• The Journal of Advanced Prosthodontics
• /
• v.8 no.6
• /
• pp.433-438
• /
• 2016

PURPOSE. The aim of this in vitro study was to evaluate the mechanical properties (bending strength and hardness) of seven different fiber reinforced composite posts, in relation to their microstructural characteristics. MATERIALS AND METHODS. Two hundred eighty posts were divided into seven groups of 40, one group for each type of post analyzed. Within each group, 15 posts were subjected to three-point bending strength test, 15 to a microhardess meter for the Knoop hardness, and 10 to Scanning Electron Microscope in order to determine the diameter of the fibers and the percentage of fibers embedded in the matrix. To compare the flexural strength in relation to the type of fiber, matrix, and the hardness of the posts, a Kruskal-Wallis H test was used. The Jonckheere-Terpstra test was used to determine if the volume percent of fibers in the post influenced the bending strength. RESULTS. The flexural strength and the hardness depended on the type of fibers that formed the post. The lower flexural strength of a post could be due to deficient bonding between the fiber and the resin matrix. CONCLUSION. According to the results, other factors, besides the microstructural characteristics, may also influence the mechanical properties of the post. The feature that has more influence on the mechanical properties of the posts is the type of fiber.

• Journal of Korean Vacuum Science & Technology
• /
• v.6 no.2
• /
• pp.105-107
• /
• 2002

a-C:H films were coated on windows of mobile telephone by RF plasma chemical vapor deposition equipment made in our company. Thickness of the coatings is about 0.7 micrometers and they have high hardness, low friction coefficient, good adhesion, high optical transparency and chemical inertness. Knoop hardness of the diamond-like carbon films on glass substrate is 2328 kg/mm$^2$. The adherence between films and substrate is good and shows to be 69 N by scratching test. The optical performance is improved obviously owing to coat the film on it. The index of the coated windows is 2.5, transmission of visible light is larger than 90%, and transmission of ultraviolet light decreases by 30% and the ultraviolet light can be obstructed obviously. The coated glass also has self-clean effect and decontamination ability. The films have hydrophobic character and the soakage angle of water drop is larger than 90 degrees. The windows have fog-proof ability owing to eliminate the capillary phenomena in the inner surface. The physics and chemical properties of the coated windows are steady. Study indicates that the performance of a-C:H coated mobile phone windows are improved notably on wear-resistance, corrosion-proof and optical properties and it is excellent mobile windows protective coatings.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.168.1-168.1
• /
• 2015

자동차 산업분야에서 차량 경량화의 한 수단으로, 자동차용 유리를 무게가 가볍고 고강도 투명 고분자 소재인 폴리카보네이트로 대체하고자 하는 연구가 이루어지고 있다. 하지만, 폴리카보네이트의 낮은 내 마모 특성과 자외선에 의한 열화 및 변색 현상은 해결해야 할 문제점으로 지적되고 있다. 본 연구에서는, 폴리카보네이트의 내마모 특성을 향상시키기 위해 HIPIMS+ (High Power Impulse Magnetron Sputtering+) 방법을 이용하여 투과율이 확보되고, 고경도 특성을 갖는 Al-Si-N 박막을 증착하였다. 고속증착을 하기 위해 Target에 인가되는 Power를 올리게 되었는데, 열팽창 계수가 큰 고분자 물질인 폴리카보네이트 시료의 온도가 상승하여 증착된 박막과의 열팽창 계수 차이에 의해 박막에 Crack이 형성되는 문제가 발생하였다. 증착되는 Al-Si-N 박막의 공정 압력에 따른 Stress 제어 방법 및 폴리카보네이트 시료의 온도 상승을 막기 위한 알루미늄 구조체를 이용함으로써 박막의 Crack 형성을 억제하고자 하였다. 박막의 Stress를 확인하기 위하여 AFM (Atomic Force Microscope)과 OM (Optical Microscope)을 이용하여 분석하였고, 박막의 경도는 Knoop ${\mu}$-hardness tester를 사용하여 측정하였다. Al-Si-N 박막 경도는 Si at.%/(Al at.% + Si at.%) 비율이 16%에서 33 GPa의 경도를 갖는 것을 확인하였다. UV-Vis Spectrometer를 이용하여 투과율을 측정한 결과, 400-700 nm 파장의 가시광 영역 평균 투과율은 80%로 측정되었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.179-179
• /
• 2013

현재 자동차 분야에서 차량 경량화를 통해 연비 향상 및 에너지 효율 향상을 기대하고 있으며, 차량 경량화의 한 수단으로 자동차용 유리를 고강도 투명 플라스틱 소재인 PC (Polycarbonate)로 대체하고자 하는 연구가 활발히 이루어지고 있다. 그러나, PC의 낮은 내마모 특성과 자외선에 의한 열화 및 변색 현상은 해결하여야 할 중요한 문제점으로 지적되고 있다. 본 연구에서는, PC의 내마모 특성을 향상시키기 위하여 transmittance가 확보되고, 고경도 특성을 갖는 Al-Si-N 박막 증착에 대한 연구를 하였다. Al-Si-N 박막 증착을 위하여 ICP-assisted reactive magnetron sputtering 장비를 이용하였으며, 고경도 특성을 갖는 Al-Si-N 박막을 제조하였다. 분석 장비로는 박막의 chemical state와 crystallinity를 확인하기 위하여 XPS (X-ray Photoelectron Spectroscopy), AES (Auger electron spectrscopy)와 XRD (X-ray diffraction)를 이용하여 분석을 수행하였으며, Knoop ${\mu}$-hardness tester와 Pin-on-disk를 이용하여 경도 및 내마모 특성을 평가하였다. Al-Si-N 박막의 두께는 ~5,000 ${\AA}$을 증착하였으며, 가시광 영역에서 평균 92%의 transmittance를 나타내었다. 박막의 Si/(Al+Si) 비율에 따라 다른 경도 특성을 나타냈는데, Si/(Al+Si) 비율이 26~32% 부근에서 최대 31 GPa의 경도 값을 확인 할 수 있었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.190.1-190.1
• /
• 2013

현재 자동차 분야에서 차량 경량화를 통해 연비 향상 및 에너지 효율 향상을 기대하고 있으며, 차량 경량화의 한 수단으로 자동차용 유리를 고강도 투명 플라스틱 소재인 PC(Polycarbonate)로 대체하고자 하는 연구가 활발히 이루어지고 있다. 그러나, PC의 낮은 내마모 특성과 자외선에 의한 열화 및 변색 현상은 해결하여야 할 중요한 문제점으로 지적되고 있다. 본 연구에서는, PC의 내마모 특성을 향상시키기 위하여 transmittance가 확보되고, 고경도 특성을 갖는 Al-Si-N 박막 증착에 대한 연구를 하였고, 자외선 차단을 위하여 SiN:H 박막을 증착 하였다. 박막 증착을 위하여 ICP-assisted reactive magnetron sputtering 장비를 이용하였으며, 고경도 특성을 갖는 Al-Si-N 박막을 제조하였다. 그리고 300 nm 파장 이하의 자외선 차단을 위하여 SiN:H 박막을 증착하였다. 분석 장비로는 박막의 chemical state와 crystallinity를 확인하기 위하여 XPS(X-ray Photoelectron Spectroscopy), XRD(X-ray diffraction)를 이용하여 분석을 수행하였으며, Knoop ${\mu}$-hardness tester와 Pin-on-disk를 이용하여 경도 및 내마모 특성을 평가하였다. SiN:H 박막 위에 Al-Si-N 박막을 증착하였고 총 두께는 ~5000 $\AA$을 증착하였으며, 가시광 영역에서 평균 70% 이상의 transmittance를 나타내었다. 박막의 Si/(Al+Si) 비율에 따라 다른 경도 특성을 나타냈는데, Si/(Al+Si) 비율이 26~32% 부근에서 최대 31 GPa의 경도 값을 확인하였고 SiN:H 박막은 300nm 이하의 파장에서 2% 이하의 transmittance를 확인하였다.

• Journal of the Korean Society for Heat Treatment
• /
• v.27 no.1
• /
• pp.10-14
• /
• 2014

Niobium nitride coatings have many potential thin film applications due to their chemical inertness, good mechanical properties, temperature stability and superconducting properties. In this study, $NbN_x$ coatings were prepared by inductively coupled plasma (ICP) assisted DC magnetron sputtering method on the surface of AISI 304 austenitic stainless steels. Effects of target power were studied on mechanical and chemical properties of the coatings. The coating structure was analyzed by X-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM). The coating hardness was measured by micro-knoop hardness tester. The coating thickness was measured using a 3D profiler and wear characteristics were estimated using a ball-on-disk wear tester. The thickness of the $NbN_x$ coatings increased linearly from 300 nm to 2000 nm as the Nb target power increased, and it showed over $HK_{0.005}$ 4000 hardness above Nb target power of 300 W. Hexagonal ${\delta}^{\prime}$-NbN phase and cubic ${\delta}$-NbN phase were observed in the coating films and the hardness of the NbNx coatings was higher when these two peaks were mixed. The corrosion resistance increased with the increase of the Nb target power.

• Restorative Dentistry and Endodontics
• /
• v.12 no.1
• /
• pp.7-24
• /
• 1986

The purpose of this study was to observe the compressive strength, compressive fatigue strength, surface hardness, water sorption and solubility of eight different posterior restorative composite resins. Eight composite resins were tested for their strength of the compressive and compressive fatigue with prepared two different types of specimens (I and T-type) using a Instron universal testing machine (model No. 1332). The hardness was measured with a Knoop hardness tester (MVH-2, Tokyo) for each cylindrical specimen, 7mm in diameter and 5mm thick. The water sorption and solubility were evaluated with the prepared composite resin disks, 20mm in diameter and 1mm thick. The results were as follows: 1. The compressive strength, compressive fatigue strength and hardness were noticed to be Increased by increasing the volume content of filler. 2. The compressive strength was appeared to be independent on the type of specimen, but the compressive fatigue strength was found to be greatly influenced by the type of specimens. 3. The composite resins having higher compressive strength had also higher compressive fatigue limits. 4. The compressive fatigue limits at $10^5$ stress cycles were about 50-80% of the compressive strength and were showen to be dependent on the materials and type of specimens. 5. The larger the filler particle size was, the lower was the water sorption. And the water sorption of BIS-GMA resin was higher than that of urethane resin. 6. The visible light-cured composite resin had a higher value of solubility than the chemically- cured composite resin. And the solubility tended to decrease by increasing the volume content of filler.

• Journal of Surface Science and Engineering
• /
• v.46 no.5
• /
• pp.187-191
• /
• 2013

Niobium nitride (NbN) films were deposited on AISI 304 stainless steels by inductively coupled plasma (ICP) assisted dc magnetron sputtering method at different ICP powers, and the effects of ICP power on the phase formation, mechanical and chemical properties of the films were investigated. X-ray diffraction analysis (XRD) and field emission scanning electron microscopy (FESEM) were used to analyze the crystal structure and micro-knoop hardness was used to measure the hardness of the films. Also, 3-D mechanical profiler and a ball-on-disk wear tester were used to measure the thickness of the films and to estimate wear characteristics, respectively. The thickness of the films decreased but their hardness increased with increasing ICP power, and it was confirmed that only cubic ${\delta}$-NbN(200) remained at high ICP power. At lower ICP powers, a mixture of the hexagonal ${\delta}^{\prime}$-NbN and cubic ${\delta}$-NbN phases was obtained in the films and the hardness decreased. The corrosion potential value increased gradually with increasing ICP power, but the changes of ICP power did not significantly influence the overall corrosion resistance.

• Restorative Dentistry and Endodontics
• /
• v.46 no.3
• /
• pp.39.1-39.12
• /
• 2021

Objectives: This study analyzed the physical-chemical behavior of 2 bulk fill resin composites (BFCs; Filtek Bulk Fill [FBF], and Tetric-N-Ceram Bulk Fill [TBF]) used in 2- and 4-mm increments and compared them with a conventional resin composite (Filtek Z250). Materials and Methods: Flexural strength and elastic modulus were evaluated by using a 3-point bending test. Knoop hardness was measured at depth areas 0-1, 1-2, 2-3, and 3-4 mm. The translucency parameter was measured using an optical spectrophotometer. Real-time polymerization kinetics was analyzed using Fourier transform infrared spectroscopy. Results: Flexural strength was similar among the materials, while TBF showed lower elastic modulus (Z250: 6.6 ± 1.3, FBF: 6.4 ± 0.9, TBF: 4.3 ± 1.3). The hardness of Z250 was similar only between 0-1 mm and 1-2 mm. Both BFCs had similar hardness until 2-3 mm, and showed significant decreases at 3-4 mm (FBF: 33.45 ± 1.95 at 0-1 mm to 23.19 ± 4.32 at 3-4 mm, TBF: 23.17 ± 2.51 at 0-1 mm to 15.11 ± 1.94 at 3-4 mm). The BFCs showed higher translucency than Z250. The polymerization kinetics of all the materials were similar at 2-mm increments. At 4-mm, only TBF had a similar degree of conversion compared with 2 mm. Conclusions: The BFCs tested had similar performance compared to the conventional composite when used in up to 2-mm increments. When the increment was thicker, the BFCs were properly polymerized only up to 3 mm.

• The korean journal of orthodontics
• /
• v.29 no.5 s.76
• /
• pp.589-597
• /
• 1999

The purpose of this study was to evaluate the effects of fluoride releasing orthodontic sealants, light-cured (Group L1&L2) and self-cured (Group S1&S2) $FluoroBond^{\circledR}$, on enamel microhardness under artificial carious solution in vitro.112 extracted human premolar teeth were collected for experiments and divided into seven groups. A Tukon microhardness tester equipped with a Knoop diamond indenter was employed to determine microhardness. Tukon 23 program converted the number of microhardness into KHN (Knoop hardness number). The results were as follows: 1. The microhardness of enamel depth of all groups were the least at the depth of $50{\mu}m$ and that of all groups except L2 group, the greatest at the depth of $200{\mu}m$, were the greatest at the depth of $300{\mu}m$. And as the enamel depth of all groups except L2 and S2 group increased, the microhardness value also increased. 2. There was a little preventive effect in enamel decalcification both light-and self-cured orthodontic sealant groups, but had no statistical significance between the groups(p>0.05). 3. Light-cured orthodontic sealant groups had a progressive inhibiting effect in enamel decalcification at the depth of $100{\mu}m,150{\mu}m,\;and\;200{\mu}m$ (p<0.05). 4. Self-cured orthodontic sealant groups had a progressive inhibiting effect in enamel decalcification at the depth of $150{\mu}m$ (p<0.05). 5. There was no difference of the anti-enamel demineralization effect between light- and self-cured orthodontic sealant groups (p>0.05).