Fabrication of YBCO films in MOD processing via chemically modified precursor solution

화학적으로 변형된 전구용액을 이용한 YBCO 박막 제조

Superconducting YBCO films were successfully fabricated by MOD process using chemically modified precursor solution. In this study, a chemically modified precursor solution for MOD processing was synthesized using metal-organic salts and organic additives. It was shown that crack-free and uniform precursor films were formed after calcination in humidified Oxygen atmosphere. Less than 3 hours are required to finish the calcination process. XRD measurement shows that $BaF_2,\;CuO,\;Y_2O_3$ are major constituent of precursor films. Furthermore, YBCO films without any secondary phases were successfully fabricated after annealing in wet $Ar/O_2$ atmosphere. The YBCO film prepared on a $LaAlO_3$ single crystal substrate ($10mm{\times}10mm$) gives transport $I_c$ of 10A at 77K. This chemical modification approach is a possible candidate for improving MOD-processing of YBCO coated conductor.