• 한국정밀공학회지
• /
• 제10권2호
• /
• pp.146-153
• /
• 1993

Thd specimens were melited in high frequency induction furnace. The samples for measurements were prepared by machining cylinder of 9.5mm diameter and 15mm height. These samples were then hot-pressed according to strain rate ( .epsilon. ). These samples were decanned and cut out, and subsequently heat treated at 1000 .deg. C for 4hours. These were investigated for the change of microstructure, domain pattern, X-ray diffraction and magnetic properties. The stress distributions in the specimens during compressing process were calculated by a finite element method program(SPID). The calculated stresses were effective stress( .sigma. $_{eff}$), compressive direction stress( .sigma. $_{z}$), and shear stress( .tau. $_{rz}$ ). These stresses were compared with the experimental data.a.a.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 1998년도 춘계연구발표회 논문개요집
• /
• pp.88-89
• /
• 1998

• 한국자기학회지
• /
• 제14권5호
• /
• pp.196-200
• /
• 2004

고에너지 Nd-Fe-B소결자석 제조용 strip-cast합금의 미세조직을 개선하기 위하여, Nd$_{14}$Fe$_{80}$B$_{6}$6의 기본 조성에 소량의 Cu (0.3 ～ 1.0 at%) Co (0.5 ～ 1.5 at%)를 각각 첨가하고 strip-casting법으로 합금을 제조한 후, 이들 Fe 치환원소의 첨가량 변화가 합금의 상형성, 상분포 및 조직 형성에 미치는 영향을 조사하였다. Cu첨가량이 증가함에 따라 용탕의 유동성이 증가하여 strip 두께가 감소함과 함께 strip표면에 수직한 방향으로의 수지상정 발달이 억제되었으나, Co첨가량이 증가한 경우에는 strip두께의 증가와 함께 strip표면에 수직한 방향으로 수지상정이 잘 발달하여 <001>방향으로의 preferred orientation이 증가하는 경향을 보였다. 이들 Cu와 Co의 첨가는 모두 수지상정을 미세화하는 효과가 있었으나, Cu는 Fe의 정출을 안정화시키는 경향이 있어서 Cu가 함유된 함금에서는 종종 Fe가 종종 정출한 반면, Co는 초정 Fe의 정출을 억제하는 효과가 있었다. 한편, 소량의 Zr (0.3, 0.5 at%)을 첨가하였을 때에는 전체적인 결정립의 조대화와 함께 수지상정의 붕괴를 초래하였다.

• 한국자기학회지
• /
• 제5권1호
• /
• pp.38-41
• /
• 1995

$\alpha$-Fe를 주상으로 하는 새로운 Nd-Fe-B계 합금을 개발하기 위하여 Nd 함유량을 4at.%로 고정시킨 Nd-Fe-B 초미세결정립합금의 제조 및 자기특성이 조사되었다. 급속응고법으로 제조된 $Nd_{4}Fe_{85.5}B_{10.5}$ 비정질합금은 결정화하여 $\alpha$-Fe 기지상에 $Nd_{2}Fe_{14}B$이 형성되나 자기특성${_{i}H_{c}=95.5kA/m(1.2kOe),\;Br=1.2T}$은 열화된다. Nb 및 Cu를 첨가한 $Nd_{4}Fe_{82}B_{10}Nb_{3}Cu_{1}$ 합금은 $\alpha$-Fe 결정립미세화(<30nm)로 보자력이 207kA/m(2.6 kOe)로 증가하나 잔류자화는 개선되지 않았다. 이 합금조성에 8at.% Co 첨가는 결정립을 더욱 미세화시키며 자기특성을 개선 시킨다. 최적열처리조건에서 $Nd_{4}Fe_{74}Co_{8}B_{10}Nb_{3}Cu_{1}$ 합금의 잔류자화, 보자력 및 최대에너지적이 각각 1.34 T, 219 kA/m (2.75kOe) 및 $95.5kJ/m^{3}$(12MGOe) 이다.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 1993년도 추계연구발표회 논문개요집
• /
• pp.52-53
• /
• 1993

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2001년도 춘계연구발표회 논문개요집
• /
• pp.70-71
• /
• 2001

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2002년도 추계학술발표강연 및 논문개요집
• /
• pp.150-150
• /
• 2002

• 한국자기학회지
• /
• 제2권1호
• /
• pp.37-43
• /
• 1992

Pr, Nd-Fe-B계 합금을 주조 및 열간압축한 후 직류자화측정기와 진동시료형 자속계를 이용하여 자기적 특성을 측정하였다. 이 결과로부터 제 2상과 보자력과의 관계를 조사하였다. 주조시 $Pr_{17}Fe_{76.5}B_{5}Cu_{1.5}$계 합금에는 ${\alpha}-Fe$가, $Nd_{14}Dy_{1}Fe_{78.5}B_{5}Cu_{1.5}$계 합금에는 $Nd_{2}Fe_{17}$상이 각각 생성 되었다. 생성된 제 2상은 R(R=Pr, Nd)-Fe-B계 주조합금의 자기적 특성을 저하시킨다. 주조합금을 열처리하면 열자기분석 곡선에서 ${\alpha}-Fe$, $Nd_{2}Fe_{17}$상이 확인되지 않았다. 열처리 시 이와 같은 연자성상이 제거됨에 따라 열처리된 Pr, Nd-Fe-B계 주소합금의 자기적 특성은 증가하였다. Nd-Fe-B-Cu계 열간압축 자석에서의 보자력의 온도계수($\beta$)는 0.48로, 이를 Nd-Fe-B계 소결자석의 ${\beta}=0.86$, Nd-Fe-Co-B계 소결자석의 ${\beta}=0.5$와 비교해 보면 열간압축된 자석이 우수한 열적안정성을 나타냄을 알 수 있었다.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.421-426
• /
• 1995

The magnetic properties of the hot-pressed magnets made from the Fe-Nd-B alloys, mechanically ground and subsequently blended with binary additives such as Al-Cu and Ag-Zn before hot pressing, were investigated. The coercivities of the magnets increased as the concentration of Al-Cu increased up to 1 wt.% or up to 3 wt.% in the case of Ag-Zn. At higher concentrations the coercivities decreased markedly. The maximum gain in coercivity by the addition was about 20 %. typical values of $_{i}H_{c}$ and $B_{r}$ of a hotpressed magnet containing 1 wt.% Al-Cu were 18 kOe and 7 kG, respectively. It was found that Cu, Ag, and Zn, which diffused into the magnet during hot pressing, were mostly concentrated on the Nd-rich grain boundary phase whereas Al was present not only in the grain boundary region but also in the matrix grains.

• 열처리공학회지
• /
• 제7권1호
• /
• pp.61-71
• /
• 1994

This study is to investigate the stress distributions, crystal orientations and magnetic properties during die-upsetting according to working temperature of Nd-Fe-B-Cu alloys. The stress distributions in the specimens during compressing process were calculated by a finite element method program(SPID). The calculated stresses were effective stress (${\sigma}_{eff}$), compression stress(${\sigma}_z$), radial direction stress(${\sigma}_r$) rotational direction stress(${\sigma}_e$) and shear stress(${\tau}_{rz}$). The stress distributions of ${\sigma}_z$, obtained by a computer simulation showed that the stress components causing the magnetic alignment during die-upsetting of the cast magnets were very high at the center-part of a specimen, and decreased toward the periphery-part of a specimen. In view of the above results the magnetic properties should be better at the center-part of a specimen than any other parts. But the measured magnetic properties were better at the mid-part. These results should be due to the fact that the specimens were casted. Normally the magnetic properties are affected by the casting process as well as by the stress levels. ${\sigma}_r$, ${\sigma}_e$ are thought to affect the liquid phase flowing and domain patterns, respectively. The influence of ${\tau}_{rz}$ was trivial, ${\sigma}_{eff}$ distributed similar throughout the specimen. The Nd-rich phase appeared at the peripheral of the specimen where the stress level of ${\sigma}_r$, ${\sigma}_z$, was low or the stress level of ${\sigma}_e$ was high. The Nd-rich phase was squeezed out during die-upsetting. This phase had an effect on the crystal orientation and grain growth. The stress distributions of alloy were irregular at the parts of the specimen where the die contacted with specimen.