• The Korean Journal of Ceramics
• /
• 제4권4호
• /
• pp.340-344
• /
• 1998

Failure mechanisms were investigated for the two layer thermal barrier coatings consisting of NiCrAlY bond coat and $ZrO_2$-8wt.% $Y_2O_3$ ceramic coating during cyclic oxidation. $Al_2O_3$ developed at the ceramic coating/bond coat interface first, followed by the Cr/Ni rich oxides such as $NiCr_2O_4$ and $Ni(Al, Cr)_2O_4$ during cyclic oxidation. It was observed that the spalling of ceramic coatings took place primarily within the NiCrAlY bond coat oxidation products or at the interface between the bond coat oxidation products and zirconia based ceramic coating or the bond coat. It was also observed that the fracture within these oxidation products occurred with the formation of $Ni(Cr, Al)_2O_4$ spinel or Cr/Ni rich oxides. It was therefore concluded that the formation of these oxides was a life-limiting event for the thermal barrier coatings.

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2005년도 제24회 춘계학술대회논문집
• /
• pp.106-111
• /
• 2005

Failure mechanisms were investigated for the two layer thermal barrier coatings consisting of NiCrAlY bond coat and $ZrO_2-8wt.\% Y_{2}O_3$ ceramic coating during cyclic oxidation. $Al_{2}O_3$ developed at the ceramic coating/bond coat interface first, followed by the Cr/Ni rich oxides such as $NiCr_{2}O_4 and Ni(Al,Cr)_{2}O_4$ during cyclic oxidation It was observed that the spalling of ceramic coatings took place primarily within the NiCrAlY bond coat oxidation products or at the interface between the bond coat oxidation products and zirconia based ceramic coating or the bond coat. It was also observed that the fracture within these oxidation products occurred with the formation of $Ni(Cr,Al)_{2}O_4$ spinel or Cr/Ni rich oxides. It was therefore concluded that the formation of these oxides was a life-limiting event for the thermal barrier coatings.

• 한국수소및신에너지학회논문집
• /
• 제16권1호
• /
• pp.49-57
• /
• 2005

[ $MO/Al_2O_3-ZrO_2$ ](M=Ni and Cu) mixed metal oxides were prepared using sol-gel method in order to investigate the applicability to the 2-step thermo-chemical water splitting process and their redox behaviors were studied by temperature programmed reaction(TPR) from room temperature to 900$^{\circ}C$ under 5% $H_2$/Ar for the reduction and $H_2O$/Ar for the oxidation, respectively. From the results, peaks of the reduction and the oxidation on temperature were shifted with the change of crystalline phases due to the addition of $Al_2O_3$ and $ZrO_2$. The intensities of the peaks were also increased with the increase of contents of NiO or CuO that could be considered as active species. In addition, based on the observation of SEM images before and after the redox test, it seemed that $Al_2O_3-ZrO_2$ added prevented high temperature sintering of active metal components such as Ni (or Cu) on the surface and played a role of dispersing the active species homogeneously in solid solution of mixed oxides.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2003년도 추계총회 및 연구발표회 초록집
• /
• pp.104.1-104
• /
• 2003

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2003년도 추계총회 및 연구발표회 초록집
• /
• pp.103.2-103
• /
• 2003

• Bulletin of the Korean Chemical Society
• /
• 제19권1호
• /
• pp.5-21
• /
• 1998

The purpose of this paper is to show that X-ray absorption spectroscopy (XANES and EXAFS) is a powerful technique for characterizing both crystalline and amorphous solids from structural (local order) and electronic point of view. The principle of this technique is briefly described by showing the main factors which must be considered for recording and fitting the experimental results. Some non-trivial examples have been selected for demonstrating that XAS spectroscopy is the only technique for bringing a definitive answer as for example: the determination of the local distortion of the $NiO_6$ octahedra in the $Li_{1-z}Ni_{1+z}O_2$ layered oxides and the evidence of the presence of copper pairs in the NASICON-type phosphate $CuZr_2 (PO_4)_3$. Are also reported some significant examples for which XAS spectroscopy is decisive with other characterization methods as (i) Raman spectroscopy for glasses (ii) Mossbauer spectroscopy for $LiNi_{1+z-t}Fe_To_2$ oxides (iii) magnetic measurements for Ce-based intermetallic compounds.

• 대한치과기공학회지
• /
• 제34권4호
• /
• pp.361-368
• /
• 2012

Purpose: The aim of this study was to analysis the composition on the centrifugal casting and the oxide on the casting temperature. Methods: The nickel based alloy were used in this study. Wax pattern specimens (10*10*2) were invested with phosphate-bonded investment in metal rings, the liquid/powder ratio and overall burn-out schedules for these investments were followed in accordance with the manufacturer's instructions. After casting, the alloy specimens were evaluated as regards composition(EPMA). The casting temperatures were as follows: $1400^{\circ}C$ and $1700^{\circ}C$. The quantitative analysis of oxides were scanning electron microscope(SEM), energy dispersive spectroscopy(EDS) and line scanning. Results: Nearer the injection lines showed that there is a large amount of nickel. Quantitative of oxides of Ni-Cr alloy cast from $1400^{\circ}C$ is lager than Ni-Cr alloy cast from $1700^{\circ}C$. Conclusion: Casting when using a centrifugal casting machine centrifugal force affects the composition of the alloy. The higher the temperature, the amount of oxide that is generated many.

• 한국자기학회지
• /
• 제23권5호
• /
• pp.149-153
• /
• 2013

이 연구에서는 방사광 연 X선 광흡수 분광법(soft x-ray absorption spectroscopy: XAS)을 이용하여 $TCr_2O_4$(T = Fe, Co, Ni) 스피넬 산화물들의 전자 구조를 연구하였다. 전이금속 이온들의 2p 준위의 흡수에 의한 XAS 측정으로부터 T(T = Fe, Co, Ni) 이온들의 원자가는 공통적으로 2가($T^{2+}$)이며, Cr 이온의 원자가는 3가 ($Cr^{3+}$) 임을 발견하였다. 그리고 T 이온들은 정사면체 대칭성을 가진 A 사이트에 주로 위치하고, Cr 이온은 정팔면체 대칭성을 가진 B 사이트에 주로 위치함을 알 수 있었는데, 이러한 발견을 통하여 $TCr_2O_4$는 정상 스피넬에 가까운 구조를 가지고 있다고 결론지을 수 있다. 또한 $FeCr_2O_4$와 $NiCr_2O_4$에서는 얀-텔러 변형이 중요한 역할을 하지만, $CoCr_2O_4$는 얀-텔러 변형이 없는 입방체 구조를 유지하는 원인을 알 수 있었다. 그러므로 $TCr_2O_4$에서 $Cr^{3+}$ 상태의 이온들과 $T^{2+}$ 상태의 이온들 간의 반강자성 결합이 이 산화물들의 자성 특성을 결정하는데 중요한 역할을 한다고 생각된다.

• 한국표면공학회지
• /
• 제29권3호
• /
• pp.163-175
• /
• 1996

Flame-sprayed Ni-based coatings are investigated in order to improve the thermal fatigue properties of gray cast iron in the presence of water spraying. The results of thermal cycling tests from room temperature to $1100^{\circ}C$ indicate that thermal fatigue endurance is increased in the order of Ni-20%Cr, NiCr-6%Al, and Ni-5%Al. The thermal fatigue failure is caused by the formation of iron oxides between the coating and the substrate and then the thermal fatigue cracks have propagated either along the brittle iron oxide layer resulting in the spatting of the coatings in case of Ni-5%Al and NiCr-6%Al coatings or to the substrate resulting in the whole specimen fracture in case of Ni-20%Cr coating. It seems that the most governing factor for thermal fatigue resistance is the thermal expansion coefficient difference between the coating and the substrate. Microstructural variations before and after the tests are also discussed.

• 한국표면공학회지
• /
• 제44권5호
• /
• pp.196-200
• /
• 2011

The Ni-based superalloy, Inconel 713, was oxidized at $800{\sim}1100^{\circ}C$ for 50 and 100 hours in air. It displayed excellent oxidation resistance, forming a few micrometer-thick scales. The major scale was ${\alpha}-Al_2O_3$. Other scales formed were $TiO_2$, $NiAl_2O_4$ and $Cr_2O_3$. Generally, uniform oxidation occurred over the alloy surface, resulting in the formation of ${\alpha}-Al_2O_3$ with and without $Cr_2O_3$. Other oxides such as $TiO_2$ and $NiAl_2O_4$ sometimes also formed. Locally, nodular oxidation occurred at the nodules that consisted of diverse alloying elements. The scales were adherent at $800^{\circ}C$. However, they spalled a little at $900{\sim}1100^{\circ}C$.