• Journal of Powder Materials
• /
• v.23 no.3
• /
• pp.207-212
• /
• 2016

In this study, Fe-Cu-Ni-Mo-C low alloy steel powder is consolidated by spark plasma sintering (SPS) process. The internal structure and the surface fracture behavior are studied using field-emission scanning electron microscopy and optical microscopy techniques. The bulk samples are polished and etched in order to observe the internal structure. The sample sintered at $900^{\circ}C$ with holding time of 10 minutes achieves nearly full density of 98.9% while the density of the as-received conventionally sintered product is 90.3%. The fracture microstructures indicate that the sample prepared at $900^{\circ}C$ by the SPS process is hard to break out because of the presence of both grain boundaries and internal particle fractures. Moreover, the lamellar pearlite structure is also observed in this sample. The samples sintered at 1000 and $1100^{\circ}C$ exhibit a large number of tiny particles and pores due to the melting of Cu and aggregation of the alloy elements during the SPS process. The highest hardness value of 296.52 HV is observed for the sample sintered at $900^{\circ}C$ with holding time of 10 minutes.

• Korean Journal of Materials Research
• /
• v.27 no.9
• /
• pp.489-494
• /
• 2017

ZnS powder was synthesized using a relatively facile and convenient glycothermal method at various reaction temperatures. ZnS was successfully synthesized at temperatures as low as $125^{\circ}C$ using zinc acetate and thiourea as raw materials, and diethylene glycol as the solvent. No mineralizers or precipitation processes were used in the fabrication, which suggests that the spherical ZnS powders were directly prepared in the glycothermal method. The phase composition, morphology, and optical properties of the prepared ZnS powders were characterized using XRD, FE-SEM, and UV-vis measurements. The prepared ZnS powders had a zinc blende structure and showed average primary particles with diameters of approximately 20~30 nm, calculated from the XRD peak width. All of the powders consisted of aggregated secondary powders with spherical morphology and a size of approximately $0.1{\sim}0.5{\mu}m$; these powders contained many small primary nanopowders. The as-prepared ZnS exhibited strong photo absorption in the UV region, and a red-shift in the optical absorption spectra due to the improvement in powder size and crystallinity with increasing reaction temperature. The effects of the reaction temperature on the photocatalytic properties of the ZnS powders were investigated. The photocatalytic properties of the as-synthesized ZnS powders were evaluated according to the removal degree of methyl orange (MO) under UV irradiation (${\lambda}=365nm$). It was found that the ZnS powder prepared at above $175^{\circ}C$ exhibited the highest photocatalytic degradation, with nearly 95 % of MO decomposed through the mediation of photo-generated hydroxyl radicals after irradiation for 60 min. These results suggest that the ZnS powders could potentially be applicable as photocatalysts for the efficient degradation of organic pollutants.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1996.11a
• /
• pp.6-6
• /
• 1996

Ceramic based nanocomposite, in which nano-sized ceramics and metals were dispersed within matrix grains and/or at grain boundaries, were successfully fabricated in the ceramic/cerarnic and ceramic/metal composite systems such as $Al_2O_3$/SiC, $Al_2O_3$/$Si_3N_4$, MgO/SiC, mullite/SiC, $Si_3N_4/SiC, $Si_3N_4$/B, $Al_2O_3$/W, $Al_2O_3$/Mo, $Al_2O_3$/Ni and $ZrO_2$/Mo systems. In these systems, the ceramiclceramic composites were fabricated from homogeneously mixed powders, powders with thin coatings of the second phases and amorphous precursor composite powders by usual powder metallurgical methods. The ceramiclmetal nanocomposites were prepared by combination of H2 reduction of metal oxides in the early stage of sinterings and usual powder metallurgical processes. The transmission electron microscopic observation for the $Al_2O_3$/SiC nanocomposite indicated that the second phases less than 70nm were mainly located within matrix grains and the larger particles were dispersed at the grain boundaries. The similar observation was also identified for other cerarnic/ceramic and ceramiclmetal nanocornposites. The striking findings in these nanocomposites were that mechanical properties were significantly improved by the nano-sized dispersion from 5 to 10 vol% even at high temperatures. For example, the improvement in hcture strength by 2 to 5 times and in creep resistance by 2 to 4 orders was observed not only for the ceramidceramic nanocomposites but also for the ceramiclmetal nanocomposites with only 5~01%se cond phase. The newly developed silicon nitride/boron nitride nanocomposites, in which nano-sized hexagonal BN particulates with low Young's modulus and fracture strength were dispersed mainly within matrix grains, gave also the strong improvement in fracture strength and thermal shock fracture resistance. In presentation, the process-rnicro/nanostructure-properties relationship will be presented in detail. The special emphasis will be placed on the understanding of the roles of nano-sized dispersions on mechanical properties.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.6
• /
• pp.1555-1559
• /
• 2008

The characteristics of 304 (Fe-18%Cr-12%Ni) and 316L (Fe-18%Cr-13%Ni-2.4%Mo) austenite stainless-steel compacts sintered with $5{\sim}15{\mu}m$ powder were investigated and the results led to the following conclusions: (1) When the sintering time was 3.6ks, the relative density of sintered compacts was $95{\sim}98%$, regardless of any other sintering condition. (2) When a vacuum sintering was done with $5{\mu}m$ stainless steel powders, almost fully-dense sintered compacts were obtained at is = 57.6ks. (3) The amount of residual oxygen in 304 and 316L sintered compacts was $0.5{\sim}0.6%$, regardless of sintering atmosphere. (4) The amount of residual oxygen in the vacuum sintered compact decreased more than 0.3 % due to addition of carbon powder, thereby reducing the formation of oxides. Furthermore, the addition of carbon improved the density of sintered compact, which enables us to make a fully-dense high performance sintered compact.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1997.04a
• /
• pp.34-34
• /
• 1997

The effect of alloying mode and porosity on the axial tension-tension fatigue behavior of a P/M steel of nominal composition Fe-4w/o Ni-1.5w/o Cu-O.5w/o Mo-O.5w/o C has been evaluated. Alloying modes utilized were elemental powder mixing, partial alloying(distaloy) and prealloying by water atomization; in each case the carbon was introduced as graphite prior to sintering. Powder compacts were sintered($1120{\circ}C$/30 min.) in 7Sv/o $H_2$/25v/o $N_2$ to densities in the range 6.77-7.2 g/$cm^3$. The dependence of fatigue limit response on alloying mode and porosity was interpreted in terms of the constituent phases and the pore and fracture morphologies associated with the three alloying modes. For the same nominal composition, the three alloying modes resulted in different sintered microstructures. In the elemental mix alloy and the distaloy, the major constituent was coarse and fine pearlite, with regions of Ni-rich ferrite, Ni-rich martensite and Ni-rich areas. In contrast, the prealloy consisted primarily of martensite by with some Ni-rich areas. From an examination of the fracture surfaces following fatigue testing it was concluded that essentially all of the fracture surfaces exhibited dimpled rupture, characteristic of tensile overload. Thus, the extent of growth of any fatigue cracks prior to overload was small. The stress amplitude for the three alloying modes at 2x$l0^6$ was used for the comparison of fatigue strengths. For load cycles <3x$l0^5$, the prealloy exhibited optimum fatigue response followed by the distaloy and elemental mix alloy, respectively. At load cycles >2x$l0^6$, similar fatigue limits were exhibited by the three alloys. It was concluded that fatigue cracks propagate primarily through pores, rather than through the constituent phases of the microstructure. A decrease in pore SIze improved the S-N behavior of the sintered steel.

• Analytical Science and Technology
• /
• v.16 no.6
• /
• pp.431-437
• /
• 2003

Metalization yield of uranium oxide to uranium metal from lithium reduction process of spent pressurized water reactor (PWR) fuels was measured using thermogravimetric analyzer. A reduced metal produced in the process was divided into a solid and a powder part, and each metalization yield was measured. Metalization yield of the solid part was 90.7~95.9 wt%, and the powder being 77.8~71.5 wt% individually. Oxidation behaviour of the quartemary alloy was investigated to take data on the thermal oxidation stability necessary for the study on dry storage of the reduced metal. At $600{\sim}700^{\circ}C$, weight increments of alloy of Mo, Ru, Rh and Pd was 0.40~0.55 wt%. Phase change on the surface of the alloy was started at $750^{\circ}C$. In particular, Mo was rapidly oxidized and then the alloy lost 0.76~25.22 wt% in weight.

• KSBB Journal
• /
• v.15 no.6
• /
• pp.594-599
• /
• 2000

The adsorption of the antimicrobial agents and their heat-resistance were investigated for the packaging film manufacture, wherein, the antimicrobial agents were adsorbed on a ceramic component. The naturally sourced antimicrobial agents were produced by methylotropic actinomycetes strains MO-16 and MO-17, extracted with ethylacetate. Antimicrobial action was stable to $121^{\circ}C$ and 1 atm. for 30 min., showing wide-ranging activity to the Gram(+) and the Gram(-) bacteria. Antimicrobial agents, adsorbed on ceramic Ce-1, retained activity to the Gram(+) and the Gram(-) species at $105^{\circ}C$ and $230^{\circ}C$ heat treatment, and methanol extracted antimicrobial agents from Ce-1 treated at $230^{\circ}C$ for 30min., retained activity to Gram(+) bacteria. In the presence of oxygen during the heat treatment process, antimicrobial agents adsorbed on ceramic Ce-1 showed antimicrobial activity to Gram(+) and the Gram(-) bacteria.

• Research in Plant Disease
• /
• v.12 no.2
• /
• pp.91-98
• /
• 2006

A filtrate powder, designated as KNF2022, produced from culture broth of Acinetobacter sp. KTB3 was tested for their inhibitory effects on Pepper mild mottle virus (PMMoV) infection to Nicotiana glutinosa or N. tabacum cv. Xanthi nc. When 1/100 dilution with distilled water was treated to the plants and PMMoV was inoculated, the inhibition was estimated to be 94.3 and 95.6%, respectively. The same concentrations of KNF2022 inhibited infections of Pepper mottle virus (PepMoV) and Cucumber mosaic virus (CMV) on Chenopodium amaranticolor by 97.1 and 92.5%, respectively. Duration of inhibitory activity of the filtrate powder from Acinetobacter sp. culture broth against PMMoV infection on N. glutinosa was maintained for 2 days at 80% inhibition level, however, the inhibitory effect was diminished from 4 days after treatment to 50% levels. To evaluate inhibitory effects on systemic host plants of the antiviral agent, symptom developments of PMMoV, PepMoV and CMV on KNF2022-treated pepper plants were investigated. Delayed symptom developments until 10 days after inoculation (DAI) were observed for all the three viruses when the viruses were inoculated individually, and these delayed symptom development effects were maintained until 30 DAI in case of PepMoV. Moreover, PepMoV was not detected by RT-PCR and ELISA until 30 DAI. These delayed symptom development effects were diminished in all combinations of three virus co-inoculations due to synergism of three viruses on symptom developments. Inhibitory effect of KNF2022 was verified under electron microscopic examinations using purified virus preparations. Particles of PMMoV and PepMoV were observed on specimens from 5 min after KNF2022 treatment, and the particle sizes were reached in the range of 200-250 nm and 400-600 nm, respectively. Furthermore, the viral particles were destructed and particle sizes were reached in the range of 100-150 nm and 300-500 nm, respectively, on 60 min after treatments. Reduction of local lesion numbers on N. tabacum cv. Xanthi nc and C. amaranticolor were accompanied with reduction of virus particle sizes. In the case of CMV destructed particle numbers were also increased according to incubation period after KNF2022 treatment and local lesions on C. amaranticolor were reduced.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.56 no.12
• /
• pp.2196-2201
• /
• 2007

Materials used at microwave are usually used as a dielectric with a manufacturing purpose of printed circuit boards, etc. Complex permittivity of them can be measured from attenuation constant or propagation constant of a transmission line using a microstrip line with bulk type. But as the technique recently which can manufacture to have complex permittivity and permeability demanded using nonferrous metals for powder-type grows up, we need sensors and methods which can measure characteristics of powder-type materials. So far measuring methods of permittivity and permeability with waveguide or coaxial cable are used but they have faults which have a complex measurement method and are difficult to simultaneously measure permittivity and permeability. In this paper, a simultaneous measuring method of permittivity and permeability with 2-port coaxial cable and a new proposed calculation. The proposed 2-port coaxial cable is designed to be easy to insert materials and to have a wideband. We measure permittivity and permeability of magnetic powder(Ni-Fe-Mo, Ni-Fe) which reveal its characteristic at $0.3{\sim}1.3GHz$ to identify the proposed sensor.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.918-920
• /
• 2006

Metal sulfide powders such as MnS, $MoS_2$ and FeS are simply used to the machinery processing improvement agent and solid lubricant in powder metallurgy industrial. And then, metal sulfide powders have received relatively little attention from powder metallurgy. Recently, the portable machine is one of the important interfaces between human or human and electronic machine. With the increase of the intelligent activity, the social and industrial demands for information display device and power source are increasing. The transition metal sulfide materials (FeS, ZnS) have received considerable attention due to the large variety of its electric, optical and magnetic properties. Among the metal sulfide, $FeS_2$ is appealing superior material for applications in $Li-2^{nd}$ battery because of high capacity. ZnS is also a famous phosphor material with various luminescence properties, such as photoluminescence (PL) and electroluminescence (EL). So generally used in the fields of display, sensors and laser. Metal sulfide materials, therefore, are provided for most widely application in all industries. In recent years, material researchers have become increasingly interested in studying with synthesis of metal sulfide.