• Fibers and Polymers
• /
• v.5 no.3
• /
• pp.198-203
• /
• 2004

Composite films were prepared by casting the solution of polyacrylonitrile (PAN) and single wall nanotube (SWNT) in DMF subsequent to sonication. The SWNTs in the films are well dispersed as ropes with 20-30 nm thickness. Moreover, AFM surface image of the composite film displays an interwoven fibrous structure of nanotubes which may give rise to conductive passways and lead to high conductivity. The polarized Raman spectroscopy is an ideal characterization technique for identification and the orientation study of SWNT. The well-defined G-peak intensity at 1580 $cm^{-1}$shows a dependency on the draw ratio under cross-Nicol. The degree of nanotube orientation in the drawn film was measurable from the sine curve obtained by rotating the drawn film on the plane of cross-Nicol of polarized Raman microscope. The threshold loading of SWNT for electrical conductivity in PAN is found to be lower than 1 wt% in the composite film. The electrical conductivity of the SWNT/PAN composite film decreased with increasing of draw ratio due to the collapse of the interwoven fibrous network of the nanotubes with uniaxial orientation.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.48 no.8
• /
• pp.1-4
• /
• 2011

This study was the coorrelation between the electrical properties and the dielectric constant of organic inorganic hybrid type low k SiOC film. SiOC film as low-k films was deposited by the chemical vapor deposition and then annealed at 30 $0{\sim}500^{\circ}C$ to find out the properties of the depending on the temperature and polarity. SiOC film decreased the dielectric constant after annealing process, and the electrical properties were improved at the sample annealed at $400^{\circ}C$. From the XRD patterns, there were two kinds of bonding structures in SiOC film. There was the difference in the bonding structure between the samples annealed under $300^{\circ}C$ and the samples annealed over $400^{\circ}C$. The change was confirmed near $400^{\circ}C$.

• Composites Research
• /
• v.28 no.3
• /
• pp.94-98
• /
• 2015

This paper reports the effects of nickel film interleaves on the interlaminar shear strength(ILSS) of carbon fiber reinforced epoxy composites(CFRPs). A nickel thin film was deposited onto the prepreg by radio frequency(RF) sputtering at room temperature. The ILSS of the nickel film interleaved hybrid composites was increased compared to that of the composites without interleaves. To understand the mechanism of enhancement of the ILSS, the fracture surface of the tested specimens was examined by scanning electron microscopy(SEM). The metal interleaves were acted as a reinforcement for the matrix rich interface and the shear property of their composites improved by enhancing the resistance to matrix cracking.

• 한국가시화정보학회:학술대회논문집
• /
• 2002.04a
• /
• pp.1-7
• /
• 2002

This papers describes the preparation and experimental results of a micro mass detection devices based on cantilever and a diffuser-type micro pump using screen printing thick-film technologies and Si micro-machining. PZT-PCW thick films were prepared by new hybrid method based on the screen printing. By applying these PZT-PCW piezoelectric thick films on actuator, a cantilever for mass detection sensor and a micropump for microfluidic element are successfully fabricated. Resonant frequency and displacement of PZT-PCW thick film actuator in air and in liquid are measured by laser vibrometer system as a function of actuator size. The resonant frequency of PZT-PCW thick film actuator in liquid decreases order of 1/2-1/4 due to damping effect. The sensitivity of cantilever is characterized by Au deposition method which has the mass loading effect such as adsorption of protein. The Sensitivity of PZT-0.12PCW thick film cantilever is proportional to detecting area.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.294-294
• /
• 2014

Developing magnetic thin films with desirable physical properties is a key step to promote research in spintronics. Organic-based magnetic material is a relatively new kind of materials which has magnetic properties in a molecular and microscopic level. These materials have been constructed by the coordination between 3d transition metal and organic materials producing long-range magnetic orders with a relatively high transition temperature. However, these materials were mostly synthesized as a form of powder, which is difficult to study for their physical properties as well as apply for electronic/spintronic devices. In this study, we have employed physical vapor deposition (PVD) to develop a new organic-based hybrid magnetic film that is achieved by the coordination of Fe and tetracyanoquinodimethane (TCNQ). The IR spectra of the grown film show modified CN vibration modes in TCNQ, which suggest a strong bonding between Fe and TCNQ. The thin film has both ferromagnetic and semiconducting behaviors, which is suitable for molecular spintronic applications. The high resolution photoemission (HRPES) spectra also show shift of 1s peak point of nitrogen and the carbon 1s peaks display traces of charge transfer from Fe to TCNQ as well as shake-up features, which suggest strong bonding and anti-bonding nature of coordination between Fe and TCNQ.

• Progress in Superconductivity and Cryogenics
• /
• v.16 no.3
• /
• pp.7-9
• /
• 2014

Single-crystal like $MgB_2$ thin film was grown on (000l) $Al_2O_3$ substrate by using hybrid physical-chemical vapor deposition (HPCVD) system. Single crystal properties were studied by X-ray diffraction (XRD) and the full width at half maximum (FWHM) of the (0001) $MgB_2$ peak is $15^{\circ}$, which is very close to that has been reported for $MgB_2$ single-crystal. It indicates that the crystalline quality of thin film is good. Temperature dependence on resistivity was investigated by physical property measurement system (PPMS) in various applied fields from 0 to 9 T. The upper critical field ($H_{c2}$) and irreversibility field ($H_{irr}$) were determined from PPMS data, and the estimated values are comparable with that of $MgB_2$ single-crystals. The thin film shows a high critical temperature ($T_c$) of 40.4 K with a sharp superconducting transition width of 0.2 K, and a high residual resistivity ratio (RRR=21), it reflects that $MgB_2$ thin film has a pure phase structure.

• 한국생물공학회:학술대회논문집
• /
• 2001.11a
• /
• pp.823-826
• /
• 2001

In the initial process of photosynthesis, a biological electron transfer system, photoelectric conversion occurs and then long-range electron transfer takes place very efficiently in one direction through the biomolecules. The metal/insulator/metal structured device consisting of GFP, viologen, cytochrome c hetero-thin film was presented based on the biomimesis. GFP, viologen, and cytochrome c was used as an electron sensitizer, a mediator, and an electron acceptor. Cytochrome c molecules and viologen molecules were deposited by Langmuir-Blodgett (LB) technique, and GFP molecules were adsorbed by self-assembly method (SAM). Surface morphology of hetero-thin film was analyzed by scanning tunneling microscopy (STM). Local photoswitching effects of a proposed photodiode were verified by current-voltage measurements using hybrid STM/I-V measurement system.

• Bulletin of the Korean Chemical Society
• /
• v.27 no.8
• /
• pp.1159-1163
• /
• 2006

Aluminum nanotube has been fabricated by a physical vapor deposition/atmospheric pressure injection using an anodic porous alumina film as a template. The pore external-, and inside diameters and the length of the aluminum nanotubes fabricated by this method are 60 nm, 35 nm and 2 $\mu$m, respectively. The structure of the fabricated aluminum nanotubes was examined by a kind of chemical treatment as extraction of copper on the cross-sectional area of these aluminum tubes in a mixed solution of $CuCl_2$ and HCl by difference of ionization tendency between aluminum and copper. The composition of the aluminum nanotube was identified by the two dimensional Hybrid Plasma Equipment Model (HPEM) employing the inductively coupled plasma.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2002.08a
• /
• pp.905-909
• /
• 2002

Characteristics of reflective LCDs, which have gained a lot of notice in recent years, rely largely on optical design of circular polarizers and the quarter-wave plates, as a component. Important design includes wavelength dispersion, viewing angle, uniformity of display and matching of refractive index. Our work has contributed to improving performance of reflective LCDs by enhancing the characteristics of polymer film using stretching and optical lamination technologies. To design that offers higher contrast and wider viewing angle, we have discovered that it is necessary to control viewing angle variation of the polarizing axis in order to compensate for the viewing angle of the polarizing film as well as the optical anisotropic properties of liquid crystal. Applying this technology to circular polarizers used for reflective LCDs enables design of wide viewing angle circular polarizers. In order to realize higher contrast for reflective LCDs, it is also necessary to design other optical materials including polarizing films. For design of hybrid optical film, it is particularly necessary to reduce surface reflection and interface reflection. This paper also reports our findings concerning this topic.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.177-181
• /
• 2009

Compositional gradient CrNx coatings were fabricated using arc ion plating in Ar/$N_2$ gaseous mixture by gradually increasing $N_2$ flux rate from 0 to 120 SCCM. The effect of negative substrate bias on the film microstructure and mechanical properties were systematically investigated with XRD, GDOES, and SEM. The results show that substrate bias has an important influence on film growth and microstructure of gradient CrNx coatings. The coatings mainly crystallized in the mixture of hexagonal $Cr_{2}N$ and fcc CrN phases. By increasing substrate bias, film microstructure evolved from an apparent columnar structure to an equiaxed one. With increasing substrate bias, deposition rate first increased, and then decreased. The maximum of deposition rate was 15 nm/min obtained at a bias of -50V.