• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.916-919
• /
• 2000

A great deal of research has been done in the field of characterization for piezoelectric thin films after the first report on the measurement for the piezoelectric coefficient of thin films in 1990. The main idea of this research is to provide a distinctive solution for the measurement of both the longitudinal and the transverse piezoelectric d-coefficients, d$\sub$33/ and d$\sub$3l/, of ferroelectric thin films and also thick films. In general, to get these two coefficients of thin films, two different measuring systems are required. Here, we propose the improved method for the evaluation of these two coefficients with single equipment and with the relatively convenient procedure. The two-step loading process of applying the both positive and the negative pressure has been designed to acquire the piezoelectric coefficients. These results have beer calibrated for both the longitudinal and the transverse piezoelectric d-coefficients, d$\sub$33/ and d$\sub$31/, of thin films. In the first stage of the experiments, we have obtained d$\sub$33/ of 108pC/N and d$\sub$31/ of 57pC/N for the PZT thin films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.11a
• /
• pp.287-290
• /
• 1998

It was investigated that the dielectric properties of ferroelectric materials using PZT-5A and PZT thin films. PZT-5A was 20mm diameters, 0.71mm, 0.51mm and 0.41mm thickness respectively and having c-axis preferred orientation. Electrodes(Al) were deposited by evaporation method. PZT thin film was deposited on Pt/SiO$_2$/Si substrate by RF magnetron sputtering method, and annealed at 750$^{\circ}C$ with RTA. Dielectric constants were measured automatically by computer measuring system. Dielectric constants were changed rapidly from 817 to 888 in 0.41mm thickness PZT-5A, 823 to 890 in 0.51mm and 822 to 839 in 0.71mm as the electric field grown. In the case of PZT thin film, dielectric constants were changed from 724 to 1173 in 4500${\AA}$ thickness, 721 to 1204 in 5500${\AA}$ thickness and 811 to 1407 in 7000${\AA}$ thickness.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.12
• /
• pp.1283-1288
• /
• 2004

Metal-ferroelectric-insulator-semiconductor(WFIS) capacitors using rapid thermal annealed LiNbO$_3$/AlN/Si(100) structure were fabricated and demonstrated nonvolatile memory operations. The capacitors on highly doped Si wafer showed hysteresis behavior like a butterfly shape due to the ferroelectric nature of the LiNbO$_3$ films. The typical dielectric constant value of LiNbO$_3$ film in the MFIS device was about 27, The gate leakage current density of the MFIS capacitor was 10$^{-9}$ A/cm$^2$ order at the electric field of 500 kV/cm. The typical measured remnant polarization(2P$_{r}$) and coercive filed(Ec) values were about 1.2 $\mu$C/cm$^2$ and 120 kV/cm, respectively The ferroelectric capacitors showed no polarization degradation up to 10$^{11}$ switching cycles when subjected to symmetric bipolar voltage pulses of 1 MHz. The switching charges degraded only by 10 % of their initial values after 4 days at room temperature.e.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.211.2-211.2
• /
• 2014

Epitaxial complex oxide thin film heterostructures have attracted a great attention for their multifunctional properties, such as ferroelectricity, and ferromagnetism. Two dimensional electron gas (2DEG) confined at the interface between two insulating perovskite oxides such as LaAlO3/SrTiO3 interface, provides opportunities to expand various electronic and memory devices in nano-scale. Recently, it was reported that the conductivity of 2DEG could be controlled by external electric field. However, the switched conductivity of 2DEG was not stable with time, resulting in relaxation due to the reaction between charged surface on LaAlO3 layer and atmospheric conditions. In this report, we demonstrated a way to control the conductivity of 2DEG in non-volatile way integrating ferroelectric materials into LAO/STO heterostructure. We fabricated epitaxial Pb(Zr0.2Ti0.8)O3 films on LAO/STO heterostructure by pulsed laser deposition. The conductivity of 2DEG was reproducibly controlled with 3-order magnitude by switching the spontaneous polarization of PZT layer. The controlled conductivity was stable with time without relaxation over 60 hours. This is also consistent with robust polarization state of PZT layer confirmed by piezoresponse force microscopy. This work demonstrates a model system to combine ferroelectric material and 2DEG, which guides a way to realize novel multifunctional electronic devices.

• Transactions on Electrical and Electronic Materials
• /
• v.5 no.2
• /
• pp.66-70
• /
• 2004

The Sr$\_$0.7/Bi$\_$2.3/Ta$_2$O$\_$9/(SBT)thin films are deposited on Pt-coated electrode (Pt/TiO$_2$/SiO$_2$/Si) using a RE magnetron sputtering method. The ferroelectric properties of SBT capacitors with annealing times were studied. As a result of conducting the X-ray diffraction analysis and the electron microscopy analysis, the perovskite phase began to grow from 10 minutes after annealing the specimen, and excellent crystallization was accomplished at 60 minutes after annealing the specimen. The remanet polarization (2P$\_$r/) value and the coercive electric field (E$\_$c/) of the SBT thin film specimen showed the most excellent characteristics at 60 minutes after annealing the specimen, which were approximately 12.40 C/$\textrm{cm}^2$ and 30 kV/cm, respectively. The leakage current density of the SBT thin film specimen as annealed for 60 minutes was approximately 2.81${\times}$10$\^$－9/A/$\textrm{cm}^2$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.4
• /
• pp.314-318
• /
• 2002

The etching behaviors of the ferroelectric $YMnO_3$ thin films were studied by an inductively coupled plasma (ICP). The maximum etch rate of $YMnO_3$ thin film is 300 ${\AA}/min$ at Ar/$Cl_2$of 2/8, RF power of 800W, dc bias voltage of 200V, chamber pressure of 15mTorr and substrate temperature of $30^{\circ}C$. Addition of $CF_4$ gas decrease the etch rate of $YMnO_3$ thin film. From the results of XPS analysis, nonvolatile $YF_x$ compounds were found on the surface of $YMnO_3$ thin film which is etched in Ar/$Cl_2$/CF$_4$plasma. The etch profile of YMnO$_3$film is improved by addition of $CF_4$ gas into the Ar/$Cl_2$ plasma. These results suggest that YF$_{x}$ compound acts as a sidewall passivants which reduce the sticking coefficient of chlorine on $YMnO_3$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.171-172
• /
• 2007

We fabricated the metal-ferroelectric-insulator-semiconductor filed-effect transistors (MFIS-FETs) using the $(Bi,La)_4Ti_3O_{12}\;and\;LaZrO_x$ thin films. The $LaZrO_x$ thin film had a equivalent oxide thickness (EOT) value of 8.7 nm. From the capacitance-voltage (C-V) measurements for an Au/$(Bi,La)_4Ti_3O_{12}/LaZrO_x$/Si MFIS capacitor, a hysteric shift with a clockwise direction was observed and the memory window width was about 1.4 V for the bias voltage sweeping of ${\pm}9V$. From drain current-gate voltage $(I_D-V_G)$ characteristics of the fabricated Fe-FETs, the obtained threshold voltage shift (memory window) was about 1 V due to ferroelectric nature of BLT film. The drain current-drain voltage $(I_D-V_D)$ characteristics of the fabricated Fe-FETs showed typical n-channel FETs current-voltage characteristics.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.38 no.12
• /
• pp.8-13
• /
• 2001

Cerium oxide ($CeO_2$) thin film has been proposed as a buffer layer between the ferroelectric thin film and the Si substrate in Metal-Ferroelectric-Insulator-Silicon (MFIS) structures for ferroelectric random access memory (FRAM) applications. In this study, $CeO_2$ thin films were etched with $Cl_2$/Ar gas mixture in an inductively coupled plasma (ICP). Etch properties were measured for different gas mixing ratio of $Cl_2$($Cl_2$+Ar) while the other process conditions were fixed at RF power (600 W), dc bias voltage (-200 V), and chamber pressure (15 mTorr). The highest etch rate of $CeO_2$ thin film was 230 ${\AA}$/min and the selectivity of $CeO_2$ to $YMnO_3$ was 1.83 at $Cl_2$($Cl_2$+Ar gas mixing ratio of 0.2. The surface reaction of the etched $CeO_2$ thin films was investigated using x-ray photoelectron spectroscopy (XPS) analysis. There is a Ce-Cl bonding by chemical reaction between Ce and Cl. The results of secondary ion mass spectrometer (SIMS) analysis were compared with the results of XPS analysis and the Ce-Cl bonding was monitored at 176.15 (a.m.u). These results confirm that Ce atoms of $CeO_2$ thin films react with chlorine and a compound such as CeCl remains on the surface of etched $CeO_2$ thin films. These products can be removed by Ar ion bombardment.

• The Korean Journal of Ceramics
• /
• v.6 no.2
• /
• pp.110-115
• /
• 2000

$SrBi_2Ta_2O_9$ thin films were deposited at room temperature on the usual (111) oriented Pt bottom electrodes using r.f. magnetron sputtering, and then post-annealed at 650-$800^{\circ}C$ for 30min in oxygen flow. Low temperature processing which shows the preferred oriented SBT thin films was obtained by controlling the sputtering pressure and/or Sr content in target. The orientation and grain growth behavior of SBT thin films were dependent on Sr contents in films. With increasing the excess Bi content up to 50% in SBT thin films, it was possible to lower the onset temperature of grain growth. The c-axis preferred oriented SBT thin films were well-grown under the condition of low post-annealing($650^{\circ}C$) by lowering post-annealing pressure. After $10^{11}$ switching cycles, no polarization degradation was observed in both preferred oriented SBT capacitors.

• Transactions on Electrical and Electronic Materials
• /
• v.6 no.5
• /
• pp.210-213
• /
• 2005

The $BaTiO_3/SrTiO_3$ heterolayered thick films were fabricated by the screen printing method on alumina substrates. The effect of the sintering temperature on the microstructure and dielectric properties of the $BaTiO_3/SrTiO_3$ thick films has been investigated. The relative dielectric constant and dielectric loss at 1 MHz of the $BaTiO_3/SrTiO_3$ heterolayered thick films with sintering temperature of $1350^{\circ}C$ were about 751 and 1.74, respectively. The remanent polarization $(P_r)$ of the pure $(Ba_{0.5}Sr_{0.5})TiO_3$ and $BaTiO_3/SrTiO_3$ heterolayered films are approximately $5.1\;{\mu}C/cm^2$ and $10\;{\mu}C/cm^2$. This study suggests that the design of the $BaTiO_3/SrTiO_3$ heterolayered thick films capacitor with different phase should be an effective method to enhance the dielectric and ferroelectric performance in devices.