• Korean Journal of Materials Research
• /
• v.25 no.1
• /
• pp.48-53
• /
• 2015

$TiH_2$ nanopowder was made by high energy ball milling. The milled $TiH_2$ and CNT powders were then simultaneously synthesized and consolidated using pulsed current activated sintering (PCAS) within one minute under an applied pressure of 80 MPa. The milling did not induce any reaction between the constituent powders. Meanwhile, PCAS of the $TiH_2$-CNT mixture produced a Ti-TiC composite according to the reaction ($0.92TiH_2+0.08CNT{\rightarrow}0.84Ti+0.08TiC+0.92H_2$, $0.84TiH_2+0.16CNT{\rightarrow}0.68Ti+0.16TiC+0.84H_2$). Highly dense nanocrystalline Ti-TiC composites with a relative density of up to 99.7% were obtained. The hardness and fracture toughness of the dense Ti-8 mole% TiC and Ti-16 mole% TiC produced by PCAS were also investigated. The hardness of the Ti-8 mole% TiC and Ti-16 mole% TiC composites was higher than that of Ti. The hardness value of the Ti-16 mole% TiC composite was higher than that of the Ti-8 mole% TiC composite without a decrease in fracture toughness.

• Korean Journal of Materials Research
• /
• v.30 no.5
• /
• pp.252-261
• /
• 2020

We prepare ZnO nanoparticles by environmentally friendly synthesis using Cyathea nilgiriensis leaf extract. Various phytochemical constituents are identified through the assessment of ethanolic extract of plant Cyathea nilgiriensis holttum by GC-MS analysis. The formation of ZnO nanoparticles is confirmed by FT-IR, XRD, SEM-EDX, TEM, SAED and PSA analysis. TEM observation reveals that the biosynthesized ZnO nanopowder has a hexagonal structure. The calculated average crystallite size from the high intense plane of (1 0 1) is 29.11 nm. The particle size, determined by TEM analysis, is in good agreement with that obtained by XRD analysis. We confirm the formation of biomolecules in plant extract by FT-IR analysis and propose a possible formation mechanism of ZnO nanoparticles. Disc diffusion method is used for the analyses of antimicrobial activity of ZnO nanoparticles. The synthesized ZnO nanoparticles exhibit antimicrobial effect in disc diffusion experiments. The biosynthesized ZnO nanoparticles display good antibacterial performance against B. subtilis (Gram-positive bacteria) and K. pneumonia (Gram-negative bacteria). Bio-synthesized nanoparticles using green method are found to possess good antimicrobial performance.

• Korean Journal of Metals and Materials
• /
• v.48 no.11
• /
• pp.989-994
• /
• 2010

A nanopowder of TiAl was synthesized by high energy ball milling. Dense nanostuctured TiAl was consolidated using a high frequency induction heated sintering method within 2 minutes from mechanically synthesized powders of TiAl and horizontally milled powders of Ti+Al. Properties of the TiAl obtained using the two methods were compared. The grain size and hardness of TiAl sintered from horizontally milled Ti+Al powders and high energy ball milled TiAl powder were 40 nm, 20 nm, and $630kg/mm^2$, $700kg/mm^2$, respectively.

• Korean Journal of Metals and Materials
• /
• v.48 no.7
• /
• pp.639-643
• /
• 2010

Nanopowder of FeAl was synthesized by high energy ball milling. Using the pulsed current activated sintering method, a dense nanostuctured FeAl was consolidated within 2 minutes from mechanically synthesized powders of FeAl and horizontally milled powders of Fe+Al. The grain size and hardness of FeAl sintered from horizontally milled Fe+Al powders and high energy ball milled FeAl powder were 150 nm, 50 nm and $466\;kg/mm^2$, $574\;kg/mm^2$, respectively.

• Korean Journal of Materials Research
• /
• v.34 no.3
• /
• pp.138-143
• /
• 2024

Ni-CNT nanocomposites were synthesized via the electrical explosion of wire (EEW) in acetone and deionized (DI) water liquid conditions with different CNT compositions. The change in the shape and properties of the Ni-CNT nanopowders were determined based on the type of fluids and CNT compositions. In every case, the Ni nanopowder had a spherical shape and the CNT powder had a tube shape. However, the Ni-CNT nanopowders obtained in DI water exhibited irregular shapes due to the oxidation of Ni. Phase analysis also revealed the existence of nickel oxide when using DI water, as well as some unknown peaks with acetone, which may form due to the metastable phase of Ni. Magnetic properties were investigated using a Vibrating Sample Magnetometer (VSM) for all cases. Nanopowders prepared in DI water conditions had better magnetic properties than those in acetone, as evidenced by the simultaneous formation of super paramagnetic NiO peaks and ferromagnetic Ni peaks. The DI water (Ni:CNT = 1:0.3) sample revealed better magnetic results than the DI water (Ni-CNT = 1:0.5) because it had less CNT contents.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.6
• /
• pp.309-313
• /
• 2013

Silicon carbide (SiC) has recently drawn an enormous industrial interest because of its useful mechanical properties such as thermal resistance, abrasion resistance and thermal conductivity at high temperature. Especially, high purity SiC is applicable to the fields of power semiconductor and lighting emitting diode (LED). In this work, high purity carbon powders as raw material for high purity SiC were prepared by a RF induction thermal plasma. Dodecane ($C_{12}H_{26}$) as hydrocarbon liquid precursor has been utilized for synthesis of high purity carbon powders. It is found that the filtercollected carbon powders showed smaller particle size (10~20 nm) and low crystallinity compared to the reactor-collected carbon powders. The purities of reactor-collected and filter-collected carbon powders were 99.9997 % (5N7) and 99.9993 % (5N3), respectively. In addition, the impurities of carbon powders synthesized by RF induction thermal plasma were mainly originated from the surrounding environment.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.17-18
• /
• 2011

Plasma in liquid phase has attracted great attention in the last few years by the wide domain of applications in material processing, decomposition of organic and inorganic chemical compounds and sterilization of water. The plasma in liquid is characterized by three main regions which interact each - other during the plasma operation: the liquid phase, which supply the plasma gas phase with various chemical compounds and ions, the plasma in the gas phase at atmospheric pressure and the interface between these two regions. The most complex region, but extremely interesting from the fundamental, chemical and physical processes which occur here, is the boundary between the liquid phase and the plasma gas phase. In our laboratory, plasma in liquid which behaves as a glow discharge type, is generated by using a bipolar pulsed power supply, with variable pulse width, in the range of 0.5~10 ${\mu}s$ and 10 to 30 kHz repetition rate. Plasma in water and other different solutions was characterized by electrical and optical measurements. Strong emissions of OH and H radicals dominate the optical spectra. Generally water with 500 ${\mu}S/cm$ conductivity has a breakdown voltage around 2 kV, depending on the pulse width and the repetition rate of the power supply. The characteristics of the plasma initiated in ultrapure water between pairs of different materials used for electrodes (W and Ta) were investigated by the time-resolved optical emission and the broad-band absorption spectroscopy. The deexcitation processes of the reactive species formed in the water plasma depend on the electrode material, but have been independent on the polarity of the applied voltage pulses. Recently, Coherent anti-Stokes Raman Spectroscopy method was employed to investigate the chemistry in the liquid phase and at the interface between the gas and the liquid phases of the solution plasma system. The use of the solution plasma allows rapid fabrication of the metal nanoparticles without being necessary the addition of different reducing agents, because plasma in the liquid phase provides a reaction field with a highly excited energy radicals. We successfully synthesized gold nanoparticles using a glow discharge in aqueous solution. Nanoparticles with an average size of less than 10 nm were obtained using chlorauric acid solutions as the metal source. Carbon/Pt hybrid nanostructures have been obtained by treating carbon balls, synthesized in a CVD chamber, with hexachloro- platinum acid in a solution plasma system. The solution plasma was successfully used to remove the template remained after the mesoporous silica synthesis. Surface functionalization of the carbon structures and the silica surface with different chemical groups and nanoparticles, was also performed by processing these materials in the liquid plasma.

• Korean Journal of Materials Research
• /
• v.22 no.5
• /
• pp.220-226
• /
• 2012

Pure zirconia and $x$ mol% calcia partially stabilized zirconia ($x$ = 1.5, 3, and 8) nanopowders were synthesized by hydrothermal method with various reaction temperatures for 24 hrs. The precipitated precursor of pure zirconia and $x$ mol% calcia doped zirconia was prepared by adding $NH_4OH$ to starting solutions; resulting sample was then put into an autoclave reactor. The optimal experimental conditions, such as reaction temperatures and times and amounts of stabilizer CaO, were carefully studied. The synthesized $ZrO_2$ and $x$ mol% CaO-$ZrO_2$ ($x$ = 1.5, 3, and 8) powders were characterized by XRD, SEM, TG-DTA, and Raman spectroscopy. When the hydrothermal temperature was as low as $160^{\circ}C$, pure $ZrO_2$ and $x$ mol% CaO-$ZrO_2$ ($x$ = 1.5 and 3) powders were identified as a mixture of monoclinic and tetragonal phases. However, a stable tetragonal phase of zirconia was observed in the 8 mol% calcia doped zirconia nanopowder at hydrothermal temperature above $160^{\circ}C$. To observe the phase transition, the 3 mol% CaO-$ZrO_2$ and 8 mol% CaO-$ZrO_2$ nanopowders were heat treated from 600 to $1000^{\circ}C$ for 2h. The 3 mol% CaO-$ZrO_2$ heat treated at above $1000^{\circ}C$ was found to undergo a complete phase transition from mixture phase to monoclinic phase. However, the 8 mol% calcia doped zirconia appeared in the stable tetragonal phase after heat treatment. The result of this study therefore should be considered as the preparation of 8 mol% CaO-$ZrO_2$ nanopowders via the hydrothermal method.

• Korean Chemical Engineering Research
• /
• v.62 no.4
• /
• pp.344-354
• /
• 2024

Silica nanoparticles were synthesized by precipitation method using a Taylor vortex reactor from sulfuric acid and water glass as precursor materials. The effects of factors controlling the average particle size of the nanopowders, such as stirring speed and concentration of water glass, were derived from the experimental data, and the differences in average particle size and standard deviation were compared with those of a conventional reactor. It was found that the Taylor vortex reactor can be used to synthesize silica powder with a relatively uniform particle size. Utilizing MTCS, a silane coupling agent, the silica particles were modified to be hydrophobic by replacing the hydroxyl groups on the silica surface with methyl groups, and the surface modification conditions affecting the amount of oil absorption per unit mass of the hydrophobic powder were derived. Particles absorbing 3.14 times more oil per gram of silica powder were prepared, and are expected to be useful in the removal of contaminants.

• Journal of the Korean Ceramic Society
• /
• v.39 no.3
• /
• pp.321-326
• /
• 2002

ZnWO$_4$ nano-powders were successfully prepared by polymerized complex method using zinc nitrate and tungstic acid as starting materials. In order to investigate the thermal decomposition and crystallization process, the polymeric precursors were heat-treated at temperatures from 300 to 600$^{\circ}$C for 3 h, and the heat-treated powders were characterized by XRD and FTIR. The surface morphology of the heat-treated powders were observed using SEM and TEM. The crystallite size was measured by X-ray analysis. Crystallization of the ZnWO$_4$ powders were detected at 400$^{\circ}$C and entirely completed at a temperature of 600$^{\circ}$C. The particles heat-treated 400 and 500$^{\circ}$C showed primarily co-mixed morphology with spherical and silkworm-like forms, while the particles heat-treated at 600$^{\circ}$C showed more homogeneous morphology. The average crystalline size were 19.9∼24.nm showing an ordinary tendency to increase with the temperatures from 400 to 600$^{\circ}$C.