• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• 제11권1호
• /
• pp.18-25
• /
• 1998

G $d_{0.2}$C $e_{0.8}$ $O_{1.9}$(CGO) for electrolyte and L $a_{0.5}$S $r_{0.5}$Mn $O_3$(LSM50) for cathode in Solid Oxide Fuel Cells(SOFC) were synthesized by citrate process. Specimens were prepared with sintering temperatures at 110$0^{\circ}C$, 120$0^{\circ}C$ and 130$0^{\circ}C$, which were fabricated by slurry coating with citric acid contents. Interfacial resistance was measured between cathode and electrolyte using AC-impedance analyzer. With various citric acid content, the degree of agglomeration for the initial particles changed. Also sintering temperature changed the particle size and the degree of densification of cathode. Factors affecting the interfacial resistance were adherent degree of the electrolyte and cathode, distribution of TPB(three phase boundaries, TPB i.e., electrolyte/electrode/gas phase area) and porosity of cathode. By increasing the sintering temperature, particle size and densification of the cathode were increased. And then, TPB area which occurs catalytic reaction was reduced and so interfacial resistance was increased.sed.sed.d.

• Journal of Powder Materials
• /
• 제26권1호
• /
• pp.49-57
• /
• 2019

Layered $LiNi_{0.83}Co_{0.11}Mn_{0.06}O_2$ cathode materials single- and dual-doped by the rare-earth elements Ce and Nd are successfully fabricated by using a coprecipitation-assisted solid-phase method. For comparison purposes, non-doping pristine $LiNi_{0.83}Co_{0.11}Mn_{0.06}O_2$ cathode material is also prepared using the same method. The crystal structure, morphology, and electrochemical performances are characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) mapping, and electrochemical techniques. The XRD data demonstrates that all prepared samples maintain a typical ${\alpha}-NaFeO_2$-layered structure with the R-3m space group, and that the doped samples with Ce and/or Nd have lower cation mixing than that of pristine samples without doping. The results of SEM and EDS show that doped elements are uniformly distributed in all samples. The electrochemical performances of all doped samples are better than those of pristine samples without doping. In addition, the Ce/Nd dual-doped cathode material shows the best cycling performance and the least capacity loss. At a 10 C-rate, the electrodes of Ce/Nd dual-doped cathode material exhibit good capacity retention of 72.7, 58.5, and 45.2% after 100, 200, and 300 cycles, respectively, compared to those of pristine samples without doping (24.4, 11.1, and 8.0%).

• Transactions on Electrical and Electronic Materials
• /
• 제3권3호
• /
• pp.25-28
• /
• 2002

In this study, microstructural, dielectric and electrical properties of (Pb$\sub$0.83/) (La$\sub$0.2/Ce$\sub$0.8/)$\sub$0.08/TiO$_3$(PCT) ceramics as a function of MnO$_2$ addition and electrode size variation were investigated for 30 MHz high frequency ceramic resonator application. Grain size was gradually increased according to the increase of MnO$_2$ addition amount. Moreover, the density showed a constant value with increasing MnO$_2$ addition amount. Dielectric constant was decreased with increasing MnO$_2$ addition amount. Curie temperature of all the composition ceramics was nearly constant around 330$^{\circ}C$. The maximum D.R.of 50.5 dB and maximum Q$\sub$mt3/ of 1842 in the 3$\^$rd/ overtone vibration mode were appeared at the composition of 0.3wt% MnO$_2$, respectively.

• Journal of the Microelectronics and Packaging Society
• /
• 제22권4호
• /
• pp.77-82
• /
• 2015

To increase the performance of solid oxide fuel cell operating at intermediate temperature ($600^{\circ}C{\sim}800^{\circ}C$), $Sm_{0.2}Ce_{0.8}O_2$ (SDC) thin layer was applied to the $La_{0.8}Sr_{0.2}Mn_{0.8}Cu_{0.2}O_3$ (LSMCu) cathode by sol-gel coating method. The SDC was employed as a diffusion barrier layer on the yttria-stabilized zirconia(YSZ) to prevent the interlayer by-product formation of $SrZrO_3$ or $La_2Zr_2O_7$. The by-products were hardly formed at the electrolyte-cathode interlayer resulting to reduce the cathode polarization resistance. Moreover, SDC thin film was coated on the cathode pore wall surface to extend the triple phase boundary (TPB) area.

• Clean Technology
• /
• 제21권3호
• /
• pp.153-163
• /
• 2015

The effects of H₂O and residue SO₂ in flue gases on the activity of the Fe/zeolite catalysts for low-temperature NH₃-SCR of NO were investigated. And the addition effect of Mn, Zr and Ce to Fe/zeolite for low-temperature NH₃-SCR of NO in the presence of H₂O and SO₂ was investigated. Fe/zeolite catalysts were prepared by liquid ion exchange and promoted Fe/zeolite catatysts were prepared by liquid ion exchange and doping of Mn, Zr and Ce by incipient wetness impregnation. Zeolite NH₄-BEA and NH₄-ZSM-5 were used to adapt the SCR technology for mobile diesel engines. The catalysts were characterized by BET, X-ray diffraction (XRD), SEM/EDS, TEM/EDS. The NO conversion at 200 ℃ over Fe/BEA decreased from 77% to 47% owing to the presence of 5% H₂O and 100 ppm SO₂ in the flue gas. The Mn promoted MnFe/BEA catalyst exhibited NO conversion higher than 53% at 200 ℃ and superior to that of Fe/BEA in the presence of H₂O and SO₂. The addition of Mn increased the Fe dispersion and prevented Fe aggregation. The promoting effect of Mn was higher than Zr and Ce. Fe/BEA catalyst exhibited good activity in comparison with Fe/ZSM-5 catalyst at low temperature below 250 ℃.

• Korean Chemical Engineering Research
• /
• 제49권5호
• /
• pp.633-638
• /
• 2011

Mn substituted La, Sr or Ba-hexaaluminate were prepared by $(NH_4)_2CO_3$ co-precipitate method and calcined at $1,200^{\circ}C$ for 5 h. Catalysts were characterized by X-ray diffraction and $N_2$ physisorption and scanning electron microscope (SEM). Compared to $SrMnAl_{11}O_{19}$ and $BaMnAl_{11}O_{19}$, $LaMnAl_{11}O_{19}$ in which La located at mirror plane showed better crystallinity and high surface area, 13 $m^2/g$. $LaMnAl_{11}O_{19}$ revealed well developed plate-like structure which is characteristic structure of hexaaluminate. The catalytic activity of methane combustion increased in the following order: $LaMnAl_{11}O_{19}$ > $SrMnAl_{11}O_{19}$ > $BaMnAl_{11}O_{19}$ and was dependent on surface area of catalysts. 60 wt% $CeO_2/LaMnAl_{11}O_{19}$ calcined at $700^{\circ}C$ showed enhanced methane activity and methane was oxidized completely at low temperature ($700^{\circ}C$). It was confirmed that addition of ceria seems to be effective for the low and middle temperature combustion of methane. But, after calcination at high temperature of $1,200^{\circ}C$, it lost the promoting effect of ceria due to increase of ceria particle size and it had a limit to applying to the high temperature catalytic combustion.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• 제36권3호
• /
• pp.249-254
• /
• 2023

La_0.7-xCe_xSr_0.3MnO₃ specimens were fabricated by a solid state reaction method and structural and electrical properties with variation of Ce⁴⁺ contents were measured. All specimens exhibited a polycrystalline rhombohedral crystal structure, and the (110) peaks were shifted to low angle side with increasing the amount of Ce⁴⁺ contents. As Ce⁴⁺ ions with different ion radii and charges are substituted with La³⁺ ions, electrical properties are thought to be affected by changes in the double exchange interaction between Mn³⁺-Mn⁴⁺ ions due to distortion of the unit lattice, a decrease in oxygen vacancy concentration, and an increase in lattice defects. Resistivity gradually decrease as the amount of Ce⁴⁺ added increased, and negative temperature coefficient of resistance (NTCR) properties were shown in all specimens. In the La_0.5Ce_0.2Sr_0.3MnO₃ specimens, electrical resistivity, TCR and B-value were 31.8 Ω-cm, 0.55%/℃ and 605 K, respectively.

• Journal of Magnetics
• /
• 제16권4호
• /
• pp.457-460
• /
• 2011

In this paper, magnetic property and magnetocaloric effect (MCE) in perovskite manganites of the type $La_{(0.75-X)}Ce_XCa_{0.25}MnO_3$ (x = 0.0, 0.2, 0.3 and 0.5) synthesized by using the standard solid state reaction method have been reported. From the magnetic measurements as a function of temperature and applied magnetic field, we have observed that the Curie temperature ($T_C$) of the prepared samples strongly dependent on Ce content and was found to be 255, 213 and 150 K for x = 0.0, 0.2 and 0.3, respectively. A large magnetocaloric effect in vicinity of $T_C$ has been observed with a maximum magnetic entropy change (${\mid}{\Delta}S_M{\mid}_{max}$) of 3.31 and 6.40 J/kgK at 1.5 and 4 T, respectively, for $La_{0.55}Ce_{0.2}Ca_{0.25}MnO_3$. In addition, relative cooling power (RCP) of the sample under the magnetic field variation of 1.5 T reaches 59 J/kg. These results suggest that $La_{0.55}Ce_{0.2}Ca_{0.25}MnO_3$ compound could be a suitable candidate as working substance in magnetic refrigeration at 213 K.

• Journal of the Korean Ceramic Society
• /
• 제14권2호
• /
• pp.78-81
• /
• 1977

The effects of variation in composition and the addition of small amount of the rare-earth oxides La2O3, CeO2 and Sm2O3 on the magnetic properties of Mn-Zn system ferrites, 0.5MnO.0.5ZnO.(1＋0.1X) Fe2O3(X=-1, 0, 1, 2), were investigated in the range of frequencies of 0.1~100 kHz. It was shown that the magnetic permeability of the specimens with the composition Mn 0.5 Zn 0.5 Fe2O4 was maximum in the Mn-Zn system ferrites, and that the addition of a small amount of the rare-earth oxides to the composition 0.5 MnO.0.5ZnO.0.9 Fe2O3 caused the sharp increase of magnetic permeability and the decrease of the loss factors.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• 제17권5호
• /
• pp.481-485
• /
• 2004

0.91 (PSN-PZT) －0.05BF －0.04PNW＋0.3wt%MnO$_2$＋0.6wt%CuO＋xwt%CeO$_2$ ceramics were fabricated with the variations of CeO$_2$addition at the sintering temperature of 95$0^{\circ}C$ and their microstructure, dielectric and piezoelectric characteristics were investigated. As the amount of CeO$_2$ addition increased, the grain size, density and electromechanical coupling factor(k$_{p}$) were increased and the mechanical quality factor(Q$_{m}$ ) was decreased. At the 0.3 wt% CeO$_2$, the density, grain size, electromechanical coupling factor(k$_{p}$), and pizoelectric constants(d$_{33}$, g$_{33}$) showed the maximum value of 7.87 g/㎤, 3.22 $\mu\textrm{m}$, 0.5, 289 pC/N, and 22.2 ㎷ㆍm/N, respectively. However, mechanical quality factor(Q$_{m}$ ) showed the minimum value of 807 at the 0.5 wt% CeO$_2$.$.EX>.EX>.