• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.328-331
• /
• 2004

Hot filament 플라즈마 화학기상 증착법(HFPECVD)를 사용하여 질산화철의 농도에 따른 탄소나노튜브의 성장 특성을 관찰하기 위해 실험을 진행하였다. 암모니아($NH_3$)를 희석가스로 사용하였고, 아세틸렌($C_2H_2$)를 탄소 원료가스로 각각 사용하였다. 암모니아 가스 플라즈마를 사용하여 전처리 된 질산화철 촉매층의 SEM(Scanning Electron Microscopy) 이미지를 관찰하여 본 결과, 나노 사이즈의 촉매 그레인(grain)을 발견할 수 있었다. 그리고 탄소 나노튜브의 직경과 성장 밀도 또한 전처리 된 촉매 층에 따라 다른 양상을 보였다. TEM(Transmission Electron Microscopy)를 사용하여 탄소나노튜브를 관찰한 결과 bamboo 구조를 한 다중벽 탄소 나노튜브(MWCNT)를 관찰할 수 있었다.

• Journal of the Korean Vacuum Society
• /
• v.16 no.3
• /
• pp.187-191
• /
• 2007

In this paper, the catalyst layer is deposited on silicon substrate using magnetron sputtering system and carbon nanotubes(CNTs) were grown in $NH_3\;and\; C_2H_2$ gas by hot-filament plasma enhanced chemical vapor deposition (HFPECVD) system. A growth temperature of carbon nanotubes was changed from $350^{\circ}C\;to\;650^{\circ}C\;by\;100^{\circ}C$. We observed the shape of CNTs by a field-emission scanning electron microscope(FE-SEM) measurement and analyzed the surface characteristic of CNTs layer by contact angle measurement. That is, the growth temperature of CNTs is the important factor leads to the variation of the properties.

• Journal of the Korean Vacuum Society
• /
• v.16 no.2
• /
• pp.128-133
• /
• 2007

In this study, we observed the shapes of CNTs formed with the thinckness of catalyst. Catalyst layer was grown by magnetron sputtering method and the thickness of Ni catalyst is the range from 20 to 80 nm. Also, the synthesis of CNT with Ni catalyst thickness was grown by hot-filament PECVD method. And, we investigated the composition of CNTs by using EDS measurement, also observed the shapes of CNTs by using HRTEM and FESEM measurements. In the result, through the TEM analysis, we observed the empty inside of CNTs and the multiwall CNTs, also confirmed the tip of CNT containing Ni. The composition of CNTs are consisted of an element of C, Ti, and Ni. As you shown the growth shapes of CNTs, the pretreatment of the catalyst before te growth of CNTs changed the particle size of the catalysts and grown the CNTs of the different shapes. Consequently, the best vertically alined and well-arranged CNTs exhibited from the substrate deposited at the catalyst thickness of 40 nm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.779-782
• /
• 2003

Hot filament 플라즈마 화학기상 증착법 (HFPECVD)를 사용하여 전처리 조건에 따른 탄소나노튜브의 성장 특성을 관찰하였다. 암모니아 ($NH_3$)를 희석가스로 사용하였고, 아세틸렌 ($C_2H_2$)를 탄소 원료가스로 각각 사용하였다. 암모니아 가스 플라즈마를 사용하여 전처리 된 니켈 촉매 층의 SEM (Scanning Electron Microscopy) 이미지를 관찰하여 본 결과, 나노 사이즈의 촉매 그레인(grain)을 발견할 수 있었다. 그리고 탄소 나노튜브의 직경과 성장 밀도 또한 전처리 된 촉매 층에 따라 다른 양상을 보였다. TEM (Transmission Electron Microscopy)를 사용하여 탄소나노튜브를 관찰한 결과 공동구조(hollow)를 한 다중벽 탄소 나노튜브(MWCNT)를 관찰할 수 있었다. 성장된 나노튜브는 끝에 금속팁을 가지고 있으며, 나노튜브의 팁은 촉매로 사용한 것과 같은 물질로 구성되어 있었다. Raman spectroscopy를 사용하여 측정된 B-밴드와 G-밴드의 피크들은 각각 $1360cm^{-1}$와 $1598cm^{-1}$ 부근에서 나타났으며, 전처리 조건을 달리하여 성장시킨 탄소나노튜브 필름에서 이들 두 피크의 위치는 이동하지 않았고, 두 피크의 강도 비율 ($I_G/I_D$)은 전처리 조건에 따라 변하였다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.8
• /
• pp.713-719
• /
• 2002

In this study, the vertically well-aligned CNTs were synthesized by DC bias-assisted inductively coupled plasma hot-filament chemical vapor deposition (ICPHFCVD) using radio-frequence plasma of high density and that CNTs were vertically grown on Ni(300 )/Cr(200 )-deposited glass substrates at 58$0^{\circ}C$. This system(ICPHFCVD) added to tungsten filament in order to get thermal decompound and DC bias in order to vertically grow to general Inductively Coupled Plasma CVD. The grown CNTs by ICPHFCVD were developed to higher graphitization and fewer field emission properties than those by general ICPCVD. In this system, DC bias was effect of vortical alignment to growing CNTs. The measured turn-on fields of field emission property by general ICPCVD and DC bias-assisted ICPHFCVD were 5 V/${\mu}{\textrm}{m}$ and 3 V/${\mu}{\textrm}{m}$, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.632-635
• /
• 2001

Microcrystalline Si films have been deposited by using five W-wire filaments of 0.5 mm diameter for hot-wire chemical vapor deposition (HWCVD). We compared the HWCVD grown films with the film exposed to transformer couple plasma system for the modification of seed layer. W-wire filament temperature was maintained below 1600$^{\circ}C$ to avoid metal contamination by thermal evaporation at the filament. Deposition conditions were varied with H$_2$dilution ratio, with and without plasma treatment. From the Raman spectra analysis, we observed that the film crystallization was strongly influenced by the H$_2$dilution ratio and weakly depended on the distance between the wire and a substrate. We were able to achieve the crystalline volume fraction of about 70% with an SiH$_4$/H$_2$ratio of 1.3%, a wire temperature of 1514$^{\circ}C$, a substrate separation distance of 4cm, and a chamber pressure of 38 mTorr. We investigated the influence of ${\mu}$c-Si film properties by using a plasma treatment. This article also deals with the influence of the H$_2$dilution ratio in crystallization modification.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.293-293
• /
• 2010

Carbon nanotubes (CNTs) have attracted considerable attention as possible routes to device miniaturization due to their excellent mechanical, thermal, and electronic properties. These properties show great potential for devices such as field emission displays, CNT based transistors, and bio-sensors. The metals such as nickel, cobalt, gold, iron, platinum, and palladium are used as the catalysts for the CNT growth. In this study, diamond-like carbon (DLC) was used for CNT growth as a nonmetallic catalyst layer. DLC films were deposited by a radio frequency (RF) plasma-enhanced chemical vapor deposition (RF-PECVD) method with a mixture of methane and hydrogen gases. CNTs were synthesized by a hot filament plasma-enhanced chemical vapor deposition (HF-PECVD) method with ammonia (NH3) as a pretreatment gas and acetylene (C2H2) as a carbon source gas. The grown CNTs and the pretreated DLC filmswere observed using field emission scanning electron microscopy (FE-SEM) measurement, and the structure of the grown CNTs was analyzed by high resolution transmission scanning electron microscopy (HR-TEM). Also, using energy dispersive spectroscopy (EDS) measurement, we confirmed that only the carbon component remained on the substrate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.239-239
• /
• 2009

As we note the electric properties of carbon nanotube, we need to generate carbon nanotubes vertically. Generally, metal catalysts are used to synthesis carbon nanotubes. But through using DLC, dense patricles could be gotten easily. Compare to the case of using metal catalysts, the case of using DLC can conduct vertical grwoth of CNTs easily. In this paper, we changed growth temperature (550, 650, $7500^{\circ}C$) and growth time (3, 6, 9 min) in order to confirm synthesize vertical growth of CNTs on substrates.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.168-168
• /
• 2016

BDD(Boron Doped Diamond) 전극은 전위창이 넓고, 다른 불용성 전극에 비해 산소발생과전압이 높아 물을 전기화학적인 방법으로 처리하는 영역에 있어 매우 효과적일 뿐만 아니라, 전통적인 불용성 전극에 비해 전극 표면에서 수산화 라디칼(-OH)과 오존(O3)의 발생량이 월등히 높아 수처리용 전극으로서의 유용성이 매우 높다. 따라서 BDD 전극을 수처리용 전극에 사용하는 경우 수산화 라디칼(-OH)과 오존(O3), 과산화수소(H2O2) 등과 같은 산화제의 생성은 물론이고, 염소(Cl2)가 포함되어 있는 전해액에서는 차아염소산(HOCl)이나 차아염소산이온(OCl-)과 같은 강력한 산화제가 발생되어 전기화학적 폐수처리, 전기화학적 정수처리, 선박평형수 처리 등의 분야에 널리 활용될 수 있다. 본 연구에서는 상온 및 상압에서 운전이 가능하고 난분해성 오염물질 제거 효과가 뛰어난 전기화학적 고도산화공정(Electrochemical Advanced Oxidation Process, EAOP)에 적합한 대면적의 BDD 전극을 개발하고 자 하였다. 이러한 BDD 전극의 성막 방법으로는 필라멘트 가열 CVD, 마이크로파 플라즈마 CVD, DC 플라즈마 CVD 등이 널리 알려져 있는데 최근에는 설비의 투자비가 비교적 저렴하고, 대면적의 기판처리가 용의한 필라멘트 가열 화학기상증착법(Hot Filament Chemical Vapor Deposition, HFCVD)이 상업적으로 각광을 받고 있다. 따라서 본 연구에서는 HFCVD 방법을 이용하여 반응 가스의 투입비율, BDD 박막의 두께, 기판의 재질 등에 따른 여러 가지 성막 조건들을 검토하여 $100{\times}100mm$ 이상의 대면적 BDD 전극을 개발하였다. Fig. 1은 본 연구를 통하여 얻어진 BDD 전극의 표면 및 단면 SEM이다.

• Journal of the Korean Ceramic Society
• /
• v.39 no.2
• /
• pp.171-177
• /
• 2002

In this study, the vertical aligned carbon nanotubes was synthesized by DC bias-assisted Inductively Coupled Plasma Hot-Filament Chemical Vapor Deposition (ICPHFCVD). The substrate used CNTs growth was Ni(300 ${\AA}$)/Cr(200 ${\AA}$)-deposited one on glass by RF magnetron sputtering. R-F, DC bias and filament power during the growth process were 150 W, 80 W, 7∼8 A, respectively. The grown CNTs showed hollow structure and multi-wall CNTs. The top of grown CNT was found to Ni-tip that the CNT end showed to metaltip. The graphitization and field emission properties of grown was better than grown CNTs by ICPCVD. The turn-on voltage of CNT grown by DC bias-assisted ICPHFCVD showed about 3 V/${\mu}m$.