• Journal of Welding and Joining
• /
• v.34 no.5
• /
• pp.70-76
• /
• 2016

In this study, Microstructure and tensile properties in arc brazed joints of 1000MPa grade DP steel using Cu-Si insert metal were investigated. The fusion zone was composed of Cu phase which solidified a little Fe and Si. The former phase formed due to dilute the edge of base material by arc, although Fe was not solid solution in Cu at the room temperature. Cu3Si particles formed by crystallization at $1100^{\circ}C$ during faster cooling. After the tensile shear test, there are no differences between the brazed joint efficiencies. The maximum joint efficient was about 37% compared to strength of base metal. It is better than that of arc brazed joint of DP steel using Cu-Sn filler metal. Fracture position of all brazing conditions was in the fusion zone. Crack initiation occurred at three junction point which was a stress singularity point of upper sheet, lower sheet and the fusion zone. And then crack propagated across the fusion zone. The reason why the fracture occurred at fusion zone was that the hardness of fusion zone was lower than that of base material and heat affected zone. The correlation among maximum load and hardness of fusion zone and EST at fractured position was $R^2=0.9338$. Therefore, this means that hardness and EST can have great impact on maximum load.

• Nuclear Engineering and Technology
• /
• v.52 no.3
• /
• pp.589-596
• /
• 2020

Many components in the assembly section of Sodium-cooled Fast Reactor are made of good corrosionresistant 316 LN Stainless Steel material. To avoid self-welding of the components with the coolant sodium at elevated temperature, hardfacing is inevitable. Ni-based colmonoy-5 is used for hardfacing due to its lower dose rate by Plasma Transferred Arc process due to its low dilution. Since Ni-Cr-B-Si alloy becomes very fluidic while depositing, the major height of the weld overlay rests inside the groove. Hardfacing is also done over the plain surface where grooving is not possible. Therefore, grooved and ungrooved hardfaced specimens were prepared at different travel speeds. Fe content at every 100 ㎛ of the weld overlay was studied by Energy Dispersive Spectroscopy and also the micro hardness was determined at those locations. A correlation between iron dilution from the base metal and the micro hardness was established. Therefore, if the Fe content of the weld overlay is known, the hardness at that location can be obtained using the correlation and vice-versa. A new correlation between micro hardness and dilution coefficient is obtained at different locations. A comparative study between those specimens is carried out to recommend the optimum travel speed for lower dilution.

• Proceedings of the KWS Conference
• /
• 2003.11a
• /
• pp.103-105
• /
• 2003

Currently, duplex and superduplex stainless steels are widely used for piping system in offshore unit because of its excellent combination of strength and corrosion resistance properties. Also, the usage of duplex and superduplex stainless steel is steadily increasing with getting into step with development of offshore industries. In spite of excellent merits in mechanical and chemical properties of base materials, sometimes stringent requirements in welding procedure qualification and fabrication of duplex class material have regulated not only the application of various high-efficiency welding processes but also applicable welding parameters. This study is focused on hardness requirement which is known as one of the most stringent factor in duplex class material welding and this study aims to evaluate the effects of cutting and welding methodology on hardness values of duplex and superduplex stainless steel weldments.

• Journal of Surface Science and Engineering
• /
• v.22 no.1
• /
• pp.26-42
• /
• 1989

It has between investigated that the optimum spaying conditions, such as, spraying distance, fusing temperature and fusing time, ect, in a Ni-cr base self fluxing alloy sprayed on the mild steel substrate by oxygen-acetylenc flame spraying. Sprayed specimens on various conditions were fuused in a vacuum furnace and the results were as follows. The optimum spraying condition for excellent coating layer are obtained under spraying distances, fusing temperature and fusing and time ; 180~240mm,1050~110$0^{\circ}C$and 15~30min, respectively. The adhesive strength and surface hurface hardness of the as sprayed specimens were very low by mechanical bonding becaus of the diffusion layer during process. The carbides and borides and formed in the sprayed coating layer and densification of the layer was resulted from the elimination of pores and oxides. The hardness of sprayed coating layer, particularly in the high temperature, was superior to ordinary tool steels.

• Journal of Welding and Joining
• /
• v.20 no.3
• /
• pp.54-59
• /
• 2002

Overlays is a treatment of the surface and near-surface regions of a material to allow the surface to perform functions that are distinct from those frictions demanded far the bulk of the material. Welding, thermal spray, quenching, carburizing and nitration have been used as the surface treatment. Especially, weld overlay is a relatively thick layer of filler metal applied to a carbon or low-alloy steel base metal for the purpose of providing a wear resistant surface. In this study, weld overlay was performed by MAG welding on the base metal(SS400) with filler metal which contain composite powders($Cr_3C_2+Mn+Mo+NbC$) and solid wire(JIS-YGW11). Characteristics of hardness and wear resistance on overlays were analyzed by EDS, EPMA, XRD and microstructures. Carbide formations were $M(Cr, Fe)_7C_3$ and NbC phases. And carbide volume fraction, hardness and specific wear resistance of overlays were increased with increasing powder feed rate and decreasing wire fred rate. Hardness and wear resistance were almost proportioned to carbide volume fraction of overlay.

• Journal of Advanced Marine Engineering and Technology
• /
• v.8 no.2
• /
• pp.39-50
• /
• 1984

The plane bending corrosion fatigue test was performed on the welded zone between SM58 steel plate and SM41 steel plate jointed with submerged arc welding in the air and in the natural sea water with various conditions. The main results obtained from the test are summarized as follows: 1) The welded zone of the steel plates has the lowest impact strength and the highest electrode potential, but the hardness was mediate of SM58 base and SM41 base. 2) The cathodic protection of the welded zone was also effective for the plane bending corrosion fatigue, and the optimum protection potential of the welded zone was -1,000 mV SCE. 3) The corrosion fatigue strength under the various stress conditions of the steel plate could be estimated and also the require safety factors on the design could be obtained from the plane bending fatigue limit diagram.

• Corrosion Science and Technology
• /
• v.21 no.1
• /
• pp.32-40
• /
• 2022

The o-Vanillin - Glutamine Schiff base [2-Hydroxy-3-Methoxy BenzylidineCarbomyl) -2-Butanoic Acid] was examined for low carbon steel corrosion inhibition in acid media. Weight loss studies were carried out at three different temperatures to determine the inhibition efficiency (IE). Electrochemical impedance spectroscopy revealed that the charge transfer resistance controlled the corrosion reaction and Tafel polarization indicated that the Schiff base acts as mixed mode of inhibitor. SEM images were recorded for the surface morphology of the low carbon steel surface. DFT studies revealed corrosion control mechanisms using quantum chemical parameters such as E_HOMO, E_LUMO, energy gap (∆E), chemical Hardness (η), chemical Softness (σ), Electronegativity (χ), and the fraction of electron transferred (∆N), which is calculated using Gaussian software 09. The gas-phase geometry was fully optimized in the Density Functional Theory (DFT/B3LYP-6-31G (d)).The DFT results are in good agreement with the experimental results. All the results proved that the Schiff Base (2-Hydroxy-3-Metoxy BenzylidineCarbomyl) -2-Butanoic is a suitable alternative for corrosion inhibition of low carbon steel in acid media.

• Laser Solutions
• /
• v.2 no.2
• /
• pp.34-41
• /
• 1999

A RS840 $CO_2$laser and a powder auto-feeding apparatus have been used to deposit single tracks of Ni-base superalloy on low carbon steel. In this paper, the effects of laser cladding parameters on clad geometry, dilution and microhardness are studied. As a results, the w/h ratio of the clad layer increases with decreasing powder feed rate and increasing laser scan speed. Increase of powder density and decrease of specific energy have little effect on dilution. It was found that the clad layer of the highest hardness has a structure in which fine and leaf like phases are dispersed in ${\gamma}$Ni matrix.

• Journal of Ocean Engineering and Technology
• /
• v.22 no.6
• /
• pp.41-45
• /
• 2008

Effectsof carbon content on the weldability of B-containing 620 grade high Cr ferritic cast steels were investigated. Cast steel with lower carbon content of 0.07% showed lower HAZ hardness because of the formation of lower carbon martensite in HAZ. It also showed less solidification cracking susceptibility in weld metal because of the formation of delta ferrite. However, hot ductility showed no difference between cast steels with lower and higher carbon contents. Cast steel with lower carbon content showed greater HAZ softening after PWHT in the region heated between AC1 and AC3 because of its higher base metal hardness.

• Proceedings of the KSME Conference
• /
• 2000.11a
• /
• pp.333-338
• /
• 2000

Induction surface hardening is widely used to enhance local strength and hardness. However, most research is only to have a focus on fatigue life and fatigue behavior is not so much studied. So, in this study, Cr-Mo steel alloy(SCM440) was used to show the effect of residual stress and micro hole on the fatigue strength for base metal and induction surface hardened specimen. In addition, the fatigue characteristic between surface hardened and fully hardened steel is somewhat different. It is caused by hardness distribution, residual stress and inclusions etc.. Crack origins are generally micro inclusions for the high strength steel. So, the distribution of inclusions is analyzed statistically.