• Korean Journal of Materials Research
• /
• v.23 no.8
• /
• pp.435-440
• /
• 2013

Transparent and conducting thin films of Ta-doped $SnO_2$ were fabricated on a glass substrate by a pulse laser deposition(PLD) method. The structural, optical, and electrical properties of these films were investigated as a function of doping level, oxygen partial pressure, substrate temperature, and film thickness. XRD results revealed that all the deposited films were polycrystalline and the intensity of the (211) plane of $SnO_2$ decreased with an increase of Ta content. However, the orientation of the films changed from (211) to (110) with an increase in oxygen partial pressure (40 to 100 mTorr) and substrate temperature. The crystallinity of the films also increased with the substrate temperature. The electrical resistivity measurements showed that the resistivity of the films decreased with an increase in Ta doping, which exhibited the lowest resistivity (${\rho}{\sim}1.1{\times}10^{-3}{\Omega}{\cdot}cm$) for 10 wt% Ta-doped $SnO_2$ film, and then increased further. However, the resistivity continuously decreased with the oxygen partial pressure and substrate temperature. The optical bandgap of the 10 wt% Ta-doped $SnO_2$ film increased (3.67 to 3.78 eV) with an increase in film thickness from 100-700 nm, and the figure of merit revealed an increasing trend with the film thickness.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.457-458
• /
• 2009

In this work, transparent conducting Al-doped zinc oxide (AZO) films were prepared on Coming glass substrate by RF magnetron sputtering using an Al-doped ZnO target (Al: 2 wt.%) at room temperature and all films were deposited with athickness of 150 nm. We investigated the effects of the post-annealing temperature and the annealing ambient on structural, electrical and optical properties of AZO films. The films were annealed at temperatures ranging from 300 to $500^{\circ}C$ in steps of $100^{\circ}C$ using rapid thermal annealing equipment in oxygen. The thickness of the film was observed by field emission scanning electron microscopy (FE-SEM) and grain size was calculated from the XRD spectra using the Scherrer equation and their electrical properties were investigated using a hole measurement and the reflectance of AZO films was investigated by UV-VIS spectrometry.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.35 no.3
• /
• pp.21-28
• /
• 2003

It is essential to use base papers having proper surface characteristics in coating operation for improving coated paper quality and coater runnability. To fulfill these purposes surface sizing of coating base stock with anionic oxidized starch is commonly practiced. It is suggested that use of cationic starch for surface sizing rather than conventional oxidized starch will improve coated paper quality since cationic starch penetrates less into paper structure because of its strong electrostatic interaction with anionically charged paper surface. Strong interaction of cationic surface sizing starch with anionic coating color is expected to promote rapid immobilization of the coating color and improve coating holdout and optical property. The immediate objective of this study was to examine the influence of surface sizing starches on the properties of coated papers. Structural characteristics of the coatings formed on the substrate surface sized with cationic and anionic starches were examined. To enhance the efficiency of cationic surface sizing starch on coated paper properties, strongly charged cationic polymers were added to the surface sizing starch and its effect on coated paper properties was evaluated. Results showed that opacity and light scattering coefficient of coated paper were higher when base paper surface sized with cationic starch was used. Addition of less than 1% of cationic poly-DADMAC to the cationic surface sizing starch improved the opacity of coated paper significantly.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.248-248
• /
• 2011

ZnO was grown on a Au-catalyzed Si(100) substrate by using a simple vapor phase transport (VPT) with a mixture of zinc oxide and graphite powders. The ZnO grown at 800$^{\circ}C$ had a soccer ball structure with diameters of <500 nm. The ZnO soccer ball structure was, for the first time, observed in this work. The optical properties of the ZnO soccer balls were investigated by photoluminescence (PL). In the room-temperature (RT) PL of the ZnO soccer balls, a strong near-band-edge emission (NBE) and a weak deep-level emission were observed at 3.25 and 2.47 eV (green emission), respectively. The weak deep-level emission (DLE) at around 2.47 eV (green emission) is caused by impurities and structural defects. The FWHM of the NBE peak from the ZnO soccer balls was 110 meV. In addition, the PL intensity ratio of the NBE to DLE was about 4. The temperature-dependent PL was also carried out to investigate the mechanism governing the quenching behavior of the PL spectra.

• Journal of the Korean Ceramic Society
• /
• v.52 no.4
• /
• pp.290-293
• /
• 2015

The properties of the IZTO thin films on the glass were studied with a variation of the $SiO_2$ buffer layer thickness. $SiO_2$ buffer layers were deposited by plasma-enhanced chemical vapor deposition (PECVD) on the glass, and the In-Zn-Tin-Oxide (IZTO) thin films were deposited on the buffer layer by RF magnetron sputtering. All the IZTO thin films with the $SiO_2$ buffer layer are shown to be amorphous. Optimum $SiO_2$ buffer layer thickness was obtained through analyzing the structural, morphological, electrical, and optical properties of the IZTO thin films. As a result, the IZTO surface roughness is 0.273 nm with a sheet resistance of $25.32{\Omega}/sq$ and the average transmittance is 82.51% in the visible region, at a $SiO_2$ buffer layer thickness of 40 nm. The result indicates that the uniformity of surface and the properties of the IZTO thin film on the glass were improved by employing the $SiO_2$ buffer layer and the IZTO thin film can be applied well to the transparent conductive oxide for display devices.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.05a
• /
• pp.127-130
• /
• 2005

The properties of phosphorus doped ZnO multilayer thin films deposited on (001) sapphire substrates by pulsed laser deposition (PLD) were investigated by using annealing treatment at various annealing temperature after deposition. The phosphorus doped ZnO multilayer was composed of phosphorus doped ZnO layer and two pure ZnO layers on sapphire substrate. The structural. electrical and optical properties of the ZnOthin films were measured by X-ray diffraction (XRD). Hall measurements and photoluminescence (PL). As the annealing temperature optimized. the electrical properties of the ZnO multilayer showed a electron concentration of $1.56{\times}10^{16}/cm^3$, a resistivity of 17.97 ${\Omega}cm$. It was observed the electrical property of the film was changed by dopant activation effect as thermal annealing process

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.4
• /
• pp.289-293
• /
• 2007

ZnO thn films are grown on five kinds of oxide substrates including $c-Al_2O_3(0001),\;r-Al_2O_3(01-12)$, MgO(100), MgO(111), $NdGaO_3(110)$ by rf magnetron sputtering and effects substrate types on properties of ZnO thin films ate investigated. In order to compare the substrate effects one growth condition is selected and all the films are grown by the same growth condition. Structural and optical properties of the ZnO films ate different depending on the substrates although the films ate not epitaxial but polycrystalline. The ZnO film grown on $NdGaO_3(100)$ substrate shows the best overall properties among the films grown on substrates investigated in this study.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.379-380
• /
• 2007

The characteristics of a co-sputtered indium zinc tin oxide (IZTO) films prepared by dual target dc magnetron sputtering from IZO and ITO targets at a room temperature are investigated. Film properties, such as sheet resistance, optical transmittance, surface work function and surface roughness were examined as a function of ITO dc power at constant IZO dc power of 100 W. It was shown that the increase of the ITO dc power during co-sputtering of ITO and IZO target resulted in an increase of sheet resistance of the IZTO films. This can be attributed to high resistivity of ITO film prepared at room temperature. Surface smoothness and roughness were investigated by Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). The synchrotron x-ray scattering results obtained from IZTO film with different ITO contents showed that introduction of ITO atoms into amorphous IZO film resulted in a crystallization of IZTO film with (222) preferred orientation due to low alc transition temperature of ITO film. However, the transmittance of the IZTO films with thickness of 150 nm is between 80 and 85 % at wavelength of 550 nm regardless of ITO content. Possible mechanism to explain the ITO and IZO co-sputtering effect on properties of IZTO is suggested.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.153-153
• /
• 2016

Polyoxymethylene copolymer (POM-C) is an attractive and widely used engineering thermoplastic across many industrial sectors owing to outstanding physical, mechanical, self-lubricating and chemical properties. In this research work, the POM-C blocks were irradiated with 1 MeV electron beam energy in five doses (100, 200, 300, 500 and 700 KGy) in vacuum condition at room temperature. The tribological and physico-chemical properties of electron beam irradiated POM-C blocks have been analyzed using Pin on disk tribometer, Raman spectroscopy, SEM-EDS, Optical microscopy, 3D Nano surface profiler system and Contact angle analyzer. Electron beam irradiation at a dose of 100 kGy resulted in a decrease of the friction coefficient and wear loss of POM-C block due to well suited cross-linking, carbonization, free radicals formation and energetic electrons-atoms collisions (physical interaction). It also shows lowest surface roughness and highest water contact angle among all unirradiated and irradiated POM-C blocks. The irradiation doses at 200, 300, 500 and 700 kGy resulted in increase of the friction coefficient as compared to unirradiated POM-C block due to severe chain scission, chemical and physical structural degradation. The electron beam irradiation transferred the wear of unirradiated POM-C block from the abrasive wear, adhesive wear and scraping to mild scraping for the 1 MeV, 100 kGy irradiated POM-C block which is concluded from SEM-EDS and Optical microscopic observations. The degree of improvement for tribological attribute relies on the electron beam irradiation condition (energy and dose rate).

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.312-312
• /
• 2013

GaN based light emitting diodes (LEDs) are important devices that are being used extensively in our daily life. For example, these devices are used in traffic light lamps, outdoor full-color displays and backlight of liquid crystal display panels. To realize high-brightness GaN based LEDs for solid-state lighting applications, the development of p-type ohmic electrodes that have low contact resistivity, high optical transmittance and high refractive index is essential. To this effect, indiumtin oxide (ITO) have been investigated for LEDs. Among the transparent electrodes for LEDs, ITO has been one of the promising electrodes on p-GaN layers owing to its excellent properties in optical, electrical conductivity, substrate adhesion, hardness, and chemical inertness. Sputtering and e-beam evaporation techniques are the most commonly used deposition methods. Commonly, ITO films on p-GaN by sputtering have better transmittance and resistivity than ITO films on p-GaN by e-bam evaporation. However, ITO films on p-GaN by sputtering have higher specific contact resistance, it has been demonstrated that this is due to possible plasma damage on the p-GaN in the sputtering process. In this paper, we have investigated the advanced sputtering using plasma damage-free p-electrode. Prepared the ITO films on the GaN based LEDs by e-beam evaporation, normal sputtering and advanced sputtering. The ITO films on GaN based LEDs by sputtering showed better transmittance and sheets resistance than ITO films on the GaN based LEDs by e-beam evaporation. Finally, fabricated of GaN based LEDs by using advanced sputtering. And compared the electrical properties (measurement by using C-TLM) and structural properties (HR-TEM and FE-SEM) of ITO films on GaN based LEDs produced by e-beam evaporation, normal sputtering and advanced sputtering. As a result, It is expected to form plasma damage free-electrode, and better light output power and break down voltage than LEDs by e-beam evaporation and normal sputter.