• 한국건축시공학회지
• /
• 제4권1호
• /
• pp.85-88
• /
• 2004

The purpose of this study was to design the self-compaction concrete mixture, having not only high strength but also compensation of shrinkage without thermal crack under 4 sides outer restraint of the member. In the experimental mix, replacement ratio of limestone Powder, CSA expansive additives, and unit water were selected as parameters, using portland blast-furnace slag cement. And, bleeding test, expansibility test. hydration heat analysis were performed. As a results, when 35% of limestone Powder, 6% CSA expansive additives are replaced at unit water 175kg/$\textrm{m}^3$, demanded performances of fresh and hardened self-compaction concrete are accomplished.

• 콘크리트학회논문집
• /
• 제16권3호
• /
• pp.369-374
• /
• 2004

$C_4A_3S$ 합성은 천연원료인 석회석과 산업폐기물 및 부산물인 수산화알루미늄, 이수석고를 일정혼합비로 균일하게 혼합하여 20, 400, 600, $1200^{\circ}C$에서 1시간 소성 후 급냉하여 $C_4A_3S$ 클링커를 합성하였다. 합성한 클링커를 보통 포틀랜드 시멘트에 10 wt%치환하여 수중 양생하에서 수화반응 및 물성특성을 조사하였다. $1200^{\circ}C$에서 $C_4A_3S$ 클링커가 합성됨을 X-Ray diffraction pattern으로 관찰할 수 있었다 $1200^{\circ}C$에서 소성된 시료는 급결성을 띠었으며, 압축강도는 보통 포틀랜드 시멘트보다 20~30% 정도 높게 나타났다. 주요 수화생성물은 ettringite, 수산화 칼슘이며, ettringite의 팽창으로 인하여 모르타르의 건조수축이 보통 포틀랜드 시멘트보다는 낮게 나타났다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 봄 학술발표회 논문집(I)
• /
• pp.255-260
• /
• 1998

As a part of the study on the development of augered pile method, this study is intended to investigate the properties of fresh and hardened mortar with the proportion of expansion additives. With the increase of proportion of expansion additives, the fluidity of mortar shows a decrease while air content increases and setting time gets retarded. It show the satisfactory property in strength at 5% of proportion, and shows more expansion with the increase of proportion of expansion additives and sand/cement ratio. In conclusion, both of strength and expansion reveal appropriate at 10% of proportion of expansion additives.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2008년도 추계 학술논문 발표대회
• /
• pp.117-120
• /
• 2008

The Purpose of this is properties of CFT filled with expansion concrete. CFT(concrete filled steel tube) is the structure that circle shape steel column filled with concrete. 3 kinds of expansive additives and variation of replacement rate. we changed expansive additive from 0%, 10%, 20%, 30% of ratio of addition rate are selected for this experiment. Merits of CFT are concrete internal force rising influenced by steel shape restriction, reinforcing the local buckling, excellent resistance to transformation. Generally, High rise building using CFT utilize the high strength and fluidity concrete for packing the tube inside. As the result a steel tube charged expensive concrete has stiffness 1.5times more than a steel tube not charged concrete. Increase of resisting power about compressive stress by binding expansion of expansive concrete affects strength increase and softness.

• 콘크리트학회논문집
• /
• 제18권2호
• /
• pp.205-211
• /
• 2006

본 연구는 팽창재와 수축저감제를 조합 사용하여 수축변형률이 저감된 저수축 고성능 콘크리트에 대하여 내구성을 평가하였다. 그리고 저수축 고성능 콘크리트와 비교를 위해 동일한 물-결합재비에서 팽창재와 수축저감제를 사용하지 않은 고성능 콘크리트와 일반 콘크리트에 대해서도 시험을 실시하였다. 그 결과, 저수축 고성능 콘크리트는 동일한 물-결합재비를 가진 고성능 콘크리트에 비해 압축강도와 인장강도가 다소 크게 나타났다. 염소이온 침투 저항성과 탄산화에 대한 저항성은 고성능 콘크리트와 일반 콘크리트에 비해 우수하며, 동결융해 저항성은 동결융해시험 600사이클에서도 내구성 지수가 거의 100으로 나타났다. 또한 수밀성과 공극분포를 검토한 결과, 저수축 고성능 콘크리트는 고성능 콘크리트 또는 일반 콘크리트에 비해 시멘트 경화체 조직이 치밀해져 내구성이 향상되는 것으로 분석되었다. 따라서 팽창재와 수축저감제를 조합사용한 저수축 고성능 콘크리트를 구조물에 적용한 경우, 콘크리트의 수축과 균열을 저감시킬 수 있을 뿐만 아니라 내구성능이 향상되는 결과를 얻을 수 있을 것으로 분석되었다.

• Geomechanics and Engineering
• /
• 제8권1호
• /
• pp.67-79
• /
• 2015

This article presents the result of laboratory study conducted on expansive soil specimens treated with lignin, rice husk powder (RHP) and rice husk ash (RHA). The amount of lignin produced from paper industry and RHP were varied from 0 to 20% and RHA from 0 to 10% by weight. The treated specimens were subjected to unconfined compressive strength (UCS),swelling test and Atterberg limit tests. The effect of additives on UCS and atterberg limit test results were reported. It was observed that the additives and curing duration had a significant effect on the strength value of treated specimens. Generally (except the sample treated with 20% RHP for 3-day) with increasing additive and curing duration the UCS value increases. A RHP content of 15% was found to be the optimum with regard to 3-day cure UCS.

• 한국세라믹학회지
• /
• 제42권7호
• /
• pp.483-489
• /
• 2005

For the raw materials of 3CaO$\cdot$3Al$_{2}$O$_{3}$ $\cdot$CaSO$_{4}$(CSA) clinker manufacturing, the applications of industrial wastes such as waste shell, spent oil-refining catalyst and desulfurized gypsum were examined. The c1inkerbility of the raw mix and the behaviour of formation of clinker minerals were studied and then some hydraulic properties of cements containing the clinker were also investigated. By virtue of the high reactivity of thermally decomposed raw materials, CSA clinkers were obtained at relatively low temperature of 1250$^{\circ}C$ and thus oil-refining catalysts were more desirable than aluminium hydroxide as an aluminous raw material. The expansive cement samples showed somewhat lower flow value than that of OPC, but their compressive strengths were developed earlier and higher than that of OPC due to formation of ettringite in the early hydration time, which indicated the possibility of practical use of low-cost CSA clinker using industrial wastes only.

• 한국세라믹학회지
• /
• 제44권9호
• /
• pp.529-535
• /
• 2007

Calcium oxide has been used as a demolition agent in fracturing rocks and old concrete structures, etc. With the agent, demolition work can be done in safety without a noise, vibration and any other pollution, since high expansive pressure is obtained gradually by only mixing the agents with water and pouring the slurry into boreholes. But application of the non-explosive demolition agent is a time-consuming job, especially in winter. Essentially, this problem is related to the reaction rate of calcium oxide with water. This study examines the influence of additives such as cement and anhydrite on expansion pressure of calcium oxide at different curing temperatures. The expansion pressure of calcium oxide began to increase steadily with the rise of the curing temperature. When mixing calcium oxide alone with water, blown-out shot occurred. But as additives were added to calcium oxide, the reaction of calcium oxide delayed and the expansion pressure showed gradual increment. Especially, anhydrite showed a superior delaying effect than cement on the reaction of calcium oxide.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 추계 학술발표회 제17권2호
• /
• pp.647-650
• /
• 2005

This paper is to investigate the shrinkage properties of ultra high strength concrete(UHSC) incorporating $5\%$ of expansive additives(EA) along with $1\%$ of shrinkage reducing agent(SRA). UHSC subjected to steam curing and incorporated with steel fiber exhibited higher compressive strength than control UHSC by as much as50MPa at 7days, while at 28days, noticeable change in compressive strength was not observed between UHSC mixtures. Control UHSC subjected to steam curing had a $922{\times}10^6$ of autogenous shrinkage strain value, which was 6.7 times of drying shrinkage strain value at 42 days. The combination of EA and SRA resulted in a decrease in autogenous shrinkage by as much as half of control mixture. Steam curing contributed to the reduction of autogenous shrinkage by as much as $11\%$ compared with that of standard curing.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 봄 학술발표회 논문집
• /
• pp.828-833
• /
• 2003

In this paper, a study on fracture characteristics of chemically prestressed mortar with addition of expansive additives was carried out. Uni-axial tension tests with reinforced mortar specimen restrained by embedded reinforcing bar and three point bending tests with notched steel fiber reinforced beams were carried out to verify the characteristics of the cracking behavior, the tension stiffening effect due to bond between rebar and mortar, and fracture characteristic. Tension stiffening curve for the chemically prestressed mortar was obtained from uni-axial tension test. And increased fracture energy due to the chemical prestress was also obtained from bending test and tension softening curve for chemically prestressed mortar was also obtained.