• Korean Journal of Materials Research
• /
• v.13 no.11
• /
• pp.721-724
• /
• 2003

A Fe-Si-B-Ni amorphous alloy manufactured by one roll melt-spinning method showed the crystallization temperature difference of a maximum $10^{\circ}C$ according to each lot. This temperature difference had a considerable influence on the annealing process to be conducted for obtaining the proper inductance of the alloy. The proper annealing temperature of the alloy was $480^{\circ}C$ and the annealing time increased as the crystallization temperature increased. The activation energy measured by Kissinger method increased as the crystallization temperature increased. Therefore, the annealing process must be adjusted by the crystallization temperature difference of the amorphous alloy.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1995.11a
• /
• pp.25-25
• /
• 1995

Liquid phase sintering of 90W-6Ni-4Mn alloy has been investigated as functions of sintering atmosphere, heating rate, and reduction temperature. The present work accounts for the thermodynamic oxidatiodreduction reactions of constituent powders of W, Ni and Mn. By discounting these reactions, the previous investigations would obtain only the alloy with large pores and the lowered relative sintered density, by the liquid phase sintering under a dry hydrogen atmosphere. the sintering cycle consisted of a rapid heating to reduction temperatures under high purity nitrogen atmosphere, and holding for 4 hours and sintering at $1260^{\circ}C$ for 1 hour under a dry hydrogen gas. The relative density of the sintered alloy increased with increasing heating rate. As the reduction temperature increased, the relative density increased to the lm theotical density at the duction temture above $1150^{\circ}C$. The mimsturcatre of sintered alloys has been analysed by a scanning election microscope. The sintered density was compared with those obtained from the other investigators. It was found that the reduction $1150^{\circ}C$ results in the lowered densification of 90W-6Ni-4Mn alloy. This is caused by the fact that reducing reactions of W and Ni oxides contained in W an Ni powders concomitantly leads to oxidizing reaction of Mn powder the oxidized Mn is hardly reduced at sintering temperature and thereby remains large pores in the alloy. It is concluded that the W-Ni-Mn alloy with full density can be obtained by the precise control of atmosphere, heating rate, and sintering temperature.

• Journal of the Korean Society of Safety
• /
• v.20 no.3 s.71
• /
• pp.27-33
• /
• 2005

The shape memory effect in Ti-50.4at.%Ni alloy after solution treatment at 1273K for 2h and aged at 350, 450, $550^{\circ}C$ for 0.5, 1, 1.5, 2, 4, 10hrs had been investigated by differential scanning calorimetry measurement. It was found that ageing in the temperature range of $350^{\circ}C{\sim}550^{\cric}C$ induced complex transformation behavior, involving the R-phase and multiple-stage martensitic transformation. Usually aged Ni-rich NiTi alloys undergo martensitic transformation on cooling from high temperatures in two step : Austenite to R-phase and then R-phase to Martensite (normal behavior). In sample aged at $350^{\circ}C$ two distinct DSC peaks arised giving evidence of intermediate stages of martensite transformation. This results in the nucleation and growth of coherent $Ni_4Ti_3$-precipitate. These explain all features of the evolution of DSC charts during ageing including the number of distinct DS peaks and their positions.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.1
• /
• pp.18-22
• /
• 2008

In this paper, the Ni-Co alloy was used for thermal stability estimation comparison with Ni structure. The proposed Ni/Ni-Co structure exhibited wider range of rapid thermal process windows, lower sheet resistance in spite of high temperature annealing up to $700^{\circ}C$ for 30 min, more uniform interface via FE-SEM analysis, NiSi phase peak. Therefore, The proposed Ni/Ni-Co structure is highly promising for highly thermal immune Ni-silicide for nano-scale MOSFET technology.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.5
• /
• pp.285-291
• /
• 1994

The effects of pulse current parameters on the composition and the microstructure of Pd-Ni alloy electrodeposits were studied. The cathode current efficiency of p.c. electrolysis conditions decreased with increasing both mean and peak current density and was lower than those under D.C. electrolysis condition. Palladium content of Pd-Ni alloy increased with increasing both peak current density and on-time, while it decreased with increasing mean current density and duty cycle. The preferred orientation of Pd-Ni alloys changed with increasing mean current density in the sequence of (111)+(110).(100) or (110)longrightarrow(111)longrightarrow(100) or random distribution of crystal structure. The surface morphology of Pd-Ni alloy changed mainly according to the mean current density and was related to the preferred orientation.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.16-17
• /
• 2006

In this paper, Ni-V alloy was studied with different structures and thickness. In case of Ni-V and Ni-V/Co/TiN, low resistive Ni silicide was formed after one step RTP (Rapid Thermal Process) with temperature range from $400^{\circ}C$ to $600^{\circ}C$ for 30sec in vacuum. After furnace annealing with temperatures range from $550^{\circ}C$ to $650^{\circ}C$ for 30min in nitrogen ambient, Ni-V single structure shows the best thermal stability compare with the other ones. To enhance the thermal stability up to 650oC and find the optimal thickness of Ni silicide, different thickness of Ni-V was studied in this work. Stable sheet resistance was obtained through Ni-V single structure with optimal Ni-V thickness.

• Journal of Powder Materials
• /
• v.28 no.4
• /
• pp.336-341
• /
• 2021

In this study, a nanocrystalline FeNiCrMoMnSiC alloy was fabricated, and its austenite stability, microstructure, and mechanical properties were investigated. A sintered FeNiCrMoMnSiC alloy sample with nanosized crystal was obtained by high-energy ball milling and spark plasma sintering. The sintering behavior was investigated by measuring the displacement according to the temperature of the sintered body. Through microstructural analysis, it was confirmed that a compact sintered body with few pores was produced, and cementite was formed. The stability of the austenite phase in the sintered samples was evaluated by X-ray diffraction analysis and electron backscatter diffraction. Results revealed a measured value of 51.6% and that the alloy had seven times more austenite stability than AISI 4340 wrought steel. The hardness of the sintered alloy was 60.4 HRC, which was up to 2.4 times higher than that of wrought steel.

• Transactions on Electrical and Electronic Materials
• /
• v.18 no.5
• /
• pp.253-256
• /
• 2017

A thin Te interlayer was applied to a Ni/n-InGaAs contact to reduce the contact resistance between Ni-InGaAs and n-InGaAs. A 5-nm-thick Te layer was first deposited on a Si-doped n-type $In_{0.53}Ga_{0.47}As$ layer, followed by in situ deposition of a 30-nm-thick Ni film. After the formation of the Ni-InGaAs alloy by rapid thermal annealing at $300^{\circ}C$ for 30 s, the extracted specific contact resistivity (${\rho}_c$) reduced by more than one order of magnitude from $2.86{\times}10^{-4}{\Omega}{\cdot}cm^2$ to $8.98{\times}10^{-6}{\Omega}{\cdot}cm^2$ than that of the reference sample. A thinner Ni-InGaAs alloy layer with a better morphology was obtained by the introduction of the Te layer. The improved interface morphology and the graded Ni-InGaAs layer formed at the interface were believed to be responsible for ${\rho}_c$ reduction.

• Journal of Power System Engineering
• /
• v.18 no.2
• /
• pp.37-42
• /
• 2014

The purpose of this paper is to investigate polarization characteristics of heat-treated Ni-based self-flux alloy coating in alkaline solution. Ni-based self-flux alloy powder was sprayed to a steel substrate using flame spray process, and heat treatments were performed in a vacuum furnace at $800^{\circ}C$, $900^{\circ}C$, $1000^{\circ}C$ and $1100^{\circ}C$. After heat treatments, corrosion tests were carried out using potentiostat/galvanostat at solution with pH 8 and pH 13. Corrosion potential(Ecorr) and corrosion current density(Icorr) could be analyzed from polarization curve. Anticorrosive effect of heat-treated coating at solution with pH 8 was relatively greater than at solution with pH 13. Heat-treated coating at $1100^{\circ}C$ showed the greatest anti-corrosion characteristics in alkaline solution.

• Korean Journal of Materials Research
• /
• v.4 no.8
• /
• pp.877-887
• /
• 1994

Cu-Ni-Si-P alloys have been studied in order to develop connector material which has a favorable combination of strength, electrical conductivity, elastic limit, thermal softening resistence and bend formability. Three kinds of trial alloys with various nickel and silicon content were melted and cast, hot rolled at about $900^{\circ}C$ and cold rolled. Mechanical properties and electrical conductivities of these alloys annealed at $450^{\circ}C$, $500^{\circ}C$ and $550^{\circ}C$ were investigated. An alloy with the composition of Cu-2.7%Ni-0.53%Si-O.O29%P, which shows a favorable combination of high strength and high electrical conductivity, has been developed. Various characteristics of the alloy 1 connector material were evaluated and compared with phospher bronze(C521OR-H) and brass(C26OOR-EH) connector material.