• Journal of Powder Materials
• /
• v.14 no.2 s.61
• /
• pp.97-100
• /
• 2007

The magnetic alloys of Cu-Fe ($Cu_{50}Fe_{50},\;Cu_{80}Fe_{20}\;and\;Cu_{90}Fe_{10}$) were prepared by a mechanical alloying method and their structural and magnetic behaviors were examined by X-ray diffraction and Mossbauer spectra. The magnetization curves did not distinctly show the saturation at 70 kOe for the concentrated alloys of $Cu_{80}Fe_{20}\;and\;Cu_{90}Fe_{10}$. The Mossbauer spectrum of $Cu_{80}Fe_{20}$ at room temperature shows one Lorentzian line of the paramagnetic phase, whereas the Mossbauer spectrum of $Cu_{90}Fe_{10}$ consists of sextet Lorentzian line at room temperature and a centered doublet line. The Mossbauer spectra of $Cu_{90}Fe_{10}$ measured in the temperature ranges from 13 to 295 K, implies that $Cu_{90}Fe_{10}$ to consists of two magnetic phases. One superimposed sextet corresponds to the ferromagnetic iron in Cu and the other one indicates the superparamagnetic iron rich phase.

• Progress in Superconductivity
• /
• v.10 no.1
• /
• pp.12-16
• /
• 2008

In this work, nano size $BaCeO_3$, which is a possible flux pinning medium of melt processed $YBa_{2}Cu_{3}O_x$ superconductor, was synthesized by the conventional solid state reaction method using powders. $BaCeO_3$ and $CeO_2$ were mixed thoroughly using a ball milling for 24 hours and calcined at $1200^{\circ}C$ for 5 hours for the formation $BaCeO_3$ powder. The obtained $BaCeO_3$ powder was attrition milled at various milling times of 60 min, 120 min and 240 min. The $BaCeO_3$ powders of various milling times were mixed with $YBa_{2}Cu_{3}O_x$ powder. Seed melt processed $YBa_{2}Cu_{3}O_x$-$BaCeO_3$ (15wt.%) superconductors were prepared and the superconducting properties were investigated. It was found that $T_c$ of $Y_{1.5}Ba_{2}Cu_{3}O_x$ samples was not significantly affected by $BaCeO_3$ addition, but $J_c$ of samples was increased by $BaCeO_3$ addition. The $J_c$ improvement by fine $BaCeO_3$ powder (120 min attrition-milled) was effective at low magnetic fields less than 2 T.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2001.05a
• /
• pp.37-37
• /
• 2001

• Journal of Powder Materials
• /
• v.9 no.1
• /
• pp.19-24
• /
• 2002

This paper reports the results of an investigation into the effect of Cu additions upon the nano-crystallization behaviour of an Al-Y-Ni alloy. 1 at.% Cu was added to a base alloy of Al/sub 88/Y₄Ni/sub 8/ either by substitution for Al to form Al/sub 87/Y₄Ni/sub 8/Cu₁, or by substitution for Ni to form Al/sub 88/Y₄Ni/sub 7/Cu₁. Consistent with previous findings in the literature, the substitution of Cu for Al was found to increase the thermal stability of the amorphous phase whereas the substitution of Cu for Ni was found to decrease its thermal stability. Comparing the microstructures of these alloys after heat treatment to produce equivalent volume fractions of Al nanocrystals showed average grain sizes of 14 nm, 12 nm and 9 nm for the alloys Al/sub 88/Y₄Ni/sub 8/, Al/sub 87/Y₄Ni/sub 8/Cu₁respectively. The effect of Cu in refining the size of the nanocrystals was attributed to enhanced nucleation increasing the number density of the nanocrystals, rather than diffusion limited or interface limited growth.

• Journal of Powder Materials
• /
• v.21 no.1
• /
• pp.16-20
• /
• 2014

In order to fabricate the porous $Al_2O_3$ with dispersion of nano-sized Cu particles, freeze-drying of camphene/$Al_2O_3$ slurry and solution chemistry process using Cu-nitrate are introduced. Camphene slurries with 10 vol% $Al_2O_3$ was frozen at $-25^{\circ}C$. Pores were generated by sublimation of the camphene during drying in air. The sintered samples at 1400 and $1500^{\circ}C$ showed the same size of large pores which were aligned parallel to the sublimable vehicles growth direction. However, the size of fine pores in the internal walls of large pores decreased with increase in sintering temperature. It was shown that Cu particles with the size of 100 nm were homogeneously dispersed on the surfaces of the large pores. Antibacterial test using fungus revealed that the porous $Al_2O_3$/1 vol% Cu composite showed antifungal property due to the dispersion of Cu particles. The results are suggested that the porous composites with required pore characteristics and functional property can be fabricated by freeze-drying process and addition of functional nano particles by chemical method.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.20 no.1
• /
• pp.1-6
• /
• 2010

CuInGaSe(CIGS) mixed-source was prepared by hydride vapor phase epitaxy (HVPE). Each metal was mixed in regular ratio and soaked at $1090^{\circ}C$ for 90 minutes in nitrogen atmosphere. After making the mixed-source to powder state, the pellet was made by the powder. The diameter of pellet is 10 mm. The CIGS thin film was deposited on soda lime glass evaporated Mo layer bye-beam evaporator. To confirm the crystallization, we measured X-ray diffraction (XRD). High intensity X-ray peaks diffracted from (112), (204)/(220), (116)/(312) and (400) of CIGS thin film and from (110) of Mo were confirmed by XRD measurement.

• Journal of Powder Materials
• /
• v.14 no.4
• /
• pp.261-264
• /
• 2007

The electromagnetic wave (EM) absorption properties of various particle size have been investigated in a sheet-type absorber using the $Fe_{73}Si_{16}B_{7}Nb_{3}Cu_{1}$ alloy powder. With decreasing the average particle size, the complex permeability (${\mu}_{r}$) and permittivity (${\varepsilon}_{r}$) increased and the matching frequency is shifted toward lower frequency. The fabricated EM wave absorbers showed permeability $2{\sim}6$, permittivity $17{\sim}23$ for a $-325{\sim}+400$ mesh sample, and the calculated power absorption was as high as 80% in the frequency range over 2 GHz.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2003.10a
• /
• pp.136-137
• /
• 2003

In this study, in order to fabricate sintered dental implant, the effects of HA, Ti and TiN on corrosion and biocompatibility, cell toxicity, osseointegration of electroless Cu-plated and sintered stainless steel implant were investigated using various characteristics. The effects of Ti/TiN/HA coating on the interface activation and surface characteristics of sintered stainless steels(SSS) by electron-beam physical vapor deposition(EB-PVD) method have been studied. Stainless steel compacts containing 2, 4, and 10 wt%Cu were prepared by electroless Cu-plating method which results in the increased homogenization in alloying powder. The specimens were coated with HA, Ti and TiN with few $\mu\textrm{m}$ thickness respectively by EB-PVD method. The microstructures and phase analysis were conducted by using SEM. Biocompatibility were investigated in experimental dog. The corrosion behaviors were investigated using potentiosat in 0.9% NaCl solution and corrosion surface was observed using SEM and XPS.

• Journal of Powder Materials
• /
• v.9 no.2
• /
• pp.110-115
• /
• 2002

In order to obtain the nano size $10wt%Cu-TiO_2$composite powders by mechanical alloying method for useful composite catalysis, the effects of mechanical alloying time on the formationof $10wt%Cu-TiO_2$ composite powders were analyzed. The phase transformation behaviors were experimented as the heat treating temperature increased. Homogeneous 10wt% Cu-rutile type $TiO_2$composite powders were synthesized in 40 hours by mechanical alloying. After 60 hours mechanical alloying 50 nm size $TiO_2$powders were obtained. Both the phase of mechanically alloyed 10 wt% $Cu-TiO_2$ and pure $TiO_2$ powders were not transformed to anatase after annealing at the temperature range between 350 to 500 $^{\circ}C$. The intermetallic compound of $Cu_2Ti_4$O was formed after 10 hours mechanical alloying, however it could be considered that this intemetallic phase dose not prevent the transformation of rutile $TiO_2$ to the anatase phase after heat treatment at the temperature between 350 and $550^{\circ}C$.

• Journal of Powder Materials
• /
• v.15 no.3
• /
• pp.227-233
• /
• 2008

Dynamic plastic deformation behavior of copper particles occurred during the cold spray processing was numerically analyzed using the finite element method. The study was to investigate the impact as well as the heat transfer phenomena, happened due to collision of the copper particle of $20{\mu}m$ in diameter with various initial velocities of $300{\sim}600m/s$ into the copper matrix. Effective strain, temperature and their distribution were investigated for adiabatic strain and the accompanying adiabatic shear localization at the particle/substrate interface.