• 한국재료학회지
• /
• 제13권4호
• /
• pp.228-232
• /
• 2003

The effects of$ Nd_2$$O_3$addition on the properties of Mn-Zn ferrite were investigated in the doping concentration range from 0.05 to 0.25 wt%. All samples were prepared by standard fabrication of ferrite ceramics. With increasing the Neodymium oxides, specific density and initial permeability increased on the whole. But, the tendencies such as upper result had the measured value on limitation and characteristics saturated or decreased properties after that. With increasing the content of Neodymium oxides. both the real and imaginary component of complex permeability and the magnetic loss(tan$\delta$) increased. Because reason that magnetic loss increases is high ratio that a real department increases than imaginary department. Magnetic loss increased none the less for increasing the real department related with magnetic permeability. But, the magnetic loss of ferrite doped with the Neodymium oxides were lower than that of none doped Mn-Zn ferrite. The small amount of percent Neodymium oxides in Mn-Zn ferrite composition led to enhancement of resistivity in bulk, and more so in the grain boundary.

• 한국방사성폐기물학회:학술대회논문집
• /
• 한국방사성폐기물학회 2003년도 가을 학술논문집
• /
• pp.447-452
• /
• 2003

산화물 핵연료의 리튬환원공정에서 생성되는 $Li_2O$와 희토류원소 산화물($RE_2O_3$)의 화학적 반응을 밝혔다. 스칸듐, 이트륨, 프라세오디뮴, 네오디뮴, 사마륨, 유러퓸, 가돌리늄, 이테르븀 및 루테튬의 산화물은 각각 어떤 $Li_2O$의 임계농도 이상에서 $Li_2O$와 반응하여 복합산화물($LiREO_2$)을 형성하고, 이들 산화물이 복합산화물을 형성하는 각각의 $Li_2O$ 임계농도는 0.1 wt%, 1.9 wt%, 5.3 wt%, 5.0 wt%, 3.0 wt%, 3.9 wt%, 2.9 wt%, 2.6 wt% 및 0.3 wt%로 나타났다. $CeO_2$ 및 란타늄 산화물은 $Li_2O$와 반응하지 않는 것으로 나타났다. 실험에서 얻은 이들 희토류원소 복합산화물의 LiCl 용융염에 대한 용해도는 매우 작았다.

• Nuclear Engineering and Technology
• /
• 제34권1호
• /
• pp.80-89
• /
• 2002

A laboratory investigation of the behavior of radioactive metals under the various waste combustion atmospheres was conducted to predict the parameters that influence their partitioning behavior during waste incineration. Neodymium, samarium, cerium, gadolinium, cesium and cobalt were used as non-radioactive surrogate metals that are representative of uranium, plutonium, americium, curium, radioactive cesium, and radioactive cobalt, respectively. Except for cesium, all of the investigated surrogate metal compounds converted into each of their stable oxides at medium temperatures from 400 to 90$0^{\circ}C$, under oxygen- deficient and oxygen-sufficient atmospheres (0.001-atm and 0.21-atm $O_2$). At high temperatures above 1,40$0^{\circ}C$, cerium, neodymium and samarium in the form of their oxides started to vaporize but the vaporization rates were very slow up to 150$0^{\circ}C$ . Inorganic chlorine (NaCl) as well as organic chlorine (PVC) did not impact the volatility of investigated Nd$_2$O$_3$, CoO and Cs$_2$O. The results of laboratory investigations suggested that the combustion chamber operating parameters affecting the entrainment of particulate and filtration equipment operating parameters affecting particle collection efficiency be the governing parameters of alpha radionuclides partitioning during waste incineration.

• 한국표면공학회지
• /
• 제26권2호
• /
• pp.82-86
• /
• 1993

An attempt was made to reduce directly Nd2O3 in a cryolited based fluoride bath. Neodymium metal was electrodeposited on the iron cathode to produce the Fe-Nd eutectic alloy in a liquid state at 90$0^{\circ}C$. Graphite was adopted for the anode and pure iron for the cathode. Electrolyte was composed of Na3AlF6 50wt.%. AlF3 34wt.% and Nd2O3 16wt.%. Analysis of typical alloy product showed Al 63.4wt.% Fe 26.9wt.% and Nd 7.0 wt.% The enrichment of neodymium in the alloy couldn't be obtained because aluminum codeposited with ne-odydmium. Experimental results proved that the cryolited based electrolyte was unstable for the electrolysis of rare earth oxides even though their prominent solubilities.

• Journal of Industrial and Engineering Chemistry
• /
• 제68권
• /
• pp.311-324
• /
• 2018

Herein,the Neodymium ion ($Nd^{3+}$) doped CoAl-LDH have been successfully prepared via co-precipitation method and was used as a precursor of Nd-doped CoAl-mixed metal oxides (MMO). The photocatalytic activity of doped LDH and MMO was investigated in the degradation of an azo dye, C.I. Acid Red 14, under visible light irradiation. DRS and PL analysis demonstrated decreasing in the band gap energy and recombination of photo-induced charge carriers of Nd-doped LDH and MMO compared with the pristine CoAL-LDH. Due to significant difference in photocatalytic performance. A power law empirical kinetic model was obtained for predicting the photocatalytic degradation efficiency.

• 한국재료학회지
• /
• 제29권4호
• /
• pp.241-251
• /
• 2019

There are several manufacturing techniques for developing thermionic cathodes for vacuum ultraviolet(VUV) ionizers. The triple alkaline earth metal emitters(Ca-Sr-Ba) are formulated as efficient and reliable thermo-electron sources with a great many different compositions for the ionizing devices. We prepare two basic suspensions with different compositions: calcium, strontium and barium. After evaluating the electron-emitting performance for europium, gadolinium, and yttrium-based cathodes mixed with these suspensions, we selected the yttrium for its better performance. Next, another transition metal indium and a lanthanide metal neodymium salt is introduced to two base emitters. These final composite metal emitters are coated on the tungsten filament and then activated to the oxide cathodes by an intentionally programmed calcination process under an ultra-high vacuum(${\sim}10^{-6}torr$). The performance of electron emission of the cathodes is characterized by their anode currents with respect to the addition of each element, In and Nd, and their concentration of cathodes. Compared to both the base cathodes, the electron emission performance of the cathodes containing indium and neodymium decreases. The anode current of the Nd cathode is more markedly degraded than that with In.

• 청정기술
• /
• 제26권2호
• /
• pp.116-121
• /
• 2020

본 연구에서는 유가금속 회수를 한 전기차 폐배터리 부산물의 재활용에 관하여 연구하였다. 폐배터리 부산물에는 희토류들이 남아있으나, 부산물의 형태로는 소재로서의 가치가 없기에 정제과정을 거쳐 희토류 산화물로 회수하였다. 희토류침전분말 형태의 부산물을 30% 수산화나트륨을 이용하여 가공이 편한 수산화물로 변환한 뒤, 옥살산의 용해도 차이를 이용하여 남아 있는 불순물을 정제한 뒤, D2EHPA (Di-(2-ethylhexyl) phosphoric acid)를 사용하여 이트륨을 분리하였다. 과망가니즈산 칼륨을 이용하여 세륨을 분리 후, PC88A (2-ethylhexylphosphonic acid mono-2-ethylhexyl ester)를 사용하여 란타넘과 네오디뮴을 분리하였다. 그 후 800 ℃의 온도에서 소성하여 란타넘, 네오디뮴 산화물로 재생하는 방법을 확인하였다.

• 공업화학
• /
• 제31권1호
• /
• pp.13-18
• /
• 2020

실크의 섬유 고분자 단백질인 피브로인을 사용하여 산화철 나노입자가 내포된 테라그노시스가 가능한 마이크로캡슐을 제조하였다. 열중량 분석으로 산화철의 함량은 4.28%, 자력계로는 5.11%로 측정되었다. 산화철 마이크로캡슐이 첨가된 마우스 섬유아세포 3T3 배양액에서 얻어진 세포 현탁액은 자력에 반응하여 맑게 변하고, 세포는 자석 방향으로 응집하였다. 배양접시 상단에 올려둔 네오디뮴 자석은 세포를 배양액 표면 중심으로 세포를 끌어모았다. 배양액 표면에 모인 세포들은 응집하여 72 h 이후 장축의 길이가 2 mm인 비대칭 타원체인 세포 집합체를 형성하였다. 세포집합체의 바깥층에는 세포들이 상대적으로 크고 서로 모여 치밀한 조직을 형성하였으나, 중심부는 물질전달제한으로 세포의 사멸이 진행되는 것으로 관찰되었다. 바깥층에는 산화철 마이크로캡슐이 자력의 방향으로 체인처럼 일렬로 늘어선 현상도 관찰되었다. 마이크로CT를 이용하여 세포응집체 내부의 산화철이 고루 분포하지 않고 자력 방향으로 비대칭적으로 분포하고 있음을 보였다.

• 공업화학
• /
• 제24권3호
• /
• pp.227-230
• /
• 2013

$(U_{1-x}Nd_x)O_2$ 소결체를 $500^{\circ}C$에서 산화하여 얻은 $(U_{1-x}Ndx)_3O_8$ 분말의 상변화를 $900{\sim}1500^{\circ}C$의 공기 중에서 고온 산화 열처리를 하여 조사하였다. $1100^{\circ}C$ 이상의 온도로 산화 열처리할 경우에 Nd 농도가 높은 $(U_{1-y}Nd_y)O_{2+z}$ 상과 $U_3O_8$ 상이 생성됨을 확인하였으며, 산화 열처리 온도가 높아질수록 $(U_{1-y}Nd_y)O_{2+z}$ 상에서의 Nd 농도는 감소하였다. 산화 열처리 온도의 증가에 따라서 $U_3O_{8-w}$ 입자로부터 $(U_{1-y}Nd_y)O_{2+z}$ 입자로의 U 양이온 및 Nd 양이온이 두 입자의 계면을 통해 농도 구배에 따른 확산에 의해서 $(U_{1-y}Nd_y)O_{2+z}$ 상 내에 U의 농도는 증가하고 Nd의 농도는 감소하게 된다. 이러한 현상은 산화 열처리 온도증가에 따라서 $U_3O_8$ 상에 대한 $(U_{1-y}Nd_y)O_{2+z}$ 상의 X-선 회절피크의 적분강도비 증가와 $(U_{1-y}Nd_y)O_{2+z}$ 상의 입자가 커지는 것과 연관하여 해석할 수 있었다.