• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.1
• /
• pp.33-40
• /
• 1998

The composite SiO$_2$/Si$_3$N$_4$/SiO$_2$(ONO) film formed by oxidation on nitride film has been widely studied as DRAM stacked capacitor multi-dielectric films. Load lock(L/L) LPCVD system by HF cleaning is used to improve electrical capacitance and to scale down of effective thickness for memory device, but is brings a new problem. Nitride film deposited using HF cleaning shows selective deposition on poly silicon and oxide regions of capacitor. This problem is avoidable by carpeting chemical oxide using $H_2O$$_2$cleaning before nitride deposition. In this paper, we study the limit of nitride thickness for abnormal oxidation and the initial deposition time for nitride deposition dependent on underlayer materials. We proposed an advanced fabrication process for stacked capacitor in order to avoid selective deposition problem and show the usefulness of nitride deposition using L/L LPCVD system by $H_2O$$_2$cleaning. The natural oxide thickness on polysilicon monitor after HF and $H_2O$$_2$cleaning are measured 3~4$\AA$, respectively. Two substrate materials have the different initial nitride deposition times. The initial deposition time for polysilicon is nearly zero, but initial deposition time for oxide is about 60seconds. However the deposition rate is constant after initial deposition time. The limit of nitride thickness for abnormal oxidation under the HF and $H_2O$$_2$cleaning method are 60$\AA$, 48$\AA$, respectively. The results obtained in this study are useful for developing ultra thin nitride fabrication of ONO scaling and for avoiding abnormal oxidation in stacked capacitor application.

• Korean Journal of Materials Research
• /
• v.11 no.7
• /
• pp.575-579
• /
• 2001

GaN buffer layer and epilayer have been grown on sapphire (0001) by metal organic chemical vapor deposition (MOCVD). GaN buffer layer ranging from 26 nm to 130 nm in thickness was grown at 55$0^{\circ}C$ prior to the 4 $\mu\textrm{m}$ thick GaN epitaxial deposition at 110$0^{\circ}C$. After GaN buffer layer growth, buffer layer surface was examined by atomic force microscopy (AFM). As the thickness of GaN buffer layer was increased, surface morphology of GaN epilayer was investigated by scanning electron microscopy (SEM). Double crystal X-ray diffraction (DCXRD) and Raman spectroscopy were employed to study crystallinity of GaN epilayers. Optical properties of GaN epilayers were measured by photoluminescence (PL). The epilayer grown with a thin buffer layer had rough surface, and the epilayer grown with a thick buffer layer had mirror-like surface of epilayer. Although the stress on the latter was larger than on the former, its crystallinity was much better. These results imply that the internal free energy is decreased in case of the thick buffer layer. Decrease in internal free energy promotes the lateral growth of the GaN film, which results in the smoother surface and better crystallinity.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.20 no.8
• /
• pp.2626-2636
• /
• 1996

A study of soot deposition and reentrainment was carried out both theoretically and experimentally to understand behavior of soot formed by incomplete combustion in a diesel engine. Theoretically, soot deposition on engine cylinder wall and/or piston head was studied with a stagnation point flow approximation. Soot reentrainment occurred upon exhaust gas blowdown was also studied by assuming a long-normal shear velocity distribution. Experimentally, a LPG$O_2/N_2$ flame impinging on a disk, produced by a concentric tubular burner, was chosen as deposition configuration and a shear flow unit with compressed air was installed for the study of reentrainment. For selected flame configuration, soot deposition measurements were conducted and showed that the dominant deposition mechanism was thermophoresis. Distributions of gas temperature and soot number density were estimated by combining data obtained by a B-type thermocouple with a thermophoretic transport theory. Disk temperature distributions were directly measured using a K-type thermocouple. Soot size and morphology were estimated from a TEM photograph. Ratios of soot deposit to reentrained amount were measured for a wide range of shear flow velocities, which showed that the reentrainment model was reasonable.

• Korean Journal of Air-Conditioning and Refrigeration Engineering
• /
• v.5 no.2
• /
• pp.130-140
• /
• 1993

Average particle deposition velocity toward a horizontal semiconductor wafer in vertical airflow is measured by a wafer surface scanner(PMS SAS-3600). Use of wafer surface scanner requires very short exposure time normally ranging from 10 to 30 minutes, and hence makes repetition of experiment much easier. Polystyrene latex (PSL) spheres of diameter between 0.2 and $1.0{\mu}m$ are used. The present range of particle sizes is very important in controlling particle deposition on a wafer surface in industrial applications. For the present experiment, convection, diffusion, and sedimentation comprise important agents for deposition mechanisms. To investigate confidence interval of experimental data, mean and standard deviation of average deposition velocities are obtained from more than ten data set for each PSL sphere size. It is found that the distribution of mean of average deposition velocities from the measurement agrees well with the predictions of Liu and Ahn(1987) and Emi et al.(1989).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.356-356
• /
• 2007

Plasma immersion ion beam deposition (PIIBD) technique is a cost-effective process for the deposition of diamond like carbon thin film, the possible solid lubricant on large surface and a complex shape. We used PIIB process for the preparation of DLC thin film on $Al_2O_3$ with deposition conditions of deposition temperature range $200^{\circ}C$, working gas pressure of 1.310-1Pa. DLC thin films were coated by $C_2H_2$ ion beam deposition on $Al_2O_3$ after the ion bombardment of SiH4 as the bonding layer. Energetic bombardment of $C_2H_2$ ions during the DLC deposition to ceramic materials generated mixed layers at the DLC-Si interface which enhanced the interface to be highly bonded. Wear test showed that the low coefficient of friction of around 0.05 with normal load 2.9N and proved the advantage of the low energy ion bombardment in PIIBD process which improved the tribological properties of DLC thin film coated alumina ceramic. Furthermore, PIIBD was recognized as a useful surface modification technique for the deposition of DLC thin film on the irregular shape components, such as molds, and for the improvement of wear and adhesion problems of the DLC thin film, high temperature solid lubricant.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.7
• /
• pp.532-536
• /
• 2011

The silicon nitride films were prepared by chemical vapor deposition using inductively coupled plasma. During the deposition, the substrate was heated at $150^{\circ}C$ and power 1,000 W. To evolution low temperature manufacture, we have studied the role of source gases, $SiH_4$, $NH_3$, $N_2$, and $H_2$, to produce Si-N and N-H bond in a-SiNx:H film growth. $SiH_4$, $NH_3$, and $N_2$ flow rate fixed at 100, 10, and 10 sccm, $H_2$ flow rate varied from 0 to 10 sccm by small scale. To get the electrical characteristics, we makes MIM structure, and analysis surface bonding state. Experimental data show that Si-N and N-H bond is increased and hence electrical characteristics is showed 3 MV/cm breakdown-voltage, and leakage-current $10^{-7}\;A/cm^2$.

• Asian Journal of Atmospheric Environment
• /
• v.5 no.2
• /
• pp.134-143
• /
• 2011

The present study aimed to investigate the diurnal variations in air concentrations and exchange fluxes of ammoniacal nitrogen ($NH_x$: ammonia ($NH_3$) and particulate ammonium) in a subalpine deciduous forest in central Japan during a week in summer. The $NH_3$ concentrations ($0.50\;{\mu}g\;N\;m^{-3}$ on average) showed a clear circadian variation, i.e., high and low in the daytime and nighttime, respectively. The concentration of particulate ammonium in the coarse fractions was extremely low, whereas that for the PM2.5 fraction was relatively high $0.55\;{\mu}g\;N\;m^{-3}$ on average). The main inorganic ion components of PM2.5 at the study site were ammonium and sulfate. The exchange fluxes of $NH_x$ were bidirectional. Both the maximum and minimum values occurred in the daytime, i.e., $0.39\;mg\;N\;m^{-2}\;hr^{-1}$ of downward flux and $0.11\;mg\;N\;m^{-2}\;hr^{-1}$ of upward flux for $NH_3$ and $0.25\;mg\;N\;m^{-2}\;hr^{-1}$ of downward flux and $0.13\;mg\;N\;m^{-2}\;hr^{-1}$ of upward flux for PM2.5 ammonium. The exchange fluxes of $NH_x$ at night could be considered as zero. The mean deposition velocity during the research period was almost zero for both $NH_3$ and PM2.5 ammonium. The atmosphere-forest exchange of $NH_x$ in the forest during the study period was balanced. The remarkably large deposition of $NH_x$ was attributable to meteorological events such as showers the night before that thoroughly washed the forest canopy and subsequent clear skies in the morning, which enhanced convection. The cleaning effect of rainfall and the rapid change in convection in the early morning should be monitored to evaluate and generalize the gas and particle exchange in a forest.

• Journal of the Semiconductor & Display Technology
• /
• v.13 no.3
• /
• pp.27-33
• /
• 2014

To develop high efficiency crystalline solar cells, the $SiN_x$ film for surface passivation and anti-reflection coating is very important and it is generally deposited by PECVD. In this paper, the $SiN_x$ film deposited by Hot-Wire chemical vapor deposition(HWCVD) that has no plasma damage was studied. First, to optimize the $SiN_x$ film deposition process, $SiH_4$ gas rate and substrate temperature were varied and then refractive index and thickness were measured. When $SiH_4$ gas rate was 22sccm and substrate temperature was $100^{\circ}C$, refractive index was 1.94 and higher than that of other process conditions. Second, the lifetime was measured by varying the annealing temperature and time. The annealing process was made from 5 to 30 minutes at $300{\sim}500^{\circ}C$. When the annealing temperature was $100^{\circ}C$ and time was 10minute, the lifetime was the highest. The lifetime of annealed samples was also measured after the firing process at $975^{\circ}C$. Although the lifetime of all samples was decreased by firing process, the lifetime of annealed samples before the firing process was higher than that of fired samples only. Finally, the characteristics of solar cells with HWCVD $SiN_x$ film were measured.

• Journal of the Korean Vacuum Society
• /
• v.7 no.s1
• /
• pp.85-99
• /
• 1998

A ultrahigh vacuum chemical vapor deposition(UHVCVD)/metalorganic chemical vapor deposition(MOMBE) system equipped with a radio frequency(RF)-plasma cell was employed to grow GaN layer on the sapphire at a low temperature. The x-ray photoelectron spectroscopy analysis of nitrogen composition on the nitridated sapphite surface indicated that a nitridation process is mostly affected by the RF power at low temperature. Atomic force microscope images of nitridated surface the protrusion density on the nitridated sapphire is dependent on the nitridation temperature. The crystallinity of GaN grown at $450^{\circ}C$ was found to be much improved when the sapphire was nitridated at low temperature prior to the GaN layer growth. Moreover, a strong photoluminescence spectrum of GaN grown by UHVCVD/MOMBE with a rf-nitrogen plasma was observed for the first time at room temperature.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.189-189
• /
• 2016

In this study, the Al-rich AlTiSiN thin films that consisted of TiN/AlSiN nano-multilayers were deposited on the steel substrate by magnetron sputtering, and their high-temperature oxidation behavior was investigated, which has not yet been adequately studied to date. Since the oxidation behavior of the films depends sensitively on the deposition method and deposition parameters which affect their crystallinity, composition, stoichiometry, thickness, surface roughness, grain size and orientation, the oxidation studies under various conditions are imperative. AlTiSiN nano-multilayer thin films were deposited on a tool steel substrate, and their oxidation behavior of was investigated between 600 and $1000^{\circ}C$ in air. Since the amount of Al which had a high affinity for oxygen was the largest in the film, an ${\alpha}-Al_2O_3-rich$ scale formed, which provided good oxidation resistance. The outer surface scale consisted of ${\alpha}-Al_2O_3$ incoporated with a small amount of Ti, Si, and Fe. Below this outer surface scale, a thin ($Al_2O_3$, $TiO_2$, $SiO_2$)-intermixed scale formed by the inwardly diffusing oxygen. The film oxidized slower than the $TiO_2-forming$ kinetics and TiN films, but faster than ${\alpha}-Al_2O_3-forming$ kinetics. During oxidation, oxygen from the atmosphere diffused inwardly toward the reaction front, whereas nitrogen and the substrate element of iron diffused outwardly to a certain extent.