• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.18 no.2
• /
• pp.169-177
• /
• 2020

Here, the stability of stainless steel 316 (SS-316) was investigated to identify its applicability in the oxide reduction process, as a component in related equipment, to produce a complicated gas mixture composed of O₂ and Cl₂ under an argon (Ar) atmosphere. The effects of the mixed gas composition were investigated at flow rates of 30 mL/min O₂, 20 mL/min O₂ + 10 mL/min Cl₂, 10 mL/min O₂ + 20 mL/min Cl₂, and 30 mL/min Cl₂, each at 600℃, during a constant argon flow rate of 170 mL/min. It was found that the corrosion of SS-316 by the chlorine gas was suppressed by the presence of oxygen, while the reaction proceeded linearly with the reaction time regardless of gas composition. Surface observation results revealed an uneven surface with circular pits in the samples that were fed mixed gases. Thermodynamic calculations proposed the combination of Fe and Ni chlorination reactions as an explanation for this pit formation phenomenon. An exponential increase in the corrosion rate was observed with an increase in the reaction temperature in a range of 300 ~ 600℃ under a flow of 30 mL/min Cl₂ + 170 mL/min Ar.

• Journal of Powder Materials
• /
• v.27 no.1
• /
• pp.31-36
• /
• 2020

Phosphorus is an element that plays many important roles in powder metallurgy as an alloy element. The purpose of this study is to investigate the influence of phosphorus addition on the microstructures and mechanical properties of sintered low-alloy steel. The sintered low-alloy steels Fe-0.6%C-3.89%Ni-1.95%Cu-1.40%Mo-xP (x=0, 0.05, 0.10, 0.15, 0.20%) were manufactured by compacting at 700 MPa, sintering in H₂-N₂ at 1260 ℃, rapid cooling, and low-temperature tempering in Ar at 160 ℃. The microstructure, pore, density, hardness, and transverse rupture strength (TRS) of the sintered low-alloy steels were evaluated. The hardness increased as the phosphorus content increased, whereas the density and TRS showed maximum values when the content of P was 0.05%. Based on microstructure observation, the phase of the microstructure changed from bainite to martensite as the content of phosphorus is increased. Hence, the most appropriate addition of phosphorus in this study was 0.05%.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.5
• /
• pp.220-225
• /
• 2011

304 stainless steel plate was colored by hot dip and electrochemical treatment in a solution containing sulphuric and chromic acids. In the process, treatment variables such as operating time and methode were changed. The surface characteristics that changed by the treatment of the samples such as surface composition, oxide film thickness, color, surface roughness and reflectivity were studied. Surface composition was varied as follows. Fe was decreased, but Cr and O were increased. Ni was increased until 20 min, but reveals decreasing tendency as time passed after that. These means the surface film becomes chrome rich oxide phase as the treatment times increase. The thickness of film was about 220 nm at 30 min by dip treatment and it reduced as the treatment times increased. On the other hand, the thickness was about 150 nm at 10 min by electrochemical method and it doesn't increased with time. Surface color changed from metallic white of the base plate to gray, black, red, and green-blue, gradually, as the treating time increased. The reflectivity of colored surface measured by UVVIS-NIR spectrophotometer was reduced from max 38% of basis metal to min 3.5%.

• Journal of Korea Foundry Society
• /
• v.23 no.5
• /
• pp.244-250
• /
• 2003

The aim of this study is fabricating of composite filler metal (CFM) by a combination of selective laser sintering (SLS) of stainless steel powders (RapidSteel $2.0^{TM}$ and liquid phase infiltration of Ag-28 wt.%Cu alloy. Porous stainless steel body with inter-connected pore channels was fabricated by SLS, binder decomposing and densification processes. By the direct contact infiltration, the narrow inter-particle channels of the porous body were completely filled with the Ag-28 wt.%Cu alloy infiltrant. During infiltration, the dissolved elements of Fe, Ni and Cr from the porous body were solved into copper solid solution phases, which consist of eutectic structure of composite metal matrix. The S10C/CFM/S10C joints, which have narrow clearance gaps between them up to 10 micrometers, were joined successfully by self-feeding of filler metal from the matrix of CFM. The CFM kept its original thickness and microstructure after brazing. The tensile strength of brazed specimen was higher than 30 kgf/$mm^2$ and showed a typical ductile fracture mode in the CFM.

• Corrosion Science and Technology
• /
• v.20 no.5
• /
• pp.281-288
• /
• 2021

Due to advancement of the industry, operation of a device in a harsh environment is increasing. Especially, the marine environment contains Cl^- ions which causes localized corrosion such as pitting and crevice corrosion of stainless steel and various metals. In this study, electrochemical corrosion behaviors of austenitic stainless steel (STS 316L) and nickel alloy (Inconel 600) with different seawater concentrations (fresh water, seawater, mixed water) were investigated. The STS 316L and Inconel 600 were etched in 10% oxalic acid and composed of an austenitic phase. Results of Tafel analysis in seawater showed that STS 316L and Inconel 600 presented the highest corrosion current densities of 7.75 × 10^-4 mA/cm² and 1.11 × 10^-4 mA/cm² and the most negative pitting potentials of 0.94 V and 1.06 V, respectively. The maximum damage depths and surface damage ratio by pitting corrosion increased with chloride concentration. The STS 316L had higher PREN than Inconel 600. However, the surface damage and weight loss of Inconel 600 were superior to STS 316L. It was difficult to compare the pitting resistance of STS 316L based on Fe and Inconel 600 based on Ni with PREN simply.

• Korean Journal of Materials Research
• /
• v.12 no.8
• /
• pp.600-607
• /
• 2002

The Ni-Zn synthetic ferrite were acquired from thermally decomposing the metal nitrates Fe(NO$_3$)$_3$.$9H_2$O, Zn($NO_3$)$_2$.$6H_2$O, Ni($NO_3$)$_2$. $6H_2$O, and Cu($NO_3$)$_2$. $3H_2$O at $150^{\circ}C$ for 24 hours and was calcined at $500^{\circ}C$. Each of those was pulverized for 3, 6, 9, and 12 hours in a steel ball mill and was sintered between $700^{\circ}C$ and $1,000^{\circ}C$ for 1 hour, and then their microstructures and electromagnetic properties were examined. We could make the initial specimens chemically bonded in liquid at the temperature as low as $150^{\circ}C$, by using the melting points less than $200^{\circ}C$ of the metal nitrates instead of the mechanical ball milling, then narrowed a distance between the particles into a molecular level, and thus lowed sintering temperature by at least $200^{\circ}C$ to$ 300^{\circ}C$. Their initial permeability was 50 to 400 and their saturation magnetic induction density and coercive force 2,400 G and 0.3 Oe to 0.5 Oe each, which were similar to those of Ni- Zn ferrite synthesized in the conventional process. In the graph of initial permeability vs frequencies, we could observe a $180^{\circ}C$rotation of the magnetic domain, which appears in a broad band of microwave near the resonance frequency.

• Journal of Magnetics
• /
• v.7 no.2
• /
• pp.29-39
• /
• 2002

The initial NiCuZn synthetic ferrite were acquired from thermally decomposing the metal nitrates $Fe(NO_3)_39H_2O, Zn(NO_3)_26H_2O, Ni(NO_3)_26H_2O, and Cu(NO_3)_23H_2O$ at $150^circ{C}$ for 24 hours, and then we calcined the synthetic powder at $500^circ{C}$, pulverized each of those for 3, 6, 9, 12, and 15 hours in a steel ball mill, sintered each at $700^circ{C}$ to $1,000^circ{C}$ for 1 hour, and thus studied their microstructures and electromagnetic properties. We could make the initial specimens chemically bonded in liquidity at a low-temperature $150^circ{C}$, by using the low melting points less than $200^circ{C}$ of the metal nitrates instead of the mechanical ball-mill pulverization, then narrow a distance between the particles into a molecular one, and thus lower the reaction point of sintering by at least $200^circ{C}$ to $300^circ{C}$. Their initial permeability was 50 to 400 and their maximum magnetic induction density and coercive force, 2,400 G and 0.3 Oe to 0.5 Oe respectively, which was similar to those of NiZnCu ferrite synthesized in the conventional process. In the graph of initial permeability by frequencies, a $180^circ{C}$ rotation of the magnetic domains which appears in a broad band of micro-wave before and after the resonance frequency, could be perceived.

• Resources Recycling
• /
• v.12 no.6
• /
• pp.13-18
• /
• 2003

The initial NiCuZn synthetic ferrite were acquired from thermally decomposing the metal nitrates Fe($NO_3$)$_3$ㆍ$9H_2$O, Zn($NO_3$)$_2$ㆍ$6H_2$O, Ni($NO_3$3)$_2$ㆍ $6H_2$O and Cu(NO$_3$)$_2$ㆍ $3H_2$O at 1$50^{\circ}C$ for 24 hours and was calcined at $500^{\circ}C$. Each of those was pulverized for 3 and 9 hours in a steel ball mill and was sintered between $700^{\circ}C$ and $1,000^{\circ}C$ for 1 hour, and then their microstructures and magnetic properties were examined. We could make the initial specimens chemically bonded in liquid at the temperature as low as $150 ^{\circ}C$, by using the melting points less than $ 200^{\circ}C$ of the metal nitrates instead of the mechanical ball milling, then narrowed a distance between the particles into a molecular level, and thus lowed sintering temperature by at least $200 ^{\circ}C$ to $300^{\circ}C$ Their initial permeability was 50 to 490 and their saturation magnetic induction density and coercive force 2,400G and 0.3 Oe to 1.2 Oe each, which were similar to those of NiCuZn ferrite synthesized in the conventional process.

• Journal of Advanced Marine Engineering and Technology
• /
• v.36 no.2
• /
• pp.276-285
• /
• 2012

The objective of this research is to develop the coating technique by a porous self-fluxing alloy for improving the mechanical properties of run-out table roller surface with the hot rolling. To enhance the durability of run-out table roller with the hot rolling, the high hardness of roller surface should be maintained at high temperatures, and the improvement of wear resistance, corrosion resistance, heat resistance, burn resistance and adhesion resistance should be maintained. In order to be able to transport reliably a hot rolled steel sheet, also, the appropriate friction coefficient on the roller surface should be maintained and the slip between roller and steel should not occur. In this study, the wear resistance of roller increases after the self-fluxing alloy is changed to a cermet by adding the tungsten carbide(WC), and the coefficient of friction increases and the ability of grip is improved because the porosities are made by coating with fine iron powder on the roller surface. As a result, it is found that the ability of grip between the steel and the roller coated by a porous self-fluxing alloy contained to 5 ~ 10 wt% of Fe in the coating layer is improved compared to the roller coated by Ni-Cr. This is because the porosities are made after Fe contained in the roller is partially alloyed by heating with a furnace in the fusing process and the rest is eliminated by oxidation and dissolution.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.24 no.3
• /
• pp.314-319
• /
• 2015

Invar is a compound metal of Fe-Ni system contained 36.5% Ni. The characteristic of invar is that the coefficient of thermal expansion is $1.0{\times}10^{-6}cm/^{\circ}C$. It is approximately 10 times smaller than series of steel. Because of this low thermal expansion characteristic of Invar, it is used to shadow mask of display device such as UHDTV or OLED TV. In this study, pulse current from pulse generator instead of DC current is used to overcome the disadvantages of the conventional electrochemical machining. Pulsed current with different duty factor in PECM affect the precise geometry. Pulse electrochemical machining is conducted to machine the micro hole to the invar sheet with different duty factor. The machined shape and overcut of invar sheet with different duty factor is observed by optical microscope and scanning electron microscope (SEM).