• Journal of the Korea institute for structural maintenance and inspection
• /
• v.25 no.6
• /
• pp.154-160
• /
• 2021

Recently, there have been increasing construction works carried out in urban centers, which are inducing frequent artificial vibration in the vicinity of existing structures due to such construction works. moreover, in case of industrial estates, vibration is induced due to operation of machines in the surrounding areas, thereby causing problems. meanwhile, in case of ordinary concrete that compose structure has low level of damping capability for vibration. accordingly, there are difficulties in blocking a wide range of vibrations delivered to the structures from outside including not only vibrations generated in the structures themselves but also ground vibration. recently, numerous studies are being carried out actively on high-damping system that markedly enhanced the damping performances of structures by utilizing polymer concrete in order to block the vibrations delivered to the structures through ground. therefore, this study compared the performances of polymer concrete with those of ordinary concrete, polyurethane pad and foamed rubber pad in order to review its performances in reducing ground vibration. for this purpose, review of FRF and vibration acceleration as dynamic characteristics was made. after comparative verification on the dynamic characteristics is made when polymer concrete and other aforementioned materials are applied to underground structures, the possibility of application of polymer concrete to structures is reviewed.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2003.05a
• /
• pp.35-38
• /
• 2003

The purpose of this study is to investigate the manufacture of light weight concrete panel using the artificial light-weight aggregate as a part of the substitution of foamed styrene and polyurethane because of narrow allocable temperature Bone in use. The experimental parameter of this study is 40, 60 and 8$0^{\circ}C$ of curing temperature at 100% relative humidity and the type of admixture such as cement, 6mm glass fiber and St/BA emulsion. Testing item is compressive and flexural strength and strength of specimen cured at standard condition is compared to that of specimen cured at 40, 60 and 8$0^{\circ}C$ of curing temperature at 100% relative humidity. As a result or this, it was revealed that the maximum or strength is developed in 6$0^{\circ}C$ or cure temperature at 100% relative humidity in case of the most of the specimen. Specimens modified by St/BA emulsion show the highest development of strength dependent on the curing tmeperature. So, it seems to be effective that evaporation curing method shoud be considered to curing the specimen as the panel core.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2015.05a
• /
• pp.169-170
• /
• 2015

This study is the experiment for manufacturing the Lightweight non-cement matrix based on the blast furnace slag, paper ash. Materials like cement and blowing agent in foamed concrete is replaced by by-products fro blast furnace slag and paper ash. Further, the experiment was performed by replacing alkali with nature gypsum and α type gypsum by (0, 5, 10, 15, 20) of weight of alkali (wt.%) in order to reduce the amount of expensive alkali-activator. Consequently, in the case of the density, plain showed the lowest density and it seems that specimen adding nature gypsum 5% has the best compressive strength and flexural strength. It is detemined that the strength is lowered in accordance with the α type gypsum replacement ratio is higher. The research that it can supplement the further intensity seems to be needed.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.125-126
• /
• 2021

In order to improve the housing culture, construction changes for the utilization of diverse and multifunctional spaces are appearing in response to the increasing diverse needs of consumers. Cellular Light-weight Concrete (CLC) is being developed for use in fire-resistant heat-insulating walls and non-bearing walls. However, manufacturing non-uniformity has become a problem as a drawback due to the use of foamed bubbles and normal temperature curing, and additional research is required. Therefore, in order to suppress cracks due to drying shrinkage, silica sand is mixed with CLC to try to understand its characteristics. In the experiment, the compressive strength from 7 to 28 days of age was measured via a constant temperature and humidity chamber, and the drying shrinkage was analyzed according to each condition using a strain gauge. The compressive strength of matrix tends to decrease as the substitution rate of silica sand increases. This is judged by the result derived from the fact that the specific surface area of silica sand is smaller than that of slag. Based on KS F 2701 (ALC block), the compressive strength of 0.6 products is 4.9 MPa or more as a guide, so the maximum replacement rate of silica sand that satisfies this can be seen at 60%. Looking at the change in drying shrinkage for just 7 days, the shrinkage due to temperature change and drying is 0.7 mm, and the possibility of cracking due to shrinkage can be seen, and it seems that continuous improvement and supplementation are needed in the future.

• Steel and Composite Structures
• /
• v.52 no.4
• /
• pp.391-403
• /
• 2024

The flexural behavior of composite sandwich wall panels with different thicknesses, numbers of holes, and hole forms, and arrangement form of longitudinal steel bar (uniform type and concealed-beam type) are investigated. A total of twelve composite sandwich wall panels are prepared, utilizing modified polystyrene particles mixed with foam concrete for the flexural performance test. The failure pattern of the composite sandwich wall panels is influenced by the extruded polystyrene panel (XPS) panel thickness and the reinforcement ratio in combination, resulting in both flexural and shear failure modes. Increasing the XPS panel thickness causes the specimens to transition from flexural failure to shear failure. An increase in the reinforcement ratio leads to the transition from flexural failure to shear failure. The hole form on the XPS panel and the steel bar arrangement form affect the loading behavior of the specimens. Plum-arrangement hole form specimens exhibit lower steel bar strain and deflection compared to linear-arrangement hole form specimens. Additionally, specimens with concealed beam-type steel bar display lower steel bar strain and deflection than uniform-type steel bar specimens. However, the hole form and steel bar arrangement form have a limited impact on the ultimate load. Theoretical formulas for cracking load are provided for both fully composite and non-composite states. When compared to the experimental values, it is observed that the cracking load of the specimens with XPS panels closely matches the calculations for the non-composite state. An accurate prediction model for the ultimate load of fully composite wall panels is developed. These findings offer valuable insights into the behavior of composite sandwich wall panels and provide a basis for predicting their performance under various design factors and conditions.

• Resources Recycling
• /
• v.29 no.1
• /
• pp.53-61
• /
• 2020

This study aimed to develop a foam concrete material for a ground repair system that has low strength and low fluidity by using an eco-friendly binder, which substitutes industrial by-products for more than 90% of cement. Basic properties were evaluated after substituting a small amount of calcium sulfo aluminate (CSA) for the binder to improve the sinking depth rate and volume change, commonly found when it had a large amount of industrial by-products. The substitution rates of CSA for the eco-friendly binder used for the foam concrete were 2.5, 5, and 10%. Fresh properties, hardened properties, pore structure, and hydrates were analyzed. Experimental results showed that using only 2.5% of CSA could improve the deep sinking depth which occurred when using an eco-friendly binder. As a result, the weight difference between the upper, middle, and lower parts of cast specimens was improved even after being hardened. The addition of CSA also contributed to the formation of small, uniformly sized closed pores and improved initial strength. However, when the proportion of CSA increased, the long-term strength decreased. However, it satisfied the target strength when 5% or less of CSA was used. The results of this study revealed that it was possible to manufacture foam concrete with low strength and high fluidity for repairing ground satisfying target qualities by adding 2.5% of CSA to the eco-friendly binder containing a large amount of industrial by-products.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.1
• /
• pp.74-79
• /
• 2022

In this study, the effect of a sudden decrease in internal humidity and a decrease in hydration level due to the tight internal structure of high-strength concrete and cement composites was investigated. To verify the change in the internal Si hydration, waste glass foam beads were used as a lightweight aggregate, and the internal unreacted hydrate reduction and hydrate formation tendency were identified over the mid- to long-term. Waste glass foam beads were mixed with 5, 10, and 20 %, and were used by pre-wetting. As the mixing rate of the waste glass foamed beads increased, the strength showed a tendency to decrease. In addition, when the mixing amount of pre-wetted waste glass foam beads increases inside through XRD analysis, TGA analysis, and Si NMR analysis, it is judged that the hydration degree of internal Si is different because moisture is supplied to the paste.