A Study on the Development for the Future Compressor Cylinder Block Using of Cold & Hot Forging Method

냉.온간포징법을 이용한 차세대 콤프레샤 실린더 블록 개발에 관한 연구

  • 김순호 (신라대학교 자동차기계공학과)
  • Published : 2006.07.01
Download PDF
⟨ Previous Next ⟩

Abstract

Aluminum alloys are gaining increased acceptance in the automotive and electronic industeries and cold & hot forging is the most efficient method of manufacturing such mass produced parts. This study has been investigated the microstructures and mechanical properties of A6061(Al-1.2Mg-0.8Si) alloy fabricated by cold & hot forging process for development of the future compressor block. The microstructure of cold & hot forginged specimen were composed of eutectic structure aluminum solid solution and $Mg_2Si$ precipitates. The tensile strength of as-solid solution treatment A6061 alloy revealed 291.7MPa. It was fabricated that a trial future compressor cylinder block using cold & hot forging.

알루미늄 합금은 자동차부품 및 전자부품산업 개발에 크게 기여하고 있는 소재로서, 제조방법 중 냉？온간 단조 공법에 의해 제조하는 것이 대량 생산되어지는 자동차 및 전자산업부품개발에 있어서 매우 효율적이다. 따라서, 본 연구에서는 차세대 콤프레샤 실린더 블록 개발을 위하여,AI소재 (AI-Mg-Si계합금)를 활용, 냉 -온간 단조법을 이용 하여 개발하고자 한다. 이를 위해, 제조 시편의 미세조직 및 기계적 성질을 조사하였는데,미세조직은 공정형으로 구성되었으며, $Mg_2Si$의 중간상이 석출되었다. 그리고 인장강도는 291.7MPa 로 나타났으며, 그러한 결과를 바탕으 로 차세대 콤프레샤 실린더 블록시제품을 제작하였다.

Keywords

References

  1. King, F., 1980 'Aluminium and Its Alloy', Cambridge University Press, p.112
  2. Polmear, I. J., Light alloy, 2nd ed., Edward Anold, p.144 (1987)
  3. Charlie R. Brooks, 1982 'Heat Treatment, Structure & Properties of Nonferrous Alloys ', American Society for Metals, pp.153-154
  4. Metals Handbook 10th ed., 2, ASM, p.152, (1990)
  5. Pharr, G. M., Courington, S. V., Wadsworth, J. and Nieh, T. G., 1991 ' Deformation of an extruded Nickel Beryllide between Room Termperature and 820,' J. Mater. Res., 6, p. 2653 https://doi.org/10.1557/JMR.1991.2653
  6. Bryant, A. J., Aluminio E. Nuova, 1977 'Crystallography of $MG_{2}Si$ Precipitates in Al-7.0Si-0.4Mg Alloy,' Metallurgia, 42, p.228
  7. A. K. Gupta and D. J. Lloyd, 1992 'Micro stuructural Study of Continuous Precipitation in Al Alloys', ICCA3, p.21
  8. Metals Handbook 9th ed.,2, ASM, p.45 (1990)
  9. Flemings, M. C. 1974 'Solidfication Process- ing', McGraw-Hill Book Company, p.207
  10. Metals Handbook 9th ed.,2, ASM, p. 61, (1990)