• 한국의류학회지
• /
• 제10권3호
• /
• pp.71-81
• /
• 1986

In order to control the formaldehyde release from D.P. finished fabric, cotton fabric was padded in DMDHEU resin bath containing either $Zn(NO_3)_2$ or $MgCl_2$ catalyst and a form-aldehyde scavenger like Glycerol, Sorbitol, Formamide, Polyvinyl alcohol (PVA, n= 2000) or diols, then dried and cured. The results are as follows : 1. When Lewis acid catalyst like $Zn(NO_3)_2$ or $MgCl_2$ was added in pad bath, the fabric finished with $Zn(NO_3)_2$ catalyst released the lower formaldehyde than with $MgCl_2$. 2. When the effect of pad bath pH was examined with varying the kinds of catalyst and the scavenger, it was found that the pad bath pH influenced on the amount of formaldehyde release and the optimum pad bath pH is at 4.3. Especially, in case of finishing at pad bath pH 4.3 with adding Formamide, the amount of formaldehyde release was decreased by about $45\~$35\%$ with $Zn(NO_3)_2$, while by about $20\~$45\%$ with $MgCl_2$ catalyst. In case of varying the concentration of a scavenger (Formamide), $1\%$ concentration of a scavenger was found to be the optimum level ana the higher the curing temperature up to $180^{\circ}C$, the lesser the amount of formaldehyde release were observed. 3. When the diol was used as scavenger, the amount of formaldehyde release was decreased by about $40\~$50\%$, but the longer the intramolecular length between OH groups, the lessor the amount of decrease of formaldehyde release were observed. 4. When the mixture of scavengers (Formamide and Glycerol) was added in the pad bath, .synergistic effect on formaldehyde release between the two scavengers wasn't observed. 5. The tensile strength of the resin finished fabric was reduced with increasing the pad lath pH and was influenced by the kind of scavengers, and the tensile strength was severely reduced when scavengers, especially Formamide, was added. The wrinkle recovery property is generally improved by resin finish on cotton fabric. When Formamide was added, the wrinkle recovery property is slightly decreased compared with that of the fabrics resin finished without a scavenger, and when polyol was added, the wrinkle recovery property showed almost no change.

• Journal of the Korean Wood Science and Technology
• /
• 제35권2호
• /
• pp.39-50
• /
• 2007

The purpose of this study was to investigate the physico-mechanical properties and characteristics on reduction of formaldehyde and total volatile organic compound (TVOC) emission from particleboard (PB) with added volcanic pozzolan. Pozzolan was added as a scavenger at the level of 1, 3, 5, and 10 wt.% of urea formaldehyde (UF) resin for PB manufacture. The moisture content, density, thickness swelling, water absorption and physical properties of PBs were examined. Three-point bending strength and internal bond strength were determined using a universal testing machine. Formaldehyde and TVOC were determined by desiccator and 20L small chamber methods. With increasing pozzolan content the physical and mechanical properties of the PBs were not significantly changed, but formaldehyde and TVOC emissions were decreased. Because pozzolan has a rough and irregular surface with porous form, it can be used as a scavenger for PBs at a content up to 10 wt.% without any detrimental effect on the physical and mechanical properties.

• Journal of the Korean Wood Science and Technology
• /
• 제8권2호
• /
• pp.1-5
• /
• 1980

This study is carried out to determine the scavenging effect of resorcinol added into the urea formaldehyde resin on the formaldehyde release of plywood, as the preliminary study of using the phenolic substances. The method for formaldehyde determination used in this report is the improved chromotropic acid determination. The results are summarized as follows: 1. Resorcinol added into the urea formaldehyde adhesive acts as a good scavenger. 4 percent of resorcinol reduced the formaldehyde release to less than half content. 2. Adding resorcinol gave better glue shear strength than that of control, showing the peak of the shear strength, at 2 percent and decreased to the same strength as control along its content of 4 percent. 3. Moisture content of air dried plywood met the standard very well.

• Journal of the Korean Wood Science and Technology
• /
• 제22권1호
• /
• pp.44-53
• /
• 1994

This research was carried out to investigate the effect of paper sludge addition on formaldehyde emission, and physical and mechanical properties of UF-particleboard. In order to investigate the effect of paper sludge addition to resin, particleboards were bonded with urea-formaldehyde resins containing 5, 10, 15% paper sludge powders of three types(A Type: -200 mesh, B Type: -100~+200 mesh. C Type: -50~+100 mesh), based on weight of resin solid. Also the effect of paper sludge addition to furnish was studied from particleboards fabricated with ratios of sludge to particle of 5:95, 10:90, 15:85 based on oven-dry weight. Tests were conducted on the manufactured particleboards to determine formaldehyde emission, bending properties, internal bond strength and thickness swelling. The obtained results were summarized as follows: The addition of paper sludge powder to resin yielded a higher pH of cured resin. Formaldehyde emission decreased with the increase of paper sludge powder addition to resin and paper sludge composition ratio to furnish. Particleboard bonded with urea-formaldehyde resin containing paper sludge powder and particleboard mixed with paper sludge have similar bending properties(MOR, MOE) and thickness swelling compared with control particleboard. Internal bond strength of particleboards treated with paper sludge were lower than that of control particleboard. The use of paper sludge as scavenger was achieved reduction of formaldehyde emission without depression of physical and mechanical properties of particleboard. Also the use of paper sludge was able to concluded that there is possibility of partial substitution of wood particle materials.

• Journal of the Korean Wood Science and Technology
• /
• 제34권5호
• /
• pp.42-51
• /
• 2006

The this study, the effect of rice husk flour (RHF) as scavenger on formaldehyde emission rate and formaldehyde content from urea-formaldehyde (UF) resin bonded RHF content wood particleboards (PB). Two type of particle size ($30{\mu}m$ and $300{\mu}m$) of RHF was premixed with the UF resin at 5% and 15% by weight. The performance of UF resins is greatly influenced by the curing characteristics in their curing processing. The curing behavior was monitored activation energy ($E_a$) by DSC and pH variation according to RHF contents. PB with dimensions of $27cm{\times}27cm{\times}0.7cm$ was prepared at a specific gravity of 0.75 using $E_1$ and $E_2$ class UF resins. Formaldehyde emission and formaldehyde content from RHF filled PB bonded with UF resin was measured by 24 h desiccator and perforator method, respectively. RHF causes an increased pH of UF resin. $E_a$ of the modified UF resin decreased independently of RHF particle size. As the pH and the $E_a$ variation of the UF resin containing RHF increased, the amount of formaldehyde content decreased. The formaldehyde emission and formaldehyde content levels of the PB bonded with 15 wt% of $30{\mu}m$ RHF and $E_2$ type UF resin were low and satisfied grade $E_1$, as measured by 24 h desiccator and perforator method. The result of a comparison between 24 h desiccator and perforator test using PB showed that the linear regression analyses show a good correlation between the results for the 24 h desiccator and the perforator tests. The linear regression of a correlation between the desiccator and the perforator was Y=4.842X-0.064 ($R^2=0.989$). RHF was effective at reducing formaldehyde emission and formaldehyde content in urea-formaldehyde adhesives when used as scavenger.

• 한국염색가공학회지
• /
• 제9권2호
• /
• pp.41-49
• /
• 1997

To control free formaldehyde release from fabric finished with N-methylol compounds, resin finished cotton fabric was treated with resorcinol solution, dried and cured. Factors affecting to control formaldehyde release have been investigated. It was shown that the aftertreatment with resorcinol greatly suppressed the free formaldehyde release. Up to concentration of about 5% of resorcinol, the concentration of resorcinol effected on the control of free and evolved formaldehyde. And at high concentration of resorcinol, however, the concentration became rather insensitive to contol formaldehyde release. Addition of some salt catalysts such as ammonium chloride, zinc nitrate, sodium acetate and ammonium acetate, was effective in decreasing formaldehyde release. Considering the effect on the control of formaldehyde and crease recovery, ammonium acetate was concidered to be the best catalyst. It was observed that the optimum curing temperature for the resorcinol treatment was about 15$0^{\circ}C$, and that the curing time did not affected formaldehyde release over three minutes. Although the treatment of resorcinol had a little adverse effect on crease recovery of resin finished fabric, this effect could be negligible.

• Journal of the Korean Wood Science and Technology
• /
• 제32권1호
• /
• pp.80-87
• /
• 2004

천연접착제인 분말상 탄닌수지를 사용한 파티클보드의 물리·기계적 성질의 개선을 위하여 분말상 탄닌수지와 액상 탄닌수지를 혼합하여 사용한 결과, 30:70 (분말 : 액상)의 혼합비가 최적조건이었으며 분말상 탄닌 수지의 비율이 높으면 물성이 저하되는 현상을 볼 수 있었으며 또한 포름알데히드 방산량이 E₀ 수준의 고내수성 제품을 제조할 수 있었다. 한편 요소수지 및 멜라민수지와 분말상 탄닌 수지와의 혼합방법은 물리·기계적 성질의 개선에 영향을 주지 못했으며, 유리포름알데히드 방산에 대한 scavenger의 역할만을 하였다.