Hot Wall Epitaxy(HWE) 방법에 의해 성장된 $CuInS_2$

Growth and Characterization of $CuInS_2$ Single Crystal Thin Film by Hot Wall Epitaxy

The stoichiometric mix of evaporating materials for he CuInS₂ single crystal thin films was prepared. To obtain the single crystal thin films, CuINS₂ mixed crystal was deposited on etched semi-insulator GaAs(100) substrate by the hot wall epitaxy(HWE) system. The source and substrate temperature were 640℃ and 430℃, respectively and the thickness of the single crystal thin films was 2 ㎛. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction(DCXD). The carrier density and mobility deduced from Hall data are 9.64x10/sup 22//㎥ and 2.95x10/sup -2/ ㎡/V·s, respectively at 293 K. he optical energy gap was found to be 1.53 eV at room temperature. From the photocurrent spectrum obtained by illuminating perpendicular light on the c-axis of the thin film, we have found that the values of spin orbit coupling splitting ΔSo and the crystal field splitting ΔCr were 0.0211 eV and 0.0045 eV at 10K, respectively. From PL peaks measured at 10K, were can assign the 807.7 nm (1.5350 eV) peak to E/sub x/ peak of the free exciton emission, the 810.3 nm(1.5301 eV) peak to I₂ peak of donar-bound exciton emission and the 815.6 nm(1.5201 eV) peak to I₁ peak of acceptor-bound excition emission. In addition, the peak observed at 862.0 nm(1.4383 eV) was analyzed to be PL peak due to donor-acceptor pair(DAP).