The effects of shear speed and tip height on the high speed shear test of Sn-3.0wt.%Ag-0.5wt.%Cu ball joints were investigated. Solder balls of $450{\mu}m$ in diameter were reflowed at $245^{\circ}C$ on a FR4 PCB (Printed Circuit Board) in order to obtain a sample for the high-speed shear test. The UBM was comprised of Cu/Ni/Au, and the shear speed and tip height varied from 0.5 to 3.0 m/s, and from 10 to $135{\mu}m$, respectively. According to the experimental results, faster shear speed enhanced the shear strength of the solder joints, regardless of the tip height. The fraction of ductile (solder) fracture decreased when the shearing speed was raised from 0.5 to 3.0 m/s. With an increasing tip height from 10 to 50 and $135{\mu}m$, the fracture mode changed from pad lift to mixed (ductile and brittle) and ductile fracture, respectively, while the shearing energy also increased in the same order. The shear energy had a proportional relationship with the fraction of the solder fracture.

• International Journal of Korean Welding Society
• /
• v.5 no.1
• /
• pp.15-28
• /
• 2005

The ball shear test was investigated in terms of the effects of test parameters, i.e., shear height and shear speed, with an experimental and non-linear finite element analysis for evaluating the solder joint integrity of area array packages. Two representative Pb-free solder compositions were examined in this work: Sn-3.5Ag-0.75Cu and In-48Sn. The substrate was a common SMD type with solder bond pad openings of 460 $\mu$m in diameter. The microstructural investigations were carried out using SEM, and the IMCs were identified with EDS. Shear tests were conducted with the two varying test parameters. It could be observed that increasing shear height, at fixed shear speed, has the effect of decreasing shear force for both Sn-3.5Ag-0.75Cu and In-48Sn solder joints, while the shear force increased with increasing shear speed at fixed shear height. Too high shear height could cause some undesirable effects on the test results such as unexpected high standard deviation values or shear tip sliding from the solder ball. The low shear height conditions were favorable for screening the type of brittle interfacial fractures or the degraded layers in the interfaces. The shear speed conditions were discussed with the stress analyses of the solder ball, and we cannot find any conspicuous finding which is related to optimum shear speed from the stress analyses.

• Korean Journal of Metals and Materials
• /
• v.49 no.8
• /
• pp.635-641
• /
• 2011

The effect of high shear speed on shear force, shear energy and fracture surface was investigated for the solder joint of a $Sn-_{3.0}Ag-_{0.5}Cu$ ball. For both ENIG and OSP pads, the shear force increased with an increase in shearing speed to 0.3 m/s. However, for an ENEPIG pad, the shear force increased with an increase in shear speed to 0.6 m/s and kept almost constant afterward. The shear energy decreased with an increase in shearing speed for ENIG and OSP pads. For the ENEPIG pad, however, the shear energy almost remained constant in a shearing speed range 0.3-3.0 m/s. The fracture mode analysis revealed that the amount of brittle fracture for the ENIG and the OSP pads increased with shearing speed, and a complete brittle fracture appeared at 1.0 m/s for ENIG and 2.0 m/s for OSP. However, the ENEPIG pad showed only a ductile fracture until 0.25 m/s, and a full brittle fracture didn't occur up to 3.0 m/s. The fracture mode matched well with the shear energy. The results from the high speed shear test of SAC305 were similar to those of SAC105.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.18 no.5
• /
• pp.449-454
• /
• 2009

This paper presents an experimental study on the failure characteristics of SnAgCu lead-free solder balls. To estimate the effect of Ag, three types of SnAgCu balls are first prepared by varying the weight percent of Ag(1.0, 3.0, 4.0 wt%) and then analyzed by reliability tests such as thermal shock, high speed ball shear, and drop tests. Thermal shock test reveals that the higher the weight percent of Ag is, the longer the fatigue lift becomes. To the contrary, high speed ball-shear test and drop test show that the shear strength and the fracture toughness of solder balls are inversely proportional to the weight percent of Ag, respectively, Reasons for these observations will be further investigated In the future work.

• Journal of the Microelectronics and Packaging Society
• /
• v.15 no.4
• /
• pp.65-70
• /
• 2008

The mechanical shear strength of BGA(Ball Grid Array) solder joints under high impact loading was investigated. The Sn-37Pb solder balls with a diameter of $500{\mu}m$ were placed on the pads of FR-4 substrates with ENIG(Electroless Nickel Immersion Gold) surface treatment and reflowed. For the High Temperature Storage(HTS) test, the samples were aged a constant testing temperature of $120^{\circ}C$ for up to 250h. After the HTS test, high speed shear tests with various shear speed of 0.01, 0.1, 1, 3 m/s were conducted. $Ni_3Sn_4$ intermetallic compound(IMC) layer was observed at the solder/Ni-P interface and thickness of IMC was increased with aging process. The shear strength increased with increasing shear speed. The fracture surfaces of solder joints showed various fracture modes dependent on shear speed and aging time. Fracture mode was changed from ductile fracture to brittle fracture with increasing shear speed.

• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.1
• /
• pp.35-39
• /
• 2011

Shearing characteristics of Sn-3.0wt%Ag-0.5wt%Cu ball for standardization of high speed shear test were investigated. The solder ball of 450 ${\mu}m$ in diameter was reflowed at $245^{\circ}C$ on FR4 PCB (Printed Circuit Board) to prepare a sample for the high-speed shear test. The metal pads on the PCB were OSP (Organic Solderability Preservative, Cu pad) and ENIG (Electroless Nickel/Immersion Gold, i.e CulNi/Au). Shearing speed was varied from 0.5 to 3.0 m/s, and tip height from 10 to 135 ${\mu}m$. As experimental results, for the OSP pad, a ductile fracture increased with tip height, and it decreased with shearing speed. In the case of ENIG pad, the ductile fracture increased with the tip height. The tip height of 10 ${\mu}m$ (2% of solder ball diameter) was unsuitable since the fracture mode was mostly pad lift. Shear energy increased with increasing shearing tip height from 10 to 135 ${\mu}m$ for both of OSP and ENIG pads.

• Korean Journal of Metals and Materials
• /
• v.49 no.3
• /
• pp.237-242
• /
• 2011

The effect of shearing speed on the shear force and energy of Sn-0Ag-0.5Cu solder ball was investigated. Various UBM (under bump metallurgy)'s on Cu pads were used such as ENEPIG (Electroless Nickel, Electroless Palladium, Immersion Gold; Ni/Pd/Au), ENIG (Electroless Nickel, Immersion Gold; Ni/Au), OSP (Organic Solderability Preservative). To fabricate a shear test specimen, a solder ball, $300{\mu}m$ in diameter, was soldered on a pad of FR4 PCB (printed circuit board) by a reflow soldering machine at $245^{\circ}C$. The solder bump on the PCB was shear tested by changing the shearing speed from 0.01 m/s to 3.0 m/s. As experimental results, the shear force increased with a shearing speed of up to 0.6 m/s for the ENIG and the OSP pads, and up to 0 m/s for the ENEPIG pad. The shear energy increased with a shearing speed up to 0.3 m/s for the ENIG and the OSP pads, and up to 0.6 m/s for the ENEPIG pad. With a high shear speed of over 0 m/s, the ENEPIG showed a higher shear force and energy than those of the ENIG and OSP. The fracture surfaces of the shear tested specimens were analyzed, and the fracture modes were found to have closer relationship with the shear energy than the shear force.

• Journal of the Korean Society for Precision Engineering
• /
• v.28 no.6
• /
• pp.745-750
• /
• 2011

In a hope to better understand the flow and convective heat transfer characteristics inside a ball bearing, air flow between the rolling elements and raceways at high speed bearing rotation is numerically investigated using a simplified inner geometry of bearing and a CFD technique. Flow simulation results reveal the pressure distribution of airflow and the shear stress distribution on the ball surface, of which nonuniformity becomes significant with the increasing rotational speed. Also, the local point of maximum shear stress coincides with the stagnation flow area on the surface of rolling elements. A complex pattern of three-dimensional vortex structures is found in the air flow due to the relative motion of bearing elements and three different types of vortex pairs exist around the rotating and orbiting rolling elements.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.1
• /
• pp.154-162
• /
• 1996

Ball screws are commonly used in linear motion feeding systems of various machine tools and automated systems. They are known to have relatively little backlash, high precision and efficiency compared to ordinary lead screws. Furthermore, the effectiveness of ball screw has made it the preferred choice of many newly developed high speed precision feeding units. The motivation of this work is to establish the groove edsigh basis of ball screws for the reduction of contact fatigue failure. In most instances, fatigue failure between ball and shaft groove is due to excessive contact pressure. Especially, the excessive load is causative of plastic flow below the contact surface, which can contribute to surface failure. But, in spite of small load, if groove conformity rate is large, contact pressure is increased and internal shear stress reach the yield value of the material. In such a point, the authors deal with design procedure for deciding the permissible conformity rate of a ball screw groove with the computational evaluation of contact pressure and maximum shear stress.

• Journal of Welding and Joining
• /
• v.32 no.3
• /
• pp.60-67
• /
• 2014

The ability of electronic packages and assemblies to resist solder joint failure is becoming a growing concern. This paper reports on a study of high speed shear energy of Sn-4.0wt%Ag-0.5wt%Cu (SAC405) solder with different electroless Ni-P thickness, with $HNO_3$ vapor's status, and with various pre-conditions. A high speed shear testing of solder joints was conducted to find a relationship between the thickness of Ni-P deposit and the brittle fracture in electroless Ni-P deposit/SAC405 solder interconnection. A focused ion beam (FIB) was used to polish the cross sections to reveal details of the microstructure of the fractured pad surface with and without $HNO_3$ vapor treatment. A scanning electron microscopy (SEM) and an energy dispersive x-ray analysis (EDS) confirmed that there were three intermetallic compound (IMC) layers at the SAC405 solder joint interface: $(Ni,Cu)_3Sn_4$ layer, $(Ni,Cu)_2SnP$ layer, and $(Ni,Sn)_3P$ layer. The high speed shear energy of SAC405 solder joint with $3{\mu}m$ Ni-P deposit was found to be lower in pre-condition level#2, compared to that of $6{\mu}m$ Ni-P deposit. Results of focused ion beam and energy dispersive x-ray analysis of the fractured pad surfaces support the suggestion that the brittle fracture of $3{\mu}m$ Ni-P deposit is the result of Ni corrosion in the pre-condition level#2 and the $HNO_3$ vapor treatment.