• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1181-1182
• /
• 2006

Y-type barium ferrite $(Ba_2Zn_2Fe_{12}O_{22})$ was prepared by the glass-ceramic method. Glasses with composition of $0.1ZnO{\cdot}0.9(0.3Fe_2O_3{\cdot}0.5BaO{\cdot}0.2B_2O_3)$ were prepared, and the precipitation behavior of Y-type ferrite from the glass matrix was investigated by heating glass specimens at various temperature. $\alpha-BaFe_2O_4$ which is a precursor of M-type ferrite $(BaFe_{12}O_{19})$ was precipitated at about 813 K and an unknown compound, phase X, was precipitated at about 850 K. M-type ferrite and Y-type ferrite started to form at about 923 K and 1103 K, respectively. The formation of Y-type ferrite was int erpreted as the result of the reaction of M-type ferrite with a melt of phase X.

• 한국자기학회지
• /
• 제19권1호
• /
• pp.12-16
• /
• 2009

Z-Type 바리움 페라이트($Ba_{3}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$)를 공침법으로 제조하고 결정구조와 자기적 성질을 조사하였다. $Ba_{3+{\delta}}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$(${\delta}$ = 3, 5, 7, 13 wt%)와 $Ba_{3}Co_{0.8}Zn_{1.2}Fe_{{24}+{\delta}}O_{41}$(${\delta}$ = 5, 7, 10 wt%)의 조성을 가진 분말의 ${\delta}$ 값에 따른 자기적 성질의 변화를 조사하였다. 제조된 모든 바리움 페라이트에는 Z-type으로 상전이 하지 않은 M-type이 상당량 잔류하고 있었다. 포화자화는 Ba와 Fe의 과잉 첨가량 ${\delta}$가 각각 7 wt%와 5 wt% 일 때 최대로 나타났고 보자력은 조사된 모든 분말에서 다소 높게 나타났다. 높은 보자력은 M-type이 잔류하기 때문이다. 과잉의 Ba와 Fe 첨가에 따른 결정구조의 변화는 없었다. Z-type 바리움 페라이트의 연자성 특성을 향상시키기 위해서는 M-type이 Z-type 형성온도에서 상전이가 일어나도록 해야 함을 알았다.

• 한국자기학회지
• /
• 제19권6호
• /
• pp.209-215
• /
• 2009

M-type 바륨 페라이트(BaFe12O19)분말을 공침법을 이용하여 합성하였다. 출발물질의 조성은 $Fe^{3+}:\;Ba^{2+}$ 몰 비를 8로 고정하고 $Fe^{3+}$와 $Ba^{2+}$의 상대적인 양을 조절하였다. 열처리 방법과 pH의 차이에 의한 자기적 성질과 결정구조, 입자형상의 변화를 XRD(XRay Diffractometer), FESEM(Field Emission Scanning Electron Microscope), VSM(Vibrating Sample Magnetometer)을 이용하여 조사하였다. pH가 8이고 $Fe^{3+}:\;Ba^{2+}$의 비가 12 : 1.5 일 때 가장 큰 보자력 값을 얻었다. pH가 8일 때는 $Fe^{3+}$와 $Ba^{2+}$의 상대적인 양과 열처리 조건에 따라 보자력과 포화 자화 값의 변화가 크게 나타났다. 이것은 바륨 페라이트로 전이가 안 된 $\alpha$-$Fe_2O_3$ 상 때문이다. pH가 10일 때는 열처리 조건과 $Fe^{3+}$와 $Ba^{2+}$의 양과 상관없이 단일 상 M-type 바륨 페라이트를 얻을 수 있었으며 우수한 자화 값과 보자력을 나타내는 분말을 얻을 수 있었다. $Fe^{3+}$와 $Ba^{2+}$의 비가 13.6 : 1.7일 때 가장 큰 자화 값(55.7 emu/g)을 얻을 수 있었으며, 산소분위기에서 열처리 후 노냉한 분말이 높은 보자력과 자화 값을 나타내었다. FESEM으로 관찰된 입자의 크기는 50~200 nm이었다.

• 한국자기학회지
• /
• 제20권4호
• /
• pp.134-142
• /
• 2010

바륨 페라이트($BaFe_{12}O_{19}$) 분말을 공침법을 이용하여 합성하였다. 출발물질의 조성은 $Fe^{3+}:Ba^{2+}$ 몰 비를 8로 고정하고 $Fe^{3+}$와 $Ba^{2+}$의 상대적인 양을 조절하였다. pH(= 8, 9, 10), 열처리 온도와 시간에 따른 자기적 성질과 결정구조 입자형상의 변화를 XRD, FESEM, VSM을 이용하여 조사하였다. pH, $Fe^{3+}$와 $Ba^{2+}$의 상대적인 양 그리고 열처리 온도와 시간에 따라 보자력과 자화 값이 다양하게 나타났다. pH가 9인 경우에는 $Fe^{3+}$와 $Ba^{2+}$의 비가 14.4 : 1.8인 경우를 제외한 모든 분말에서 바륨 페라이트의 단일 상을 얻을 수 있었다. $Fe^{3+}$와 $Ba^{2+}$의 비가 12.8 : 1.6이며 공기중에서 $900^{\circ}C$로 열처리한 분말이 가장 큰 자화 값(65.7 emu/g)을 얻을 수 있었으며 산소분위기에서 $900^{\circ}C$로 열처리한 분말이 가장 큰 보자력 값(5280 Oe)을 얻을 수 있었다.

• Journal of Magnetics
• /
• 제4권2호
• /
• pp.65-68
• /
• 1999

The M-type barium ferrite ($BaFe_{12}O_{19}$) is well known magnetic material to be used as a permanent magnet due to its strong uniaxial anisotropy. The substitution of nonmagnetic $Ti^{+4}$ and magnetically weak $Co+^2ion for Fe^{+3}$ to its strong uniaxial anisotropy. The substitution of nonmagnetic $Ti^{+4}$ and magnetically weak $Co+^2ion for Fe^{+3}$ sublattices reduces the uniaxial anisotropy and those compounds open a new application field of noise suppressor at high frequencies. In this study, the magnetic and microwave absorbing properties are investigated in Ti-and Co-substituted barium ferrites ($BaFe_{12-2X} Ti_XCo_XO_{19}$). The saturated magnetization decreases linearly with the substitution of Ti and Co. The rapid drop in coercive force is observed with Ti and Co substitution upto x=1.2. The magnetic permeability spectrum shows the natural magnetic resonance in the specimens with small coercive force and large attenuation of microwave is predicted in those specimens at high frequencies (above 4 GHz).

• 산업기술연구
• /
• 제28권A호
• /
• pp.119-123
• /
• 2008

Structural and magnetic properties of $CO_{1-x}Zn_xZ$ ($Ba_3Co_{1-x}Zn_xFe_{24}O_{41}$) hexa-ferrite are studied using XRD, VSM and SEM, respectively. Powder was prepared from co-precipitation and firstly heat treated at $1350^{\circ}C$ for 6 hours in $O_2$ atmosphere. Second heat treatment was performed at 900, 1000, $1100^{\circ}C$ for 6 hours in air, respectively. Saturation magnetization value of first heat treated powder is acceptable and coercivity is high for applying to device. These result may be originated from incomplete formation reaction from M and Y phases to Z phase. Second heat treatment leads to small value of coercivity.

• 한국자기학회지
• /
• 제19권6호
• /
• pp.203-208
• /
• 2009

Ka 대역 (26.5~40 GHz)용 전파흡수체의 자성손실재로 Ti-Co가 치환된 M형 바륨 페라이트($BaTi_{0.5}Co_{0.5}Fe_{11}O_{19}$)를 제조하고, 페라이트-고무 복합체에서 자기적 성질 및 전파흡수특성에 관해 조사하였다. M형 바륨 페라이트에서 Ti-Co가 치환됨에 따라 보자력의 감소가 급격히 일어났다. 이는 c 축으로 강한 자기이방성을 갖던 M형 바륨 페라이트의 자기이방성이 a-b 면내 자기이방성으로 변화함에 기인한다. 이에 따라 자연공명주파수를 Ka 주파수 대역으로 이동시킬 수 있었고, 복소투자율의 주파수 분산특성의 제어가 가능하였다. Ti-Co가 치환된 M형 바륨 페라이트 복합체의 경우 Ka 대역에서 임피던스 정합조건을 만족시킬 수 있었다. 흡수대역폭 증가에 페라이트/고무 함량비(F/R)의 조절이 매우 중요함을 제시하였다. F/R = 4의 함량비에서 ?20㏈ 이하의 반사손실을 갖는 흡수대역폭이 7 GHz 정도로 매우 우수한 광대역 전파흡수특성을 보였다. F/R 비가 증가할수록 정합주파수 및 정합두께는 감소하였으나, 흡수대역폭은 줄어들었다.

• 한국자기학회지
• /
• 제24권1호
• /
• pp.1-10
• /
• 2014

$Co_2Z$-type hexaferrite 시편을 다양한 합성법을 이용하여 제조하였다. 수열합성법을 이용하여 M-type, $Co_2Y$-type, $Co_2Z$-type을 제조하였으며, 제조된 M-type과 $Co_2Y$-type을 출발물질로 하여 고상반응법(ball milling)과 수열합성법(hydrothermal)으로 $Co_2Z$-type을 제조하였다. 제조된 시편의 결정구조와 미세구조 자기적 성질은 XRD, FESEM, VSM, impedance analyzer를 이용하여 조사하였다. M-type과 $Co_2Y$-type은 단일상의 결정구조를 얻을 수 있었다. 여러 합성법 중에 M+Y ball milling, M+Y hydrothermal에서 제조한 시편이 $Co_2Z$-type hexaferrite의 단일상과 대체로 일치하는 것을 알 수 있었으며, $Co_2Z$-type의 모든 시편들은 이론적인 포화 자화값(50 emu/g)과 비슷한 값을 나타내었다. 소결한 시편들의 투자율은 시약을 precusor로 하여 제조한 $Co_2Z$-type의 투자율이 가장 높았으며, 열처리 온도가 증가함에 따라 투자율은 낮아졌다. 다른 합성법에서는 열처리 온도에 따른 변화가 거의 나타나지 않는 것을 확인할 수 있었다.

• 한국자기학회지
• /
• 제9권1호
• /
• pp.17-22
• /
• 1999

육방구조의 M형 BaFe12O19를 NaCl를 첨가한 경우와 첨가하지 않은 경우에 질소가스 분위기와 공기 중에서 여러 온도로 가열하여 고상반응법으로 제조하였다. X-선 회절법과 Mossbauer분광법에 의하여 BaFe12O19상과 $\alpha$-Fe2O3상의 공존 정도를 알아냈다. 동일한 조건에서 NaCl를 첨가한 경우가 NaCl를 첨가하지 않은 경우 보다 $\alpha$-Fe2O3상이 적음을 확인하였다.

• 한국자기학회지
• /
• 제9권1호
• /
• pp.35-40
• /
• 1999

M-type Ba 페리이트를 Ba 대신 Sr으로 치환시킨 페라이트 분말과 Fe대신 Co-Ti으로 치환시킨 육방 페라이트 분말을 각각 citrate sol-gel법과 2 MOE sol-gel법으로 합성하였다. 이들 분말들을 소결 처리 후 수소 분위기 하에서 온도를 변화시키면서 환원처리 하였다. X-선 회절을 이용한 결정구조 해석에서 105$0^{\circ}C$에서 소결 처리된 분말의 경우 단일상의 M-type 육방정 구조로 나타났다. X-선 회절실험 결과 Sr0.5Ba0.5Fe12O19과 다르게, Co-Ti 치환형 페라이트인 Sr0.7Ba0.3Fe10CoTiO19에서는 Co-Ti 치환이 환원과정을 저지시키는 효과가 있는 것으로 나타났다. 육방 페라이트에서 수소환원에 의한 포화자화 Ms값의 증가 원인을 알아보기 위하여 Mossbauer 분광실험을 실시하였다. Mossbauer 실험결과는 대부분의 $\alpha$-Fe가 4fvi자리와 12k자리로부터 발생되는 것으로 나타났으며, 이 $\alpha$-Fe 형성에 의한 Fe3+이온의 결함이 자기 상호작용의 붕괴를 가져와서, 자기이방성의 변화를 초래하고 또한 Ms값의 증가를 가져오는 것으로 추측된다.