• 한국재료학회지
• /
• 제17권2호
• /
• pp.96-99
• /
• 2007

The effects of post-annealing of high-k $HfO_2$ thin films grown by atomic layer deposition method were investigated by the annealing treatments of $400-600^{\circ}C$. $Pt/HfO_2/p-Si\;MOS$ capacitor structures were fabricated, and then the capacitance-voltage and current-voltage characteristics were measured to analyze the electrical characteristics of dielectric layers. The X-ray diffraction analyses revealed that the $500^{\circ}C-annealed\;HfO_2$ film remained to be amorphous, and the $600^{\circ}C-annealed\;HfO_2$ film was crystallized. The annealing treatment at $500^{\circ}C$ resulted in the highest capacitance and the lowest leakage current due to the reduction of defects in the $HfO_2$ films and non-crystallization. Our results suggest that post-annealing treatments are a critical factor in improving the characteristics of gate dielectric layer.

• 한국표면공학회지
• /
• 제41권1호
• /
• pp.1-5
• /
• 2008

In this work, improvement of mechanical and electrical properties of gate dielectric layer for flexible organic thin film transistor (OTFT) devices was investigated. In order to increase the mechanical flexibility of PVP (poly(4-vinyl phenol) organic gate dielectric, a very thin inorganic $HfO_2$ layers with the thickness of $5{\sim}20nm$ was inserted in between the spin-coated PVP layers. Insertion of the inorganic $HfO_2$ in the laminated organic/inorganic structure of PVP/$HfO_2$/PVP layer led to a dramatic reduction in the leakage current compared to the pure PVP layer. Under repetitive cyclic bending, the leakage current density of the laminated PVP/$HfO_2$/PVP layer with the thickness of 20-nm $HfO_2$ layer was not changed, while that of the single PVP layer was increased significantly. Mechanical flexibility tests of the OTFT devices by cyclic bending with 5 mm bending radius indicated that the leakage current of the laminated PVP/$HfO_2$(20 nm)/PVP gate dielectric in the device structure was also much smaller than that of the single PVP layer.

• 한국전기전자재료학회논문지
• /
• 제36권2호
• /
• pp.125-128
• /
• 2023

Recently, as the process of the MOS device becomes more detailed, and the degree of integration thereof increases, many problems such as leakage current due to an increase in electron tunneling due to the thickness of SiO₂ used as a gate oxide have occurred. In order to overcome the limitation of SiO₂, many studies have been conducted on HfO₂ that has a thermodynamic stability with silicon during processing, has a higher dielectric constant than SiO₂, and has an appropriate band gap. In this study, HfO₂, which is attracting attention in various fields, was doped with Al and the change in properties according to its concentration was studied. Al-doped HfO₂ thin film was deposited using Plasma Enhanced Atomic Layer Deposition (PEALD), and the structural and electrical characteristics of the fabricated MIM device were evaluated. The results of this study are expected to make an essential cornerstone in the future field of next-generation semiconductor device materials.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2010년도 제39회 하계학술대회 초록집
• /
• pp.164-164
• /
• 2010

The impurity doped ZnO has been extensively studied because of its optoelectric properties. GIZO (Ga-In-Zn-O) amorphous oxide semiconductors has been widely used as transparent flexible semiconductor material. Recently, various amorphous transparent semiconductors such as IZO (In-Zn-O), GIZO, and HIZO (Hf-In-Zn-O) were developed. In this work, we examined the local structures of IZO, GIZO, and HIZO. The local coordination structure was investigated by the extended X-ray absorption fine structure. The IZO, GIZO and HIZO thin films ware deposited on the glass substrate with thickness of 400nm by the radio frequency sputtering method. The targets were prepared by the mixture of $In_2O_3$, ZnO and $HfO_2$ powders. The percent ratio of In:Zn in IZO, Ga:In:Zn in GIZO and Hf:In:Zn in HIZO was 45:55, 33:33:33 and 10:35:55, respectively. In this work, we found that IZO, GIZO and HIZO are all amorphous and have a similar local structure. Also, we obtained the bond distances of $d_{Ga-O}=1.85\;{\AA}$, $d_{Zn-O}=1.98\;{\AA}$, $d_{Hf-O}=2.08\;{\AA}$, $d_{In-O}=2.13\;{\AA}$.

• Transactions on Electrical and Electronic Materials
• /
• 제8권6호
• /
• pp.229-233
• /
• 2007

In this study, we carried out an investigation of the etching characteristics(etch rate, selectivity) of $HfO_2$ thin films in the $CH_4/Ar$ inductively coupled plasma. It was found that variations of input power and negative dc-bias voltage are investigated by the monotonic changes of the $HfO_2$ etch rate as it generally expected from the corresponding variations of plasma parameters. At the same time, a change in either gas pressure or in gas mixing ratio result in non-monotonic etch rate that reaches a maximum at 2 Pa and for $CH_4(20%)/Ar(80%)$ gas mixture, respectively. The X-ray photoelectron spectroscopy analysis showed an efficient destruction of the oxide bonds by the ion bombardment as well as showed an accumulation of low volatile reaction products on the etched surface. Based on these data, the ion-assisted chemical reaction was proposed as the main etch mechanism for the $CH_4-containing$ plasmas.

• 한국전기전자재료학회논문지
• /
• 제33권6호
• /
• pp.433-438
• /
• 2020

To enhance the tunneling electroresistance (TER) ratio of a ferroelectric tunnel junction (FTJ) device using Al-doped HfO₂ thin films, a thin insulating layer was prepared on a TiN bottom electrode, for which TiN was preliminarily treated at various temperatures in O₂ ambient. The composition and thickness of the inserted insulating layer were optimized at 600℃ and 50 Torr, and the FTJ showed a high TER ratio of 430. During the heat treatments, a titanium oxide layer formed on the surface of TiN, that suppressed oxygen vacancy generation in the ferroelectric thin film. It was found that the fabricated FTJ device exhibits two distinct resistance states with higher tunneling currents by properly heat-treating the TiN bottom electrode of the HfO₂-based FTJ devices in O₂ ambient.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 추계학술대회 논문집 Vol.18
• /
• pp.364-365
• /
• 2005

This paper report nanotribological behavior between Si tip and Cu wafer surfaces which was treated various concentration of $H_2O_2$. This experimental approach has proven atomic level insight into Cu CMP. It has been used to study interfacial friction and adhesion force between Si tip and Cu wafer surfaces in air by atomic force microscopy (AFM). Adhesion force of Cu surfaces which was pre-cleaned in diluted HF solution was lager than Cu oxide surfaces. Adhesion force of Cu oxide surface was saturated around 7 nN. Slope of normal force vs lateral signal was increased as increasing concentration of $H_2O_2$ and it was saturated around 24. Friction force of Cu oxide was lager than Cu.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2005년도 International Meeting on Information Displayvol.I
• /
• pp.496-498
• /
• 2005

We reported that high dielectric hafnium oxide nano-film deposited by thermal atomic layer deposition on the poly-silicon film (poly-Si). The poly -Si film was produced by plasma enhanced chemical vapor deposition and excimer laser annealing. We used the hafniu m chloride ($HfCl_4$) and water as the precursors and analyzed the hafnium oxide film by transmission electron microscope and secondary ion mass spectrometer. Hafnium oxide produced by the ALD method showed very good coverage on the rough surface of poly-Si film. While deposited with 200 cycles, these hafnium oxide films revealed a relatively smooth surface and good uniformity, but the cumulative roughness produced by the incomplete reaction was apparent when the amount of deposition cycle increased to 600 cycles.

• 열처리공학회지
• /
• 제20권6호
• /
• pp.299-305
• /
• 2007

The effect of spray deposition of oxide particles on oxidation behaviors of as-cast Mo-14.2Si-9.6B (at%) alloys at $1200^{\circ}C$ up to for 100 hrs has been investigated. Various oxide powders are utilized to make coatings by spray deposition, including $SiO_2,\;TiO_2,\;ZrO_2,\;HfO_2$ and $La_2O_3$. It is demonstrated that the oxidation resistance of the cast Mo-Si-B alloy can be significantly improved by coating with those oxide particles. The growth of the oxide layer is reduced for the oxide particle coated Mo-Si-B alloy. Especially, for the alloy with $ZrO_2$ coating, the thickness of oxide layer becomes only one fifth of that of uncoated alloys when exposed to in air for 100 hrs. The reduction of oxide scale growth of the cast Mo-Si-B alloy due to oxide particle coatings are discussed in terms of the change of viscosity of glassy oxide phases that form during oxidation at high temperature.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 추계학술대회 논문집
• /
• pp.48-48
• /
• 2009

최근 빠른 동작속도와 고 집적도를 얻기 위해 metal oxide semiconductor field effect transistor (MOSFET) 의 크기는 계속 해서 줄어들고 있다. 동시에 게이트의 절연층도 얇아지게 된다. 절연층으로 사용되는 $SiO_2$ 의 두께가 2nm 이하로 얇아 지게 되면 터널링에 의해 누설 전류가 발생하게 된다. 이 문제를 해결하기 위해 $SiO_2$ 를 대체할 고유전체 물질의 연구가 활발하다. 고유전체 물질 중에는 $ZrO_2,\;Al_2O_3,\;HfO_2$ 등이 많이 연구 되어 왔다. 하지만 유전상수 이외에 band gap energy, thermodynamic stability, recrystallization temperature 등의 특성이 좋지 않아 대체 물질로 문제점이 있다. 이를 보안하기 위해 산화물을 합금과 결합시키면 서로의 장점들이 합쳐져 기준들을 만족하는 물질을 만들 수 있고 $HfAlO_3$가 그 중 하나이다. Al를 첨가하는 이유는 문턱전압을 낮추기 위해서다. $HfAlO_3$는 유전상수 18.2, band gap energy 6.5 eV, recrystallization temperature 800 $^{\circ}C$이고 열역학적 특성이 안정적이다. 게이트 절연층은 전극과 기판사이에 적층구조를 이루고 있어 이방성인 드라이 에칭이 필요하고 공정 중 마스크물질과의 선택비가 높아야한다. 본 연구는 $HfAlO_3$박막을 $BCl_3/Ar,\;N_2/BCl_3/Ar$ 유도결합 플라즈마를 이용해 식각했다. 베이스 조건은 RF Power 500 W, DC-bias -100 V, 공정압력 15 mTorr, 기판온도 40 $^{\circ}C$ 이다. 가스비율, RF Power, DC-bias, 공정 압력에 의한 마스크물질과 의 선택비를 알아보았다.