• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.1398-1401
• /
• 2005

The nano/microstructure, the aging response (in T5 heat treatment), and the mechanical/tribological properties of the eutectic regions in squeeze-cast A356 alloy were investigated using nano/micro-indentation and mechanical scratching, combined wit optical microscopy and atomic force microscope(AFM). Most eutectic Si crystals in the A356 alloy showed a modified morphology as fine-fibers. The loading curve for the eutectic region was more irregular than that of the primary Al region due to the presence of various particles of varying strength. In addition, the eutectic region showed lower pile-up and higher elastic recovery than the primary Al region. The aging responses of the eutectic regions in the squeeze-cast A356 alloys aged at $150^{\circ}C$ for different times(0, 2, 4, 8, 10, 16, 24, 36 and 72 h) were investigated. As the aging time increased, acicular Si particles in the eutectic regions gradually came to a fine structure. Both Vickers hardness ($H_V$) and indentation ($H_{IT}$) test results showed almost the same trend of aging curves, and the peak was obtained at the same aging time of 10 h. A remarkable size-dependence of the tests was found. The friction coefficient for the eutectic region was lower than that for the primary Al region.

• Journal of the Korean Society for Heat Treatment
• /
• v.4 no.2
• /
• pp.38-46
• /
• 1991

Effects of aging treatment on the microstructures and microhardness of a rapidly solidified Al-Li-Cu-Mg-Zr alloy were investigated by differential scanning calorimetry(DSC) and transmission electron microscopy(TEM). The as-melt-spun ribbon was consisted of fine ${\delta}^{\prime}$ and icosahedral intermetallic compound which were precipitated in the matrix. Two exothermic peaks with the range of $120^{\circ}C-190^{\circ}C$ and $280^{\circ}C-344^{\circ}C$ corresponded to ${\delta}^{\prime}$ and ${\theta}^{\prime}$, S', $T_1$ precipitating reaction respectively, and two endothermic peaks with the range of $190^{\circ}C-280^{\circ}C$ and $344^{\circ}C-550^{\circ}C$ corresponded to dissolution of ${\delta}^{\prime}$ and ${\theta}^{\prime}$, S', $T_1$ respectively in DSC curves. Peak hardness value was obtained at $210^{\circ}C$ for 1 hr aging treatment.

• Korean Journal of Materials Research
• /
• v.9 no.6
• /
• pp.609-614
• /
• 1999

The effect of the amount of $SiO_2$dopant on the behavior of $AlO_2$$O_3$-composite formation by melt oxdation of Al-alloy was examined in this paper. The $SiO_2$powder was spread on the top surface of the Al-1Mg-3-Si-5Zn-1Cu alloy in th alumina crucible. The selected amount of each powder was 0.03, 0.10, 0.16g/$\textrm{cm}^2$. The oxidation behavior was determined by observing the weight gain after the heat treatment for 10 hours at 1373K. The macroscopic structure of formed oxide layer was examined by an optical microscope. The top surface and the cross-section of the grown oxide layer were investigated by SEM and analysed by EDX. The $SiO_2$ powder was determined to enhance oxidation by thermit reaction with Al which reduced the growth incubation period of the oxidation layer. As the amount of the $SiO_2$dopant increased, the growth rate decreased due to the precipitated Si which blocked the Al-alloy channel in the composite materials. However, more uniform layer was obtained due to the occurrance of the enhanced oxidation reaction in the whole alloy surface compared to the case of addition of less amount of dopant.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.10 no.7
• /
• pp.1301-1306
• /
• 2006

Aluminum alloys are gaining increased acceptance in the automotive and electronic industeries and cold & hot forging is the most efficient method of manufacturing such mass produced parts. This study has been investigated the microstructures and mechanical properties of A6061(Al-1.2Mg-0.8Si) alloy fabricated by cold & hot forging process for development of the future compressor block. The microstructure of cold & hot forginged specimen were composed of eutectic structure aluminum solid solution and $Mg_2Si$ precipitates. The tensile strength of as-solid solution treatment A6061 alloy revealed 291.7MPa. It was fabricated that a trial future compressor cylinder block using cold & hot forging.

• Resources Recycling
• /
• v.24 no.1
• /
• pp.35-42
• /
• 2015

To obtain the fundamental information on the dissolution of nickel into the slag in the pyrometallurgical processes for treatment of wasted PCB, the distribution ratios of nickel between CaO-$SiO_2-Al_2O_3$-MgO slag and copper-5 wt%Ni alloy were measured at 1623 K to 1823 K under a controlled $CO_2$-CO atmosphere. The distribution ratio of Ni increased linearly with increasing oxygen partial pressure. Therefore, the dissolution reaction of nickel into the slags could be described by the following equation; $$Ni(l)_{metal}+\frac{1}{2}O_2(g)NiO(l)_{slag}$$ The distribution ratio of Ni increased linearly with increasing content of basic oxides(CaO and MgO) in slag. However, the distribution ratio of Ni decreased linearly with increasing temperature. From these results, the empirical equation of distribution ratio of Ni was obtained by the following equation from the analysis of experimental conditions by multiple regression. $${\log}L_{Ni}=0.4000{\log}P_{O2}-5.1{\times}10^{-4}T+0.3375\(\frac{X_{CaO}+X_{MgO}}{X_{SiO2}}\)$$

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.4 no.2
• /
• pp.169-177
• /
• 1994

Dilute Al-Cu and Al-Mg alloys were solidified unidirectionally upward by Bridgman method. It is necessary that solute concentration of initial melt is uniform to be able to control the concentration of crystal. When solute concentration is not uniform, it can cause unusual macro-segregation in grown solid. A non-steady state solidification was observed where the solute concentration in the grown solid decreased with the progress of solidification, when a dilute Al-Cu melt with positive axial temeprature gradient was solidified. This was caused by leaking out of Cu-rich melt into the gap between ingot and crucible during melt-down and its sedimentation after complete melting. In the case of Al-Mg alloy, the solute concentration has a minimum in the middle of grown specimen because Mg-rich melt flowed down the gap between ingot and crucible and floated after complete melting. Uniform initial melt concentration can be achieved by the homogenization of the ingot or by the absence of the gap between ingot and crucible.

• Korean Journal of Materials Research
• /
• v.28 no.9
• /
• pp.534-538
• /
• 2018

The annealing characteristics of a cold rolled Al-6.5Mg-1.5Zn alloy newly designed as an automobile material is investigated in detail. The aluminum alloy in the ingot state is cut to a thickness of 4 mm, a total width of 30 mm and a length of 100 mm and then reduced to a thickness of 1 mm (reduction of 75 %) by multi-pass rolling at room temperature. Annealing after rolling is performed at temperatures ranging from 200 to $400^{\circ}C$ for 1 hour. The tensile strength of the annealed material tends to decrease with the annealing temperature and shows a maximum tensile strength of 482MPa in the material annealed at $200^{\circ}C$. The tensile elongation of the annealed material increases with the annealing temperature, while the tensile strength does not, and reaches a maximum value of 26 % at the $350^{\circ}C$ annealed material. For the microstructure, recovery and recrystallization actively occur as the annealing temperature increases. The recrystallization begins to occur at $300^{\circ}C$ and is completed at $350^{\circ}C$, which results in the formation of a fine grained structure. After the rolling, the rolling texture of {112}<111>(Cu-Orientation) develops, but after the annealing a specific texture does not develop.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2000.04a
• /
• pp.183-186
• /
• 2000

The high temperature deformation behavior of spray-formed Al-19wt%Si-1.87wt%Mg-0.085wt.%Fe alloy was studied by torsion testing in the strain rate range of 0.001-1 sec-1 and in the temperature range of 300-500 $^{\circ}C$. The relationship between stress temperature and strain rate is expressed using the Power law. the behavior of dynamic recrystallization is showed in 300-35$0^{\circ}C$, 1-0.1sec-1 and the behavior of dynamic recovery is showed in 450-50$0^{\circ}C$, 0.01-0.001sec-1 The size of Si particles is mall when the temperature is low and the strain rate is high. The strain rate sensitivity(m) and the apparent activation energy(Q) indicate the dependence on strain rate and temperature for flow stress respectively. The hot ductility is high when m is high and Q is low. The maps of strain rate sensitivity and apparent activation energy suggest the optimum processing conditions.

• Journal of Korea Foundry Society
• /
• v.19 no.6
• /
• pp.456-465
• /
• 1999

The overall objective of this study is to investigate the effect of Ag addition on the mechanical properties and microstructure of rapid solidified 7000 Al series alloys. Al-Zn-Mg-Cu alloys with small amounts of Ag was fabricated into the powder by gas atomization. The powder was extruded after the cold compaction and degassing and then followed by T6 heat treatment. Microstructure observation, phase analysis, room and high temperature tensile test and hardness test were pursued. The tensile strength and hardness of Ag-added alloy after heat treatment was increased with increasing Ag contents. However, the elongation of extruded alloys was not increased as much as to be expected. The reason of this result seems to be related to $the{\Omega}$ phase, which contribute to the high temperature strength stability of Al-Cu-Zn alloys through the formation of eutectoid with Ag addition.

• Korean Journal of Materials Research
• /
• v.7 no.6
• /
• pp.453-459
• /
• 1997

용탕단조법에 의해 제조된 Mg-9AI-2Zn 합금을 미세조직관찰, 미소경도측정, 인장시험 등을 행하여 시효거동과 기계적 성질을 조사하였다. 용탕에 가압을 한 결과 주조결함이 제거된 미세한 주조조직을 얻었으며 미세조직은 초정 $\alpha$(Mg 고용체), 과포화고용체 $\alpha$상 및 $\beta$(Mg$_{17}$AI$_{12}$)화합물의 3가지 상으로 구성되어 있었다. 16$0^{\circ}C$및 20$0^{\circ}C$에서 시효열처리한 결과 $\beta$석출물에 의한 피크 경도값이 나타났으며 피크경도에서의 석출물의 형태는 lamella 형태의 불연속 석출물이 대부분이었고 과시효에 따라 불연속석출물의 조대화와 함께 연속석출물의 분율이 증가하였다. 용탕단조방법에 의해 제조된 Mg-9AI-2Zn 합금의 인장특성은 인장강도 261.4MPa, 연산율 7.6%로서 상용 AZ 92 합금보다 인장강도 및 연신율에서 우수한 기계적 성질을 가졌는데 이는 Zn의 고용강화 및 용탕의 가압에 의한 효과였다.다.