• Macromolecular Research
• /
• 제14권1호
• /
• pp.38-44
• /
• 2006

Vacuum deposited copper phthalocyanine (CuPc) was placed as a thin interlayer between indium tin oxide (ITO) electrode and a hole transporting layer (HTL) in a multi-layered, organic, light-emitting diode (OLEOs). The well-stacked CuPc layer increased the stability and efficiency of the devices. Thermal annealing after CuPc deposition and magnetic field treatment during CuPc deposition were performed to obtain a stacked-CuPc layer; the former increased the stacking density of the CuPc molecules and the alignment of the CuPc film. Thermal annealing at about 100$^{circ}C$ increased the current flow through the CuPc layer by over 25$\%$. Surface roughness decreased from 4.12 to 3.65 nm and spikes were lowered at the film surface as well. However, magnetic field treatment during deposition was less effective than thermal treatment. Eventually, a higher luminescence at a given voltage was obtained when a thermally-annealed CuPc layer was placed in the present, multi-layered, ITO/CuPc/NPD/Alq3/LiF/AI devices. Thermal annealing at about 100$^{circ}C$ for 3 h produced the most efficient, multi-layered EL devices in the present study.

• 한국응용과학기술학회지
• /
• 제31권4호
• /
• pp.694-702
• /
• 2014

마이크론 크기를 가지는 ITO(indium tin oxide) 입자들은 인듐과 틴의 수용성 전구체들과 유기 첨가제를 분무 열분해하여 얻었다. 유기 첨가제로서는 에틸렌글리콜과 시트르산을 이용하였다. 분무 열분해 시 에틸렌글리콜과 시트르산과 같은 유기첨가제를 첨가하지 않고 얻어진 ITO 입자들은 구형이며 속이 꽉찬 형태를 가지는데 비해 유기 첨가제를 첨가하여 분무 열분해를 하면 얻어지는 ITO 입자들은 유기 첨가제의 양이 증가 할수록 껍질이 얇고 다공성이 증대된 중공 입자가 얻어진다. 유기첨가제를 첨가하지 않고 분무 열분해를 통해 얻어지는 마이크론 크기를 가지는 ITO는 $700^{\circ}C$에서 두 시간 동안의 후소성과 24 시간동안의 습식 볼밀링에 의해 나노 크기의 ITO로 전환되지 않으나, 유기첨가제를 첨가하고 분무 열분해를 통해 얻어지는 마이크론 크기를 가지는 ITO는 $700^{\circ}C$에서 두 시간 동안의 후소성과 24 시간 동안의 습식 볼밀링에 의해 나노 크기의 ITO로 쉽게 전환되었다. 응집된 나노 크기의 ITO의 일차 입자의 크기를 Debye-Scherrer 식에 의해 계산하였고 ITO 입자를 압축하여 만든 펠렛의 표면저항을 측정하였다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2008년도 제34회 동계학술대회 초록집
• /
• pp.204-204
• /
• 2008

• 한국전기전자재료학회논문지
• /
• 제19권11호
• /
• pp.1044-1049
• /
• 2006

We reported on characteristics of the fluorescent OLED fabricated on commercial ITO/glass and BCS grown IZO/glass substrate, respectively. The amorphous IZO anode film grown by box cathode sputtering(BCS) exhibited similar electrical and optical characteristics to commercial ITO anode even though it was deposited at room temperature. In addition, the amorphous IZO anode showed higher workfunction (5.2 eV) than that of the commercial ITO anode (5.0 eV) after ozone treatment for 10 min. Furthermore, fluorescent OLED fabricated on amorphous IZO anode film showed improved current-voltage-luminance characteristics, external quantum efficiency and power efficiency en contrast with fluorescent OLED fabricated on commercial ITO anode film. It was thought that smooth surface and high workfunction of amorphous IZO anode lead to more efficient hole injection by reduction of interface barrier height between anode and organic layers.

• Journal of Advanced Marine Engineering and Technology
• /
• 제40권4호
• /
• pp.325-329
• /
• 2016

본 연구에서는 Indium-Tin-Oxide 인쇄 박막의 원격 검출이 가능한 해양오염 방제용 센서로서의 응용 가능성에 대해 연구하였다. 우선 양질의 박막제작을 위한 바인더 비율, Indium-Tin-Oxide 중 주석 농도, 열처리 온도 등의 Indium-Tin-Oxide 인쇄박막 제작 조건을 최적화시켰다. 이를 이용하여 전기저항형 액체 센서를 제작하였고, 센서 동작을 확인하기 위하여 대기 중과 해수 중에서 저항 변화를 확인하였다. 이때 저항 변화의 원인은 전해질 속에서 표면에서 일어나는 환원반응에 의한 것으로 해석하였다. 또한 제작된 센서를 Arduino를 사용하여 작동시키고 취득한 데이터의 원격 검출이 가능함을 확인하였다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2005년도 추계학술발표회 및 workshop
• /
• pp.173-174
• /
• 2005

• The Korean Journal of Ceramics
• /
• 제6권1호
• /
• pp.15-20
• /
• 2000

Thick inorganic-organic hybrid films were prepared on ITO-coated glass substrates by the electrophoretic sol-gel deposition of polyphenylsilsesquioxane particles. The morphology of the deposited films changed from the aggregate of the spherical particles to monolith by heat treatment at temperatures higher than $200^{\circ}C$. Transparency of the films was significantly improved accompanied by the morphological change of the particles. The degree of the morphological change was governed by two factors; maximum heat treatment temperature and heating rate. Transparent thick films of ca. 3$\mu\textrm{m}$ in thickness were obtained only by heat treatment at $400^{\circ}C$ for 2h with rapid heating from room temperature to $400^{\circ}C$. These films obtained were strongly adhered to the ITO-coated glass substrates and has a very smooth surface.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2007년도 춘계학술대회
• /
• pp.309-312
• /
• 2007

Sputter deposition followed by surface treatment was studied using reactive RF plasma as a method for preparing titanium oxide($TiO_{2}$) films on indium tin oxide(ITO) coated glass substrate for dye-sensitized solar cells(DSSCs). Anatase structure $TiO_{2}$ films deposited by reactive RF magnetron sputtering under the conditions of $Ar/O_{2}$(5%) mixtures, RF power of 600W and substrate temperature of $400^{\circ}C$ were surface-treated by inductive coupled plasma(ICP) with $Ar/O_{2}$ mixtures at substrate temperature of $400^{\circ}C$, and thus the films were applied to the DSSCs, The $TiO_{2}$ Films made on these exhibited the BET specific surface area of 95, the pore volume of $0.3cm^{2}$ and the TEM particle size of ${\sim}25$ nm. The DSSCs made of this $TiO_{2}$ material exhibited an energy conversion efficiency of about 2.25% at $100mW/cm^{2}$ light intensity.

• Journal of Electrochemical Science and Technology
• /
• 제7권1호
• /
• pp.27-32
• /
• 2016

Although the time dependences of the electrocatalytic activities of Pt and Pd nanoparticles during electrochemical operations have been widely studied, the time dependences under nonpolarized conditions have never been investigated in depth. This study reports the changes in the electrocatalytic activities of Pt and Pd nanoparticles with aging in air and in solution. Pt (or Pd) nanoparticle-modified electrodes are obtained by adsorbing citrate-stabilized Pt (or Pd) nanoparticles on amine-modified indium-tin oxide (ITO) electrodes, or by electrodeposition of Pt (or Pd) nanoparticles on ITO electrodes. The electrocatalytic activities of freshly prepared Pt and Pd nanoparticles in the oxygen reduction reaction slowly decrease with aging. The electrocatalytic activities decrease more slowly in solution than in air. An increase in surface contamination may cause electrocatalytic deactivation during aging. The electrocatalytic activities of long-aged Pt (or Pd) nanoparticles are significantly enhanced and recovered by NaBH₄ treatment.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.51-52
• /
• 2015

Organic light emitting diode (OLED) 나 organic photovoltaic device (OPV)와 같은 유기소자에 전극으로 쓰이고 있는 indium tin oxide (ITO)는 유연한 디바이스에 적용하기에는 유연성이 떨어진다는 문제가 있다. 이를 해결하기 위해서 ITO를 대체할 수 있는 CNT, Graphene, AgNWs, 전도성 고분자 등의 투명전극에 관한 연구가 활발히 진행되고 있다. 그러나 CNT, Grapene, 전도성 고분자는 여전히 전기적 특성이 좋지 못하기 때문에 차세대 투명전극으로 사용되기는 어려움이 있다. 반면에 AgNWs는 용액공정으로 제조 단가가 비교적 저렴하며, 높은 전기전도도 특성과 우수한 유연성을 가지는 투명 전극이기 때문에 많은 주목을 받고 있다. 그러나 NW-NW간의 접촉저항이 높아 전도성이 저하된다는 문제점과 Environmental stability가 좋지 못하다는 단점이 여전히 존재한다. 본 연구에서는 AgNW 전극 위에 플라즈마처리를 진행하여 AgNW의 전도성과 Stability를 향상시키고자하였다. 플렉서블한 PET기판위에 AgNW 전극을 Spray Coating하여 균일하게 전극을 형성하였고, 플라즈마 처리를 통해서 기판의 변형없이 AgNW의 저항을 45%이상 향상시켰으며, Stability 또한 아무것도 처리하지 않은 AgNW에 대비하여 2배 이상 향상된 것을 확인하였다.