• Korean Journal of Materials Research
• /
• v.10 no.2
• /
• pp.117-123
• /
• 2000

In this study, to fabricate the semi-solid Al alloy, the 3phase-2poles electromagnetic stirring system was adopted. The changes of primary grain size, aspect ratio, standard deviation, hardness and the size morphology of eutectic Si with pouring temperatures and input voltages were investigated. At the same pouring temperature, with increasing input voltage, aspect ratio, standard deviation and primary grain size were decreased. The optimum condition for fabrication of semisolid Al alloys by EMS horizontal continuous casting process was determined that the input voltage was 220V and the pouring temperature was 68$0^{\circ}C$. At this optimum conditions the primary grain size was 54$\mu\textrm{m}$, the aspect ratio was 1.56 and the size of eutectic Si was 0.5$\mu\textrm{m}$. The micro-hardness of the Al alloy was 72.1 Hv. The semi-solid A356 Al alloy which has very low aspect ratio and standard deviation value could be fabricated by adopting the EMS horizontal continuous casting facility that was manufactured for this study.

• Membrane Journal
• /
• v.22 no.3
• /
• pp.224-233
• /
• 2012

To improve permeation performance of gas separation membrane, polysulfone hollow fiber membrane was prepared by wet-dry phase inversion method using Triton X-100 as non-ionic additive. And variation of gas permeation behavior by additive was investigated. Various spinning conditions such as air gap, concentration of polymer, dope tank temperature were controlled and these effects were studied. The morphology and gas permeation property of hollow fiber membranes were investigated using scanning electron microscope (SEM) and bubble flow meter respectively. We confirmed that the membranes added with Triton X-100 had a smooth external skin at various air gap length conditions. The macrovoids of these hollow fiber membranes were more developed with increase of air-gap from 4 to 90 cm and that induced higher permeance. The permeance of polysulfone membranes has the higher value at comparatively lower concentration polymer (30 wt% polysulfone) and lower concentration of additive (15 wt% Triton X-100). When temperature in dope tank was controlled, the membranes prepared at $100^{\circ}C$ showed low permeance because of volatilization of additive and solvent.

• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.2 s.35
• /
• pp.161-166
• /
• 2005

Glass formation, thermal property and crystallization behavior were investigated in $xK_2O-(33.3-x)BaO-16.7TiO_2-50SiO_2(mole\%)$ with fresnoite($Ba_2TiSi_2O_8$) crystal by replacement BaO for $K_2O$. As x(0$\le$x$\le$20) contents increased, glass formation became easy, and crystallization temperature moved on to the low temperature. Crystal phase of the $Ba_2TiSi_2O_8$ was confirmed by XRD, and the replaced x was not effected on the formation of new crystals. The kinetics of crystallization of fresnoite were studied by applying the DTA measurements carried out at different heating rates. The average avrami exponent(n) and activation energy were changed $2.26 {\pm}0.1,\;2.03 {\pm}0.1,\;1.93{\pm}0.15$, $279 {\pm}12kJ/mole,\;302{\pm}7kJ/ mole,\;319{\pm}1kJ/mole$ according to x contents, respectively. The replaced x improved the orientation of crystal growth.

• Journal of the Korean Chemical Society
• /
• v.10 no.1
• /
• pp.32-42
• /
• 1966

The electrolysis of tungstic oxide dissolved in the bath of calcium chloride and calcium oxide was studied to produce metallic tungsten using carbon as anode and iron as cathode in the temperature range of 900^{\circ}$ to $1200^{\circ}C$. The binary phase diagrams $CaCl_2$-CaO and $CaCl_2-CaWO_4$ systems were constructed to determine the suitability of bath composition and the range of temperatures for the electrolysis. As $WO_3$ reacted with $CaCl_2$ to form oxychloride in the fused salt, the addition of the proper amount of CaO was necessary to avoid the loss of $WO_3$. The optimum compositions of fused bath were $CaCl_2$ 100 parts, CaO and $WO_3$ each 10 to 20 parts, with the CaO, $WO_3$ ratio greater than unity, to keep freezing point low and to prevent the vaporization of $CaCl_2$. The observed decomposition voltage at which $WO_3$ decomposes to W and CO was-0.1 volt, whereas the calculated was -0.3 volt. Metallic tungsten deposited at the cathode reacted easily with CO formed secondarily at the anode surface, to form WC below $1050^{\circ}C$, so that the cell temperature should be above $1050^{\circ}C$. The effects of cathode current densities on current efficiency were minor in the range of 1 to 5 $amp/cm^2$.

• Economic and Environmental Geology
• /
• v.42 no.5
• /
• pp.427-434
• /
• 2009

Indigenous bacterium which shows a tolerance to high metal toxicity was isolated from soil concomitantly contaminated with oil and heavy metals. The characteristics of the bacterium for Pb and Cd biosorption was investigated under the various experimental conditions such as bacterial growth phase, the initial metal concentration, the input biomass amount, temperature and pH. The Langmuir adsorption isotherm modeling was described to know the capacity and intensity of biosorption. The low initial concentration of heavy metals and high biomass has a maximum heavy metal removal efficiency, but biosorption capacity of Pb and Cd has different values. Biosorption efficiency was highest in the end of the microbial growth stage and under pH 5~9 condition, but was less affected by temperature variation of 25~$35^{\circ}C$. The maximum biosorption capacity for Pb and Cd was 62.11 and 192.31 mg/g, respectively and each $R^2$ was calculated as 0.71 and 0.98 by applying Langmuir isothermal adsorption equation. Biosorption for Cd was considered as monomolecular adsorption to single layer on the surface of cells, whereas biosorption for Pb was considered as accumulation process into the cell by the microbial metabolism and precipitation reaction with anion of bacteria.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.14-15
• /
• 2010

Recently there has been growing interest in topological insulators or the quantum spin Hall (QSH) phase, which are insulating materials with bulk band gaps but have metallic edge states that are formed topologically and robust against any non-magnetic impurity [1]. In a three-dimensional material, the two-dimensional surface states correspond to the edge states (topological metal) and their intriguing nature in terms of electronic and spin structures have been experimentally observed in bulk Bi1-xSbx single crystals [2,3,4]. However, if we want to know the transport properties of these topological metals, high purity samples as well as very low temperature will be needed because of the contribution from bulk states or impurity effects. In a recent report, it was also shown that an intriguing coupling between the surface and bulk states will occur [5]. A simple solution to this bothersome problem is to prepare a topological metal on an ultrathin film, in which the surface-to-bulk ratio is drastically increased. Therefore in the present study, we have investigated if there is a method to make an ultrathin Bi1-xSbx film on a semiconductor substrate. From reflection high-energy electron diffraction observation, it was found that single crystal Bi1-xSbx films (0${\sim}30\;{\AA}A$ can be prepared on Si(111)-$7{\times}7$. The transport properties of such films were characterized by in situ monolithic micro four-point probes [6]. The temperature dependence of the resistivity for the x=0.1 samples was insulating when the film thickness was $240\;{\AA}A$. However, it became metallic as the thickness was reduced down to $30\;{\AA}A$, indicating surface-state dominant electrical conduction. Figure 1 shows the Fermi surface of $40\;{\AA}A$ thick Bi0.92Sb0.08 (a) and Bi0.84Sb0.16 (b) films mapped by angle-resolved photoemission spectroscopy. The basic features of the electronic structure of these surface states were shown to be the same as those found on bulk surfaces, meaning that topological metals can be prepared at the surface of an ultrathin film. The details will be given in the presentation.

• Journal of the Korean Institute of Gas
• /
• v.2 no.1
• /
• pp.59-65
• /
• 1998

Morphology and thermal properties of polyurethane synthesized from 4,4'-diphenylmethane diisocyanate (MDI), polyester polyol, and 1,4-butane diol are investigated using fourier transform infrared spectroscopy (FT-IR), differential scanning calorimeter (DSC), and dynamic mechanical thermal analysis (DMTA). From the FT-IR study, it is found that the stretching peaks of hydrogen bonded N-H and C=O are shifted to the low frequencies with the increase of hard segment content of the polyurethanes. The shift of the stretching peaks of hydrogen bonded N-H and C=O indicates that the degree of hydrogen bonding is increased. From the DSC study, it appears that the glass transition temperature ($T_g$) of the polyurethanes is increased with the increase of the hard segment content. Also, it is found that the polyurethanes investigated in this study have the homogeneous network structure due to the high functionality of the MDI. From the DMTA study, transition of the soft segment was not found. Therefore it is concluded that the polyurethanes investigated in this study have the one-phase morphology which is consistent with the DSC results.

• Journal of Conservation Science
• /
• v.37 no.6
• /
• pp.807-820
• /
• 2021

A study on the Joseon Dynasty's furnace walls, excavated from south Korea, was conducted to identify the correlations and differences of the furnace walls found in Jeolla and Gyeongsang regions. Three ruins in the Jeolla region and two in the Gyeongsang region were selected for the analysis. The results showed a layer change depending on the degree of plasticity and difference in the number of layers and particle phase. Furthermore, although the temperature to be subjected to heat was divided into 1300℃ and 1100℃, it was not a phenomenon that appeared according to the region. Additionally, analysis result of major components revealed that the TiO₂ content of most samples does not exceed 1wt%, This means that the furnace did not smelt iron sand or smelted it into low-titanium sand. This study indicated a slight similarity between the furnace walls found in the two regions, and the correlation was determined based on the nature of the ruins, raw materials of the metals ores, and composition of the raw materials constituting the furnace walls.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.20 no.3
• /
• pp.147-152
• /
• 2010

In this study, the artificial coarse aggregate was manufactured by using coal ash and low grade clay. The characteristics of a coal ash-clay system were investigated using XRD, XRF, TG-DTA, SEM and Dilatometer with various coal ash contents. The chemical compositions are the fly ash, bottom ash and clay, $Al_2O_3$ are 28.5 wt%, 32.4 wt% and 18.1 wt%, and $SiO_2$ are 33.0 wt%, 53.7 wt% and 68.4 wt% in weight ratio, respectively. The shrinkage of specimens started at around $850^{\circ}C$ and changed little up to $1100^{\circ}C$, but increased markedly at above $1100^{\circ}C$. The shrinkage rate is strongly related to the decarbonization amount of coal ash. At the sintering temperature $1150^{\circ}C$, it was found that quartz, mullite, anorthite and albite phase exist in all specimens. It was found that bottom-clay system specimen sintered at $1150^{\circ}C$ had a good compressive strength of 87.5 kg/$cm^2$, and the compressive strength of bottom-clay specimen was higher than that of fly-clay system specimen. The reusability of coal ash as a raw material in the process of shotcrete resources such as artifical coarse aggregate is highly expected.

• Herbal Formula Science
• /
• v.21 no.2
• /
• pp.133-143
• /
• 2013

Objectives : We carry out the simultaneous quantification for quality control of four components in Bangpungtongseong-san (BPTSS) sample. In addition, we assessed the antioxidant effects of BPTSS sample. Methods : The used column for separation and analysis of four compounds was Luna C18 column and column oven temperature was maintained at $40^{\circ}C$. The mobile phase for simultaneous determination consisted of two solvent systems, 1.0% acetic acid in water and 1.0% acetic acid in acetonitrile. High performance liquid chromatography-photodiode array (HPLC-PDA) method for analysis was performed at a flow rate of 1.0 mL/min with PDA detection at 254 and 280 nm. The injection volume was 10 ${\mu}L$. The antioxidant activities of BPTSS were evaluated by measuring free radical scavenging activities on 2,2'-Azinobis-3-ethyl-benzothiazoline-6-sulfonic acid (ABTS) and 1-1-diphenyl-2-picrylhydrazyl (DPPH). The inhibitory effects on low-density lipoprotein (LDL) oxidation were evaluated by the formation of thiobarbituric acid relative substances (TBARS) and relative electrophoretic mobility (REM). Results : Calibration curves were acquired with $r^2{\geq}0.9999$. The values of limit of detection (LOD) and quantification (LOQ) were 0.06-0.29 ${\mu}g/mL$ and 0.20-0.98 ${\mu}g/mL$, respectively. The amounts of geniposide, liquiritin, baicalin, and glycyrrhizin in BPTSS were 5.06, 7.33, 27.56, and 7.81 mg/g, respectively. The BPTSS showed the radical scavenging activity in a dose-dependent manner. The concentration required for 50% reduction (RC50) against ABTS and DPPH radicals were 72.51 ${\mu}g/mL$ and 128.49 ${\mu}g/mL$. Furthermore, GMGHT reduced the oxidation properties of LDL induced by CuSO4. Conclusions : The established HPLC-PDA method will be helpful to improve quality control of BPTSS. In addition, BPTSS has potentials as therapeutic agent on anti-atherosclerosis.