• Composites Research
• /
• v.27 no.4
• /
• pp.168-173
• /
• 2014

The optimum condition of glass fiber/epoxy composites was investigated according to mixing ratio of two epoxy matrices. Novolac type epoxy and isocyanate modified epoxy were used as composites matrix. Based on chemical composition of mixing matrix, optimum mixing ratio of epoxy resins was obtained through various experiments. In order to investigate thermal stability and interface of epoxy resin, glass transition temperature was observed by DSC instrument, and static contact angle was measured by reflecting microscope. Change of IR peak and $T_g$ was conformed according to different epoxy mixing ratio. After fabrication of glass fiber/epoxy composites, tensile, compression, and flexural properties were tested by UTM by room and high temperature. The composites exhibited best mechanical properties when epoxy mixing ratio was 1:1.

• Progress in Superconductivity and Cryogenics
• /
• v.25 no.3
• /
• pp.43-48
• /
• 2023

Polymer composites, especially glass fiber reinforced polymer (GFRP) are finding ever-increasing applications in areas such as superconductivity, space technology, cryogenic rocket engines, and cryogenic storage vessels. Various components made of polymer composites are much lighter than their metallic counterparts but have equivalent strength for ultra-low temperature applications. In this paper, we have investigated the tensile properties of an indigenously prepared unidirectional cylindrical hollow composite tube for its use as a neck of the cryogenic vessel. XRD and SEM of the tube are completed before cryogenic conditioning to ascertain the fiber and resin distribution in the matrix. The result shows that for composites, after 15, 30, 45, and 60 minutes of cryogenic conditioning at 77K in a liquid nitrogen bath, the strength and modulus increase significantly with the increase of strain rate and reach the optimum value for 45 minutes of conditioning. The results are encouraging as they will be helpful in assessing the suitability of GFRP in the structural design of epoxy-based components for cryogenic applications.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.13 no.1
• /
• pp.15-20
• /
• 1993

This study describes ultrasonic reflection at a water/fiber reinforced polymer composite/water interface. Theoretical predictions of reflected beam amplitudes are also presented. Four different polymer composite laminates are investigated : T300/5208 graphite/epoxy $[0]_{31T},\;[45/90/-45/0]_{3S},\;[45/-45]_{2S}$, and S-2 glass/epoxy $[0/90]_{4S}$. The analytical leaky plate wave dispersion curves for the unidirectional laminate and other three laminates can be obtained by searching for the minimum magnitude of the reflection coefficient.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.4
• /
• pp.159-165
• /
• 2021

The fiber composites have been investigated as lightweight structure material platforms for aerospace applications because their strength can be enhanced by adding reinforcement without a significant increase in weight. In this study, the fabrication and characterization of carbon nanotube (CNT) reinforced glass fiber composites are demonstrated to enhance the tensile strength of longitudinal direction along the glass fibers. Due to the reinforcement of CNT in epoxy layers, the yield strength of fiber/epoxy composites is enhanced by about 10 %. Furthermore, using scanning electron microscopy, analysis of fracture surfaces shows that mixed CNT in epoxy layers acts as necking agents between fractured surfaces of fiber/epoxy; thereby, initiation and evolution of crack across fiber composite can be suppressed by CNT necking between fractured surfaces.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.32 no.9
• /
• pp.788-795
• /
• 2008

To understand the tensile behaviors of GFRP at low temperature, three types of specimen have been used in this study. Tensile properties and fracture mechanisms for three orthogonal orientations of plain weave glass fabric reinforced epoxy resin laminate were investigated at temperature range of about -30 to $15^{\circ}C$. The tensile properties of axial and edge type specimen decrease slightly with decreasing temperature to $-20^{\circ}C$. However, at $-30^{\circ}C$ the decreases in the tensile properties increased considerably. Below $-20^{\circ}C$, thickness type specimen showed a marked decreases in the tensile properties. It was obvious that the fracture manner of thickness type specimen was adhesive failure at above $-10^{\circ}C$ and a mixed adhesive and cohesive failure at below $-20^{\circ}C$.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.17 no.3
• /
• pp.15-21
• /
• 2009

The anisotropic mechanical properties were measured for the three orthogonal orientations of plain weave glass fabric reinforced epoxy resin laminate. In tensile and flexural tests, axial and edge type specimens failed by pull-out of warp and fill yarns, respectively. In contrast, the thickness type specimens failed by adhesive failure process. Longitudinal cracking occurred in several of the edge type specimens during tensile test. That cracking caused pop-in in the stress-strain curve. Defects induced by improper coupon machining caused that cracking.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10a
• /
• pp.444-449
• /
• 1998

The Glass-Fiber Reinforced Epoxy-Panel(GFREP) is a composite material developed for repairing and strengthening of RC structures. The objective of this study is to verify the applicability of finite element modeling technique to analyze behaviors of RC beams strengthened by the GFREP. In this study, the basic material properties obtained by experiments on the GFREP and the reinforced concrete constitutive models were considered and the comparison between analyses and experiments of RC beam specimens strengthened by the GFREP was made. Although analysis method in this paper was reasonably good, the necessities which can consider the effect of plate-end shear and plate separation were recognized.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.04a
• /
• pp.158-161
• /
• 2005

The fiber-reinforced composite materials have been advanced for various applications because of its excellent mechanical and electromagnetic properties. On their manufacturing processes, however, thermo-curing inherently produces the undesired thermal deformation mainly from temperature drop from the process temperature to the room temperature, so called spring-back. The spring-back must be removed to keep the precision of designed shape. In this research, the spring-back of {glass fiber / epoxy}+{carbon fiber / epoxy} unsymmetric hybrid composites were predicted using Classical Lamination Theory (CLT), and compared with the experimental data. Additionally, using finite element analysis (ANSYS), the predicted data and experimental data were compared. The predicted values by CLT and ANSYS were well matched with experimental data.

• Structural Engineering and Mechanics
• /
• v.55 no.1
• /
• pp.137-160
• /
• 2015

The one-way (two-way) flexural strength of RCC prisms (circular slabs) reinforced with glass fiber textiles is addressed. To this end, alkaline-resistant glass fiber textiles with three surface weights were used in the composite, the matrix concrete was designed with zero/nonzero slump, and the textiles were used with/without an intermediate layer provided by epoxy resin and sand mortar. Prisms were tested under a four-point loading apparatus and circular slabs were placed on simple supports under a central load. Effects of the amount and geometry of reinforcement, matrix workability, and the intermediate layer on the ultimate load and deflection were investigated. Results revealed that, with a specific reinforcement amount, there is an optimum textile tex for each case, depending on the matrix mix design and the presence of intermediate layer. Similar results were obtained in one-way and two-way bending tests.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.10
• /
• pp.1514-1519
• /
• 2001

This paper is concerned with design, manufacturing and performance test of LIPCA ( Lightweight Piezo- composite Curved Actuator) using a top carbon fiber composite layer with near -zero CTE(coefficient of thermal expansion), a middle PZT ceramic wafer and a bottom glass/epoxy layer with high CTE. The main point of this design is to replace the heavy metal layers of THUNDER by thigh tweight fiber reinforced plastic layers without losing capabilities to generate high force and large displacement. It is possible to save weight up to about 30% if we replace the metallic backing material by the light fiber composite layer. We can also have design flexibility by selecting the fiber direction and the size of prepreg layers. In addition to the lightweight advantage and design flexibility, the proposed device can be manufactured without adhesive layers when we use epoxy resin prepreg system. Glass/epoxy prepregs, a ceramic wafer with electrode surfaces, and a graphite/epoxy prepreg were simply stacked and cured at an elevated temperature (177 $^{circ}C$ after following an autoclave bagging process. It was found that the manufactured composite laminate device had a sufficient curvature after detached from a flat mold. The analysis method of the cure curvature of LIPCA using the classical lamination theory is presented. The predicted curvatures are fairly in agreement with the experimental ones. In order to investigate the merits of LIPCA, a performance test of both LIPCA and THUNDE$^{TM}$ were conducted under the same boundary conditions. From the experimental actuation tests, it was observed that the developed actuator could generate larger actuation displacement than THUNDERT$^{TM}$.