• The Journal of Advanced Prosthodontics
• /
• 제10권1호
• /
• pp.25-31
• /
• 2018

PURPOSE. The aim of the present study was to record the metal-ceramic bond strength of a feldspathic dental porcelain and a Co-Cr alloy, using the Direct Metal Laser Sintering technique (DMLS) for the fabrication of metal substrates. MATERIALS AND METHODS. Ten metal substrates were fabricated with powder of a dental Co-Cr alloy using DMLS technique (test group) in dimensions according to ISO 9693. Another ten substrates were fabricated with a casing dental Co-Cr alloy using classic casting technique (control group) for comparison. Another three substrates were fabricated using each technique to record the Modulus of Elasticity (E) of the used alloys. All substrates were examined to record external and internal porosity. Feldspathic porcelain was applied on the substrates. Specimens were tested using the three-point bending test. The failure mode was determined using optical and scanning electron microscopy. The statistical analysis was performed using t-test. RESULTS. Substrates prepared using DMLS technique did not show internal porosity as compared to those produced using the casting technique. The E of control and test group was $222{\pm}5.13GPa$ and $227{\pm}3GPa$, respectively. The bond strength was $51.87{\pm}7.50MPa$ for test group and $54.60{\pm}6.20MPa$ for control group. No statistically significant differences between the two groups were recorded. The mode of failure was mainly cohesive for all specimens. CONCLUSION. Specimens produced by the DMLS technique cover the lowest acceptable metal-ceramic bond strength of 25 MPa specified in ISO 9693 and present satisfactory bond strength for clinical use.

• Earthquakes and Structures
• /
• 제12권1호
• /
• pp.55-65
• /
• 2017

Earthquake resilience of substations is essential for reliable and sustainable service of electrical grids. The majority of substation equipment consists of cylindrical porcelain components, which are vulnerable to earthquake shakings due to the brittleness of porcelain material. Failure of porcelain equipment has been repeatedly observed in recent earthquakes. Hence, proper seismic modelling of porcelain equipment is important for various limit state checks in both product manufacturing stage and detailed substation design stage. Sheds on porcelain core and cemented joint between porcelain component and metal cap have significant effects on the dynamic properties of the equipment, however, such effects have not been adequately parameterized in existing design guidelines. This paper addresses this critical issue by developing a method for taking these two effects into account in seismic modelling based on numerical and analytical approaches. Equations for estimating the effects of sheds and cemented joint on flexural stiffness are derived, respectively, by regression analyses based on the results of 12 pieces of full-scale equipment in 500kV class or higher. The proposed modelling technique has further been validated by shaking table tests.

• 대한치과보철학회지
• /
• 제38권1호
• /
• pp.73-84
• /
• 2000

Dental porcelain should have adequate strength and similar esthetics as natural teeth. Recently esthetics has become a high priority in clinical dentistry. Thus the evaluation of color stability of dental porcelain has become an important part in dental research. The purpose of this study was to evaluate the difference in color stability of 3 types of porcelain(Vintage, VMK 95, CERAMCO II). The porcelain were divided into groups by 2 types of treatment(glazing or non-glazing and thermocycling or non-thermocycling). The porcelain were dyed with methylene blue and distilled water, and then the color stability was evaluated with a spectrophotometer The results were as follows; 1. The color change of porcelain increased in the order of VMK 95, Vintage, CERAMCO II. But there was no significant difference. 2. The color change decreased in the glazing group compared to the non-glazing group(p<0.05). 3. The color change increased after thermocycling But there was no significant difference. 4. The color change according to dye method was significantly larger with methylene blue copared to distilled water(p<0.05).

• 대한치과보철학회지
• /
• 제25권1호
• /
• pp.41-54
• /
• 1987

The purposes of this study were to evaluate the color differences those can exist between different brands of porcelain with identical shade designation, and to find their causes. For these purposes the following experiments were executed: The color of each opaque and layered porcelain specimen was determined by spectral reflectance measurements with a spectrophotometer. The compositions of each opaque porcelain powder were analyzed by qualitative, and quantitative analysis. Microscopic structures of each opaque porcelain were observed by scanning electron microscope. The results were as follows: 1. Identical shade of different brands of porcelain produced significantly different colors. 2. Color differences among the three brands were found under different light sources. 3. Color differences among the three brands were mostly a result of differences in kinds and amounts of opacifying agents and fluxes and microstructure of porcelain systems. 4. When porcelain systems have similar compositions and firing cycles, they produced similar colors.

• 대한치과보철학회지
• /
• 제28권1호
• /
• pp.203-216
• /
• 1990

The purpose of this study was to evaluate the cervical margin fitness in the collarless metal ceramic crowns formed by different techniques. Specimens were divided as follows : the metal ceramic crowns with metal butt margin as group I, the collarless metal ceramic crowns formed with resin binder technique as group II, and the collarless metal ceramic crowns formed with shoulder powder mixed with phosphate-bonded investment liquids on a refractory die as group III. Each group was made of five specimens, and their marginal fitness on each epoxy die was evaluated under scanning electron microscope of x200 magnification at three measuring points : mesial, central, distal. The following results were obtained. 1. The metal ceramic crowns with metal butt margin exhibited significantly better marginal fitness than the collarless metal ceramic crowns. The marginal fitness in descending order was group I, III, II. 2. The collarless metal ceramic crown formed with resin binder technique had the worst marginal fitness & showed cervical color variation and dermacation between the corrected porcelain & the dentin porcelain. 3. The collarless metal ceramic crowns formed with shoulder powder mixed with phosphate-bonded investment liquids on a refractory die exhibited significantly better marginal fitness & sharper marginal configuration than the other collarless group.

• 대한치과보철학회지
• /
• 제26권1호
• /
• pp.51-61
• /
• 1988

The recently introduced castable glass ceramics incorporate properties characteristic of natural teeth and they are regarded as an ideal material to restore lost tooth structure. The purpose of this study was to compare the marginal fit of castable ceramic crown with that of the metal-ceramic crown in the process of heat treatment. Two master dies for castable ceramic crowns and metal-ceramic crowns were fabricated from being cast with the base metal. Each master die was duplicated with addition silicone and hard stone. Ten castable ceramic crowns were made on each hard stone die and their marginal openings were measured three times first, after casting; second, after ceramming; third, after shading. The other ten metal-ceramic crowns were made on each hard stone die and their marginal openings were measured three times : first, after casting; second, after degassing; third, after porcelain veneering. Each crown was seated on its master die with the constant force delivered by loading jig. And then, marginal openings were measured on four locations by optical projector at X50 magnification. The results were as follows: 1. The mean marginal openings of castable ceramic crowns were $31.1{\pm}12.7{\mu}m$ after casting; $44.6{\pm}12.8{\mu}m$ after ceramming; $51.2{\pm}16.8{\mu}m$ after shading. 2. The mean marginal openings of the metal-ceramic crowns were $26.2{\pm}13.8{\mu}m$ after casting; $29.8{\pm}10.3{\mu}m$ after degassing; $38.0{\pm}14.5{\mu}m$ after porcelain veneering. 3. There was significant increase in the marginal opening of castable ceramic crowns after ceramming, while metal-ceramic crowns sho(wed significant increase after porcelain veneering (p<0.05). 4. Marginal fit of metal-ceramic crown was better than that of castable ceramic crown (p<0.01).

• 박물관보존과학
• /
• 제9권
• /
• pp.1-15
• /
• 2008

국립중앙박물관에 소장되어 있는 신안 해저 출토 유물인 경덕진 백자 중'복소법(覆燒法)'으로 제작되어 구연부에 유약이 시유되지 않은 부분에 금속 테두리(金屬釦)를 덧씌운 '청백자인각화훼문은구완' 4점과 '백자은구대접' 1점에 대해 구연에 주사전자현미경(SEM)으로 단면과 미세 구조를 관찰하였고, 성분 분석은 에너지분산형분석기(EDS)의 반사전자상(BEI)으로 측정한 결과, 금속 테두리는 은(銀)이 아닌 주석 재질임을 알 수 있었다. 또한 구연부에 금속 테두리를 접합 방법을 알아 보기 위해 퓨리어변환 적외선 분석기(FT-IR)로 조사해 본 결과, 접합 재료는 옻 성분을 사용하여 고정하였음을 알 수 있었다.

• 대한치과보철학회지
• /
• 제32권1호
• /
• pp.47-76
• /
• 1994

This study was carried out to evaluate the effect of the crack propagation characteristics and bond stress of ceramo-metal system. In order to characterize the crack propagation, the static crack propagation stored in $37^{\circ}C$ distilled water of two commerical porcelains and the dynamic crack propagation under cyclic flexure load of ceramo-metal system were examined. In order to characterize the bond stress, the shear bond test, the 3-point flexure bond test, and the finite element stress analysis of ceramo-metal system were conducted. The results obtained were as follows : 1. Bulk densities and Young's moduli of opaque porcelains increased with repeated firing. 2. Maximum fracture toughness during 4 firing cycles showed at the group of 4 firing cycles in Ceramco porcelain and 2 firing cycles in Vita porcelain. 3. Shear bond strength and flexure bond strength of Ceramco-Verabond specimen were larger than those of Ceramco-Degudent G specimen (p<0.05). 4. Interfacial stresses under three point flexure bond test were concentrated at the edges of ceramometal system. 5. When a cyclic flexure load was applied, the crack growth rate of porcelain surface of ceramometal specimens was decreased as load cycles increased.

• 대한치과기공학회지
• /
• 제11권1호
• /
• pp.103-109
• /
• 1989

Bond strength between alloy and ceramic plays an important role in deciding the quaring the processing of metalceramic restorations. Now the author had an experiment on the measurement of bond strength differences accoding to the contents of recast alloy used during the processing of metal-ceramic restorations. In the experiment, Anusavice's Planar Interface Shear Bond Test was employed to determine the bond strength. Total 25 specimens were divided as 5 groups, that is, 5 specimens in a group respections : Group I (new alloy 100%) Group II (new 75%$\cdot$recast 25%), Group III (new 50%$\cdot$recast 50%), Group IV (new 25%$\cdot$recast 75%), Group V(recast 100%). All specimens examined micropically and respective strength values of the group specimens were checked simultaneously. The results were as follows, 1. In the analtsis of variance the result showed the significant differences of 1%(P<0.01) among the each group classifid according to the recast contents. 2. When the interfaces of specimens were examined with an electron microscope, the air bubble were evenly occurred in all the specimens, and the occurrence frequencies and the sizes of air bubble were different between Group I and Group III, especially marked different Group I and Croup V. 3. In respective verification of each group through T-test, between Group I and Group II, between Group I and Group III did not show significant differences. 4. There was significant difference between Group I and Group IV, between Group I and Group V as 1%(P<0.01). 5. In the Shear Bond Test of all the groups, Croup V showed the lowest value. Explanatoion of Figures Fig 1. Main fracture type of metal-porcelain interlace showed in group I, II, III from shear Bond Test resets. Fig 2. Main fracture type of metal-porcelain interface showed In group Ⅳ, Ⅴ form shear Bond Test resets. Air bubble and their size appeared around interface of metal-porcelain. Fig 3. Group I, Fig 4. Group II Fig 5. Group III, Fig 6. Group IV, Fig 7. Group V.

• 대한치과보철학회지
• /
• 제45권2호
• /
• pp.203-215
• /
• 2007

Statement of problem: Titanium and its alloy, with their excellent bio-compatibility and above average resistance to corrosion, have been widely used in the field of dentistry. However, the excessive oxidization of titanium which occurs during the process of firing on porcelain makes the bonding of titanium and porcelain more difficult than that of the conventional metal-porcelain bonding. To solve this problem related to titanium-porcelain bonding, several methods which modify the surfaces, coat the surfaces of titanium with various pure metals and ceramics, to enable the porcelain adhesive by limiting the diffusion of oxygen and forming the adhesive oxides surfaces, have been investigated. Purpose: The purpose of this study was to know whether the titanium-porcelain bonding strength could be enhanced by treating the titanium surface with gold and TiN followed by fabrication of clinically applicable porcelain-fused-to-titanium crown Material and method: The porcelain-fused-to-titanium crown was fabricated after sandblasting the surface of the casting titanium coping with $Al_2O_3$ and treating the surface with gold and TiN coating followed by condensation and firing of ultra-low fusing porcelain. To compare with porcelain-fused-to-titanium crowns, porcelain-fused-to-gold crowns were fabricated and used as control groups. The bonding strengths of porcelain-fused-to-gold crowns and porcelain-fused-totitanium crowns were set for comparison when the porcelain was fractured on purpose to get the experimental value of fracture strength. Then, the surface were examined by SEM and each fracturing pattern were compared with each other Result:Those results are as follows. 1. The highest value of fracture strength of porcelain-fused-to-titanium crowns was in the order of group with gold coating, group with TiN coating, group with $Al_2O_3$ sandblasting. No statistically significant difference was found among the three (P>.05). 2. The porcelain-fused-to-gold crowns showed the highest value in bonding strength. The bonding strength of crowns porcelain-fused-to-titanium crowns of rest groups showed bonding strength reaching only 85%-94% of that of PFG, though simple comparision seemed unacceptable due to the difference in materials used. 3. The fracturing patterns between metal and porcelain showed mixed type of failure behavior including cohesive failure and adhesive failure as a similar patterns by examination with the naked eye and SEM. But porcelain-fused-to-gold crowns showed high incidence of adhesive failure and porcelain-fused-to-titanium crowns showed high incidence of cohesive failure. Conclusion: Above results proved that when fabricating porcelain-fused-to-titanium crowns, treating casting titanium surface with gold or TiN was able to enhance the bonding strength between titanium and porcelain. Mean value of masticatory force was found to showed clinically acceptable values in porcelain bonding strength in all three groups. However, more experimental studies and evaluations should be done in order to get better porcelain bonding strength and various surface coating methods that can be applied on titanium surface with ease.