• KSTLE International Journal
• /
• 제9권1_2호
• /
• pp.13-16
• /
• 2008

Surface Engineering is a field closely related to Tribology. Surfaces are engineered to reduce adhesion, friction and wear between moving components in engineering applications. On the contrary, it is also necessary to have high adhesion between surfaces so as to hold/stick surfaces together. In this context, surface engineering plays an important role. In recent times, scientists are drawing inspiration from nature to create effective artificial adhesive surfaces. This article provides some examples of novel surface engineering approaches conducted by various research groups worldwide that have significantly contributed in the creation of bio-inspired artificial adhesive surfaces.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2000년도 제32회 추계학술대회 정기총회
• /
• pp.18-22
• /
• 2000

An experimental study was carried out to investigate the effect of nano-contact condition on the nano-adhesion phenomena. SPM(scanning probe microscope) tips with different radius of curvature were fabricated by a series of masking and etching processes. DLC(diamond-like carbon) and W-DLC (tungsten-incorporated diamond-like carbon) were coated on (100) silicon wafer by PACVD(plasma assisted chemical vapor deposition). Pull-off forces of Pure Si-wafer, DLC and W-DLC were measured with SPM(scanning probe microscope). Also, the same series of tests were carried out with the tips with different radius of curvature. Results showed that DLC and W-DLC showed much lower pull-off force than Si-wafer and Pull-off force increased with the tip radius.

• 한국전기전자재료학회논문지
• /
• 제29권11호
• /
• pp.690-695
• /
• 2016

Induction cooktop has a great attention due to its safety, quick heating and cleanness compared to gas oven. However, the materials for induction cookware is limited to steel or stainless-steel which has the magnetic property. Recently, it has been tried to apply various porcelain to induction cookware after printing the silver layer on the bottom of cookware plates and co-firing at high temperature. Glass frits are added in the silver paste to improve an adhesion force between porcelain materials containers and transferred silver layer. The hybrid silver pastes for induction cookware requires the proper electrical resistance and the thermal conductivity with base plates. After sintering process at $800^{\circ}C$, a part of melted glass migrated to the porcelain and the rest of the glass frit was exposed to the surface. It was confirmed that most of the glass frit formed an adhesion layer between the porcelain and transferred silver layer that enhances the adhesion force.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2001년도 제34회 추계학술대회 개최
• /
• pp.35-42
• /
• 2001

Nanotribological characteristics between a Si$_3$N$_4$ AFM tip and hydrophobic thin films were experimentally studied. Tests were performed to measure the nano adhesion and friction in both AFM(atomic force microscope) and LFM(lateral force microscope) modes in various ranges of normal load. Plasma-modified thin polymeric films were deposited on Si-wafer (100). Results showed that wetting angle of plasma-modified thin polymeric film increased with the treating time, which resulted in the hydrophobic surface and the decrease of adhesion and friction. Nanotribological characteristics of these surfaces were compared with those of other hydrophobic surfaces, such as DLC, OTS and IBAD-Ag coated surfaces. Those of OTS coated surface was superior to those of others, though wetting angle of plasma-modified thin polymeric film is higher.

• BMB Reports
• /
• 제46권5호
• /
• pp.276-281
• /
• 2013

In this study, we aimed to compare the morphogenetic and neuronal characteristics between monolayer cells and spheroids. For this purpose, we established spheroid formation by growing SH-SY5Y cells on the hydrophobic surfaces of thermally-collapsed elastin-like polypeptide. After 4 days of culture, the relative proliferation of the cells within spheroids was approximately 92% of the values for monolayer cultures. As measured by quantitative assays for mRNA and protein expressions, the production of synaptophysin and neuronspecific enolase (NSE) as well as the contents of cell adhesion molecules (CAMs) and extracellular matrix (ECM) proteins are much higher in spheroids than in monolayer cells. Under the all-trans-retinoic acid (RA)-induced differentiation condition, spheroids extended neurites and further up-regulated the expression of synaptophysin, NSE, CAMs, and ECM proteins. Our data indicate that RA-differentiated SH-SY5Y neurospheroids are functionally matured neuronal architectures.

• 폴리머
• /
• 제39권1호
• /
• pp.99-106
• /
• 2015

나노케냐프 섬유가 포함된 셀룰로스 섬유를 알카리(NaOH)로 처리 후 PP 수지에 첨가하여 물성에 미치는 영향에 대하여 조사하였다. 알카리를 섬유에 처리한 효과로는 M.I., 신장율, 충격강도가 증가하는 반면 인장강도, 휨모듈러스, 열변형온도가 처리하지 않은 섬유에 비해 감소하였다. 알카리를 나노섬유에 처리하였을 때 섬유표면의 불순물과 화학물질을 제거하여 섬유표면의 특성을 변화시켜서 나노섬유와 PP 수지간의 계면간 접착력을 감소시키고 PP의 특성을 변화시키는 것으로 보인다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 추계학술대회 논문집
• /
• pp.245-245
• /
• 2009

l-D nanostructured materials have much more attention because of their outstanding properties and wide applicability in device fabrication. Copper oxide(CuO) has been realized as a p-type metal oxide semiconductor with narrow band gap of 1.2 -1.5eV. Copper oxide nanostructures can be synthesized by various growth method such as oxidation reaction, thermal evaporation thermal decomposition, sol-gel. and Mostly CuO nanowire prepared on the Cu substrate such as Copper foil, grid, plate. In this study, CuO NWs were grown by thermal oxidation (at various temperatures in air (1 atm)) of Cu metal deposited on CuO (20nm)/$SiO_2$(250nm)/Si. A 20nm-thick CuO layer was used as an adhesion layer between Cu metal and $SiO_2$

• KSTLE International Journal
• /
• 제3권1호
• /
• pp.12-16
• /
• 2002

Micro/nano tribological and water wetting characteristics of ion beam treated PTFE (polytetrafluoroethylene) surfaces were experimentally studied. The ion beam treatment was performed with a hollow cathode ion gun at different argon ion dose conditions in a vacuum chamber to modify the topography of PTFE surface. Micro/nano tribological characteristics, water wetting angles and roughness were measured with a micro tribe tester, SPM (scanning probe microscope), contact anglemeter and profilometer, respectively. Results showed that surface roughness increased with the argon ion dose. Water wetting angle of the ion beam treated samples increased with the ion dose, so the surface shows an ultra-hydrophobic nature. Micro-adhesion and micro-friction depend on the wetting characteristics of the PTFE samples. However, nano-tribological characteristics showed different results. The scale effect of surface topography on tribological characteristics was discussed. Also, the water wetting characteristics of modified PTFE samples were discussed in terms of the surface topographic characteristics.

• 한국초전도ㆍ저온공학회논문지
• /
• 제11권1호
• /
• pp.1-4
• /
• 2009

Mechanical and electrical properties of silver stabilizer layer of coated conductor, which as prepared with nano silver paste as starting materials, have been investigated, Nano silver paste was coated on a YBCO film by dip coating process at a diping speed of 20m/min. Coated film was dried in air and heat treated at $400{\sim}700^{\circ}C$ in an oxygen atmosphere. Adhesion strength between YBCO and silver layer was measured by a tape est(ASTM D 3359). Hardness and electrical conductivity of the samples were measured by pencil hardness test (ASTM D 3363) and volume resistance test by LORESTA-GP (MITSHUBISHD, respectively. The sample heat-treated at $500^{\circ}C$ showed poor adhesion 1B, but samples heat treated at higher than $600^{\circ}C$ showed enhanced adhesion of 5B. The silver layer heat-treated at $700^{\circ}C$ showed the high hardness value larger than 9 H, low volume resistance, surface resistance value as well as superior current carrying capacity compared to sputtered silver. SEM observations showed that a dense silver layer was formed with a thickness of about $2{\mu}m$. Dip coated silver layer prepared by using nano silver paste showed superior electrical and mechanical characteristics.

• 접착 및 계면
• /
• 제6권1호
• /
• pp.7-10
• /
• 2005

Condensation control of nano-particles has become important in order to fabricate minute condensed structures. In this study, we focus our attention on condensation mechanism of polymer aggregates in a resist film. The polymer aggregate is structural component of a resist material which is used in lithography process. The condensation nature of polymer aggregates in the resist film surface is observed by using atomic force microscope (AFM). By using the AFM, the condensation of polymer aggregates can be observed clearly. The condensation of polymer aggregate strongly affects to precise fabrication of resist pattern below 100nm size. The interaction force among polymer aggregates can be analyzed based on Derjaguin approximation. We also discuss about condensation nature of polymer aggregates in the resist film surface with the help of micro sphere model.