of 1018.8 F/g, 690.8 F/g, and 475.1 F/g at 1 A/g in 1 M KOH electrolyte, and shows a performance retention rate of 77.48%, 63.30%, and 58.16% after 2000cycles at 7 A/g.

• Nuclear Engineering and Technology
• /
• 제54권3호
• /
• pp.1062-1070
• /
• 2022

In the present communication, pure and stable α-Bismuth Oxide (Bi₂O₃) nanoparticles (NPs) were synthesized by low temperature solution combustion method using urea as a fuel and calcined at 500℃. The synthesized sample was characterized by using powder X-ray Diffraction (PXRD), Scanning Electron Microscopy (SEM), Energy dispersive X-ray analysis (EDAX), Transmission Electron Microscopy (TEM), Fourier Transform Infrared Spectroscopy (FTIR) and UV-Visible absorption spectroscopy. The PXRD pattern confirms the formation of mono-clinic, stable and low temperature phase α-Bi₂O₃. The direct optical energy band gap was estimated by using Wood and Tauc's relation which was found to be 2.81 eV. The characterized sample was studied for X-ray/gamma ray shielding properties in the energy range 0.081-1.332 MeV using NaI (Tl) detector and multi channel analyzer (MCA). The measured shielding parameters agrees well with the theory, whereas, slight deviation up to 20% is observed below 356 keV. This deviation is mainly due to the influence of atomic size of the target medium. Furthermore an accurate theory is necessary to explain the interaction of X-ray/gamma ray with the NPs.The present work opens new window to use this facile, economical, efficient, low temperature method to synthesize nanomaterials for X-ray/gamma ray shielding purpose.

• 센서학회지
• /
• 제31권5호
• /
• pp.343-347
• /
• 2022

Recently, the problem of global warming caused by greenhouse gases is getting serious due to the development of industry and the increase in transportation means. Accordingly, the need for a technology to reduce carbon dioxide, which accounts for most of the greenhouse gas, is increasing. Among them, a catalyst for converting carbon dioxide into fuel is being actively studied. Catalysts for reducing carbon dioxide are classified into thermal catalysts and photocatalysts. In particular, the photocatalyst has the advantage that carbon dioxide can be reduced only by irradiating ultraviolet rays at room temperature without high temperature or additional gas. TiO₂ is widely used as a photocatalyst because it is non-toxic and has high stability, but has a disadvantage of low carbon dioxide reduction efficiency. To increase the reduction efficiency, 1-propanol was used in the synthesis process. This prevents agglomeration of the catalyst and increases the specific surface area and pores of TiO₂, thereby increasing the surface area in contact with carbon dioxide. As a result of measuring the CO₂ reduction efficiency, it was confirmed that the efficiency of TiO₂ with 1-propanol and TiO₂ without 1-propanol was 19% and 12.3%, respectively, and the former showed a 1.5 times improved efficiency.

• 청정기술
• /
• 제16권4호
• /
• pp.297-303
• /
• 2010

본 연구에서는 유체유동해석프로그램인 Fluent를 이용하여 연료극 지지채식 관형 고체산화물 연료전지(SOFC)에서의 연결재 구조에 따른 성능 변화를 고찰하였다. 실험적 사실과 부합되는 이론적 결과를 확보하기 위해서는 전기적으로 전극과 하나로 되어있는 연결재의 구조가 전지 성능에 어떠한 영향을 미치는지 살피는 것이 중요하다. 두께가 작은 연결재가 단전지 성능을 우수하게 하는 것으로 보아 옴(ohmic) 저항에 직결되는 연결재의 두께가 전지 성능에 있어 주요 변수임을 확인하였다. 일정 두께로 고정된 조건 하에 연결재 폭을 변화시킨 경우, 전지 성능은 상대적으로 큰 차이를 보이지 않았다. 이는 본 연구에서 고려한 SOFC의 관형 구조 특성상 연결재의 폭으로는 원주 방향으로 흘러가는 전류 경로를 효과적으로 단축시킬 수 없기 때문으로 사료된다.

• 한국수소및신에너지학회논문집
• /
• 제33권1호
• /
• pp.8-18
• /
• 2022

With rapid industrialization and population growth, fossil fuel use has increased, which has a significant impact on the environment. Hydrogen does not cause contamination in the energy production process, so it seems to be a solution, but it is essential to find an appropriate storage method due to its low efficiency. In this study, Mg-based alloys capable of ensuring safety and high volume and hydrogen storage density per weight was studied, and Mg₂NiH_x synthesized with Ni capable of improving hydrogenation kinetics. In addition, in order to improve thermal stability, a hydrogen storage composite material synthesized with CaO was synthesized to analyze the change in hydrogenation reaction. In order to analyze the changes in the metallurgical properties of the materials through the process, XRD, SEM, BET, etc. were conducted, and hydrogenation behavior was confirmed by TGA and hydrogenation kinetics analysis. In addition, in order to evaluate the impact of the process on the environment, the environmental impact was evaluated through "Material Life Cycle Assessments" based on CML 2001 and EI99' methodologies, and compared and analyzed with previous studies. As a result, the synthesis of CaO caused additional power consumption, which had a significant impact on global warming, and further research is required to improve this.

• 분석과학
• /
• 제21권2호
• /
• pp.143-147
• /
• 2008

사용후핵연료를 지하 심부에 처분하였을 경우 예상되는 원자가가 4가인 우라늄(U(IV)) 이온을 제조하여 6가 우라늄(U(VI)) 이온과 분리하였다. U(IV) 이온을 제조하기 위하여 우라닐 용액에 몇 가지 환원제를 첨가하거나 환원제가 들어있는 혼합산으로 우라늄 산화물을 용해하는 시험을 수행하였다. 제조한 용액중 우라늄의 원자가는 Dowex AG 50W-X8 양이온교환수지에 의한 두 이온의 분리 및 레이저 유도 형광 분광광도계로 용액을 측정하여 확인하였다. 그러나 Lichroprep Si60 교환수지를 사용하였을 경우 Pu(IV)와 Pu(VI)의 분리조건으로 U(IV)와 U(VI)가 분리되지 않았다.