• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1104-1105
• /
• 2006

Several boride sintered bodies such as $TiB_2$, $ZrB_2$, and $SiB_6$ were previously reported. In the present study, the sinterability and physical properties of chromium boride $(CrB_2)$ containing chromium carbide $(Cr_3C_2)$ sintered bodies were investigated in order to determine its new advanced material. The samples were sintered at desired temperature for 1 hour in vacuum under a pressure by hot pressing. The relative density of sintered bodies was measured by Archimedes' method. The relative densities of $CrB_2$ addition of 0, 5, 10, 15 and 20 mass% $Cr_3C_2$ composites were 92 to 95%. The Vickers hardness of the $CrB_2$ with 10 and 15 mass% $Cr_3C_2$ composites were about 14 and 15 GPa at room temperature, respectively. The Vickers hardness at high temperature of the $CrB_2$ addition of 10 mass% $Cr_3C_2$ composite decreased with increasing measurement temperature. The Vickers hardness at 1273 K of the sample was 6 GPa. The Vickers hardness of $CrB_2$ addition of $Cr_3C_2$ composites was higher than monolithic $CrB_2$ sintered body. The powder X-ray diffraction analysis detected CrB and $B_4C$ phases in $CrB_2$ containing $Cr_3C_2$ composites.

• Journal of Powder Materials
• /
• v.19 no.3
• /
• pp.215-219
• /
• 2012

An attempt was made to evaluate creep reliability of two commercial Ni-based superalloys by using ultrasonic wave. The materials include fine-grained PM alloy fabricated by mechanical alloying and subsequent hot isostatic pressing, and IN738LC cast alloy with a grain size of a few cm. Microstructural parameters (fraction of creep cavity and size of ${\gamma}^{\prime}$ precipitates) and ultrasonic parameters (velocity, attenuation) were measured to try to find relationships between them. Ultrasonic velocity decreased with creep cavity formation in PM alloy. On the other hand, no distinct changing trend of ultrasonic velocity was observed for IN738LC alloy. Ultrasonic attenuation was found to have a linear correlation with the size of ${\gamma}^{\prime}$ precipitates and was suggested as a potential parameter for monitoring creep reliability of IN738LC alloy.

• Journal of Powder Materials
• /
• v.25 no.4
• /
• pp.340-345
• /
• 2018

Additive manufacturing by electron beam melting is an affordable process for fabricating near net shaped parts of titanium and its alloys. 3D additive-manufactured parts have various kinds of voids, lack of fusion, etc., and they may affect crack initiation and propagation. Post process is necessary to eliminate or minimize these defects. Hot isostatic pressing (HIP) is the main method, which is expensive. The objective of this paper is to achieve an optimum and simple post heat treatment process without the HIP process. Various post heat treatments are conducted for the 3D-printed Ti-6Al-4V specimen below and above the beta transus temperature ($996^{\circ}C$). The as-fabricated EBM Ti-6Al-4V alloy has an ${\alpha}^{\prime}$-martensite structure and transforms into the ${\alpha}+{\beta}$ duplex phase during the post heat treatment. The fatigue strength of the as-fabricated specimen is 400 MPa. The post heat treatment at $1000^{\circ}C/30min/AC$ increases the fatigue strength to 420 MPa. By post heat treatment, the interior pore size and the pore volume fraction are reduced and this can increase the fatigue limit.

• Composites Research
• /
• v.18 no.3
• /
• pp.21-30
• /
• 2005

Vacuum hot pressing has been used for the development of titanium metal matrix composites using foil-fiber-foil method. Heterogeneous microstructures prior to and following consolidation have been quantified, and the relations to densification behavior investigated. As shown by the results, dramatic variations of the microstructures including equiaxed $\alpha$, transformed $\beta$ and $ Widmanst\ddot{a}tten$ $\alpha$ are obtained during the process according to the fiber distributions. The dependence of microstructures on the consolidation then has been explained in terms of the change in mechanisms such as grain growth and recrystallization that occur with changing levels of inhomogeneity of deformation. Further, micro-mechanics based constitutive model enabling the evolution of density over time together with the evolutions of microstructure to be predicted has been developed. The mode developed is then implemented into finite element scheme so that practical process simulation has been carried out.

• Nuclear Engineering and Technology
• /
• v.49 no.1
• /
• pp.178-188
• /
• 2017

To study the effects of zirconium (Zr) addition on the microstructure, hardness and the tensile properties of oxide dispersion strengthened (ODS) ferritic-martensitic steels, two kinds of 9Cr-ODS ferritic-martensitic steels with nominal compositions (wt.%) of $Fe-9Cr-2W-0.3Y_2O_3$ and $Fe-9Cr-2W-0.3Zr-0.3Y_2O_3$ were fabricated by the mechanical alloying (MA) of premixed powders and then consolidated by hot isostatic pressing (HIP) techniques. The experimental results showed that the average grain size decreases with Zr addition. The trigonal ${\delta}$-phase $Y_4Zr_3O_{12}$ oxides and body-centered cubic $Y_2O_3$ oxides are formed in the 9Cr-Zr-ODS steel and 9Cr non-Zr ODS steel, respectively, and the average size of $Y_4Zr_3O_{12}$ particles is much smaller than that of $Y_2O_3$. The dispersion morphology of the oxide particles in 9Cr-Zr-ODS steel is significantly improved and the number density is $1.1{\times}10^{23}/m^3$ with Zr addition. The 9Cr-Zr-ODS steel shows much higher tensile ductility, ultimate tensile strength and Vickers hardness at the same time.

• Journal of the Korean Ceramic Society
• /
• v.49 no.6
• /
• pp.549-555
• /
• 2012

Silicon carbide(SiC) exhibits many unique properties, such as high strength, corrosion resistance, and high temperature stability. In this study, a SiC-fiber web was prepared from polycarbosilane(PCS) solution by employing the electrospinning process. Then, the SiC-fiber web was pyrolyzed at $1800^{\circ}C$ in argon atmosphere after it was subjected to a thermal curing. The SiC-fiber web (ground web)/phenolic resin (resol) composite was fabricated by hot pressing after mixing the SiC-fiber web and the phenolic resin. The SiC-fiber web composition was controlled by changing the fraction of filler (filler/binder = 9:1, 8:2, 7:3, 6:4, 5:5). Thermal conductivity measurement indicates that at the filler content of 60%, the thermal conductivity was highest, at 6.6 W/mK, due to the resulting structure formed by the filler and binder being closed-packed. Finally, the microstructure of the composites of SiC-fiber web/resin was investigated by FE-SEM, EDS, and XRD.

• Journal of the Korean Ceramic Society
• /
• v.51 no.6
• /
• pp.554-559
• /
• 2014

Gadolinium zirconate, $Gd_2Zr_2O_7$, is one of the most promising candidates for replacing yttira-stabilized zirconia (YSZ) in thermal barrier coating (TBC) applications due to its low thermal conductivity and chemical stability at high temperature. In this study, rare-earth zirconate ceramics in the $GdO_{1.5}-ZrO_2$ system with reduced gadolinia contents were fabricated via solid-state reaction as well as hot-pressing at $1800^{\circ}C$. The phase formation, microstructure, and thermo-physical properties of these oxides were examined. The potential application of $GdO_{1.5}-ZrO_2$ ceramics for TBC was also discussed.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.60 no.11
• /
• pp.2083-2087
• /
• 2011

The SiC-$ZrB_2$ composites were produced by subjecting a 40:60 vol.% mixture of zirconium diboride($ZrB_2$) powder and ${\beta}$-silicon carbide (SiC) matrix to spark plasma sintering(SPS). Sintering was carried out for 60sec at $1400^{\circ}C$ (designation as TP145 and TP146), $1500^{\circ}C$(designation as TP155 and TP156) and uniaxial pressure 50MPa, 60MP under argon atmosphere. The physical, electrical, and mechanical properties of the SiC-$ZrB_2$ composites were examined. The relative density of TP145, TP146, TP155 and TP156 were 94.75%, 94.13%, 97.88% and 95.80%, respectively. Reactions between ${\beeta}$-SiC and $ZrB_2$ were not observed via x-ray diffraction (hereafter, XRD) analysis. The flexural strength, 306.23MPa of TP156 was higher than that, 279.42MPa of TP146 at room temperature, but lower than that, 392.30MPa of TP155. The properties of a SiC-$ZrB_2$ composites through SPS under argon atmosphere were positive temperature coefficient resistance (hereafter, PTCR) in the range from $25^{\circ}C$ to $500^{\circ}C$. The electrical resistivities of TP145, TP146, TP155 and TP156 were $6.75{\times}10^{-4}$, $7.22{\times}10^{-4}$, $6.17{\times}10^{-4}$ and $6.71{\times}10^{-4}{\Omega}{\cdot}cm$ at $25^{\circ}C$, respectively. The densification of a SiC-$ZrB_2$ composite through hot pressing depend on the sintering temperature and pressure. However, it is convinced that the densification of a SiC-$ZrB_2$ composite do not depend on sintering pressure under SPS.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.31 no.6
• /
• pp.392-397
• /
• 2018

In this paper, the ZnS nanoparticles were synthesized according to the process conditions of hydrothermal synthesis. When the molar ratio of Zn to S was 1:1.2, it was confirmed that it had a cubic single phase and a high crystal phase. After the molar ratio is fixed, hydrothermal synthesis was conducted at $180^{\circ}C$ for 24, 36, 72 and 96 h in order to confirm the structural change with the change of hydrothermal synthesis times. As the hydrothermal synthesis times increased, the particle size increased. The hydrothermal synthesized particle size for 72 h was considered to be suitable for sintering. The ZnS ceramic had a density of 99.7% and an excellent transmittance of ~70% in the long-wavelength region.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1303-1304
• /
• 2007

The composites were fabricated, respectively, using 61[vol.%]SiC-39[vol.%]$TiB_2$ and using 61[vol.%]SiC-39[vol.%]$ZrB_2$ powders with the liquid forming additives of 12[wt%] $Al_{2}O_{3}+Y_{2}O_{3}$ by hot pressing annealing at $1650[^{\circ}C]$ for 4 hours. Reactions between SiC and transition metal $TiB_2$, $ZrB_2$ were not observed in this microstructure. ${\beta}{\rightarrow}{\alpha}$-SiC phase transformation was occurred on the SiC-$TiB_2$ and SiC-$ZrB_2$ composite. The relative density, the flexural strength and Young's modulus showed the highest value of 98.57[%], 226.06[Mpa] and 86.38[Gpa] in SiC-$ZrB_2$ composite at room temperature respectively. The electrical resistivity showed the lowest value of $7.96{\times}10^{-4}[{\Omega}{\cdot}cm]$ for SiC-$ZrB_2$ composite at $25[^{\circ}C]$. The electrical resistivity of the SiC-$TiB_2$ and SiC-$ZrB_2$ composite was all positive temperature coefficient resistance (PTCR) in the temperature ranges from $25[^{\circ}C]$ to $700[^{\circ}C]$. The resistance temperature coefficient of composite showed the value of $6.88{\times}10^{-3}/[^{\circ}C]$ and $3.57{\times}10^{-3}/[^{\circ}C]$ for SiC-$ZrB_2$ and SiC-$TiB_2$ composite in the temperature ranges from $25[^{\circ}C]$ to $700[^{\circ}C]$.