• 한국염색가공학회지
• /
• 제24권4호
• /
• pp.313-320
• /
• 2012

For the preparation of hardened films which can be applied as a binder for flame-resistant materials such as silica, linseed oil was subjected to a low temperature plasma treatment with argon, or oxygen gas. The film was produced much faster than so-called drying of oil in air. The SEM analysis for silica particles embedded in the hardened film after plasma treatment showed that the silica particles were immobilized on substrate and were evenly dispersed. The FT-IR spectral analysis for the plasma-treated linseed oil films demonstrated that the radicals which were formed during the plasma treatments caused the linseed oil to be cross-linked, and the plasmas attacked carbon chains of the oil randomly without focusing on specific vulnerable bonds such carbon double and carbonyl bonds intensively unless exposure times of the plasmas were prolonged too much, while the cross-linking of the air-dried film was considered to occur at the well-known typical sites, i.e., carbon-carbon double bond and ${\alpha}$-methylene carbon. Burning times, as a measure of flame/fire resistance, of silica-filled cellulose substrates, increased with increasing contents of silica.

• 한국정밀공학회지
• /
• 제14권8호
• /
• pp.73-81
• /
• 1997

The hard turning process defined as a single point turning of materials harder than $H_{R}$C 58 differs from conventional turning because of hardness of the work materials and cutting toos needed in the process. In hard turning, tool life is very short, of the order of a few minutes, during which the cutting tool is subjected to the extremes of stress and temperature. In this regard, it is well known that CBN tool is proper for this process in spite of expensive cost. In this research, we studied the feasibility of the use of the low cost cutting tool such as a aTiN coated tool. To this end, a new cooling system was designed with an air-oil method for reducing tool temperature, which is based on the principle of air vortex flow. That is, the outlet temperature of the air becomes aver 20 .deg. C lower than atmosphere temperature by entering pressurized air of 5kgf/c $m^{2}$ into the inlet. This cooled air ejected to the top of the cutting tool lowered tool temperature, which reduced the wear of a TiN coated tool by the 30% of CBN tool life with respect to the same cutting length.h.

• 대한기계학회논문집A
• /
• 제34권5호
• /
• pp.645-649
• /
• 2010

고주파열처리(induction hardening)는 엔진의 구동력을 차동장치에서 바퀴까지 전달해주는 부품인 액슬축(axle shaft)의 비틀림 강도를 증가시키기 위해 적용되는 열처리 방법이다. 고주파 열처리 과정의 급속가열과 급속냉각은 소재에 잔류응력과 물성치를 변화시켜 액슬축의 허용 전달토크를 변화시킨다. 본 연구에서는 고주파 열처리한 액슬축의 잔류응력의 분포와 열처리 깊이에 따른 비틀림 강도 변화를 열물성 및 상변태를 고려한 유한요소 해석을 통해 예측하였으며 이를 시험과 비교하였다.

• 한국재료학회지
• /
• 제26권7호
• /
• pp.388-392
• /
• 2016

A cold roll-bonding process was applied to fabricate an AA1050/AA6061/AA1050 laminate complex sheet. Two AA1050 and one AA6061 sheets of 2 mm thickness, 40 mm width and 300 mm length were stacked up after surface treatment that included degreasing and wire brushing; material was then reduced to a thickness of 3 mm by one-pass cold rolling. The laminate sheet bonded by the rolling was further reduced to 1.2 mm in thickness by conventional rolling. The rolling was performed at ambient temperature without lubricant using a 2-high mill with a roll diameter of 210 mm. The rolling speed was 5.0 m/sec. The AA1050/AA6061/AA1050 laminate complex sheet fabricated by roll bonding was then hardened by natural aging T4) and artificial aging (T6) treatments. The microstructures of the as-roll bonded and the age hardened Al complex sheets were revealed by optical microscope observation; the mechanical properties were investigated by tensile testing and hardness testing. The strength of the as-roll bonded complex sheet was found to increase by 2.9 times compared to that value of the starting material. In addition, the hardness of the complex sheets increased with cold rolling for AA1050 and age-hardening treatment for AA6061, respectively. After heat treatment, both AA1050 and AA6061 showed typical recrystallization structures in which the grains were equiaxed; however, the grain size was smaller in AA6061 than in AA1050.

• 한국전기전자재료학회논문지
• /
• 제32권1호
• /
• pp.6-12
• /
• 2019

Bonding properties of epoxy-containing solder joints were investigated by a high temperature aging test. Specimens were prepared by bonding an R3216 standard chip resistor to an OSP-finished PCB by a reflow process with two basic types of solder (SAC305 & Sn58Bi) pastes and two epoxy-solder (SAC305+epoxy & Sn58Bi+epoxy) pastes. In all epoxy solder joints, an epoxy fillet was formed in the hardened epoxy, lying around the outer edge of the solder joint, between the chip and the Cu pad. In order to analyze the bonding characteristics of solder joints at high temperatures, a high-temperature aging test at $150^{\circ}C$ was carried out for 14 days (336 h). After aging, the intermetallic compound $Cu_6Sn_5$ was found to have formed in the solder joint on the Cu pad, and the shear stress on the conventional solder joint was reduced by a significant amount. The reason that the shear force did not decrease much, even though in epoxy solder, was thatbecause epoxy hardened at the outer edge of the supported solder joints. Using epoxy solder, strong bonding behavior can be ensured due to this resistance to shear force, even in metallurgical changes such as those where intermetallic compounds form at solder joints.

• 한국재료학회지
• /
• 제31권3호
• /
• pp.172-180
• /
• 2021

In this study, using the plasma spray method, tensile and compression fatigue tests are performed in saline solution to examine the effect of Ti undercoat on corrosion fatigue behavior of alumina-coated specimens. The alumina-coated material using Ti in the undercoat shows better corrosion fatigue strength than the base material in the entire stress amplitude range. Fatigue cracking of UT specimens occurs in the recess formed by grit-blasting treatment and progresses toward the base metal. Subsequently, the undercoat is destroyed at a stage where the deformation of the undercoat cannot follow the crack opening displacement. The residual stress of the UT specimen has a tensile residual stress up to about 100 ㎛ below the surface of the base material; however, when the depth exceeds 100 ㎛, the residual stress becomes a compressive residual stress. In addition, the inside of the spray coating film is compressive residual stress, which contributes to improving the fatigue strength characteristics. A hardened layer due to grit-blasting treatment is formed near the surface of the UT specimen, contributing to the improvement of the fatigue strength characteristics. Since the natural potential of Ti spray coating film is slightly higher than that of the base material, it exhibits excellent corrosion resistance; however, when physiological saline intrudes, a galvanic battery is formed and the base material corrodes preferentially.

• 한국건설순환자원학회논문집
• /
• 제6권4호
• /
• pp.103-111
• /
• 2012

압축강도 50 MPa이상의 압출성형 시멘트 패널은 고온고압 증기양생으로 생산된다. 고온고압 증기양생에서 요구 강도를 얻기 위해서는 시멘트에 포함되어 있는 CaO와의 반응에 필요한 적정량의 $SiO_2$를 공급하는 것이 관건이다. $SiO_2$의 공급원으로 가장 널리 사용되는 원료는 규석분인데, 이는 환경파괴를 전제로 하기 때문에 친환경적인 제품 생산을 위하여 본 연구에서는 규석분을 대신하여 폐석분을 활용한 시멘트 2차 제품을 생산하고 이에 대한 압출성과 물리적인 특성비교를 실시하였다. 이를 위하여 화성 석산에서 채취한 폐석분을 건조 파쇄한 후 이를 규석분 사용량의 최대 50%까지 치환하여 압출성 및 물리적 특성 실험을 수행하였다. 실험결과 평균 입경은 폐석분과 규석분의 크기가 유사하였으나 물리적 특성은 규석분을 폐석분으로 단순 치환하였을 경우, 대부분 낮게 발현되었다. 따라서 폐석분을 활용할 경우 수화활성을 위한 첨가제 등의 활용이 필요할 것으로 판단된다.

• 대한기계학회논문집
• /
• 제11권1호
• /
• pp.53-62
• /
• 1987

본 논문에서는 1 KW CW CO$_{2}$레이저 발생자장치를 사용하여 표면경화 처리 를 행할때 공정과 관련된 변수들이 용접부 및 표면경화층에 미치는 영향들을 이론과 실험을 통해서 규명하고, 이 결과들을 실제공정에 사용할 수 있는 기초자료로서 제시 하고자 한다. 이를 위해서 해석에 사용될 수 있는 유한요소법(Finite Element Meth- od)에 근거한 2차원 열유동 해석용 프로그램 및 데이타 처리 프로그램을 개발하고, 중 탄소강에 레이저 표면처리를 수행하여 실험 및 이론해석의 결과를 비교 검토하였다. 비교 검토하여 그 설정기준을 고찰하였다.

• International Journal of Concrete Structures and Materials
• /
• 제8권2호
• /
• pp.165-172
• /
• 2014

Recycled coarse aggregate (RCA) made from waste concrete is not a suitable structural material as it has high absorption of cement mortar, which adheres on the aggregate surface and on the tiny cracks thereon. Therefore, when using RCA made from waste concrete, much water must be added with the concrete, and slump loss occurs when transporting. Hence, its workability is significantly worse than that of other materials. In this study, surface of RCA was coated with water-soluble polycarboxylate (PC) dispersant so that its characteristics improved. Each possibility was evaluated: whether its slump loss can be controlled, by measuring its workability based on the elapsed time; and whether it can be used as a structural material, by measuring its strength. Moreover, the carbonation due to cement mortar adhesion was measured through a carbonation test. As a result, RCA coated with PC dispersant was found to be better than crushed coarse aggregate and RCA when the physical properties of the fresh concrete and the mechanical, durability of the hardened concrete were tested.

• 대한기계학회논문집
• /
• 제6권4호
• /
• pp.367-376
• /
• 1982

Stress concentration mainly occurs near holes and notches. Then local stress is larger than nominal stress. It is necessary that stress concentration phenomena are studied because it can act as a cause of fracture of material. In order to analyze fracture of material including holes, stress concentration factor and stress distribution must be studied more carefully. In this paper the stress concentration and distribution of a slotted plate is examined. Hardened 7:3 brass plate with 4 different slots including a circular hole is used. And ratios of slot length to its root radius are 1, 2, 3, 24, 4. The stress distribution is measured by using strain gages attached to the plate with variable width. And obtained experimental data are adjusted by using calibrated gage factor.