• Journal of Dental Rehabilitation and Applied Science
• /
• v.17 no.3
• /
• pp.199-204
• /
• 2001

This study was to investigate the reused possibility of zirconia reinforced glass-ceramic(IPS Empress Cosmo ceramic) with sprue button in the flexure strength and fracture toughness. 40 disk-shaped ceramic specimens (20 specimens: as-pressed material; 20 specimens: reused material) with approximately 1.7 mm thickness and 15 mm diameter were prepared by "lost wax" technique. The remnants(sprue buttons) were used for repressing. The surface treatments for the discs were gradually abraded with 320, 800, 1200, and 2000 grit SiC sandpaper. The specimens were evaluated their flexure strength with the biaxial flexure jig(ball-on-three balls) and their fracture toughness with Vickers Indentation-microfracture test. The Weibull moduli were calculated for biaxial flexural strength. The mean flexure strength and fracture toughness of each group were $122.2{\pm}18.3MPa$, $1.00{\pm}0.09MPa{\cdot}m^{0.5}$ (as-pressed ceramics), and $122.2{\pm}20.3MPa$, $1.01{\pm}0.10MPa{\cdot}m^{0.5}$ (reused ceramics). There were no significant differences in the strength and the fracture toughness between the as-pressed and the reused IPS Empress Cosmo ceramic (P>0.05). This implied zirconia reinforced glass-ceramic(IPS Empress Cosmo ceramic) could be used one more time by reusing of sprue button in the flexure strength and fracture toughness.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.6
• /
• pp.821-828
• /
• 2000

Metal - ceramic restorations have been the standard of fixed oral rehabilitation for over 30 years, and while many advances have been made in materials and research, the esthetic challenges of the light reflective metal substructure will always put clinician in an esthetic dilemma, for only a very talented ceramist / dentist team can create esthetics that rival nature on a repeatable basis. All ceramic restorations have also been a choice in our restorative armamentarium, but in the past, the materials have also had their own limitation, number on being question-able strength to withstand occlusal forces generated during mastication. IPS Empress 2 offers dentistry a metal free alternative to traditional restorative techniques. This clinical report describes the treatment of patients with esthetic problem of anterior dentition using Empress 2 system.

• The Journal of Korean Academy of Prosthodontics
• /
• v.36 no.6
• /
• pp.789-805
• /
• 1998

The purpose of this study was to compare the microleakage of the IPS Empress ceramic crown according to 1) margin types such as rounded shoulder and bevel, 2) margin locations such as enamel and dentine, 3) resin cement types such as Variolink and Bistite. For this study, 80 extracted premolar teeth were used. After 10 experimental dies were prepared for each group, the IPS Empress ceramic crowns were fabricated on the dies and cemented with one of two types of resin cement. After 1,000 cycles of thermal changes were given with the thermocycling unit, each specimen was sectioned with a low speed diamond saw in both the buccolingual and the mesiodistal direction. The microleakage was then measured with a stereo microscope. The obtained results were as follows : 1. Every experimental group showed microleakage. The microleakage of the crowns which had a rounded shoulder on enamel cemented with Variolink was the lowest of all. The resulting rank of the mean microleakage was rounded shoulder on enamel using Variolink(0.601mm), rounded shoulder on enamel using Bistite (0.794mm), bevel on enamel using Variolink (0.826mm), rounded shoulder on dentine using Variolink(1.054mm), bevel on enamel using Bistite(1.087mm), rounded shoulder on dentine using Bistite(1.176mm), bevel on dentine using Variolink(1.258mm), and bevel on dentine using Bistite(1.467mm). 2. The statistically significant differences in the microleakage were found in 4 cases: rounded shoulder on enamel using Variolink and bevel on dentine using Variolink, rounded shoulder on enamel using Variolink and bevel on dentine using Bistite, rounded shoulder on enamel using Bistite and bevel on dentine using Bistite, bevel on enamel using Variolink and bevel on dentine using Bistite. 3. The microleakage of rounded shoulder finish line was lower than that of bevel finish line. The statistically significant differences were found with respect to the type of finish lines. 4. The microleakage of the finish line on enamel was lower than that of finish line on dentine. The statistically significant differences were found with respect to the location of the finish lines. 5. The microleakage of the Variolink cement was lower than that of the Bistite cement. The statistically significant differences were found with respect to the resin cements.

• Restorative Dentistry and Endodontics
• /
• v.24 no.3
• /
• pp.473-481
• /
• 1999

This study evaluated the shear bond properties of IPS Empress glass ceramic to enamel and dentin surfaces with three ceramic surface treatments, and three resin cements. The influence of thermocycling was also investigated. The purpose of this study was to investigate the influences of resin cements, ceramic surface treatments, and thermocycling on shear bond properties. Ninety freshly extracted, noncarious human molars were selected for this study. The surface treatments of ceramic were etching <5.0% hydrofluoric acid, application of silane coupling agents(Tokuso Ceramic Primer, Clearfil porcelain bond, Monobond-S), and the combination of the two methods. Empress cylinders were bonded to enamel and dentin surfaces with three kinds of resin cements(Bistite resin cement, Panavia 21, Variolink). The specimens were aged in $37^{\circ}C$ distilled water for 24 hours. Half of the specimens were then thermocycled 500times between $5^{\circ}C$ and $55^{\circ}C$ with a dwell time of 15 seconds. Each specimen was debonded in shear mode and measured shear bond properties by using the universal testing machine(Zwick 020, Germany). The data were analyzed by SPSS/PC+(one-way ANOVA, Scheffe' s test and t-test). The results were as follows : 1. Without thermocyling, there was significant difference of shear bond strength to enamel surface between Bistite Resin Cement and Panavia 21 in case of etched and silane-treatment(p<0.05). 2. Without thermocyling, the shear bond strength of a group treated with silane and etching was significantly higher than that of a group treated with silane or etching with the application of Panavia 21 and Variolink(p<0.05). 3. A group treated with etching with the application of Variolink only showed a decrease of shear bond strength after thermocycling(p<0.05).

• The Journal of Korean Academy of Prosthodontics
• /
• v.42 no.5
• /
• pp.514-523
• /
• 2004

Statement of problem: All-ceramic restorations have been advocated for superior esthetics. Various post and core systems have been used to improve the strength of damaged teeth, but it is unclear whether they affect the final shade of finished all-ceramic restorations. Purpose: The influence of different types of post and core systems on light transmission through all-ceramic crowns was assessed by spectrophotometric analysis. Also the masking effect of different thickness of ceramic ingot was evaluated. Material and Methods : Forty-five sample disks (15mm in diameter) at several thickness(1.0, 1.5, 2.0mm) and value(shade 100, 200, 300) were made in heat pressed ceramic(IPS-Empress). Background specimens simulating gold-alloy cast posts(Type III casting gold alloy), metal posts(Ni-Cr casting alloy) and ceramic posts(CosmoPost) were fabrica-ted. Resin composite(Z250, A3 shade) was used as a tooth substrate reference. For each combination, the change in color was measured with a spectrophotometer. Readings were performed for 2 conditions (1) ability of ceramic to mask the core in relation to its thickness(1.0, 1.5, or 2.0mm) ; (2) influence of post and core types on the final color of the ceramic. Data were recorded according to the CIE $L^*a^*b^*$ systems and color difference($\Delta$E) was calculated. Results: 100 shade ingot: when ceramic thickness was 1.0mm, $\Delta$E value for ceramic post larger than 1 but $\Delta$E value for metal and gold post was larger than 2. For ceramic thickness of 1.5mm, only $\Delta$E value for metal was larger than 2, and the other samples' $\Delta$E value was smaller than 2. For ceramic thickness of 2.0mm, $\Delta$E values for all specimens was smaller than 2. 200 shade ingot: when ceramic thickness was 1.0mm, $\Delta$E value for ceramic post was smaller than 1 but $\Delta$E value for metal and gold post was larger than 2. For ceramic thickness of 1.5 mm, only the $\Delta$E value for metal was larger than 2, and the other samples' $\Delta$E value was smaller than 2. For ceramic thickness of 2.0mm, $\Delta$E values for all specimens was smaller than 1. 300 shade ingot: when ceramic thickness was 1.0mm, only $\Delta$E value for metal was larger than 2 and the other samples' $\Delta$E value was smaller than 2. For ceramic thickness of 1.5mm, $\Delta$E values for all specimens was smaller than 1. For ceramic thickness of 2.0mm, $\Delta$E values for all specimens was smaller than 1. Conclusion: The final esthetic result of the IPS-Empress glass-ceramic restoration was not affected by the presence of different core materials when the thickness was more than 2.0 mm. When ceramic thickness decreases to 1.5mm, it is advised to take the substrate aspects into consideration. If the ceramic thickness is less than 1.0mm, using the tooth color matched substrate is strongly recommended.

• The Journal of Advanced Prosthodontics
• /
• v.9 no.3
• /
• pp.200-207
• /
• 2017

PURPOSE. In this study, three bioceramic materials, [IPS Empress CAD (Ivoclar), IPS e.max CAD (Ivoclar), and Lava Ultimate CAD (3M ESPE)] were treated with three commercial mouthrinses [Listerine, Tantum Verde, and Klorhex]; and changes in colour reflectance and surface roughness values were then quantitatively assessed. MATERIALS AND METHODS. One hundred and twenty ceramic samples, with dimensions of $2{\times}12{\times}14mm$, were prepared and divided into nine sample groups, except three control samples. The samples were immersed in the mouthrinse solutions for 120 hrs, and changes in colour reflectance and surface roughness values were measured by UV light spectrophotometry (Vita Easyshade; VITA Zahnfabrik) and by profilometer device (MitutoyoSurftest SJ-301), respectively. The change of surface roughness was inspected by Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). RESULTS. There was a positive correlation between the ${\Delta}E$ and increase in the surface roughness. Two of the ceramic materials, IPS Empress and Lava Ultimate, were affected significantly by the treatment of the mouthrinse solutions (P<.05). The most affecting solution was Tantum Verde and the most affected material was Lava Ultimate. As expected, the most resistant material to ${\Delta}E$ and chemical corrosion was IPS e max CAD among the materials used. CONCLUSION. This work implied that mouthrinse with lower alcohol content had less deteriorating effect on colour and on the surface morphology of the bioceramic materials.

• The Journal of Korean Academy of Prosthodontics
• /
• v.37 no.4
• /
• pp.416-424
• /
• 1999

Simulation of naturally appearing enamel in fixed prosthodontics could be achieved with all ceramics. The purpose of this study was to investigate the stain resistance of 4 different all ceramics materials (In-ceram, IPS Empress, Celay, Vintage). Forty specimens were prepared using manifacture's instruction and the samples were divided into two groups. The specimens for one group were glazing and those for other group were ground to remove the glazing layer. All specimens were immersed in methylene-blue for 24hours. The color values for each specimen was measured with colorimeter (Mode Tc-6Fx, Tokyo Denshoku Co.) prior to and after immersion in methylene-blue. The following conclusions were drawn from this study. 1 The stain resistance of glazing ceramics was higher than that of unglazing ceramics. 2. The changes of ${\Delta}E^*$\;and\;L^*$ values were revealed in Vintage and unglazing Celay. 3. The changes of $a^*$ values were revealed in unglazing vintage, Celay, In-ceram. 4. The changes of $b^*$ value were revealed in Vintage, IPS Empress and unglazing Celay.

• The Journal of Korean Academy of Prosthodontics
• /
• v.42 no.4
• /
• pp.386-396
• /
• 2004

Statement of problem: It is not clear how to make a stable bonding between zirconia ceramic and resin cement. And the study about surface treatment of zirconia ceramic or bonding resin cement are not enough. Purpose: To measure and compare the shear bond strength of some resin cements on zirconia ceramic after different surface treatments. Material and method: 48 ceramic discs were made of 3 ceramic materials, zirconia ceramics (Zi-Ceram), heat-pressed ceramics (IPS Empress 2) and slip cast alumina ceramics (In-Ceram). According to the surface treatments of ceramic specimens and resin cements, specimens were classified into 6 groups and each group was composed of 8 specimens. For the surface treatment of Zi-Ceram group (test group), sandblasting and diamond bur preparation were applied and Superbond C&B and Panavia F were bonded respectively. For IPS Empress 2 group (control group), Variolink II was bonded after sandblasting, acid etching, silanization and for In-Ceram ALUMINA group (control group), Panavia F was bonded after sandblasting. After storing specimens in distilled water for 24 hours, the shear bond strength was measured by the universal testing machine. Results and conclusion: 1. Zi-Ceram group with Superbond C&B cement showed higher bond strength than with Panavia F cement regardless to the surface treatments (p<0.05). 2. In Zi-Ceram group with Superbond C&B cement, sandblasting treatment group (12.1MPa) showed higher bond strength than diamond bur treatment group (7.7MPa) (p<0.05). In Zi-Ceram group with Panavia F cement, there were no significant differences in the bond strength according to the surface treatments (p>0.05). 3. Zi-Ceram group with sandblasting and Superbond C&B cement (12.1MPa) showed the highest bond strength. The bond strength of this group was not significantly different from In-Ceram ALUMINA group (10.4MPa) (p>0.05) and lower than IPS Empress 2 group (15.9MPa) (p<0.05).

• Journal of Dental Rehabilitation and Applied Science
• /
• v.18 no.3
• /
• pp.205-215
• /
• 2002

This study investigated the compressive fracture strength of Targis ceromer crown by the difference of occlusal thickness on a maxillary first premolar. Control group was a castable IPS-Empress all-ceramic crown with occlusal thickness of 1.5 mm constructed by layered technique. Experimental groups were Targis crowns having different occlusal thicknesses of 1.0 mm, 1.5 mm, 2.0 mm, 2.5 mm, respectively. The classification of Targis group is T10, T15, T20, T25 and T15N (for no-thermocycling and occlusal thickness of 1.5mm). Ten samples were tested per each group. Except occlusal thickness, all dimension of metal die is same with axial inclination of $10^{\circ}$and marginal width 0.8mm chamfer. All crowns were cemented with Panavia F and thermocycled 1,000 times between $5^{\circ}$ and $55^{\circ}$ water bath with 10 sec dwelling time and 10 sec resting time. The compressive fracture strength was measured by universal testing machine. The results were as follows : 1. Fracture strength was increased as the occlusal thickness increased : compressive fracture strength of Group T10, T15, T20, T25 was $66.65{\pm}4.88kgf$, $75.04{\pm}3.01kgf$, $87.07{\pm}7.06kgf$ and $105.03{\pm}10.56kgf$, respectively. 2. When comparing material, Targis crown had higher fracture strength than IPS-Empress crown : the mean compressive strength of group T15 was $75.04{\pm}3.01kgf$ and the value of group Control was $37.66{\pm}4.28kgf$. 3. Fracture strength was decreased by thermocycling : the compressive fracture strength of T15 was $75.04{\pm}3.01kgf$, which is lower than $90.69{\pm}6.88kgf$ of group T15N. 4. The fracture line of crowns began at the loading point and extended along long axis of tooth. IPS-Empress showed adhesive failure pattern whereas Targis had adhesive and cohesive failure. In the SEM view, stress was distributed radially from loading point and the crack line was more prominent on Targis crown.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.2
• /
• pp.184-196
• /
• 2001

The objective of this study was to investigate the influence of resin cements and ceramic etching on shear bond strength of Empress 2 ceramic and observe the change of microstructure of ceramic according to etching time. Sixty-six square ceramic specimens($6{\times}6{\times}1.5mm$) were prepared. 6 specimens were etched with different etching times(0, 10, 20, 30, 40 and 60 seconds) and observed by means of a scanning electron microscope(SEM). Other sixty specimens were divided into 6 groups with 10 specimens in each group. 3 groups were etched with 4% hydrofluoric acid and each groups was bonded with 3 resin cements(Variolink II, Super-Bond C&B, Panavia F). Each specimen was subjected to a shear load in an Instron at a cross-head speed of 0.5mm/min and was observed with SEM after mechanical testing to establish modes of failure. The results were as follows : 1. Within etched groups, Variolink II and Super-Bond C&B exhibited significantly greater bonding strengths than Panavia F(p<0.05) 2. Bond strength of etching groups had three to five times greater than that of no-etching groups. 3. All of no-etching groups showed adhesive failure and etching groups mostly showed mixed failure. And, 20-second etching specimen showed the most distinct lithium disilicate crystal. so it is considered that 20-second etching is optimal time for bonding.