• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.2
• /
• pp.93-98
• /
• 2001

YMnO$_3$ films are excellent gate dielectric materials of ferroelectric random access memories (FRAMs) with MFSFET (metal -ferroelectric-semiconductor field effect transistor) structure because YMnO$_3$ films can be deposited directly on Si substrate and have a relatively low permittivity. Although the patterning of YMnO$_3$ thin films is the requisite for the fabrication of FRAMs, the etch mechanism of YMnO$_3$ thin films has not been reported. In this study, YMnO$_3$thin films were etched with Cl$_2$/Ar gas chemistries in inductively coupled plasma (ICP). The maximum etch rate of YMnO$_3$ film is 285$\AA$/min under Cl$_2$/(Cl$_2$+Ar) of 1.0, RF power of 600 W, dc-bias voltage of -200V, chamber pressure of 15 mTorr and substrate temperature of $25^{\circ}C$. The selectivities of YMnO$_3$ over CeO$_2$ and $Y_2$O$_3$ are 2.85, 1.72, respectively. The selectivities of YMnO$_3$ over PR and Pt are quite low. Chemical reaction in surface of the etched YMnO$_3$ thin films was investigated with X-ray photoelectron spectroscopy (XPS) surface of the selected YMnO$_3$ thin films was investigated with X-ray photoelectron spectroscopy(XPS) and secondary ion mass spectrometry (SIMS). The etch profile was also investigated by scaning electron microscopy(SEM)

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.36D no.4
• /
• pp.56-62
• /
• 1999

In this study, (Ba, Sr)$TiO_3$ thin films were etched with $Cl_2$/Ar gas mixing ratio in an inductively coupled plasma (ICP) by varying the etching parameter such as rf power, dc bias voltage, and chamber pressure. The etch rate was 56 nm/min under $Cl_2$/($Cl_2$+Ar) gas mixing ratio of 0.2, rf power of 600 W, dc bias voltage of 250 V, and chamber pressure of 5 mTorr. At this time, the selectivity of BST to Pt, $SiO_2$ was respectively 0.52, 0.43. The surface reaction of the etched (Ba, Sr)$TiO_3$ thin films was investigated with X-ray photoelectron spectroscopy (XPS). Ba is removed by chemical reaction between Sr and Cl to remove Sr. Ti is removed by chemical reaction such as $TiCl_4$ with ease. The results of secondary ion mass spectrometer (SIMS) analysis compared with the results of XPS analysis and the results were the same.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.6
• /
• pp.449-453
• /
• 2003

Ferroelectric YMnO$_3$ thin films were etched with Ar/Cl$_2$ and CF$_4$/Cl$_2$ inductively coupled plasma (ICP). The maximum etch rate of YMnO$_3$ thin film was 300 $\AA$/min at a Ar/Cl$_2$ gas mixing ratio of 2/8, a RF power of 800 W, a DE bias of 200 V, a chamber pressure of 15 mTorr, and a substrate temperature of 30 $^{\circ}C$. From the X-ray photoelectron spectroscopy (XPS) analysis, yttrium etched by chemical reactions with Cl radicals assisted by Ar ion bombardments in Ar/Cl$_2$ plasma. In CF$_4$/Cl$_2$ plasma, yttrium are remained on the etched surface of YMnO$_3$ and formed of nonvolatile YF$_{x}$ compounds manganese etched effectively by chemical reactions with Cl and F radicals. From the X-ray diffraction (XRD) analysis, the (0004) diffraction peak intensity of the YMnO$_3$ thin film etched in Ar/Cl$_2$ plasma shows lower value than that in CF$_4$/Cl$_2$ plasma. It indicates that the crystallinty of YMnO$_3$ thin film is more easily damaged by the Ar ion bombardment than the changes of stoichiometry due to nonvolatile etch by-products.s.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.3
• /
• pp.83-87
• /
• 2008

This study described the effects of RF power, DC bias voltage, chamber pressure and gas mixing ratio on the etch rates of TiN thin film and selectivity of TiN thin film to $SiO_2$ with $BCl_3$/Ar gas mixture. When the gas mixing ratio was $BCl_3$(20%)/Ar(80%) with other conditions were fixed, the maximum etch rate of TiN thin film was 170.6 nm/min. When the DC bias voltage increased from -50 V to -200 V, the etch rate of TiN thin film increased from 15 nm/min to 452 nm/min. As the RF power increased and chamber pressure decreased, the etch rate of TiN thin film showed an increasing tendency. When the gas mixing ratio was $BCl_3$(20%)/Ar(80%) under others conditions were fixed, the intensity of optical emission spectra from radical or ion such as Ar(750.4 nm), $Cl^+$(481.9 nm) and $Cl^{2+}$(460.8 nm) was highest. The TiN thin film was effectively removed by the chemically assisted physical etching in $BCl_3$/Ar ICP plasma.

• Journal of the Korean Vacuum Society
• /
• v.15 no.6
• /
• pp.630-636
• /
• 2006

Scale down of semiconductor gate pattern will make progress centrally line width into transistor according to the high integration and high density of flash memory semiconductor. Recently, the many researchers are in the process of developing research for using the ONO(oxide-nitride-oxide) technology for the gate pattern give body to line breadth of less 100 nm. Therefore, etch rate and etch profile of the line width detail of less 100 nm affect important factor in a semiconductor process. In case of increasing of the platen power up to 50 W at the ICP etcher, etch rate and PR selectivity showed good result when the platen power of ICP etcher has 100 W. Also, in case of changing of HBr gas flux at the platen power of 100 W, etch rate was decreasing and PR selectivity is increasing. We founded terms that have etch rate 320 nm/min, PR selectivity 3.5:1 and etch slope have vertical in the case of giving the platen power 100 W and HBr gas 35 sccm at the ICP etcher. Also notch was not formed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.74-74
• /
• 2009

Titanium nitride has been used as hardmask for semiconductor process, capacitor of MIM type and diffusion barrier of DRAM, due to it's low resistivity, thermodynamic stability and diffusion coefficient. Characteristics of the TiN film are high intensity and chemical stability. The TiN film also has compatibility with high-k material. This study is an experimental test for better condition of TiN film etching process. The etch rate of TiN film was investigated about etching in $BCl_3/Ar/O_2$ plasma using the inductively coupled plasma (ICP) etching system. The base condition were 4 sccm $BCl_3$ /16 sccm Ar mixed gas and 500 W the RF power, -50 V the DC bias voltage, 10 mTorr the chamber pressure and $40\;^{\circ}C$ the substrate temperature. We added $O_2$ gas to give affect etch rate because $O_2$ reacts with photoresist easily. We had changed $O_2$ gas flow rate from 2 sccm to 8 sccm, the RF power from 500 W to 800 W, the DC bias voltage from -50 V to -200 V, the chamber pressure from 5 mTorr to 20 mTorr and the substrate temperature from $20\;^{\circ}C$ to $80\;^{\circ}C$.

• Journal of the Korean Chemical Society
• /
• v.44 no.3
• /
• pp.200-206
• /
• 2000

The metal impurities in specific regions at near surface of silicon wafer were determined by constant depth etching·lt is possible to etch uniformly over the entire wafer surface by 1$\mu\textrm{m}$ depth with 5 mL of etching solution made up of HF and HNO$_3$ mixed by l:3 volume ratio. The microwave oven was used to evaporate the solution after etching. After spiking, The recoveries of Cu, Ni, Zn, Cr, Mg and K were found to be 99∼105%ted in polysilicon region and could be quantified by 1$\mu\textrm{m}$ depth.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.169-169
• /
• 2011

STT-MRAM (수직자화 자기메모리)는 자화반전 현상을 원리로 구동하는 비휘발성 메모리로 기존의 메모리 장치에 비해 빠른 접근 속도와 높은 저장 밀도를 가지며 영구적인 기록이 가능하다. 이러한 장점들에 더해 적은 소모 전력을 지니므로 기존의 SRAM등의 한계를 극복할 대안으로 각광받고 있으며 차세대 메모리 군의 선두주자로 가장 적합한 후보중 하나이다. STT-MRAM의 건식 식각 방식에 있어 가장 큰 이슈는 소자 구동에 핵심적인 역할을 하는 MTJ(Magnetic Tunnel Junction)의 식각이다. MTJ는 free layer, tunnel barrier, pinned layer 3개의 층으로 구성되어 있으며 양 끝 layer에는 강자성체인 CoFeB가 사용되고 tunnel barrier에는 절연층인 MgO가 사용되고 있다. 이러한 물질들은 기존의 반도체 소자에서는 사용되지 않았던 물질들로 기존 공정에서 사용되던 Cl2 based plasma etching에서는 측벽에 비화발성 반응물과 잔류 Cl2에 의해 부식이 발생하는 문제점이 드러나고 있다. 이러한 문제점을 해결하기 위한 새로운 대안으로 CO/NH3/Ar나 CH4/Ar 같은 새로운 가스 조합을 사용하는 연구가 진행되고 있다. 이러한 연구에 의해 기존의 Cl2 plasma를 이용한 식각에서 나타나는 문제점은 해결이 되었으나 또 다른 문제점들이 보고되고 있다. 본 연구에서는 stack MRAM sample을 사용하여 기존의 사용되는 Cl2/Ar plasma와 대안 gas인 CO/NH3, CH4/Ar plasma에서의 식각을 진행하였으며 실험 조건(gas 비율 변화, Bias power 변화, 식각 시간)에 따른 식각 속도의 변화나 식각 후의 profile에 대하여 관찰하였다. 이에 따라 식각후에 어떠한 차이점이 있는 지를 알아보았으며 CO/NH3나 CH4/Ar plasma에서 식각시 나타나는 문제점에 대하여도 조명해 보았다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.190-194
• /
• 2002

In this study, the etching of Au thin films have been performed in an inductively coupled CF4/Cl2/Ar plasma. The etch properties were measured as the CF4 adds from 0 % to 30 % to the Cl2/(Cl2 + Ar) gas mixing ratio of 0.2. Other parameters were fixed at a rf power of 700 W, a dc bias voltage of 150 V, a chamber pressure of 15 mTorr, and a substrate temperature of $30^{\circ}C$. The highest etch rate of the Au thin film was 370 nm/min at a 10 % additive CF4 into Cl2/(Cl2 + Ar) gas mixing ratio of 0.2. The surface reaction of the etched Au thin films was investigated using x-ray photoelectron spectroscopy (XPS) analysis. From x-ray photoelectron spectroscopy (XPS) analysis, the intensities of Au peaks are changed. There is a chemical reaction between Cl and Au. Au-Cl is hard to remove on the surface because of its high melting point and the etching products can be sputtered by Ar ion bombardment. We obtained the cleaned and steep profile.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.5
• /
• pp.378-384
• /
• 2003

Etching species in CF$_4$/Ar plasma and the behavior of etching rate of Bi$_4$-$_{x}$L$_{x}$rTi$_3$O$_2$ (BLT) films were investigated in inductively coupled plasma (ICP) reactor in terms of etch parameters. The etching rate as functions of CF$_4$ contents showed the maximum 803 $\AA$/min at 20% CF$_4$ addition in CF$_4$/Ar plasma. The increase of RF power and DC bias voltage caused to an increase of etch rate. The variation of relative volume densities for F and he atoms were measured with the optical emission spectroscopy (OES). The chemical states of BLT were investigated with using X-ray photoelectron spectroscopy (XPS). XPS narrow scan analysis shows that La-fluorides remained on the etched surface. The presence of maximum etch rate at CF$_4$(20%)/Ar(80%) may be explained by the concurrence of two etching mechanisms such as physical sputtering and chemical reaction. The roles of he ion bombardment include destruction of metal (Bi, La, Ti)-O bonds as well as assistant for chemical reaction of metals with fluorine atoms.oms.