• Progress in Superconductivity and Cryogenics
• /
• v.9 no.1
• /
• pp.1-4
• /
• 2007

The total Fluorine content in the precursor solution for MOD processing of YBCO coated conductors can be significantly reduced by synthesizing precursor solution with F-free Y & Cu precursor and Barium trifluoroacetate(TFA). It was shown that crack-free and uniform precursor films were formed after calcinations in humidified oxygen atmosphere. Less than 2 hours are required to finish the calcinations process and XRD measurement shows that $BaF_2,\;CuO,\;Y_2O_3$ are major constituent of calcined precursor films. Film thickness after calcinations was improved to be 2.8um by applying slot-die coating method. In particular, addition of Samarium shows critical current of $I_c=273A/cm-w(J_c=3.8MA/cm^2)$. It is shown that uniform and fast processing route to YBCO coated conductor with high Ic can be provided by employing F-free Y & Cu precursor solution in MOD process.

• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.22-26
• /
• 2006

Total Fluorine content in the precursor solution for MOD processing of YBCO coated conductors can be significantly reduced by synthesizing precursor solution with F-free Y & Cu precursor and Barium trifluoroacetate(TFA). It was shown that crack-free and uniform precursor films were formed after calcinations in humidified oxygen atmosphere. Less than 2 hours are required to finish the calcination process, and XRD measurement shows that $BaF_2,\;CuO,\;and\;Y_2O_3$ are major constituent of calcined precursor films. Film thickness after calcination was measured to be ${\sim}2.8$ um by applying slot-die coating method. In particular, addition of Samarium shows critical current of Ic=226 A/cm-w($Jc=3.4\;MA/cm^2$). Also discussed are recent developments in the reel-to-reel processing using F-free Y & Cu precursor solutions. It is shown that uniform and fast processing route to YBCO coated conductor with high Ic can be provided by employing F-free Y & Cu precursor solutions in MOD process.

• Progress in Superconductivity and Cryogenics
• /
• v.7 no.3
• /
• pp.5-8
• /
• 2005

Superconducting YBCO films were successfully fabricated by MOD process using F-free Cu precursor solution. In this study. a chemically modified precursor solution for MOD Processing was synthesized using metal-organic salts and F-free Cu precursor. It was shown that crack-free and uniform precursor films were formed after calcination in humidified oxygen atmosphere. Less than 3 hours are required to finish the calcination process. XRD measurement shows that $BaF_2,\;CuO,\;Y_2O_3$ are major constituent of precursor films. Furthermore. YBCO films without any secondary phases were successfully fabricated after annealing in wet $Ar/O_2$ prepared on a $LaA1O_3$ single crystal substrate $(10mm{\times}10mm)$ gives transport Ic of 10A at 77K. This chemical modification approach is a possible candidate for improving MOD-processing of YBCO coated conductor.

• Progress in Superconductivity and Cryogenics
• /
• v.8 no.1
• /
• pp.15-18
• /
• 2006

A new precursor solution wilt low fluorine content was synthesized for MOD processing of coated conductors. In this study, the precursor solution for MOD processing was synthesized using F-free yttrium and copper precursor. It was shown that crack-free and uniform precursor films were formed after calcination in humidified oxygen atmosphere. Less than 2 hours were required to finish the calcination process. The relatively gradual weight loss during the calcination process is attributed to the feasibility of fast calcination profile. The calcined precursor film was converted to a YBCO film without any secondary phases after annealing in wet $Ar/O_2$ atmosphere. Fully converted film shows uniform microstructure and high critical current density. $(Jc=2.7MA/cm^2) $.

• 한국초전도학회:학술대회논문집
• /
• v.16
• /
• pp.7-7
• /
• 2006

• Progress in Superconductivity and Cryogenics
• /
• v.8 no.4
• /
• pp.12-14
• /
• 2006

YBCO coated conductors have been fabricated by the reel-to-reel processing using TFA-MOD method. In this work, the fluorine-free Y & Cu precursor solution was synthesized to shorten the calcining time by reducing the evolution of HF gas, thus the meter-long YBCO precursor films can be made within few hours by the continuous slot-die coating & calcination step using the F-free Y & Cu precursor solution. The annealing step was followed to make the YBCO films by the reel-to-reel method with the vertical gas flow system onto the moving tape. To increase the growth rate of the YBCO films by enhancing the removal of HF gas, the low total pressure was adopted in the annealing processing. And the water partial pressure and the oxygen partial pressure were varied to optimize the growth conditions of the MOD-YBCO films on the buffered metal tape. FE-SEM and XRD were used to investigate the surface morphologies and the texture of the meter-long YBCO films. The end-to-end critical current $(I_c)$ of 63A/cm-width and the critical current density $(J_c)$of $0.9MA/cm^2$ with the thickness of $0.7{\mu}m$ were obtained in the 0.42m long coated conductor.

• Progress in Superconductivity
• /
• v.7 no.2
• /
• pp.158-161
• /
• 2006

Superconducting YBCO films were successfully fabricated by MOD process using chemically modified precursor solution. In this study, a chemically modified precursor solution for MOD processing was synthesized using metal-organic salts and organic additives. It was shown that crack-free and uniform precursor films were formed after calcination in humidified Oxygen atmosphere. Less than 3 hours are required to finish the calcination process. XRD measurement shows that $BaF_2,\;CuO,\;Y_2O_3$ are major constituent of precursor films. Furthermore, YBCO films without any secondary phases were successfully fabricated after annealing in wet $Ar/O_2$ atmosphere. The YBCO film prepared on a $LaAlO_3$ single crystal substrate ($10mm{\times}10mm$) gives transport $I_c$ of 10A at 77K. This chemical modification approach is a possible candidate for improving MOD-processing of YBCO coated conductor.

• Progress in Superconductivity and Cryogenics
• /
• v.9 no.1
• /
• pp.14-17
• /
• 2007

The slot-die coating & calcination process was adopted to fabricate the long YBCO precursor films on the buffered metal tape for the $2^{nd}$ generation coated conductors. To obtain the smooth and crack-free surface of long YBCO precursor films, the parameters of slot-die coating and the process variables of calcination step must be optimized simultaneously in reel-to-reel method. Among the parameter of slot-die coating process, the viscosities of the precursor solution was controlled from 60cP to 200cP to obtain the thicker films from on single coating. The slot-die gap, the injection rate of precursor solution, the moving speed of buffered metal tape etc. are controlled lot the full coverage and smooth surface of YBCO precursor films. The slot-die coated films are moved through the tube furnace with predetermined heating profiles in humid oxygen ambient The YBCO precursor films was identifed with $Y_2O_3,\;BaF_2$, and CuO phase by XRD and consisted of fine grains of about 20nm size observed by FE-SEM. The YBCO films show the critical current density over $MA/cm^2$ using the precursor films formed by the continuous slot-die coating & calcination process.

• 한국초전도학회:학술대회논문집
• /
• 2007.07a
• /
• pp.76-76
• /
• 2007

• Progress in Superconductivity and Cryogenics
• /
• v.9 no.2
• /
• pp.23-26
• /
• 2007

The influence of water partial pressure in Metal-organic Deposition (MOD) method was investigated on the texture and the morphology of $YBa_2Cu_3O_{7-x}$ (YBCO) films grown on the buffered metal tapes. The water partial pressure was varied from 4.2% up to 10.0% with the other process variables, such as annealing temperature and oxygen partial pressure, kept constant. In this work, the fluorine-free Y & Cu precursor solution added with Sm was synthesized and coated by the continuous slot-die coating & calcination step. The next annealing step of the YBCO films was done by the reel-to-reel method with the gas flowed vertically down. From the x-ray diffraction analysis, the un-reacted phase like $BaF_2$ peak was found at the water partial pressure of 4.2%, but $BaF_2$ peak intensity is much reduced as the water partial pressure is increased. However, the higher water partial pressure of about 10% in this experiment leads to the poor crystallinity of YBCO films. The morphologies of the YBCO films were not different from each other when the water partial pressure was varied in this work. The maximum critical current density of 3.8MA/$cm^2$ was obtained at the water partial pressure of 6.2% with the annealing temperature of 780$^{\circ}C$ and oxygen partial pressure of 500ppm.