• Journal of Magnetics
• /
• v.19 no.1
• /
• pp.5-9
• /
• 2014

The amine functionalized $CoFe_2O_4$ nanoparticles were prepared by thermal decomposition method at reflux temperatures $160^{\circ}C$ and $172^{\circ}C$. The obtained $CoFe_2O_4$ nanoparticles at $160^{\circ}C$ reflux temperature show aggregation free poly-dispersed nanoparticles in 4-15 nm range. In an elevated reflux temperature of $172^{\circ}C$, $CoFe_2O_4$ show aggregated poly-dispersed nanoparticles in the size range of 20-46 nm. The saturation magnetization value at 300 K exhibited 51 emu/g at reflux temperature of $160^{\circ}C$. However, the sample synthesized at an elevated temperature of $172^{\circ}C$ has shown a coercive field value of 560 Oe with saturation magnetization of 68 emu/g.

• Bulletin of the Korean Chemical Society
• /
• v.27 no.2
• /
• pp.237-242
• /
• 2006

$Fe_3O_4$ and $CoFe_2O_4$ magnetic nanoparticles have been synthesized successfully in aqueous solution and coated with oleic acid. The solid and organic solution of the synthesized nanoparticles was obtained. Self-assembled monolayer films were formed using organic solution of these nanoparticles. The crystal sizes determined by Debye-Scherre equation with XRD data were found close to the particle sizes calculated from TEM images, and this indicates that the synthesized particles are nanocrystalline. Especially, EDS, ED, FT-IR, TGA/DTA and DSC were used to characterize the nanoparticles and the oleic acid adsorption, and it was found that oleic acid molecule on the $Fe_3O_4$ nanoparticle is a bilayer adsorption, while that on $CoFe_2O_4$ nanoparticle is single layer adsorption. The superparamagnetic behavior of the nanoparticles was documented by the hysteresis loop measured at 300 K.

• Corrosion Science and Technology
• /
• v.22 no.2
• /
• pp.90-98
• /
• 2023

In this study, cobalt oxide (Co₃O₄) and cobalt-doped magnetite (CoFe₂O₄) nanoparticles were synthesized by a hydrothermal method. They were then used as corrosion inhibitors for corrosion protection of AA2024-T3 aluminum alloys. These obtained nanoparticles were characterized by x-ray diffraction, field-emission scanning electron microscopy, and Zeta potential measurements. Corrosion inhibition activities of Co₃O₄ and CoFe₂O₄ nanoparticles were determined by performing electrochemical measurements for bare AA2024-T3 aluminum alloys in 0.05 M NaCl + 0.1 M Na₂SO₄ solution containing Co₃O₄ or CoFe₂O₄ nanoparticles. Corrosion protection for AA2024-T3 aluminum alloys by a water-based epoxy with or without the synthesized Co₃O₄ or CoFe₂O₄ nanoparticles was investigated by electrochemical impedance spectroscopy during immersion in 0.1 M NaCl solution. The corrosion protection of epoxy coating deposited on the AA2024-T3 surface was improved by incorporating Co₃O₄ or CoFe₂O₄ nanoparticles in the coating. The corrosion protection performance of the epoxy coating containing CoFe₂O₄ was higher than that of the epoxy coating containing Co₃O₄.

• Journal of Magnetics
• /
• v.16 no.2
• /
• pp.164-168
• /
• 2011

Magnetic nanoparticles can potentially be used in drug delivery systems and for hyperthermia therapy. The applicability of $Fe_3O_4$, $CoFe_2O_4$, $MgFe_2O_4$, and $NiFe_2O_4$ nanoparticles for the same was studied by evaluating their magnetization, thermal efficiency, and biocompatibility. $Fe_3O_4$ and $CoFe_2O_4$ nanoparticles exhibited large magnetization. $Fe_3O_4$ and $NiFe_2O_4$ nanoparticles exhibited large induction heating. $MgFe_2O_4$ nanoparticles exhibited low magnetization compared to the other nanoparticles. $NiFe_2O_4$ nanoparticles were found to be cytotoxic, whereas the other nanoparticles were not cytotoxic. This study indicates that $Fe_3O_4$ nanoparticles could be the most suitable ones for hyperthermia therapy.

• Particle and aerosol research
• /
• v.13 no.1
• /
• pp.33-40
• /
• 2017

Cobalt-iron oxides have emerged as alternative electrode materials for supercapacitors because they have advantages of low cost, natural abundance, and environmental friendliness. Graphene loaded with cobalt ferrite ($CoFe_2O_4$) nanoparticles can exhibit enhanced specific capacitance. In this study, we present three-dimensional (3D) crumpled graphene (CGR) decorated with $CoFe_2O_4$ nanoparticles. The $CoFe_2O_4$-graphene composites were synthesized from a colloidal mixture of GO, iron (III) chloride hexahydrate ($FeCl_3{\cdot}6H_2O$) and cobalt chloride hexahydrate ($CoCl_2{\cdot}6H_2O$) respectively, via one step aerosol spray pyrolysis. Size of $CoFe_2O_4$ nanoparticles was ranged from 5 nm to 10 nm when loaded onto 500 nm CGR. The electrochemical performance of the $CoFe_2O_4$-graphene composites was examined. The $CoFe_2O_4$-graphene composite electrode showed the specific capacitance of $253F\;g^{-1}$.

• Journal of the Korean Vacuum Society
• /
• v.10 no.1
• /
• pp.87-92
• /
• 2001

Magnetic Fe-Co(C) nanocapsules and Fe-Co nanoparticles were prepared by arc-discharge in two kinds of atmospheres, i.e. methane and a mixture of ($H_2$+Ar), respectively. Characterization and magnetic properties of this two kinds of ultrafine particles were investigated systematically by means of X-ray diffraction, Mssbauer spectroscopy, X-ray photoelectron spectroscopy, transmission electron microscopy, energy disperse spectroscopy analysis, chemical analysis, oxygen determination and magnetization measurement. Effects of carbon element, decomposed from a methane atmosphere in carbon arc process, on phase structures, magnetic states and surface characterization were studied in comparison to that of Ar element. Two ultrafine particles showed a little difference in the weight ratio of (Fe/co) and the size for Fe-Co nanoparticles was about two times bigger than Fe-Co(C) nanocapsules. The saturation magnetization of Fe-Co (C) nanocapsules was about 8% higher than that of Fe-Co nanoparticles while their phase constitutions were similar. Although no carbon could be detected by XRD measurement because of extremely thin shells on the surfaces of the cores, it is still believed that they are carbon and oxygen layers.

• Journal of the Korean Ceramic Society
• /
• v.47 no.4
• /
• pp.338-342
• /
• 2010

Co, $Fe_3O_4$ and Co/$Fe_3O_4$ nanoparticles were synthesized by a polyol process in order to develop their new applications and improve chemical, magnetic properties. The synthesis involved a polyol process using Fe, Co acetylacetonate as precursors and 1-2 hexadecanediol as the polyol. The synthesized $Fe_3O_4$ and Co/$Fe_3O_4$ nanocomposite particles were monodispersed and self arrayed ranging in size of 8~10 and 10~25 nm, respectively. The Co nanoparticle has a crystallite size of 10~40 nm. The synthesized nanoparticles were characterized by their structural, morphological, compositional and magnetic properties using TEM-EDS, XRD, and PPMS techniques.

• Journal of Magnetics
• /
• v.6 no.3
• /
• pp.94-100
• /
• 2001

Fe-Co-Ni particles with an average size of 45 and 135 nm are characterized in terms of magnetic phase transformation and magnetic properties at room temperature. BCC structure of Fe-Co-Ni spherical particles can be synthesized from Fe-Co-Ni-Al-Cu precursor films by heating at 600-80$0^{\circ}C$ for the phase separation of Fe-Co rich Fe-Co-Ni particles, followed by a post heating at $600^{\circ}C$ for 5 hours. The average size of nanoparticles was directly determined by the thickness of precursor films. Exchange interactive hysteresis was observed for the nano-composite (Fe-Co-Ni)+(Fe-Ni-Al) films resulting from the short exchange interface between ferromagnetic Fe-Co-Ni particles surrounded by almost papramagnetic Ni-Al-Fe matrix. Arraying the isolated Fe-Co-Ni nano-particles in a random arrangement on $Al_2O_3$substrate the particle assembly showed a behavior of dipole interactive ferromagnetic clusters depending on their volume and inter-particle distance.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2014.05a
• /
• pp.148-148
• /
• 2014

• Journal of Magnetics
• /
• v.11 no.3
• /
• pp.123-125
• /
• 2006

Co-ferrite nanoparticles have been synthesized by the decomposition of iron(III) acetylacetonate, $Fe(acac)_3$ and Co acetylacetonate, $Co(acac)_2$ in benzyl/phenyl ether in the presence of oleic acid and oleyl amine at the refluxing temperature of $295^{\circ}C$/$265^{\circ}C$ for 30 min. before cooling to room temperature. Particle diameter detected by PSA can be turned from 4 nm to 20 nm by seed-mediated growth and reaction conditions. Structural and magnetic characterization of Co-ferrite were measured by use of HRTEM, SAED (selected area electron diffraction), XRD and SQUID. The as-synthesized Co-ferrite nanoparticles have a cubic spinel structure and coercivity of 20 nm $CoFe_{2}O_{4} nanoparticles reached 1 kOe at room temperature and 18 kOe at 10 K.