• Proceedings of the Materials Research Society of Korea Conference
• /
• 2000.11a
• /
• pp.39-39
• /
• 2000

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.87-90
• /
• 2002

In recent year, BLT($Bi_{3.25}La_{0.75}Ti_{3}O_{12}$) has been one of promising substitute materials at the ferroelectric random access memory applications. We manufactured $Bi_{3.25}La_{0.75}Ti_3O_{12}$ Target with a ceramic process. The BLT target was sintered at ${1100^{\circ}C}$ for 4 hours. Using RF magnetron sputtering, a deposited BLT thin films were estimated about ferroelectric properly as a functions of post annealing temperatures. The BLT thin films showed a promoted ferroelectric characteristics at the post annealied sample of ${700^{\circ}C}$. This sample exhibited the (117) preferred crystal orientation, current density of $3{\times}10^{-8}A/cm^2$, a remanent polarization of $8{\mu}C/cm^2$ and a coercive field of 42.1 KV/cm respectively.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.11C no.2
• /
• pp.18-22
• /
• 2001

The thin films of high permitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)TiO$_3$ thin as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Sio$_2$/Si substrate at 4,000 [rpm] for 10 seconds. The structural characteristics of the surface were analyzed by fractal dimension. The thickness of BST ceramics thin films was about 260∼280 [nm]. The property of the leakage current was stable with 10-9∼10-11[A] when the applied voltage was 0∼3[V]. BST thin films ha low leakage current properties when fractal dimension was low and a coating area was high.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.55 no.12
• /
• pp.549-554
• /
• 2006

In this paper we first applied the chemical mechanical polishing (CMP) process to the planarization of ferroelectric film in order to obtain a good planarity between electrode and ferroelectric film. $Pb_{1.1}(Zr_{0.52}Ti_{0.48})O_3$ (shortly PZT) ferroelectric film was fabricated by the sol-gel method. And then, we compared the structural characteristics before and after CMP process of PZT films. Removal rate, WIWNU% and surface roughness have been found to depend on slurry abrasive types and their hardness, especially, surface roughness and planarity were strongly depends on its pH value. A maximum in the removal rate is observed in the silica slurry, in contrast with the minimum removal rate occurs at ceria slurry. We found that the surface roughness of PZT films can be significantly reduced using the CMP technique.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.107-108
• /
• 2005

In this paper, we first applied the chemical mechanical polishing (CMP) process to the planarization of ferroelectric film in order to obtain a good planarity of electrode/ferroelectric film interface. $Pb_{1.1}(Zr_{0.52}Ti_{0.48})O_3$ (shortly PZT) ferroelectric film was fabricated by the sol-gel method. And then, we compared the structural characteristics before and after CMP process of PZT films. Their dependence on slurry composition was also investigated. We expect that our results will be useful promise of global planarization for ferroelectric random access memories (FRAM) application in the near future.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.309-312
• /
• 2002

Ferroelectric $Sr_{0.3}Ba_{0.7}Nb_{2}O_{6}$ (SBN30) thin films were deposited on Pt/Ti/$SiO_{2}$/Si(100) substrates by ion beam sputtering. During annealing treatment at $750^{\circ}C$, poling was attempted by applying dc voltage bias across polished surfaces. Phase relation, microstructure and crystallization behavior were examined using XRD and FE-SEM. Ferroelectric hysteresis characteristics were also determined where both remanent polarization and coercive values decreased with the increase of bias voltage. The measured remanent polarization and coercive field values at 5 V and 10 V bias were $36{\mu}C/cm^2$, $10{\mu}C/cm^2$ and 100kV /cm, 80kV /cm, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.05a
• /
• pp.103-104
• /
• 2006

In this paper. we first applied the chemical mechanical polishing (CMP) process to the planarization of ferroelectric film in order to obtain a good planarity of electrode/ferroelectric film interlace. $Pb_{1.1}(Zr_{0.52}Ti_{0.48})O_3$ (shortly PZT) ferroelectric film was fabricated by the sol-gel method. And then. we compared the structural characteristics before and alter CMP process of PZT films. Their dependence on slurry composition was also investigated. We expect that our results will be useful promise of global planarization for ferroelectric random access memories (FRAM) application in the near future.

• Transactions on Electrical and Electronic Materials
• /
• v.7 no.2
• /
• pp.72-75
• /
• 2006

Ferroelectric PZT heterolayered thick films were fabricated by the alkoxide-based sol-gel method. PZT(Zr/Ti=60/40) paste was made and alternately screen-printed on the $Al_2O_3$ substrates. We have introduced a press-treatment to obtain a good densification of screen printed films. The porosity of the thick films was decreased with increasing the applied pressure and the thick films pressed at $0.6ton/cm^2$ showed the dense microstructure and thickness of about $76{\mu}m$. The relative dielectric constant increased with increasing the applied pressure. The remanent polarization and coercive field increased with increasing applied pressure and the values for the PZT thick films pressed at $0.6ton/cm^2$ were $16.6{\mu}C/cm^2$, 76.9 kV/cm, respectively.

• Journal of the Korean Ceramic Society
• /
• v.32 no.12
• /
• pp.1408-1416
• /
• 1995

Microstructure and ferroelectric properties of sol-gel derived PZT(52/48) and PT interlayered PZT(52/48) thin films on Pt/Ti/SiO2/Si substrates were investigated. Films were fabricated using Acetylacetone chelated PT and PZT(52/48) sols. PZT(52/48) thin films annealed at $700^{\circ}C$ for 20 min showed the rosette structure with the size of 1.2~1.6${\mu}{\textrm}{m}$ and the pyrochlore phse was contained. PT interlayered PZT thin films, which is inserted by PbTiO3 thin layer with the thickness of 130 $\AA$ between PZT thin film and electrode, consisted of a single perovskite phase after annealing above 55$0^{\circ}C$. They exhibited the uniform and columnar grains of 0.1~0.16${\mu}{\textrm}{m}$, which are applicable for microelectronic device including non-volatile memory. Typical P-E hysteresis loops could be obtained from PT interlayered PZT thin film at as low as the annealing temperature of 50$0^{\circ}C$. Ferroelectric properties of PT interlayered PZT thin films were improved as increasing annealing temperature up to $700^{\circ}C$, and then deteriorated at 75$0^{\circ}C$. PZT(52/48) and PT interlayered PZT(52/48) thin film annealed at $700^{\circ}C$ for 20 min displayed Ps=38.8$\mu$C/$\textrm{cm}^2$, Pr=10.0$\mu$C/$\textrm{cm}^2$, Ec=65.3 kV/cm and Ps=28.5$\mu$C/$\textrm{cm}^2$, Pr=9.8$\mu$C/$\textrm{cm}^2$, Ec=76.1 kV/cm, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.12 no.1
• /
• pp.62-68
• /
• 1999

Ferroelectric $Sr_{0.7}/B_{2.3}(Ta_{1-x}Nb_x)_2O_9$(x=0, 0.1, 0.2, 0.3) thin films were deposited on $Pt/SiO_2/Si$ substrate by MOD(Metalorganic Decomposition) process. Metal carboxylate and metal alkoxide were used as precursors, and 2-methoxyethanol, xylene as solvents. After spin coating, thin films were pre-annealed at $400^{\circ}C$, followed by RTA(Rapid Thermal Annealing) and final annealing at $800^{\circ}C$ in oxygen atmosphere. These procedures were repeated three times to obtain thin films with the thickness of $2000{\AA}$. To enhance the nucleation and growth of layered-perovskite phase, thin films were rapid-thermally annealed above $720^{\circ}C$ in oxygen atmosphere. As RTA temperature increased, fluorite phase was transformed to layered-perovskite phase. And the change of Nb contents affected dielectric / electrical properties and microstructure. The ferroelectric characteristics of $Sr_{0.7}/B_{2.3}(Ta_{1-x}Nb_x)_2O_9$ thin film were Pr=8.67 $\mu{C}/cm^2$, Ec=62.4kV/cm and $I_{L}=1.4\times10^{-7}A/cm^2$ at the applied voltage of 5V, respectively.