This paper presents experimental and analytical results on flexural behavior of flexural members made of SIFCON. Twelve SIFCON beams were subjected to bending tests and their flexural behavior was evaluated. Experimental variables included steel fiber type, presence of tensile reinforcement, and height of section. The specimens using Type-B steel fibers, which had better pullout resistance than Type-A steel fibers, showed flexural failure behavior without shear failure. The aspect ratio of steel fiber had a great influence on the behavior of SIFCON beams without tensile steel, however the effect on the behavior of SIFCON beams was negligible. In addition, the flexural strength equation for SIFCON was proposed in the study. The mean and standard deviation of the ratios of the predicted value to the experimental value are 1.02 and 0.04, respectively. Therefore, the proposed flexural strength equation can be useful for the design and performance evaluation of SIFCON beam.

• International Journal of Highway Engineering
• /
• v.18 no.6
• /
• pp.105-113
• /
• 2016

OBJECTIVES : This study is to develop the optimum mixing proportions for cement concrete pavement with using recycled aggregates. METHODS : The mixture varied recycled coarse aggregates content from 50 % to 100 % to replace the natural coarse aggregates by weight. Tests for fundamental properties as a cement concrete pavement were conducted before and after hardening of the concrete. RESULTS : It was found that the variation in the amount of the recycled aggregate affected the compressive and flexural strength development, as well as the chloride ion penetration resistance. As the amount of the recycled aggregate content increased the compressive and flexural strength and the resistance to chloride ion penetration decreased. However, the resistance to freeze-thaw reaction was affected significantly. In addition, the gradation of the aggregate became worse and hence so did the coarseness factor as the recycled aggregate amount increased. CONCLUSIONS : The fundamental properties of the concrete with recycled aggregate does not seem to be appropriate when the recycled aggregate quality is not guaranteed up to a some level and its replacement ratio is over 50%. The optimized gradation of the aggregates should also be sought when the recycled aggregate is used for the cement concrete pavement materials.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.47 no.7
• /
• pp.25-33
• /
• 2005

This study was performed to develop environment-friendly porous polymer concrete utilizing recycled aggregates [RPPC] for permeable pavement of uniform quality with high permeability and flexural strength as well as excellent freezing and thawing resistance. The void ratios of RPPC are in the range of 15$\sim$$24\%$, showing the tendency that it is reduced to a great extent as the mixing ratio of the binder increases. The compressive and flexural strength of RPPC are in the range of 19$\sim$26 MPa and 6.2$\sim$7.4 MPa, respectively. Also, it shows a tendency to increase as the mixing ratio of the binder and filler increases. The permeability coefficients of RPPC are in the range of $6.3\times$$10_{-1}$$\sim$$1.5\times$$10_{-2}$cm/s. The flexural loads of RPPC are in the range of 18$\sim$32 KN. The weight reduction ratios obtained from the test for freezing and thawing resistance are in the range of 1.1$\sim$$2.4\%$ after 300 cycles of repeated freezing and thawing of the specimen for all mixes. The relative compressive strengths of RPPC after 300 cycles of freezing and thawing against the compressive strength before freezing and thawing test are in the range of 89$\sim$$96\%$.

• Journal of Korean Society of Steel Construction
• /
• v.26 no.3
• /
• pp.205-217
• /
• 2014

In this study, flexural strength and ductility requirements of composite hybrid steel I-girder with its HSB(high performance steel for bridge) applied to tension flanges are examined in positive bending. In AASHTO LRFD specification, flexural strength and ductility requirements of composite I-girder in positive bending are specified in terms of plastic moment and plastic neutral axis that are derived from plastic behavior of conventional steel. However, plastic zone cannot be defined clearly from the stress-strain behavior of HSB unlike the behavior of conventional steel. Therefore, through idealized stress-strain curves of HSB, the plastic moment of composite hybrid steel I-girder with its HSB applied to tension flanges is defined by assuming the plastic zone of HSB. By using the consequences of numerical analysis regarding arbitrary cross-sections that have various dimensions, ductility requirements and flexural strength of composite hybrid I-girder with its HSB applied to tension flange are proposed.

• Journal of the Korea Concrete Institute
• /
• v.17 no.4 s.88
• /
• pp.595-602
• /
• 2005

The purpose of this study is to utilize recycled concrete aggregates as permeable pavement materials. This study evaluates mechanical properties and durability of porous concrete depending on mixing rates of recycled aggregates and polyme. As a result, void ratio and permeability coefficient of porous concrete for pavement increased a little as mixing rate of recycled aggregates increased. Void ratio and permeability coefficient increased a lot as mixing rate of polymer increased. As polymer was mixed $20\%$, national regulation of permeable concrete for pavement($8\%$ and 0.01cm/sec) was met. Compressive strength and flexural strength decreased as mixing rate of recycled aggregates increased but they increased a lot as mixing rate of polymer increased. Even when recycled aggregates were mixed $75\%\;with\;10\%$ polymer mixed, national regulation of pavement concrete(18MPa and 4.5MPa) was met. In addition, regarding sliding resistance, BPN increased as mixing rate of recycled aggregates increased. But BPN decreased as polymer was mixed. Compared to crushed stone aggregates, abrasion resistance and freeze-thaw resistance decreased as mixing rate of recycled aggregates Increased. When polymer was mixed, abrasion resistance and freeze-thaw resistance improved remarkably. Compared to non-mixture, $10\%$ mixture of polymer improved abrasion resistance and freeze-thaw resistance about $8.6\%$ and 3.8times respectively.

• Computers and Concrete
• /
• v.17 no.3
• /
• pp.337-351
• /
• 2016

This paper presents the properties of pervious concrete containing high-calcium fly ash. The water to binder ratios of 0.19, 0.22, and 0.25, designed void ratios of 15, 20, and 25%, and fly ash replacements of 10, 20, and 30% were used. The results showed that the use of fly ash as partial replacement of Portland cement enhanced the mixing of paste resulting in a uniform mix and reduced amount of superplasticizer used in the mixture. The compressive strength and flexural strength of pervious concrete were slightly reduced with an increase in fly ash replacement level, while the abrasion resistance increased due mainly to the pozzolanic and filler effects. The compressive strength and flexural strengths at 28 days were still higher than 85% of the control concrete. The aggregate size also had a significant effect on the strength of pervious concrete. The compressive strength and flexural strength of pervious concrete with large aggregate were higher than that with small aggregate.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.2
• /
• pp.75-86
• /
• 2012

This paper presents some research results on the shrinkage characteristics and frost resistance before and after cracking of FR-ECC(Fire Resistance-Engineered Cementitious Composite). Also, a waterstop performance and exfoliating resistance of multi-layer lining specimens using FR-ECC and flexural performance of beam member by repaired FR-ECC are estimated in this paper. Experimental results indicate that the plastic shrinkage crack and length change ratio of FR-ECC have been reduced as compared with that of the existing repair mortar, and that its crack resistance on the dry shrinkage is improved under the confining stress. As well as FR-ECC has been great in the frost resistance and its tensile properties under the cracked state have been not reduced by freezing and thawing reaction. In addition, beam member by repaired FR-ECC have been increased in the flexural properties such as initial crack moment, yeild moment, and its crack width has been controled in a stable by the frexural failure.

• Journal of Adhesion and Interface
• /
• v.23 no.4
• /
• pp.137-143
• /
• 2022

In this study, the polyurethane acrylates (PUA) resin with good adhesive and flexibility for adhesive for shoes and clothing were synthesized using that poly(tetramethylene adiphate glycol) (PTAd), poly(tetramethylene ether glycol) (PTMG) as polyester polyol and polyether polyol respectively, including 4,4'-methylene diphenyl diisocyanate (MDI), isophorone diisocyanate (IPDI), 1,4-butandiol (1,4-BD), 2-hydroxyethyl methacrylate (2-HEMA) and dibutyl amine (DBA). The effect of polyol blend in the polyurethane acrylate on thermal and mechanical properties, adhesion strength and flexural strength were studied. The glass transition temperature (T_g) of PUA was confirmed in range of -70~-40 ℃. In addition, the glass transition temperature (T_g), decomposition temperature (T_d), tensile strength adhesion strength and heat resistance were increased as increasing of PTAd amount while the elongation, water resistance and flexural properties were decreased. The synthesized polyurethane acrylate with 5:5 ratio of PTAd and PTMG indicated the highest adhesion strength and flexural properties.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.15 no.2
• /
• pp.161-169
• /
• 2011

Two-way slabs reinforced with high-performance steels, which have several practical advantages of a reduction of congestion in heavily reinforced members, savings in the cost of labor and repair, the higher corrosion resistance, and a reduction of construction time, were constructed and tested. The influences of the flexural reinforcement ratio, concentrating the reinforcement in the immediate column region, and using steel fiber-reinforced concrete (SFRC) in the slab on the punching shear resistance and post-cracking stiffness were investigated, and compared with the punching shear test results of the slabs reinforced with conventional steels and GFRP bars. In addition, the strain distribution of flexural reinforcements and crack control were investigated, and the effective width calculating method for the average flexural reinforcement ratio was estimated. The use of high-performance steel reinforcement increased the punching shear strength of slabs, and decreased the amount of flexural reinforcements. The concentrating the top mat of flexural reinforcement increased the post-cracking stiffness, and showed better strain distribution and crack control. In addition, the use of SFRC showed beneficial effects on the punching shear strength and crack control. It was suggest that the effective width should be changed to larger than 2 times the slab thickness from the column faces.

• Korean Chemical Engineering Research
• /
• v.49 no.1
• /
• pp.120-127
• /
• 2011

For the development of the environment-friendly insulating composite materials, natural cellulose (wood chip and sawdust) was used as a core material and activated Hwangtoh was used as a binder. Various specimens were prepared with the water/binder ratio and natural cellulose/binder ratio. The physical properties of these specimens were then investigated through compressive and flexural strength test, absorption test, hot water resistance test, thermal conductivity, measurement of pore distribution and observation of micro-structures using scanning electron microscope (SEM). Results showed that the absorption ratio increased with the increase of natural cellulose/binder ratio but decreased remarkably with the increase of polymer/binder ratio. The compressive and flexural strength development varied appreciably with the increase of water/binder ratio and natural cellulose/binder ratio. On the other hand, thermal conductivity decreased with the increase of natural cellulose/binder ratio and polymer/binder ratio. Through SEM, it was found that activated Hwangtoh that reacted with water formed a hydrate crystal leading to the compact structure and the total pore volume of the specimen using activated Hwangtoh was smaller than that of the non-activated Hwangtoh.