• 한국분말재료학회지
• /
• 제18권6호
• /
• pp.526-531
• /
• 2011

Fecralloy is the promising materials for high temperature exhaust filtering system due to the excellent its oxidation resistance property. In this research, Fecralloy nanoparticles coated Fecralloy thin foil was prepared by a single nozzle electrospray system in order to increase surface area of Fecralloy foil. Fecralloy nanoparticles were fabricated by electrical wire explosion method in ethanol using Fecralloy wires as a source material. Electrospray modes with applied D.C voltages to Fecralloy colloidal solution were investigated to make a stable cone-jet mode. Coated layers with and without additional heat treatment were observed by FE-SEM (field emission-scanning electron microscope) and tape test for evaluating their adhesion to substrate were performed as well.

• 한국분말재료학회지
• /
• 제24권1호
• /
• pp.46-52
• /
• 2017

Fecralloy coating layer with large surface area is suitable for use as a filter media for efficient removal of hot gaseous pollutants exhausted from combustion processes. For uniform preparation of a Fecralloy coating layer with large surface area and strong adhesion to substrate, electrospray coating and thermal treatment processes are experimentally optimized in this study. A nano-colloidal solution with 0.05 wt% Fecralloy nanoparticles is successfully prepared. Optimized electrospraying conditions are experimentally discovered to prepare a uniform coating layer of Fecralloy nano-colloidal solution on a substrate. Drying the electrospray coated Fecralloy nano-colloidal solution layer at $120^{\circ}C$ and subsequent heating at $600^{\circ}C$ are the best post-treatment for enhancing the adhesion force and surface roughness of the Fecralloy coating layer on a substrate. An electrospray coating system, consisting of several multi-groove nozzles, is also experimentally confirmed as a reasonable device for uniform coating of Fecralloy nano-colloid on a large area substrate.

• 한국분말재료학회지
• /
• 제23권6호
• /
• pp.426-431
• /
• 2016

The Fe-Cr-Al alloy system shows an excellent heat resistance because of the formation of an $Al_2O_3$ film on the metal surface in an oxidizing atmosphere at high temperatures up to $1400^{\circ}C$. The Fecralloy needs an additive that can act as a binder because of its bad compactability. In this study, the green compacts of STS434L and Al powder added to Fecralloy are oxidized at $950^{\circ}C$ for up to 210 h. Fecralloy and Al is mixed by two types of ball milling. One is vented to air and the other was performed in a sealed jar. In the case of Al addition, there are no significant changes in the electrical resistance. Before the oxidation test, Al oxides are present in the Fecralloy surface, as determined from the energy dispersive spectroscopy results. The addition of Al improves the compactability because of an increased density, and the addition of STS434L increases the electrical resistivity by forming a composite oxide.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1996년도 재료학회 추계학술발표회
• /
• pp.10-10
• /
• 1996

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1997년도 한국재료학회 추계학술발표회
• /
• pp.23-23
• /
• 1997

• 한국분말재료학회지
• /
• 제24권4호
• /
• pp.292-297
• /
• 2017

A metallic oxide layer of a heat-resistant element contributes to the high-temperature oxidation resistance by delaying the oxidation and has a positive effect on the increase in electrical resistivity. In this study, green compacts of Fecralloy powder mixed with amorphous and crystalline silica are oxidized at $950^{\circ}C$ for up to 210 h in order to evaluate the effect of metal oxide on the oxidation and electrical resistivity. The weight change ratio increases as per a parabolic law, and the increase is larger than that observed for Fecralloy owing to the formation of Fe-Si, Fe-Cr composite oxide, and $Al_2O_3$ upon the addition of Si oxide. Si oxides promote the formation of $Al_2O_3$ and Cr oxide at the grain boundary, and obstruct neck formation and the growth of Fecralloy particles to ensure stable electrical resistivity.

• 한국분말재료학회지
• /
• 제23권3호
• /
• pp.240-246
• /
• 2016

In order to improve the high-temperature oxidation stability, sintered 434L stainless steel is studied, focusing on the effect of the addition of metallic oxides to form stable oxide films on the inner particle surface. The green compacts of Fecralloy powder or amorphous silica are added on STS434L and oxidized at $950^{\circ}C$ up to 210 h. The weight change ratio of 434L with amorphous silica is higher than that of 434L mixed with Fecralloy, and the weight increase follows a parabolic law, which implies that the oxide film grows according to oxide diffusion through the densely formed oxide film. In the case of 434L mixed with Fecralloy, the elements in the matrix diffuse through the grain boundaries and form $Al_2O_3$ and Fe-Cr oxides. Stable high temperature corrosion resistance and electrical resistivity are obtained for STS434L mixed with Fecralloy.

• 한국분말재료학회지
• /
• 제19권6호
• /
• pp.435-441
• /
• 2012

A new manufacturing process of Fe-Cr-Al powder porous metal was attempted. First, ultra-fine fecralloy powders were produced by using the submerged electric wire explosion process. Evenly distributed colloid (0.05~0.5% powders) was dispersed on PU (Polyurethane) foam through the electrospray process. And then degreasing and sintering processes were conduced. In order to examine the effect of sintering temperature in process, pre-samples were sintered for two hours at temperatures of $1350^{\circ}C$, $1400^{\circ}C$, $1450^{\circ}C$, and $1500^{\circ}C$, respectively, in $H_2$ atmospheres. A 24-hour TGA (thermo gravimetric analysis) test was conducted at $1000^{\circ}C$ in a 79% $N_2$+21% $O_2$ to investigate the high temperature oxidation behavior of powder porous metal. The results of the high temperature oxidation tests showed that oxidation resistance increased with increasing sintering temperature (2.57% oxidation weight gain at $1500^{\circ}C$ sintered specimen). The high temperature oxidation mechanism of newly manufactured Fe-Cr-Al powder porous metal was also discussed.

• 전기화학회지
• /
• 제7권2호
• /
• pp.94-99
• /
• 2004

연료극 지지체 평관형 고체산화물 연료전지(SOFC)의 셀 전력밀도를 증가시키기 위하여 압출법에 의하여 제조하고 그 특성을 연구하였다. 연료극 지지체로써 Ni/YSZ($8mol\%$ yttria stabilized zirconia) cermet는 기공율 $50.6\%,\;0.23{\mu}m$의 기공크기를 나타내었다. 지지체에서의 Ni의 분포는 균일하였으며 전자전도 경로로써의 Ni의 연결성은 양호하였다. 지지체에 YSZ전해질과 복합 공기극층인 $LSM((La_{0.85}Sr_{0.15})_{0.9}MnO_3)/YSZ$ 복합층, LSM, LSCF $(La_{0.6}Sr_{0.4}Co_{0.2}Fe_{0.8}O_3)$층이 슬러리 디핑법에 의하여 코팅 및 소결된 연료극 지지체식 평관형 고체산화물 연료전지 단위전지의 성능은 $800^{\circ}C$에서 $300mW/cm^2(0.6V,\;500mA/cm^2)$의 성능을 나타내었다. 임피던스 분석에 의하여 평관형 셀의 전기화학적 분극저항을 평가하고 연료측의 가습에 따라 분극저항이 감소되어 성능이 향상됨을 알 수 있었다 슬러리 디핑법으로 LSM이 코팅된 SUS430 금속연결재를 $Ar+10\%\;H_2$에서 소결하였으며, $750^{\circ}C$에서 면저항의 측정할 결과, 초기에는 $148m{\Omega}cm^2$를 나타내었으며, 450시간 경과 후에 $43m{\Omega}cm^2$의 낮은 면저항을 유지하였다. 반면에 동일한 조건으로 LSM이 코팅된 Fecralloy는 높은 면저항을 나타내었다.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2010년도 춘계학술대회 초록집
• /
• pp.230.2-230.2
• /
• 2010

천연가스 수증기 개질 반응에 사용되는 펠릿 촉매의 단점인 열 및 물질 전달 제한, 낮은 effectiveness factor, 압력강화와 channeling 등의 문제점을 해결 하고자 모노리스 형태의 금속 구조체 촉매를 본 연구에 적용 하였다. Fecralloy 재질의 금속 구조체에 Ni 촉매를 워시코팅 (wash coating) 하여 제조 하였으며, 이를 천연가스 수증기 개질 반응에 적용하여 수소를 생산하였다. 실험 조건으로는 S/C ratio를 3으로 고정하여 온도를 $600^{\circ}C{\sim}800^{\circ}C$로 변화 시켰으며, GHSV $3000{\sim}30000h^{-1}$에서 진행 되었다. 구조체 촉매 코팅에 사용된 Ni 촉매의 BET, TPR, H2-chemisorption, SEM, EDS의 특성분석을 수행 하였다. 온도별 테스트에서 모노리스 형태의 금속 구조체 촉매가 펠릿 형태의 촉매에 비해 우수한 열전달 효과로 인해 낮은 퍼니스 온도와 높은 반응 활성을 나타내었으며, GHSV 변화에 따른 성능평가 결과도 15wt% $Ni/MgAl_2O_4$펠릿 촉매와 비교하여 금속 구조체 촉매가 높은 활성을 보였다.