• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.6
• /
• pp.460-464
• /
• 2003

The barium strontium titannate ((Ba,Sr)TiO$_3$:BST) thin films were etched in an inductively coupled plasma (ICP) as a function of CF$_4$/Ar gas mixing ratio. Under CF$_4$(20%)/Ar(80%), the maximum etch rate of the BST films was 400 $\AA$/min. Etching products were redeposited on the surface of BST and then the nature of crystallinity were varied. Therefore, we investigated the etched surface of BST by X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM). The plasma damages were evaluated in terms of leakage current density by Agilent 4145C and dielectric constant by HP 4192 impedance analyzer. After the BST thin films exposed in the plasma, the leakage current density and roughness increases. After annealing at 600 $^{\circ}C$ for 10 min in $O_2$ ambient, the leakage current density, roughness and nonvolatile etch byproducts reduced. From this results, the plasma induced damages were recovered by annealing process owing to the relaxation of lattice mismatches by Ar ions and the desorption of metal fluorides in high temperature.

• Journal of Sensor Science and Technology
• /
• v.1 no.2
• /
• pp.165-172
• /
• 1992

To determine the effect of additions of trivalent and pentavalent ions on the electrical conductivity and sensing behaviour, indium and antimony were incorporated in tin oxide by the coprecipitation method. Antimony may be considered to enter the cassiterite structure as pentavalent ions, thermal energy could excite electrons from these ions into the conduction band. Similarly the indium ions would enter the lattice as $In^{3+}$ but could accept electrons from the valence band, thereby becoming monovalent or divalent. These phenomena, however, how the potential barrier existing $SnO_{2}$ by addition of two kinds of ions could influence on the sensing behaviour in comparison with their influence on the resistivity were observed.

• Journal of the Korean institute of surface engineering
• /
• v.46 no.5
• /
• pp.192-196
• /
• 2013

Stainless steels (AISI 316L) are carburized by Inductively coupled plasma using $CH_4$ and Ar gas. The ${\gamma}_c$ phase(S-phase) is formed on the surface of stainless steel after carburizing process. The XRD peak of carburized samples is shifted to lower diffracting angle due to lattice expansion. Overall, the thickness of ${\gamma}_c$ phase showed a linear dependence with respect to increasing temperature due to the faster rate of diffusion of carbon. However, at temperatures above 500, the thickness data deviated from the linear trend. It is expected that the deviation was caused from atomic diffusion as well as other reactions that occurred at high temperatures. The interfacial contact resistance (ICR) and corrosion resistance are measured in a simulated proton exchange membrane fuel cell (PEMFC) environment. The ICR value of the carburized samples decreased from 130 $m{\Omega}cm^2$ (AISI 316L) to about 20 $m{\Omega}cm^2$. The sample carburized at 200 showed the best corrosion current density (6 ${\mu}Acm^{-2}$).

• Nuclear Engineering and Technology
• /
• v.53 no.12
• /
• pp.4052-4059
• /
• 2021

The microstructure of the fuel pellet plays an essential role in fission gas buildup and release and is critical for the safe and continued operation of nuclear power stations. Structural analysis of uranium dioxide (UO₂)-molybdenum (Mo) composite fuel pellets prepared at a range of sintering temperatures from 1300 to 1800 ℃ was performed. Mo micro and nanoparticles were used in making the composite pellets. A systematic investigation into the influence of processing parameters during Spark Plasma Sintering (SPS) of the pellets on the microstructure, texture, grain size, and grain boundary characters of UO₂-Mo is presented. UO₂-Mo composite show significant differences in the fraction of general boundaries and also special/coincident site lattice (CSL) boundaries. EBSD orientation maps demonstrated that <111> texturing was observed in the pellets fabricated at 1500 ℃. The experimental investigations suggest that UO₂-Mo composite pellets have favorable microstructural features compared to the UO₂ pellet.

• Nuclear Engineering and Technology
• /
• v.31 no.3
• /
• pp.335-343
• /
• 1999

The effects of N $b_2$ $O_{5}$ and oxygen potential on the densification and grain growth of U $O_2$ fuel have been investigated.0.3 wt% N $b_2$ $O_{5}$ -doped U $O_2$fuel pellets were sintered at 1$700^{\circ}C$ for 4 hours in sintering atmospheres which have various ratios of $H_2O$ to $H_2$ gas. Compared with those of undoped U $O_2$ pellets, the sintered density and grain size of the 0.3 wt% N $b_2$ $O_{5}$ -doped U $O_2$ pellet increase under the $H_2O$/ $H_2$ gas ratio of 5.0$\times$10$^{-3}$ to 1.0$\times$10$^{-2}$ and under the $H_2O$/ $H_2$gas ratio of 5.0$\times$10$^{-3}$ to $1.5\times$10$^{-2}$ , respectively. The sintering of U $O_2$fuel pellets containing 0.1 wt% to 0.5 wt% N $b_2$ $O_{5}$ was carried out at 168$0^{\circ}C$ for 4 hours. The enhancing effect of N $b_2$ $O_{5}$ on the sintered density and grain size becomes larger as the N $b_2$ $O_{5}$ content increases. The solubility limit of N $b_2$ $O_{5}$ in U $O_{2}$ seems to be between 0.3 wt% and 0.5 wt%, and beyond the solubility limit the second phase whose composition corresponds near to N $b_2$U $O_{6}$ is precipitated on grain boundary. The enhancement of densification and grain growth in U $O_2$ is attributed to the increased concentration of a uranium vacancy which is formed by the interstitial N $b^{4+}$ ion in the U $O_2$ lattice.

• Applied Chemistry for Engineering
• /
• v.5 no.6
• /
• pp.1044-1055
• /
• 1994

The preparation of ZrC/SiC mixed powders from $ZrSiO_4/C$ and $ZrSiO_4/Al/C$ systems was attempted in the temperature range below $1600^{\circ}C$ under Ar or $Ar/H_2$ gas flow(100-500ml/min). The formation mechanism and kinetics of ZrC/SiC were suggested and the resultant powders were characterized. In $ZrSiO_4/C$ system, ZrC and SiC were formed by competitive reaction of $ZrO_2(s)$ and SiO(g) with carbon at temperature higher than $1400^{\circ}C$. The apparent activation energy for the formation of ZrC was approximately 18.5kcal/mol($1400-1600^{\circ}C$). In $ZrSiO_4/Al/C$ system, ZrC was formed by reaction of ZrO(g) with Al(l, g) and carbon at temperature higher than $1200^{\circ}C$, and SiC was formed by reduction-carbonization of SiO(g) with Al(l, g) and carbon at temperature higher than $1300^{\circ}C$. The products obtained at $1600^{\circ}C$ for 5h consisted of ZrC with lattice constant of $4.679{\AA}$ and crystallite size of $640{\AA}$, and SiC with lattice constant of $4.135{\AA}$ and crystallize size of $500{\AA}$. And also, the mean particle size was about $21.8{\mu}m$.

• Journal of the Korean Vacuum Society
• /
• v.17 no.1
• /
• pp.51-57
• /
• 2008

we have demonstrated structural evolution and optical properties of Si-nanowires (NWs) synthesized on Si (111) substrates with nanoscale Au-Si islands by rapid thermal chemical vapor deposition (RTCVD). The Au-Si nano-islands (10-50nm in diameter) were employed as a liquid-droplet catalysis to grow Si-NWs via vapor-liquid-solid mechanism. The Si-NWs were grown by a mixture gas of SiH4 and H2 at a pressure of 1.0 Torr and temperatures of $500{\sim}600^{\circ}C$. Scanning electron microscopy measurements showed that the Si-NWs are uniformly sized and vertically well-aligned along <111> direction on Si (111) surfaces. The resulting NWs are ${\sim}60nm$ in average diameter and ${\sim}5um$ in average length. High resolution transmission microscopy measurements indicated that the NWs are single crystals covered with amorphous SiOx layers of ${\sim}3nm$ thickness. In addition, the optical properties of the NWs were investigated by micro-Raman spectroscopy. The downshift and asymmetric broadening of the Si main optical phonon peak were observed in Raman spectra of Si-NWs, which indicates a minute stress effects on Raman spectra due to a slight lattice distortion led by lattice expansion of Si-NW structures.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.32 no.5
• /
• pp.426-431
• /
• 2019

In this study, we report the effect of pre-treatment of alpha-$Ga_2O_3$ grown on a sapphire substrate by halide vapor phase epitaxy (HVPE). During the pre-treatment process, 10 sccm of GaCl gas was injected to the sapphire substrate at $470^{\circ}C$. The surface morphologies of the alpha-$Ga_2O_3$ layers grown with various pre-treatment time (3, 5, and 10 min) were flat and crack-free. The transmittance of the alpha-$Ga_2O_3$ epi-layers was measured to analyze their optical properties. The transmittance was over 80% within the range of visible light. The strain in the alpha-$Ga_2O_3$ grown with a pre-treat 5 min was measured, and was found to be close to the theoretical XRD peak position. This can be explained by the reduction of strain having caused a lattice mismatch between the alpha-$Ga_2O_3$ layer and sapphire substrate. The calculated dislocation density of the screw and edge were $2.5{\times}10^5cm^{-2}$ and $8.8{\times}10^9cm^{-2}$, respectively.

• Journal of Sensor Science and Technology
• /
• v.10 no.1
• /
• pp.62-70
• /
• 2001

The ZnSe sample grown by chemical bath deposition (CBD) method were annealed in Ar gas at $45^{\circ}C$. Using extrapolation method of X-ray diffraction pattern, it was found to have zinc blend structure whose lattice parameter $a_o$ was $5.6687\;{\AA}$. From Hall effect, the mobility was likely to be decreased by impurity scattering at temperature range from 10 K to 150 K and by lattice scattering at temperature range from 150 K to 293 K. The band gap given by the transmission edge changed from $2.700{\underline{5}}\;eV$ at 293 K to $2.873{\underline{9}}\;eV$ at 10 K. Comparing photocurrent peak position with transmission edge, we could find that photocurrent peaks due to excition electrons from valence band, ${\Gamma}_8$ and ${\Gamma}_7$ and to conduction band ${\Gamma}_6$ were observed at photocurrent spectrum. From the photocurrent spectra by illumination of polarized light on the ZnSe thin film, we have found that values of spin orbit coupling splitting ${\Delta}so$ is $0.098{\underline{1}}\;eV$. From the PL spectra at 10K, the peaks corresponding to free bound excitons and D-A pair and a broad emission band due to SA is identified. The binding energy of the free excitons are determined to be $0.061{\underline{2}}\;eV$ and the dissipation energy of the donor -bound exciton and acceptor-bound exciton to be $0.017{\underline{2}}\;eV$, $0.031{\underline{0}}\;eV$, respectively.

• Journal of the Korean Magnetics Society
• /
• v.14 no.2
• /
• pp.71-75
• /
• 2004

$\alpha$-LiFe $O_2$ powders have been prepared by a sol-gel method. The crystallographic and magnetic properties were characterized with a x-ray diffractometry, Mossbauer spectroscopy, and vibrating Samples magnetometry. The ${\gamma}$-LiFe $O_2$+LiFe$_{5}$ $O_{8}$ phase is observed in the Samples annealed at $600^{\circ}C$ for 3h in air and $\alpha$-LiFe $O_2$ phase is observed in the Samples annealed at $600^{\circ}C$ for 3 h in $H_2$(5％)/Ar(Bal.) gas atmosphere. The crystal structure of $\alpha$-LiFe $O_2$ is found to be cubic with a lattice a=4.193$\pm$0.0005 $\AA$. The Neel temperature of $\alpha$-LiFe $O_2$ is found to be 130$\pm$3 K.