• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.5
• /
• pp.173-181
• /
• 2015

A stoichiometric mixture of evaporating materials for $BaIn_2S_4$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, $BaIn_2S_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperatures were $620^{\circ}C$ and $420^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by double crystal X-ray diffraction (DCXD). The carrier density and mobility of $BaIn_2S_4$ single crystal thin films measured from Hall effect by van der Pauw method are $6.13{\times}10^{17}cm^{-3}$ and $222cm^2/v{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $BaIn_2S_4$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=3.0581eV-(3.9511{\times}10^{-3}eV/K)T^2/(T+536K)$. The crystal field and the spin-orbit splitting energies for the valence band of the $BaIn_2S_4$ have been estimated to be 182.7 meV and 42.6 meV, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the ${\Delta}so$ definitely exists in the ${\Gamma}_5$ states of the valence band of the $BaIn_2S_4/GaAs$ epilayer. The three photocurrent peaks observed at 10 K are ascribed to the $A_1$-, $B_1$-exciton for n = 1 and $C_{24}$-exciton peaks for n = 24.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.84-84
• /
• 2003

The ZnSe epilayers were grown on the GaAs substrate by hot wall epitaxy. After the ZnSe epilayers treated in the vacuum-, Zn-, and Se-atmosphere, respectively, the defects of the epilayer were investigated by means of the low-temperature photoluminescence measurement. The dominant peaks at 2.7988 eV and 2.7937 eV obtained from the PL spectrum of the as-grown ZnSe epilayer were found to be consistent with the upper and the lower polariton peak of the exciton, I$_2$ (D$^{\circ}$, X), bounded to the neutral donor associated with the Se-vacancy. This donor-impurity binding energy was calculated to be 25.3meV The exciton peak, lid, at 2.7812 eV was confirmed to be bound to the neutral acceptor corresponded with the Zn-vacancy. The I$_1$$\^$d/ peak was dominantly observed in the ZnSe/GaAs:Se epilayer treated in the Se-atmosphere. This Se-atmosphere treatment may convert the ZnSe/GaAs:Se epilayer into the p-type. The SA peak was found to be related to a complex donor like a (V$\sub$se/ - V$\sub$zn/) - V$\sub$zn-/

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.3
• /
• pp.105-110
• /
• 2003

The ZnSe epilayers were grown on the GaAs substrate by hot wall epitaxy. After the ZnSe epilayers treated in the vacuum-, Zn-, and Se-atmosphere, respectively, the defects of the epilayer were investigated by means of the low-temperature photoluminescence measurement. The dominant peaks at 2.7988 eV and 2.7937 eV obtained from the PL spectrum of the as-grown ZnSe epilayer were found to be consistent with the upper and the lower polariton peak of the exciton, $I_{2}$ ($D^{\circ}$, X), bounded to the neutral donor associated with the Se-vacancy. This donor-impurity binding energy was calculated to be 25.3 meV, The exciton peak, $I_{1}^{d}$ at 2.7812 eV was confirmed to be bound to the neutral acceptor corresponded with the Zn-vacancy. The $I_{1}^{d}$ peak was dominantly observed in the ZnSe/GaAs : Se epilayer treated in the Se-atmosphere. This Se-atmosphere treatment may convert the ZnSe/GaAs : Se epilayer into the p-type. The SA peak was found to be related to a complex donor like a $(V_{se}-V_{zn})-V_{zn}$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.25-28
• /
• 2004

Photocurrent spectrum, photoresponse, and I-V measurements were made for close-packed HgTe nanoparticles without organic capping materials to investigate their photocurrent characteristics in the infrared range. In absorption and photoluminescence (PL) spectra taken for the close-packed nanoparticles film, the wavelengths of exciton peaks was red-shifted, compared with organic capped HgTe nanoparticles dispersed in solution. This red-shift is caused by the lessening of the exciton binding energy. The I-V curves and photoresponse for the close-packed nanoparticles film reveal their dark current and fast photoresponse with no current decay, respectively. The observation suggests that the HgTe nanoparticles are a very prospect material applicable for photodetectors in the whole IR range.

• Korean Journal of Crystallography
• /
• v.11 no.3
• /
• pp.137-146
• /
• 2000

The stoichiometric mix of evaporating materials for he CuInS₂ single crystal thin films was prepared. To obtain the single crystal thin films, CuINS₂ mixed crystal was deposited on etched semi-insulator GaAs(100) substrate by the hot wall epitaxy(HWE) system. The source and substrate temperature were 640℃ and 430℃, respectively and the thickness of the single crystal thin films was 2 ㎛. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction(DCXD). The carrier density and mobility deduced from Hall data are 9.64x10/sup 22//㎥ and 2.95x10/sup -2/ ㎡/V·s, respectively at 293 K. he optical energy gap was found to be 1.53 eV at room temperature. From the photocurrent spectrum obtained by illuminating perpendicular light on the c-axis of the thin film, we have found that the values of spin orbit coupling splitting ΔSo and the crystal field splitting ΔCr were 0.0211 eV and 0.0045 eV at 10K, respectively. From PL peaks measured at 10K, were can assign the 807.7 nm (1.5350 eV) peak to E/sub x/ peak of the free exciton emission, the 810.3 nm(1.5301 eV) peak to I₂ peak of donar-bound exciton emission and the 815.6 nm(1.5201 eV) peak to I₁ peak of acceptor-bound excition emission. In addition, the peak observed at 862.0 nm(1.4383 eV) was analyzed to be PL peak due to donor-acceptor pair(DAP).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.11a
• /
• pp.120-123
• /
• 2003

The ZnSe epilayers were grown on the GaAs substrate by hot wall epitaxy. After the ZnSe epilayers treated in the vacuum-, Zn-, and Se-atmosphere, respectively, the defects of the epilayer were investigated by means of the low-temperature photoluminescence measurement. The dominant peaks at 2.7988 eV and 2.7937 eV obtained from the PL spectrum of the as-grown ZnSe epilayer were found to be consistent with the upper and the lower polariton peak of the exciton, $I_2$ ($D^{\circ}$, X), bounded to the neutral donor associated with the Se-vacancy. This donor-impurity binding energy was calculated to be 25.3 meV. The exciton peak, $I_1^d$, at 2.7812 eV was confirmed to be bound to the neutral acceptor corresponded with the Zn-vacancy. The $I_1^d$ peak was dominantly observed in the ZnSe/GaAs:Se epilayer treated in the Se-atmosphere. This Se-atmosphere treatment may convert the ZnSe/GaAs:Se epilayer into the p-type. The SA peak was found to be related to a complex donor like a $(V_{Se}-V_{Zn})-V_{Zn}$.

• Korean Journal of Crystallography
• /
• v.11 no.4
• /
• pp.212-223
• /
• 2000

A stochiometric mix of CuInTe₂ polycrystal was prepared in a honizonatal furnace. To obtain the single crystal thin films, CuInTe₂ mixed crystal was deposited on throughly etched GaAs(100) by the HWE system. The source and substrate temperatures were 610℃ and 450℃ respectively, and the thickness of the deposited single crystal thin film was 2.4㎛. CuInTe₂ single crystal thin film was proved to be the optimal growth condition when the excition emission spectrum was the strongest at 1085.3 nm(1.1424 eV) of photoluminescence spectrum at 10 K, and also FWHM of Double Crystal X-ray Rocking Curve (DCRC) was the smallest, 129 arcsec. The Hall effect on this sample was measured by the method of Van der Pauw, and the carrier density and mobility dependent on temperature were 9.57x10/sup 22/ electron/㎥, 1.31x10/sup -2/㎡/V·s at 293 K, respectively. The ΔCr(Crystal field splitting) and the ΔSo (spin orbit coupling splitting( measured at f10K from the photocurrent peaks in the short wavelength of the CuInTe₂ single crystal thin film were about 0.1200 eV, 0.2833 eV respectively. From the PL spectra of CuInTe₂ single crystal thin film at 10 K, the free exciton (E/sub x/) was determined to be 1064.5 nm(1.1647 eV) and the donor-bound exciton(D/sup 0/, X) and acceptor-bound exciton (A/sup 0/, X) were determined to be 1085.3 nm(1.1424 eV) and 1096.8 nm(1.1304 eV0 respectively. And also, the donor-acciptor pair (DAP)P/sub 0/, DAP-replica P₁, DAP-replica P₂ and self-activated (SA) were determined to be 1131 nm (1.0962 eV), 1164 nm(1.0651 eV), 1191.1 nm(1.0340 eV) and 1618.1 nm (0.7662 eV), respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.230-233
• /
• 2004

The stochiometric mix of evaporating materials for the $CuInS_2$ single crystal thin films was prepared from horizontal furnance. Using extrapolation method of X-ray diffraction patterns for the $CuInS_2$ polycrystal, it was found tetragonal structure whose lattice constant $a_0$ and $c_0$ were $5.524\;{\AA}$ and $11.142\;{\AA}$, respectively. To obtain the single crystal thin films, $CuInS_2$ mixed crystal was deposited on throughly etched semi-insulator GaAs(100) substrate by the hot wall epitaxy (HWE) system. The source and substrate temperature were 640 t and 430 t, respectively and the thickness of the single crystal thin films was $2{\mu}m$. Hall effect on this sample was measured by the method of van dot Pauw and studied on carrier density and temperature dependence of mobility. The carrier density and mobility deduced from Hall data are $9.64{\times}10^{22}/m^3,\;2.95{\times}10^{-2}\;m^2/V{\cdot}s$ at 293 K, respectively The optical energy gaps were found to be 1.53 eV at room temperature. From the photocurrent spectrum by illumination of perpendicular light on the c - axis of the thin film, we have found that the values of spin orbit coupling splitting ${\Delta}So$ and the crystal field splitting ${\Delta}Cr$ were 0.0211 eV and 0.0045 eV at 10 K, respectively. From PL peaks measured at 10K, 807.7nm (1.5350ev) mean Ex peak of the free exciton emission, also 810.3nm (1.5301eV) expresses $I_2$ peak of donor-bound exciton emission and 815.6nm (1.5201eV) emerges $I_1$ peak of acceptor-bound exciton emission. In addition, the peak observed at 862.0nm (1.4383eV) was analyzed to be PL peak due to donor-acceptor pair(DAP).

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.131-133
• /
• 2012

The photoluminescence (PT) properties of Al-doped ZnO thin films grown by the sol-gel dip-coating method have been investigated. At 12 K, nine distinct PL peaks were observed at 2.037, 2.592, 2.832, 3.027, 3.177, 3.216, 3.260, 3.303, and 3.354 eV. The deep-level emissions (2.037, 2.592, 2.832, and 3.027 eV) were attributed to native defects. The near-band-edge (NBE) emission peaks at 3.354, 3.303, 3.260, 3.216, and 3.177 eV were attributed to the emission of the neutral-donor-bound excitons (D0X), two-electron satellite (TES), free-to-neutral-acceptors (e,A0), donor-acceptor pairs (DAP), and second-order longitudinal optical (2LO) phonon replicas of the TES (TES-2LO), respectively. According to Haynes' empirical rule, we calculated the energy of a free exciton (FX) to be 3.374 eV. The thermal activation energy for D0X in the nanocrystalline ZnO thin film was found to be ~25 meV, corresponding to the thermal dissociation energy required for D0X transitions.

• Journal of Sensor Science and Technology
• /
• v.10 no.1
• /
• pp.62-70
• /
• 2001

The ZnSe sample grown by chemical bath deposition (CBD) method were annealed in Ar gas at $45^{\circ}C$. Using extrapolation method of X-ray diffraction pattern, it was found to have zinc blend structure whose lattice parameter $a_o$ was $5.6687\;{\AA}$. From Hall effect, the mobility was likely to be decreased by impurity scattering at temperature range from 10 K to 150 K and by lattice scattering at temperature range from 150 K to 293 K. The band gap given by the transmission edge changed from $2.700{\underline{5}}\;eV$ at 293 K to $2.873{\underline{9}}\;eV$ at 10 K. Comparing photocurrent peak position with transmission edge, we could find that photocurrent peaks due to excition electrons from valence band, ${\Gamma}_8$ and ${\Gamma}_7$ and to conduction band ${\Gamma}_6$ were observed at photocurrent spectrum. From the photocurrent spectra by illumination of polarized light on the ZnSe thin film, we have found that values of spin orbit coupling splitting ${\Delta}so$ is $0.098{\underline{1}}\;eV$. From the PL spectra at 10K, the peaks corresponding to free bound excitons and D-A pair and a broad emission band due to SA is identified. The binding energy of the free excitons are determined to be $0.061{\underline{2}}\;eV$ and the dissipation energy of the donor -bound exciton and acceptor-bound exciton to be $0.017{\underline{2}}\;eV$, $0.031{\underline{0}}\;eV$, respectively.